CN107778705A - A kind of PVC calcium modeling flooring material and preparation method thereof - Google Patents
A kind of PVC calcium modeling flooring material and preparation method thereof Download PDFInfo
- Publication number
- CN107778705A CN107778705A CN201610784652.8A CN201610784652A CN107778705A CN 107778705 A CN107778705 A CN 107778705A CN 201610784652 A CN201610784652 A CN 201610784652A CN 107778705 A CN107778705 A CN 107778705A
- Authority
- CN
- China
- Prior art keywords
- parts
- pvc
- flooring material
- calcium
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a kind of PVC calcium modeling flooring material and preparation method thereof, by weight, flooring material raw material is made up of following component：30 parts of PVC resin powder, 30 50 parts of PVC regenerating resins powder, 30 50 parts of powdered whiting, 20 40 parts of 100 mesh kaolin, dialkyl group are to 8 12 parts of biphenol, 35 parts of barium ferrite, 35 parts of calcium stearate, 2 parts of caprolactam, present invention also offers PVC calcium modeling flooring material and preparation method thereof, above-mentioned formula combination preparation method solves the problems, such as that existing calcium modeling flooring material texture is poor, non-skid property is bad.
Description
Background technology
Calcic-plastic composite material is using inorganic calcium salt as primary raw material, is equipped with the synthetic resin such as few TPO most and is kneaded what is formed
A kind of composite.With chemical stability, high-low temperature resistant, there are good thermal insulation, water resistance, there is good anti-flammability, its
Burning velocity is slow, and smoke is few, not fire hazardous, public hazards.It is widely used as construction material, fitment material for family, furniture and commodity material
Material etc., existing calcium mould flooring material, while above-mentioned advantage is possessed, the problem of texture is poor, non-skid property is bad be present.
The content of the invention
The technical problems to be solved by the invention are that providing a kind of PVC calcium moulds flooring material and preparation method thereof, can
Solve the problems, such as that existing calcium modeling flooring material texture is poor, non-skid property is bad.
To solve above-mentioned existing technical problem, the present invention uses following scheme：
A kind of PVC calcium moulds flooring material, by weight, is made up of following component：30 parts of PVC resin powder, PVC regenerating resin powder
30-50 parts, powdered whiting 30-50 parts, 100 mesh kaolin 20-40 parts, dialkyl group are to biphenol 8-12 parts, barium ferrite 3-5
Part, calcium stearate 3-5 parts, 2 parts of caprolactam.
The PVC calcium moulds the preparation method of flooring material, comprises the following steps：
（1）Dispensing：According to raw material proportioning, by PVC resin powder, PVC regenerating resins powder, powdered whiting, 100 mesh kaolin, two
Alkyl adds stirrer for mixing to biphenol, barium ferrite, calcium stearate, caprolactam, and rotating speed is 1200 revs/min, when
Between be 20-30 minutes, temperature is 100 DEG C, and it is standby to obtain mixture；
（2）It is granulated：The mixture obtained in step (1) is added at a temperature of 130 DEG C of comminutor and is granulated, the grain that will be obtained
After material cooling, a kind of PVC calcium modeling flooring material is obtained；
（3）The granular calcic-plastic composite material obtained in step (2) is controlled at 200 DEG C -220 DEG C by extruding production line, extrusion temperature
Between, after extruding blank, two roll-ins prolong, cool down, cut-parts, block product examine, packaging, obtain a kind of PVC calcium modeling floor.
The present invention is advantageous in that：The present invention using above-mentioned technical proposal provide a kind of PVC calcium modeling flooring material and
Its preparation method, improved by adding kaolin and formula, solve existing calcium modeling flooring material texture is poor, non-skid property not
The problem of good.
Embodiment
The present invention is described in detail below in conjunction with specific embodiment, herein illustrative examples and explanation of the invention
For explaining the present invention, but it is not as a limitation of the invention.
Embodiment
A kind of PVC calcium moulds flooring material, by weight, is made up of following component：30 parts of PVC resin powder, PVC regeneration trees
30 parts of cosmetics, 30 parts of powdered whiting, 20 parts of 100 mesh kaolin, dialkyl group are to 8 parts of biphenol, 3 parts of barium ferrite, stearic acid
3 parts of calcium, 2 parts of caprolactam.
The PVC calcium moulds the preparation method of flooring material, comprises the following steps：
（1）Dispensing：According to raw material proportioning, by PVC resin powder, PVC regenerating resins powder, powdered whiting, 100 mesh kaolin, two
Alkyl adds stirrer for mixing to biphenol, barium ferrite, calcium stearate, caprolactam, and rotating speed is 1200 revs/min, when
Between be 20 minutes, temperature be 100 DEG C, it is standby to obtain mixture；
（2）It is granulated：The mixture obtained in step (1) is added at a temperature of 130 DEG C of comminutor and is granulated, the grain that will be obtained
After material cooling, a kind of PVC calcium modeling flooring material is obtained；
（3）The granular calcic-plastic composite material obtained in step (2) is controlled at 200 DEG C -220 DEG C by extruding production line, extrusion temperature
Between, after extruding blank, two roll-ins prolong, cool down, cut-parts, block product examine, packaging, obtain a kind of PVC calcium modeling floor.
The above-described embodiments merely illustrate the principles and effects of the present invention, not for the limitation present invention.It is any ripe
Know the personage of this technology all can carry out modifications and changes under the spirit and scope without prejudice to the present invention to above-described embodiment.Cause
This, those of ordinary skill in the art is complete without departing from disclosed spirit and institute under technological thought such as
Into all equivalent modifications or change, should by the present invention claim be covered.
Claims (2)
1. a kind of PVC calcium modeling flooring material and preparation method thereof, it is characterised in that by weight, be made up of following component：
30 parts of PVC resin powder, PVC regenerating resin powder 30-50 parts, powdered whiting 30-50 parts, 100 mesh kaolin 20-40 parts, dioxane
Base is to biphenol 8-12 parts, barium ferrite 3-5 parts, calcium stearate 3-5 parts, 2 parts of caprolactam.
2. the preparation method of PVC calcium modeling flooring material according to claim 1, it is characterised in that comprise the following steps：
（1）Dispensing：According to raw material proportioning, by PVC resin powder, PVC regenerating resins powder, powdered whiting, 100 mesh kaolin, two
Alkyl adds stirrer for mixing to biphenol, barium ferrite, calcium stearate, caprolactam, and rotating speed is 1200 revs/min, when
Between be 20-30 minutes, temperature is 100 DEG C, and it is standby to obtain mixture；
（2）It is granulated：By step（1）In obtained mixture be added to 130 DEG C of comminutor at a temperature of be granulated, the grain that will be obtained
After material cooling, a kind of PVC calcium modeling flooring material is obtained；
（3）By step（2）In obtained granular calcic-plastic composite material controlled by extruding production line, extrusion temperature at 200 DEG C -220 DEG C
Between, after extruding blank, two roll-ins prolong, cool down, cut-parts, block product examine, packaging, obtain a kind of PVC calcium modeling floor.