CN107793638A - Mothproof plastic woven bag - Google Patents
Mothproof plastic woven bag Download PDFInfo
- Publication number
- CN107793638A CN107793638A CN201711049185.5A CN201711049185A CN107793638A CN 107793638 A CN107793638 A CN 107793638A CN 201711049185 A CN201711049185 A CN 201711049185A CN 107793638 A CN107793638 A CN 107793638A
- Authority
- CN
- China
- Prior art keywords
- parts
- woven bag
- bag
- mothproof
- plastic woven
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a mothproof plastic woven bag which comprises 100 parts of polypropylene, 50 parts of linear low-density polyethylene, 20 parts of polystyrene, 10 parts of aniline methyl triethoxysilane, 5 parts of limestone, 2 parts of epoxy resin, 0.5 part of decabromodiphenyl ether, 5 parts of an auxiliary agent and 5 parts of an additive master batch.
Description
Technical field
The present invention relates to a kind of Anti-moth-eating Polywoven Bag.
Background technology
Polywoven Bag is configured to Polypropylene Bag, Polythene Bag by main material；It is divided into seam bottom bag, tape edge by method of sewing
Bottom bag.It is now widely used for a kind of packaging material of fertilizer, chemical products and other items.It is now widely used for fertilizer, chemical industry
A kind of packaging material of product and other items.It is deposited in storehouse and is easy to be broken by insect bite and caused content to spill.
The content of the invention
In view of the deficienciess of the prior art, it is an object of the present invention to provide a kind of Anti-moth-eating Polywoven Bag, with solution
State the problem of being proposed in background technology.
The present invention solves its technical problem and is achieved through the following technical solutions：
A kind of Anti-moth-eating Polywoven Bag, including 100 parts of polypropylene, 50 parts of LLDPE, polystyrene 20
Part, 10 parts of anilinomethyl triethoxysilane, 5 parts of lime stone, 2 parts of epoxy resin, 0.5 part of deca-BDE, 5 parts of auxiliary agent, add
Add 5 parts of masterbatch.
The preparation method of the Anti-moth-eating Polywoven Bag is specific as follows：
Ith, by 100 parts of polypropylene, 50 parts of LLDPE, 20 parts of polystyrene, anilinomethyl triethoxysilicane
5 parts 10 parts of alkane, 5 parts of lime stone, 2 parts of epoxy resin, 0.5 part of deca-BDE, 5 parts of auxiliary agent, addition of masterbatch sequentially add mixing
In machine, it is well mixed at being 79 DEG C in temperature, obtains mixture；
IIth, mixture is added in extruder with 100kg/min charging rate and extruded, is then cooled and shaped,
Obtain producing the coating woven cloth of woven bag；
IIIth, first by the preheating temperature of preheating roller tube to 85 DEG C, the temperature of cooling stick is adjusted to 25 DEG C, then with membrana oralis to life
The coating woven cloth for the production woven bag that step II obtains is put into screw rod for 120mm and squeezed by the coating woven cloth gap of production woven bag
Go out in machine and extruded, obtain the flat filament of woven bag coated cloth；
IVth, the flat filament for the woven bag coated cloth that step III obtains is compiled using flat die technique using cylindrical knitting machine
Knit, then in turn through cutting, severing and sewing, that is, obtain Polywoven Bag.
The auxiliary agent is made from the following raw materials in parts by weight：Phthalic acid ester 40%, clay 20%, alum 15%, rush
Enter agent DM 5%, hexanediyl ester 5%, crosslinking agent TAC5%, antioxidant 1010 4%, actinolite 4%, ferrocene
3%th, vanadium diboride 2%
The auxiliary agent preparation method is to be sent into calcining furnace and calcine 2.5 hours at 735 DEG C clay, actinolite, then,
Take out, be sent into 20% sulfuric acid solution and soak 1.5 hours, filter, obtain filter residue, cleaned with clear water, dry, be ground into 350 mesh
Powder；Gained powder mixes with other residual components, is heated to 65 DEG C, stirring reaction 40-50 minutes, cooling, is ground into slurry,
Produce.
The present invention has the beneficial effect that：
The present invention extends the service life of woven bag and improves tensile property, can effectively prevent and treat and damage by worms, woven bag is not easy always
Change, service life length, tensile force is high so that the article of loading is not likely to produce putrid and deteriorated, and cracky, does not extend making for woven bag
With the life-span and improve tensile property.
Embodiment
The present invention will be described in detail below.
Embodiment：
A kind of Anti-moth-eating Polywoven Bag, including 100 parts of polypropylene, 50 parts of LLDPE, polystyrene 20
Part, 10 parts of anilinomethyl triethoxysilane, 5 parts of lime stone, 2 parts of epoxy resin, 0.5 part of deca-BDE, 5 parts of auxiliary agent, add
Add 5 parts of masterbatch.
The preparation method of the Anti-moth-eating Polywoven Bag is specific as follows：
Ith, by 100 parts of polypropylene, 50 parts of LLDPE, 20 parts of polystyrene, anilinomethyl triethoxysilicane
5 parts 10 parts of alkane, 5 parts of lime stone, 2 parts of epoxy resin, 0.5 part of deca-BDE, 5 parts of auxiliary agent, addition of masterbatch sequentially add mixing
In machine, it is well mixed at being 79 DEG C in temperature, obtains mixture；
IIth, mixture is added in extruder with 100kg/min charging rate and extruded, is then cooled and shaped,
Obtain producing the coating woven cloth of woven bag；
IIIth, first by the preheating temperature of preheating roller tube to 85 DEG C, the temperature of cooling stick is adjusted to 25 DEG C, then with membrana oralis to life
The coating woven cloth for the production woven bag that step II obtains is put into screw rod for 120mm and squeezed by the coating woven cloth gap of production woven bag
Go out in machine and extruded, obtain the flat filament of woven bag coated cloth；
IVth, the flat filament for the woven bag coated cloth that step III obtains is compiled using flat die technique using cylindrical knitting machine
Knit, then in turn through cutting, severing and sewing, that is, obtain Polywoven Bag.
The auxiliary agent is made from the following raw materials in parts by weight：Phthalic acid ester 40%, clay 20%, alum 15%, rush
Enter agent DM 5%, hexanediyl ester 5%, crosslinking agent TAC5%, antioxidant 1010 4%, actinolite 4%, ferrocene
3%th, vanadium diboride 2%.
The auxiliary agent preparation method is to be sent into calcining furnace and calcine 2.5 hours at 735 DEG C clay, actinolite, then,
Take out, be sent into 20% sulfuric acid solution and soak 1.5 hours, filter, obtain filter residue, cleaned with clear water, dry, be ground into 350 mesh
Powder；Gained powder mixes with other residual components, is heated to 65 DEG C, stirring reaction 40-50 minutes, cooling, is ground into slurry,
Produce.
Although disclosing embodiments of the invention for the purpose of illustration, it will be appreciated by those skilled in the art that：Not
Depart from the present invention and spirit and scope of the appended claims in, it is various replace, change and modifications all be it is possible, therefore, this
The scope of invention is not limited to embodiment disclosure of that.
Claims (1)
1. a kind of Anti-moth-eating Polywoven Bag, it is characterised in that including 100 parts of polypropylene, 50 parts of LLDPE, gather
20 parts of styrene, 10 parts of anilinomethyl triethoxysilane, 5 parts of lime stone, 2 parts of epoxy resin, 0.5 part of deca-BDE, help
5 parts 5 parts of agent, addition of masterbatch.