CN107815149A - A kind of height adsorbs inorganic diatomite paint and its preparation technology - Google Patents
A kind of height adsorbs inorganic diatomite paint and its preparation technology Download PDFInfo
- Publication number
- CN107815149A CN107815149A CN201711123979.1A CN201711123979A CN107815149A CN 107815149 A CN107815149 A CN 107815149A CN 201711123979 A CN201711123979 A CN 201711123979A CN 107815149 A CN107815149 A CN 107815149A
- Authority
- CN
- China
- Prior art keywords
- parts
- diatomite
- weight
- mesh
- revs
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention belongs to diatomite paint technical field, more particularly to a kind of height adsorbs inorganic diatomite paint and its preparation technology.Reduced present invention mainly solves diatomite porosity existing for existing diatomite paint, absorption pore plugging, active low technical problem.The present invention is achieved by the following technical solutions：A kind of high inorganic diatomite paint of absorption, it is formulated by the raw material of following weight parts：Granularity is 300~600 parts of the diatomite of 100~150 mesh, granularity is 300~400 mesh 200~400 parts of diatomite, 100~200 parts of the diatomite that granularity is 600~800 mesh, 300~600 parts of deionized water, 10~50 parts of pigment, 100~300 parts of Ludox, 10~20 parts of bentonite, 10~50 parts of wollastonite fibre；Dissolvability solid amount is less than 50mg/L in the deionized water；The Ludox is alkaline silica sol；The bentonite is organic modified bentonite；The granularity of the wollastonite fibre is 100~500 mesh.The present invention has the advantages that energy-conserving and environment-protective, porosity is high, absorption property is good.
Description
Technical field
The invention belongs to diatomite paint technical field, more particularly to a kind of height adsorbs inorganic diatomite paint and its preparation
Technique.
Background technology
Diatomite is widely used in purification of air, food chemistry, pharmaceutical wastewater processing as a kind of natural filtering material
Etc. industry.In recent years, diatomite is even more to be widely used in decoration material field, mainly to purify air, breathing damping and sound-absorbing
Based on decrease of noise functions.In decorative paint products application, to ensure the application property of coating, durability, usability and intensity, can also
High-molecular organic material and inorganic material are added, such as cement, lime, gypsum and acrylic acid rubber powder, color stuffing and auxiliary agent, due to depositing
The reason for the competitive Adsorption, after adding these different materials, diatomite porosity is reduced, and adsorbs pore plugging, and activity is reduced, reached
Less than expected effect, and the addition of organic artificial's high polymer material, new pollution sources are formed, it is influenceed and promotes the use of.
The content of the invention
The shortcomings that it is an object of the invention to overcome prior art, there is provided a kind of height adsorbs inorganic diatomite paint and its system
Standby technique, solve the technology that diatomite porosity existing for existing diatomite paint reduces, absorption pore plugging, activity are low and ask
Topic.
The present invention is achieved by the following technical solutions：
A kind of high inorganic diatomite paint of absorption, it is formulated by the raw material of following weight parts：Granularity is 100~150
300~600 parts of purpose diatomite, 200~400 parts of the diatomite that granularity is 300~400 mesh, the silicon that granularity is 600~800 mesh
100~200 parts of diatomaceous earth, 300~600 parts of deionized water, 10~50 parts of pigment, 100~300 parts of Ludox, bentonite 10~20
Part, 10~50 parts of wollastonite fibre；
Dissolvability solid amount is less than 50mg/L in the deionized water；The Ludox is alkaline silica sol；It is described swollen
It is organic modified bentonite to moisten soil；The granularity of the wollastonite fibre is 100~500 mesh.
A kind of preparation technology of the high inorganic diatomite paint of absorption, comprises the following steps：
1) water that parts by weight are 250~500 parts is added in reactor, paddle is opened, with 400~600 revs/min of speed
Degree is stirred；
2) it is that 100~200 parts of granularities are the diatomite of 600~800 mesh, weight that parts by weight are sequentially added in whipping process
Part be the diatomite of 300~400 mesh for 200~400 parts of granularities, parts by weight be silicon that 300~600 parts of granularities are 100~150 mesh
Diatomaceous earth, it is 400~600 revs/min to keep rotating speed, continues stirring 10~15 minutes；
3) Ludox that parts by weight are 100~300 parts is added, adjusts mixing speed to 600~800 revs/min, stirring 5~
10 minutes；
4) wollastonite fibre that parts by weight are 10~50 parts is added, adjustment mixing speed is to 400~600 revs/min, stirring 5
~10 minutes；
5) pigment that parts by weight are 10~50 parts is added, is stirred 5~10 minutes with 400~600 revs/min of mixing speed；
6) water that parts by weight are 50~100 parts is added in Scattered Kettle, scattered leaf is opened, with 600~800 revs/min of speed
Degree is stirred, and the bentonite that parts by weight are 10~20 parts is added in its whipping process, rotating speed is adjusted extremely after the completion of addition
1500~1800 revs/min, inorganic gel is made after disperseing 25~30 minutes at a high speed；
7) obtained inorganic gel in step 6) is added in stirred tank, thickening processing is carried out to the material in step 5),
400~600 revs/min of rotating speed is kept to stir after the completion of addition 5~10 minutes, you can be made high and adsorb inorganic diatomite paint.
The present invention first makes its complete adsorption saturation with Enough Dl water infiltration natural diatomaceous earth, plays occupy-place effect, with
Avoid impurity from polluting it, then add the raw material such as Ludox material adhesive, wollastonite fibre, bentonite, pigment, so
Maximum activity and absorption property that diatomite has after the drying are may insure, coating purification of air speed and effect can be effectively improved
Rate；Ludox and diatomaceous main component are all silica, and after coating is constructed onto base material, the water in coating separates
Begin to volatilize, Ludox dries out, and monomeric silicic acid gradually polymerize, with moisture evaporation, colloid molecules increase, silicon dioxide granule
Between form firm silicon oxygen bond, then formed silica chain network structure, turn into continuous paint film；With the further volatilization of moisture,
Moisture in diatomite porous structure is cleared and restored to the original state, and is provided with absorption and the effect of degraded harmful substance again.
Compared with prior art, the present invention has the advantages that energy-conserving and environment-protective, porosity is high, absorption property is good.
Embodiment
Technical scheme is clearly and completely described below in conjunction with embodiment.
Embodiment 1
The high inorganic diatomite paint of absorption of one kind in the present embodiment, it is formulated by the raw material of following weight parts：Grain
Spend 300 parts of the diatomite for 100~150 mesh, 200 parts of the diatomite that granularity is 300~400 mesh, granularity are 600~800 purposes
100 parts of diatomite, 300 parts of deionized water, 10 parts of pigment, 100 parts of Ludox, 10 parts of bentonite, 10 parts of wollastonite fibre；
Dissolvability solid amount is less than 50mg/L in the deionized water；The Ludox is alkaline silica sol；It is described swollen
It is organic modified bentonite to moisten soil；The granularity of the wollastonite fibre is 100~500 mesh.
A kind of preparation technology of the high inorganic diatomite paint of absorption, comprises the following steps：
1) water that parts by weight are 250 parts is added in reactor, opens paddle, stirred with 400 revs/min of speed
Mix；
2) sequentially added in whipping process parts by weight be 100 parts of granularities be the diatomite of 600~800 mesh, parts by weight be
200 parts of granularities are the diatomite of 300~400 mesh, parts by weight are diatomite that 300 parts of granularities are 100~150 mesh, keep rotating speed
For 400 revs/min, continue stirring 10 minutes；
3) Ludox that parts by weight are 100 parts is added, adjustment mixing speed stirs 5~10 minutes to 600 revs/min；
4) wollastonite fibre that parts by weight are 10 parts is added, adjustment mixing speed stirs 5 minutes to 400 revs/min；
5) pigment that parts by weight are 10 parts is added, is stirred 5 minutes with 400 revs/min of mixing speed；
6) water that parts by weight are 50 parts is added in Scattered Kettle, opens scattered leaf, be stirred with 600 revs/min of speed,
The bentonite that parts by weight are 10 parts is added in its whipping process, rotating speed is adjusted after the completion of addition to 1500 revs/min, it is scattered at a high speed
Inorganic gel is made after 25 minutes；
7) obtained inorganic gel in step 6) is added in stirred tank, thickening processing is carried out to the material in step 5),
400 revs/min of rotating speed is kept to stir after the completion of addition 5 minutes, you can be made high and adsorb inorganic diatomite paint.
Embodiment 2
The high inorganic diatomite paint of absorption of one kind in the present embodiment, it is formulated by the raw material of following weight parts：Grain
Spend 600 parts of the diatomite for 100~150 mesh, 400 parts of the diatomite that granularity is 300~400 mesh, granularity are 600~800 purposes
200 parts of diatomite, 600 parts of deionized water, 50 parts of pigment, 300 parts of Ludox, 20 parts of bentonite, 50 parts of wollastonite fibre；
Dissolvability solid amount is less than 50mg/L in the deionized water；The Ludox is alkaline silica sol；It is described swollen
It is organic modified bentonite to moisten soil；The granularity of the wollastonite fibre is 100~500 mesh.
A kind of preparation technology of the high inorganic diatomite paint of absorption, comprises the following steps：
1) water that parts by weight are 500 parts is added in reactor, opens paddle, stirred with 600 revs/min of speed
Mix；
2) sequentially added in whipping process parts by weight be 200 parts of granularities be the diatomite of 600~800 mesh, parts by weight be
400 parts of granularities are the diatomite of 300~400 mesh, parts by weight are diatomite that 600 parts of granularities are 100~150 mesh, keep rotating speed
For 600 revs/min, continue stirring 15 minutes；
3) Ludox that parts by weight are 300 parts is added, adjustment mixing speed stirs 10 minutes to 800 revs/min；
4) wollastonite fibre that parts by weight are 50 parts is added, adjustment mixing speed stirs 10 minutes to 600 revs/min；
5) pigment that parts by weight are 50 parts is added, is stirred 10 minutes with 600 revs/min of mixing speed；
6) water that parts by weight are 100 parts is added in Scattered Kettle, opens scattered leaf, stirred with 800 revs/min of speed
Mix, the bentonite that parts by weight are 20 parts is added in its whipping process, rotating speed is adjusted after the completion of addition to 1800 revs/min, at a high speed
Inorganic gel is made after scattered 30 minutes；
7) obtained inorganic gel in step 6) is added in stirred tank, thickening processing is carried out to the material in step 5),
600 revs/min of rotating speed is kept to stir after the completion of addition 10 minutes, you can be made high and adsorb inorganic diatomite paint.
Embodiment 3
The high inorganic diatomite paint of absorption of one kind in the present embodiment, it is formulated by the raw material of following weight parts：Grain
Spend 450 parts of the diatomite for 100~150 mesh, 300 parts of the diatomite that granularity is 300~400 mesh, granularity are 600~800 purposes
150 parts of diatomite, 400 parts of deionized water, 30 parts of pigment, 200 parts of Ludox, 15 parts of bentonite, 30 parts of wollastonite fibre；
Dissolvability solid amount is less than 50mg/L in the deionized water；The Ludox is alkaline silica sol；It is described swollen
It is organic modified bentonite to moisten soil；The granularity of the wollastonite fibre is 100~500 mesh.
A kind of preparation technology of the high inorganic diatomite paint of absorption, comprises the following steps：
1) water that parts by weight are 325 parts is added in reactor, opens paddle, stirred with 500 revs/min of speed
Mix；
2) sequentially added in whipping process parts by weight be 150 parts of granularities be the diatomite of 600~800 mesh, parts by weight be
300 parts of granularities are the diatomite of 300~400 mesh, parts by weight are diatomite that 450 parts of granularities are 100~150 mesh, keep rotating speed
For 500 revs/min, continue stirring 12 minutes；
3) Ludox that parts by weight are 200 parts is added, adjustment mixing speed stirs 8 minutes to 700 revs/min；
4) wollastonite fibre that parts by weight are 30 parts is added, adjustment mixing speed stirs 8 minutes to 500 revs/min；
5) pigment that parts by weight are 30 parts is added, is stirred 8 minutes with 500 revs/min of mixing speed；
6) water that parts by weight are 75 parts is added in Scattered Kettle, opens scattered leaf, be stirred with 700 revs/min of speed,
The bentonite that parts by weight are 15 parts is added in its whipping process, rotating speed is adjusted after the completion of addition to 1600 revs/min, it is scattered at a high speed
Inorganic gel is made after 26 minutes；
7) obtained inorganic gel in step 6) is added in stirred tank, thickening processing is carried out to the material in step 5),
500 revs/min of rotating speed is kept to stir after the completion of addition 7 minutes, you can be made high and adsorb inorganic diatomite paint.
The present invention can be embodied without departing from the spiritual or substantive of invention in a variety of forms, it should therefore be appreciated that on
State embodiment and be not limited to foregoing details, and should widely be explained in the range of claim limits, therefore fall into right and want
Ask or the change in its equivalent scope and remodeling all should be claim and covered.
Claims (2)
- A kind of 1. high inorganic diatomite paint of absorption, it is characterised in that：It is formulated by the raw material of following weight parts：Granularity is 300~600 parts of the diatomite of 100~150 mesh, 200~400 parts of the diatomite that granularity is 300~400 mesh, granularity be 600~ 100~200 parts of the diatomite of 800 mesh, 300~600 parts of deionized water, 10~50 parts of pigment, 100~300 parts of Ludox, swelling Native 10~20 parts, 10~50 parts of wollastonite fibre；Dissolvability solid amount is less than 50mg/L in the deionized water；The Ludox is alkaline silica sol；The bentonite For organic modified bentonite；The granularity of the wollastonite fibre is 100~500 mesh.
- A kind of 2. preparation technology of the inorganic diatomite paint of absorption high as defined in claim 1, it is characterised in that：Including Following steps：1) water that parts by weight are 250~500 parts is added in reactor, opens paddle, the speed with 400~600 revs/min is entered Row stirring；2) sequentially added in whipping process parts by weight be 100~200 parts of granularities be the diatomite of 600~800 mesh, parts by weight be 200~400 parts of granularities are the diatomite of 300~400 mesh, parts by weight are diatom that 300~600 parts of granularities are 100~150 mesh Soil, it is 400~600 revs/min to keep rotating speed, continues stirring 10~15 minutes；3) Ludox that parts by weight are 100~300 parts is added, adjustment mixing speed stirs 5~10 points to 600~800 revs/min Clock；4) wollastonite fibre that parts by weight are 10~50 parts is added, adjustment mixing speed is to 400~600 revs/min, stirring 5~10 Minute；5) pigment that parts by weight are 10~50 parts is added, is stirred 5~10 minutes with 400~600 revs/min of mixing speed；6) water that parts by weight are 50~100 parts is added in Scattered Kettle, opens scattered leaf, the speed with 600~800 revs/min is entered Row stirring, it is 10~20 parts of bentonite to add parts by weight in its whipping process, adjusted after the completion of addition rotating speed to 1500~ 1800 revs/min, inorganic gel is made after disperseing 25~30 minutes at a high speed；7) obtained inorganic gel in step 6) is added in stirred tank, thickening processing is carried out to the material in step 5), added After the completion of keep 400~600 revs/min of rotating speed to stir 5~10 minutes, you can be made high and adsorb inorganic diatomite paint.