CN107774711A - A kind of composite blank preparation method for producing ultra-thick steel plates - Google Patents
A kind of composite blank preparation method for producing ultra-thick steel plates Download PDFInfo
- Publication number
- CN107774711A CN107774711A CN201610785787.6A CN201610785787A CN107774711A CN 107774711 A CN107774711 A CN 107774711A CN 201610785787 A CN201610785787 A CN 201610785787A CN 107774711 A CN107774711 A CN 107774711A
- Authority
- CN
- China
- Prior art keywords
- mrow
- rolling
- billet
- raw material
- composite
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
A kind of composite blank preparation method for producing ultra-thick steel plates, it is characterised in that composite billet intermediate layer material is used as using base among rolling;Particular content is as follows:1st, blank design:Need to reformulate blank specification for final finished specification, it is necessary to formulate corresponding crop end amount and edged amount according to compression ratio;2nd, middle base rolling:Middle base is rolled using 300mm thickness product, using manual rolling, is ensured that previous three passes drafts is not less than 60mm, is ensured that degeneration area form factor is not less than 0.5.The present invention makees the intermediate layer material as composite billet using base among rolling, can be effectively improved the center portion segregation of composite billet product, improve flaw detection qualification rate.
Description
Technical field
The present invention relates to a kind of composite blank preparation method of ultra-thick steel plates.
Background technology
The raw materials for production for producing more than 200mm super-thick steel plate in the world at present mainly have two kinds, and one kind is steel ingot, another
Kind is composite billet.But there are the following problems for composite billet production:Composite billet is combined using continuous casting billet, and thickness is in 400-900mm
Between, in rolling because initial passage torque limit can not realize that super large is depressed, therefore center portion deformation is insufficient, is limited by
Continuous casting billet itself center portion is more loose, causes center portion easily to produce segregation, and flaw detection does not conform to.
The content of the invention
It is an object of the invention to provide a kind of composite blank preparation method for the ultra-thick steel plates for producing more than 200mm, uses
Base makees the intermediate layer material as composite billet among rolling, can be effectively improved the center portion segregation of composite billet product, improve flaw detection and close
Lattice rate.
To achieve the above object, the present invention is achieved through the following technical solutions:
A kind of composite blank preparation method for producing ultra-thick steel plates, middle base is rolled first as composite billet intermediate layer material
Material;The middle base through rolling and continuous casting billet are welded into composite billet in vacuum chamber again, particular content is as follows:
1) composite billet finished product blank design
Need to reformulate blank specification for final finished specification, it is necessary to according to compression ratio formulate corresponding crop end amount and
Edged amount, it is specially:
Wide+0.283 × finished product of thick thick -0.241 × raw material of -1.12 × finished product of width edged amount=789+0.641 × raw material
Wide -598 × broadening ratio -143 × ratio of elongation
Wide+1.58 × trim width of thick thick -1.72 × raw material of+4.40 × finished product of length edged amount=1844-1.13 × raw material -
2322 × broadening ratio+160 × ratio of elongation
Wherein:Broadening ratio=finished width/raw material width;Ratio of elongation=finished product length/raw material length
2) base rolling among
Middle base is rolled using 300mm thickness product, using manual rolling, ensures that previous three passes drafts is not less than 60mm,
Ensure that shape parameter of transforming field is not less than 0.5, wherein, shape parameter of transforming field is calculated as follows
For shape parameter of transforming field
R:Working roll roll neck, unit mm
H:Workpiece thickness before rolling, unit mm
h:Workpiece thickness after rolling, unit mm
3) base cutting among
It must assure that middle base cutting is carried out under the conditions of whole process is without magnetic, steel billet operating uses clamp, prohibits the use of electromagnetism
Hang;
4) steel billet welds
To reduce arc blow, middle base eventually enters into vacuum chamber with using submerged-arc welding upper and lower two layers of continuous casting billet compound early stage
It is welded into composite billet.
Compared with prior art, the beneficial effects of the invention are as follows:
The composite blank preparation method of present invention production more than 200mm ultra-thick steel plates, using base conduct among rolling
The intermediate layer material of composite billet, the center portion segregation of composite billet product can be effectively improved, improves flaw detection qualification rate.
Embodiment
Technical scheme is described in further detail below by specific embodiment.
A kind of composite blank preparation method for producing ultra-thick steel plates, middle base is rolled first as composite billet intermediate layer material
Material;The middle base through rolling and continuous casting billet are welded into composite billet in vacuum chamber again, particular content is as follows:
1) composite billet finished product blank design
Need to reformulate blank specification for final finished specification, it is necessary to according to compression ratio formulate corresponding crop end amount and
Edged amount, it is specially:
Wide+0.283 × finished product of thick thick -0.241 × raw material of -1.12 × finished product of width edged amount=789+0.641 × raw material
Wide -598 × broadening ratio -143 × ratio of elongation
Wide+1.58 × trim width of thick thick -1.72 × raw material of+4.40 × finished product of length edged amount=1844-1.13 × raw material -
2322 × broadening ratio+160 × ratio of elongation
Wherein:Broadening ratio=finished width/raw material width;Ratio of elongation=finished product length/raw material length
2) base rolling among
Middle base is rolled using 300mm thickness product, using manual rolling, ensures that previous three passes drafts is not less than 60mm,
Ensure that shape parameter of transforming field is not less than 0.5, wherein, shape parameter of transforming field is calculated as follows
For shape parameter of transforming field
R:Working roll roll neck, unit mm
H:Workpiece thickness before rolling, unit mm
h:Workpiece thickness after rolling, unit mm
3) base cutting among
It must assure that middle base cutting is carried out under the conditions of whole process is without magnetic, steel billet operating uses clamp, prohibits the use of electromagnetism
Hang;
4) steel billet welds
To reduce arc blow, middle base eventually enters into vacuum chamber with using submerged-arc welding upper and lower two layers of continuous casting billet compound early stage
It is welded into composite billet.
Claims (1)
1. a kind of composite blank preparation method for producing ultra-thick steel plates, it is characterised in that base is as composite billet among rolling first
Intermediate layer material;The middle base through rolling and continuous casting billet are welded into composite billet in vacuum chamber again, particular content is as follows:
1) composite billet finished product blank design
Need to reformulate blank specification for final finished specification, it is necessary to formulate corresponding crop end amount and edged according to compression ratio
Amount, it is specially:
Wide+0.283 × trim width of thick thick -0.241 × raw material of -1.12 × finished product of width edged amount=789+0.641 × raw material -
598 × broadening ratio -143 × ratio of elongation
Wide+1.58 × trim width -2322 of thick thick -1.72 × raw material of+4.40 × finished product of length edged amount=1844-1.13 × raw material
× broadening ratio+160 × ratio of elongation
Wherein:Broadening ratio=finished width/raw material width;Ratio of elongation=finished product length/raw material length
2) base rolling among
Middle base is rolled using 300mm thickness product, using manual rolling, is ensured that previous three passes drafts is not less than 60mm, is ensured
Shape parameter of transforming field is not less than 0.5, wherein, shape parameter of transforming field is calculated as follows
<mrow>
<mi>l</mi>
<mo>/</mo>
<mover>
<mi>h</mi>
<mo>&OverBar;</mo>
</mover>
<mo>=</mo>
<mfrac>
<msqrt>
<mrow>
<mi>R</mi>
<mi>&Delta;</mi>
<mi>h</mi>
</mrow>
</msqrt>
<mfrac>
<mrow>
<mi>H</mi>
<mo>+</mo>
<mi>h</mi>
</mrow>
<mn>2</mn>
</mfrac>
</mfrac>
<mo>=</mo>
<mfrac>
<mrow>
<mn>2</mn>
<msqrt>
<mrow>
<mi>R</mi>
<mrow>
<mo>(</mo>
<mi>H</mi>
<mo>-</mo>
<mi>h</mi>
<mo>)</mo>
</mrow>
</mrow>
</msqrt>
</mrow>
<mrow>
<mi>H</mi>
<mo>+</mo>
<mi>h</mi>
</mrow>
</mfrac>
</mrow>
For shape parameter of transforming field
R:Working roll roll neck, unit mm
H:Workpiece thickness before rolling, unit mm
h:Workpiece thickness after rolling, unit mm
3) base cutting among
It must assure that middle base cutting is carried out under the conditions of whole process is without magnetic, steel billet operating uses clamp, prohibits the use of electromagnetic lifter;
4) steel billet welds
To reduce arc blow, middle base eventually enters into vacuum chamber welding with using submerged-arc welding upper and lower two layers of continuous casting billet compound early stage
Into composite billet.