CN105885306A - PVC (polyvinyl chloride) calcium-plastic flooring and preparation method thereof - Google Patents
PVC (polyvinyl chloride) calcium-plastic flooring and preparation method thereof Download PDFInfo
- Publication number
- CN105885306A CN105885306A CN201610502196.3A CN201610502196A CN105885306A CN 105885306 A CN105885306 A CN 105885306A CN 201610502196 A CN201610502196 A CN 201610502196A CN 105885306 A CN105885306 A CN 105885306A
- Authority
- CN
- China
- Prior art keywords
- pvc
- calcium
- parts
- resin powder
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides PVC (polyvinyl chloride) calcium-plastic flooring and a preparation method thereof. The flooring is prepared from the following raw materials in parts by weight: 30 parts of PVC resin powder, 30-50 parts of PVC regenerated resin powder, 30-50 parts of calcium carbonate, 20-40 parts of 100-mesh quartz sand, 8-12 parts of dicumyl peroxide, 3-5 parts of triallyl isocyanurate, 3-5 parts of calcium stearate and 2 parts of ethylene bisstearamide. The problems of poor textures and slip resistance of existing calcium-plastic floorings are solved by combining the formula with the preparation method.
Description
Technical field
The invention belongs to flooring material technical field, be specifically related to a kind of PVC calcium and mould flooring material and preparation method thereof.
Background technology
Calcic-plastic composite material is with inorganic calcium salt as primary raw material, is equipped with the class composite that the synthetic resin such as TPO are mixing.Having chemical stability, high-low temperature resistant, have good thermal insulation, resistance to water, have good anti-flammability, its burning velocity is slow, and smoke is few, not fire hazardous, public hazards.Being widely used as construction material, fitment material for family, furniture and consumer goods materials etc., existing calcium moulds flooring material, while having above-mentioned advantage, there is the problem that texture is poor, non-skid property is bad.
Summary of the invention
The technical problem to be solved is to provide a kind of PVC calcium to mould flooring material and preparation method thereof, it is possible to solves existing calcium and moulds the problem that flooring material texture is poor, non-skid property is bad.
For solving above-mentioned existing technical problem, the present invention uses following scheme:
A kind of PVC calcium moulds flooring material, by weight, it is made up of following component: PVC resin powder 30 parts, PVC regenerating resin powder 30-50 part, calcium carbonate 30-50 part, 100 mesh quartz sand 20-40 parts, cumyl peroxide 8-12 part, triallyl isocyanuric acid vinegar 3-5 part, calcium stearate 3-5 part, ethylene bis stearic acid amide 2 parts.
This PVC calcium moulds the preparation method of flooring material, comprises the following steps:
(1) dispensing: according to proportioning raw materials, PVC resin powder, PVC regenerating resin powder, calcium carbonate, 100 mesh quartz sands, cumyl peroxide, triallyl isocyanuric acid vinegar, calcium stearate, ethylene bis stearic acid amide are added stirrer for mixing, rotating speed is 1200 revs/min, time is 20-30 minute, temperature is 100 DEG C, obtains mixture standby；
(2) pelletize: carry out pelletize at a temperature of the mixture obtained in step (1) is joined comminutor 130 DEG C, after the granulate cooling that will obtain, obtains a kind of PVC calcium and moulds flooring material；
(3) by the granular calcium moulding material that obtains in step (2) by extruding production line, extrusion temperature controls between 200 DEG C-220 DEG C, after extrusion blank, two roll-ins prolong, cool down, cut-parts, block product examine, packaging, obtain one PVC calcium and mould floor.
The invention have benefit that: the present invention uses technique scheme to provide a kind of PVC calcium to mould flooring material and preparation method thereof, by adding quartz sand and compositional refinements, solves existing calcium and moulds the problem that flooring material texture is poor, non-skid property is bad.
Detailed description of the invention
Describing the present invention in detail below in conjunction with specific embodiment, illustrative examples and explanation in this present invention are used for explaining the present invention, but not as a limitation of the invention.
Embodiment 1
A kind of PVC calcium moulds flooring material, by weight, it is made up of following component: PVC resin powder 30 parts, 30 parts of PVC regenerating resin powder, calcium carbonate 30 parts, 100 mesh quartz sand 20 parts, cumyl peroxide 8 parts, triallyl isocyanuric acid vinegar 3 parts, calcium stearate 3 parts, ethylene bis stearic acid amide 2 parts.
This PVC calcium moulds the preparation method of flooring material, comprises the following steps:
(1) dispensing: according to proportioning raw materials, PVC resin powder, PVC regenerating resin powder, calcium carbonate, 100 mesh quartz sands, cumyl peroxide, triallyl isocyanuric acid vinegar, calcium stearate, ethylene bis stearic acid amide are added stirrer for mixing, rotating speed is 1200 revs/min, time is 20 minutes, temperature is 100 DEG C, obtains mixture standby；
(2) pelletize: carry out pelletize at a temperature of the mixture obtained in step (1) is joined comminutor 130 DEG C, after the granulate cooling that will obtain, obtains a kind of PVC calcium and moulds flooring material；
(3) by the granular calcium moulding material that obtains in step (2) by extruding production line, extrusion temperature controls between 200 DEG C-220 DEG C, after extrusion blank, two roll-ins prolong, cool down, cut-parts, block product examine, packaging, obtain one PVC calcium and mould floor.
Embodiment 2
A kind of PVC calcium moulds flooring material, by weight, it is made up of following component: PVC resin powder 30 parts, 40 parts of PVC regenerating resin powder, calcium carbonate 40 parts, 100 mesh quartz sand 30 parts, cumyl peroxide 10 parts, triallyl isocyanuric acid vinegar 4 parts, calcium stearate 4 parts, ethylene bis stearic acid amide 2 parts.
This PVC calcium moulds the preparation method of flooring material, comprises the following steps:
(1) dispensing: according to proportioning raw materials, PVC resin powder, PVC regenerating resin powder, calcium carbonate, 100 mesh quartz sands, cumyl peroxide, triallyl isocyanuric acid vinegar, calcium stearate, ethylene bis stearic acid amide are added stirrer for mixing, rotating speed is 1200 revs/min, time is 26 minutes, temperature is 100 DEG C, obtains mixture standby；
(2) pelletize: carry out pelletize at a temperature of the mixture obtained in step (1) is joined comminutor 130 DEG C, after the granulate cooling that will obtain, obtains a kind of PVC calcium and moulds flooring material；
(3) by the granular calcium moulding material that obtains in step (2) by extruding production line, extrusion temperature controls between 200 DEG C-220 DEG C, after extrusion blank, two roll-ins prolong, cool down, cut-parts, block product examine, packaging, obtain one PVC calcium and mould floor.
Embodiment 3
A kind of PVC calcium moulds flooring material, by weight, it is made up of following component: PVC resin powder 30 parts, 50 parts of PVC regenerating resin powder, calcium carbonate 50 parts, 100 mesh quartz sand 40 parts, cumyl peroxide 12 parts, triallyl isocyanuric acid vinegar 5 parts, calcium stearate 5 parts, ethylene bis stearic acid amide 2 parts.
This PVC calcium moulds the preparation method of flooring material, comprises the following steps:
(1) dispensing: according to proportioning raw materials, PVC resin powder, PVC regenerating resin powder, calcium carbonate, 100 mesh quartz sands, cumyl peroxide, triallyl isocyanuric acid vinegar, calcium stearate, ethylene bis stearic acid amide are added stirrer for mixing, rotating speed is 1200 revs/min, time is 30 minutes, temperature is 100 DEG C, obtains mixture standby；
(2) pelletize: carry out pelletize at a temperature of the mixture obtained in step (1) is joined comminutor 130 DEG C, after the granulate cooling that will obtain, obtains a kind of PVC calcium and moulds flooring material；
(3) by the granular calcium moulding material that obtains in step (2) by extruding production line, extrusion temperature controls between 200 DEG C-220 DEG C, after extrusion blank, two roll-ins prolong, cool down, cut-parts, block product examine, packaging, obtain one PVC calcium and mould floor.
The principle of above-described embodiment only illustrative present invention and effect thereof, not for limiting the present invention.Above-described embodiment all can be modified under the spirit and the scope of the present invention or change by any person skilled in the art.Therefore, art has all equivalence modification or changes that usually intellectual is completed under without departing from disclosed spirit and technological thought such as, must be contained by the claim of the present invention.
Claims (2)
1. a PVC calcium moulds flooring material and preparation method thereof, it is characterized in that, by weight, it is made up of following component: PVC resin powder 30 parts, PVC regenerating resin powder 30-50 part, calcium carbonate 30-50 part, 100 mesh quartz sand 20-40 parts, cumyl peroxide 8-12 part, triallyl isocyanuric acid vinegar 3-5 part, calcium stearate 3-5 part, ethylene bis stearic acid amide 2 parts.
PVC calcium the most according to claim 1 moulds the preparation method of flooring material, it is characterised in that comprise the following steps:
(1) dispensing: according to proportioning raw materials, PVC resin powder, PVC regenerating resin powder, calcium carbonate, 100 mesh quartz sands, cumyl peroxide, triallyl isocyanuric acid vinegar, calcium stearate, ethylene bis stearic acid amide are added stirrer for mixing, rotating speed is 1200 revs/min, time is 20-30 minute, temperature is 100 DEG C, obtains mixture standby；
(2) pelletize: carry out pelletize at a temperature of the mixture obtained in step (1) is joined comminutor 130 DEG C, after the granulate cooling that will obtain, obtains a kind of PVC calcium and moulds flooring material；
(3) by the granular calcium moulding material that obtains in step (2) by extruding production line, extrusion temperature controls between 200 DEG C-220 DEG C, after extrusion blank, two roll-ins prolong, cool down, cut-parts, block product examine, packaging, obtain one PVC calcium and mould floor.