CN107815100A - A kind of preparation method of Nylon for Automobile fan material - Google Patents
A kind of preparation method of Nylon for Automobile fan material Download PDFInfo
- Publication number
- CN107815100A CN107815100A CN201711065368.6A CN201711065368A CN107815100A CN 107815100 A CN107815100 A CN 107815100A CN 201711065368 A CN201711065368 A CN 201711065368A CN 107815100 A CN107815100 A CN 107815100A
- Authority
- CN
- China
- Prior art keywords
- nylon
- preparation
- automobile fan
- fan material
- material according
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of preparation method of Nylon for Automobile fan material, including:(1) silane coupler is added in the nylon base-material containing auxiliary agent and carries out coupling processing, be sent into electronics Weightlessness balance;(2) toughener is sent into another electronics Weightlessness balance and distinguishes blanking with the nylon base-material after coupling processing, added alkali-free glass fibre blending extrusion while being sent into dual-screw-stem machine outside and be granulated, produce.The present invention improves the combination compatibility between glass fibre, and the blanking in bielectron Weightlessness balance, ensures that blending is granulated uniform and stable, being granulated than traditional-handwork stirring blanking has better performance quality by carrying out coupling processing on nylon base-material surface.
Description
Technical field
The invention belongs to automobile component field, more particularly to a kind of preparation method of Nylon for Automobile fan material.
Background technology
Domestic Automotive Industry flourishes in recent years, turns into Global Auto production and marketing big country, as petroleum resources are nervous, oil price
Rise steadily, automotive light weight technology turns into the key subjects of China Automobile Industry, and the application of engineering plastics is automotive light weight technology
Inevitable choice.Plasticization of Automobile degree shows industry manufacture level.Foreign Automobile inner and outer decorative parts are all using working of plastics.Automobile using
Plastics are more than 160 kilograms/.The exploitation and application of nonmetal structure part are carried forward vigorously in recent years, with metal phase ratio, engineering plastic
Many advantages, such as material has light specific gravity, corrosion-resistant, easy-formation, is especially suitable for maker complex component, and production efficiency is high.As
Automobile structure engineering plastics, it is largely glass or the fine enhancing modification of nylon of carbon.Glass fiber enhanced nylon has intensity high, resistance to
The features such as warm nature can be good, moderate.
Cooling fan is one of critical component for ensureing automotive safety operation.Technique mistake is removed using metal manufacture cooling fan
Journey is complicated, and low into production efficiency, metal fan easily gets rusty, weight is big.With fiberglass reinforced PP manufacture cooling fan can realize once into
Type, and the performance such as corrosion-resistant, high temperature resistant, impact strength, flexural strength is good, meets automobile requirement.But PP and glass
Consistency problem between fibre be present, influence the performance quality of final products.
The content of the invention
The technical problems to be solved by the invention are to provide a kind of preparation method of Nylon for Automobile fan material, this method
By carrying out coupling processing on nylon base-material surface, the combination compatibility between glass fibre is improved, and lose in electronics
Blanking in weight scale, ensure that blending is granulated uniform and stable, being granulated than traditional-handwork stirring blanking has better performance quality.
The invention provides a kind of preparation method of Nylon for Automobile fan material, including:
(1) add silane coupler by the 1-2% of base-material quality in the nylon base-material containing auxiliary agent and carry out coupling processing, send
Enter electronics Weightlessness balance;
(2) toughener is sent into another electronics Weightlessness balance with the nylon base-material after coupling processing by 5-10%:90-95%'s
Ratio distinguishes blanking, adds alkali-free glass fibre blending extrusion while being sent into dual-screw-stem machine outside and is granulated, produces Nylon for Automobile
Fan material.
The lubrication of filler of the auxiliary agent including 5-30%, 0.1-0.5% age resisters and 0.1-1% in the step (1)
Agent.
The filler is platy talc, and mesh number is 2000-3000 mesh.
The toughness reinforcing compatilizer is the thermoplastic elastomer (TPE) maleic anhydride grafted polymer of ethene and octene in-situ polymerization.
The filler and auxiliary agent are previously added homogenizer and are stirred 15-30min in 50-70 DEG C with nylon base-material.
Silane coupler in the step (1) is isobutyl triethoxy silane, gamma-aminopropyl-triethoxy-silane,
Vinyltrimethoxy silane, vinyl trichlorosilane, 3- mercaptopropyltriethoxysilanes, 3- (methacryloxypropyl) propyl group three
One or more in methoxy silane.
Toughener in the step (2) is ethylene-octene copolymer POE, SBS elastomer
SBS, at least one of the terpolymer EPDM, ethylene-vinyl acetate EVA of ethene, propylene and alkadienes maleic acid
Acid anhydride graft polymers.
The addition of alkali-free glass fibre in the step (2) is total prescription quality (i.e. toughener and nylon base-material
Gross mass) 20-25%.
The rotating speed of dual-screw-stem machine in the step (2) is 300-350rpm, and temperature is 235-255 DEG C.
Feed proportioning uses automatic material-dispensing system dispensing.
Beneficial effect
(1) present invention improves the combination phase between glass fibre by carrying out coupling processing on nylon base-material surface
Capacitive;
(2) blanking of the invention in bielectron Weightlessness balance, ensure that blending is granulated uniform and stable, under being stirred than traditional-handwork
Material, which is granulated, has better performance quality;
(3) automatic material-dispensing system of the present invention carries out dispensing, ensures that formula materials processing is accurate, is turned into efficiently and continuously
Industry, while greatly reduce cost of labor.
Embodiment
With reference to specific embodiment, the present invention is expanded on further.It should be understood that these embodiments are merely to illustrate the present invention
Rather than limitation the scope of the present invention.In addition, it is to be understood that after the content of the invention lectured has been read, people in the art
Member can make various changes or modifications to the present invention, and these equivalent form of values equally fall within the application appended claims and limited
Scope.
Embodiment 1
(1) homogenizer and nylon base-material are added in 10% 2000 mesh platy talcs, the ratio that remaining is auxiliary agent
15min is stirred in 70 DEG C, adding gamma-aminopropyl-triethoxy-silane by the 1% of base-material quality carries out coupling processing, is sent into
Electronics Weightlessness balance;
(2) ethylene-octene copolymer POE maleic anhydride grafted polymers are sent into another electronics Weightlessness balance and coupling processing
Nylon base-material afterwards presses 5%:95% ratio difference blanking, 20% alkali-free glass fibre is added while being sent into dual-screw-stem machine outside
Tie up blending extrusion to be granulated, the rotating speed of dual-screw-stem machine is 300rpm, and temperature is 235-245 DEG C, produces Nylon for Automobile fan material.
The mechanical property of material
Embodiment 2
(1) in 5% 2000 mesh platy talcs, remaining for the ratio of auxiliary agent add homogenizer and nylon base-material in
50 DEG C are stirred 30min, and adding isobutyl triethoxy silane by the 2% of base-material quality carries out coupling processing, is sent into electronics
Weightlessness balance;
(2) SBS elastomer SBS maleic anhydride grafted polymers are sent into another electronics weightlessness
Scale presses 10% with the nylon base-material after coupling processing:90% ratio difference blanking, is added outside while being sent into dual-screw-stem machine
25% alkali-free glass fibre blending extrusion is granulated, and the rotating speed of dual-screw-stem machine is 350rpm, and temperature is 245-255 DEG C, produces vapour
Automobile-used nylon fan material.
The mechanical property of material
Claims (10)
1. a kind of preparation method of Nylon for Automobile fan material, including:
(1) add silane coupler by the 1-2% of base-material quality in the nylon base-material containing auxiliary agent and carry out coupling processing, be sent into electricity
Sub- Weightlessness balance;
(2) toughener is sent into another electronics Weightlessness balance with the nylon base-material after coupling processing by 5-10%:90-95% ratio
Blanking respectively, alkali-free glass fibre blending extrusion is added while being sent into dual-screw-stem machine outside and is granulated, produces Nylon for Automobile fan
Material.
A kind of 2. preparation method of Nylon for Automobile fan material according to claim 1, it is characterised in that:The step
(1) lubricant of filler of the auxiliary agent including 5-30%, 0.1-0.5% age resisters and 0.1-1% in.
A kind of 3. preparation method of Nylon for Automobile fan material according to claim 2, it is characterised in that:The filler
For platy talc, mesh number is 2000-3000 mesh.
A kind of 4. preparation method of Nylon for Automobile fan material according to claim 2, it is characterised in that:The toughness reinforcing
Compatilizer is the thermoplastic elastomer (TPE) maleic anhydride grafted polymer of ethene and octene in-situ polymerization.
A kind of 5. preparation method of Nylon for Automobile fan material according to claim 2, it is characterised in that:The filler
Homogenizer, which is previously added, with auxiliary agent is stirred 15-30min in 50-70 DEG C with nylon base-material.
A kind of 6. preparation method of Nylon for Automobile fan material according to claim 1, it is characterised in that:The step
(1) silane coupler in is isobutyl triethoxy silane, gamma-aminopropyl-triethoxy-silane, vinyl trimethoxy silicon
One in alkane, vinyl trichlorosilane, 3- mercaptopropyltriethoxysilanes, 3- (methacryloxypropyl) propyl trimethoxy silicane
Kind is a variety of.
A kind of 7. preparation method of Nylon for Automobile fan material according to claim 1, it is characterised in that:The step
(2) toughener in is ethylene-octene copolymer POE, SBS elastomer SBS, ethene, propylene and two
At least one of the terpolymer EPDM, ethylene-vinyl acetate EVA of alkene maleic anhydride grafted polymer.
A kind of 8. preparation method of Nylon for Automobile fan material according to claim 1, it is characterised in that:The step
(2) addition of the alkali-free glass fibre in is the 20-25% of total prescription quality.
A kind of 9. preparation method of Nylon for Automobile fan material according to claim 1, it is characterised in that:The step
(2) rotating speed of the dual-screw-stem machine in is 300-350rpm, and temperature is 235-255 DEG C.
A kind of 10. preparation method of Nylon for Automobile fan material according to claim 1, it is characterised in that:Raw material is matched somebody with somebody
Material uses automatic material-dispensing system dispensing.