CN107760845A - A kind of processing technology for low temperature environment bearing pin - Google Patents
A kind of processing technology for low temperature environment bearing pin Download PDFInfo
- Publication number
- CN107760845A CN107760845A CN201610684397.XA CN201610684397A CN107760845A CN 107760845 A CN107760845 A CN 107760845A CN 201610684397 A CN201610684397 A CN 201610684397A CN 107760845 A CN107760845 A CN 107760845A
- Authority
- CN
- China
- Prior art keywords
- bearing pin
- low temperature
- processing technology
- temperature environment
- treatment process
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of processing technology for low temperature environment bearing pin, including the following steps that order is carried out：Blanking, mechanical preliminary working, heat treatment, machine finishing and Surface Machining, the material of bearing pin is 40CrNiMo, and heat treatment includes the Quenching Treatment and temper that order is carried out；During Quenching Treatment, including the holding stage of order progress and slow cooling stage, for the temperature of holding stage between 853 DEG C to 860 DEG C, soaking time is no less than 2.5h；Heating-up temperature during temper is between 580 DEG C to 600 DEG C；Also include being arranged at the Carburization Treatment process before Quenching Treatment process, Carburization Treatment process is incubated for bearing pin blank is placed in carburizing environment, between being heated to 890 DEG C to 900 DEG C and is no less than 5h.Using processing technology provided above, the bearing pin at low ambient temperatures with long service life is can obtain, while there is good surface abrasion resistance, while product qualification rate is high.
Description
Technical field
The present invention relates to mechanical fastener manufacturing technology field, more particularly to a kind of processing for low temperature environment bearing pin
Technique.
Background technology
Bearing pin is the fastener of a kind of standardization, is typically locked by split pin, both can static state be fixedly connected, also can be with quilt
Connector does relative motion, and is mainly used in the hinged place of two parts, forms hinge connection.Bearing pin reliable operation, convenient disassembly, quilt
It is widely used as the mechanical fastener of construction applications.
In the prior art, bearing pin is used for different working environments, for specific requirement, generally requires selection and closes
The raw material that suitable material makes as bearing pin, but raw material are carried out with the heat treatment of different process, also can be to bearing pin product
Performance produce large effect.The bearing pin durability being used in the prior art under cold environment is poor, is typically implemented in
In low-temperature impact property, the bearing pin Technology for Heating Processing under cold environment is made further research, to optimize under the use condition
The service life of bearing pin, it is urgent problem to be solved in the prior art.
The content of the invention
It is poor for the above-mentioned bearing pin durability being used in the prior art under cold environment, it is typically implemented in low-temperature impact resistance
In performance, the bearing pin Technology for Heating Processing under cold environment is made further research, to optimize the use of the use condition lower bearing pin
In the life-span, it is urgent problem to be solved in the prior art, the invention provides a kind of processing technology for low temperature environment bearing pin.
In view of the above-mentioned problems, a kind of processing technology for low temperature environment bearing pin provided by the invention will by following technology
Put to reach goal of the invention：A kind of processing technology for low temperature environment bearing pin, including the following steps that order is carried out：Blanking,
Mechanical preliminary working, heat treatment, machine finishing and Surface Machining, the material of the bearing pin is 40CrNiMo, the heat treatment bag
Include Quenching Treatment and temper that order is carried out；
During the Quenching Treatment, including the holding stage of order progress and slow cooling stage, the temperature of the holding stage are situated between
Between 853 DEG C to 860 DEG C, soaking time is no less than 2.5h；
Heating-up temperature during the temper is between 580 DEG C to 600 DEG C；Also include being arranged at Quenching Treatment process
Carburization Treatment process before, the Carburization Treatment process are heated to 890 DEG C extremely for bearing pin blank is placed in carburizing environment
Insulation is no less than 5h between 900 DEG C.
Specifically, in above Technology for Heating Processing, for this materials of 40CrNiMo, the selection of conventional hardening heat is 800
DEG C or so, with mainly for austenitizing, then in rapid cooling to realize martensite transfor mation；The existing tempering for 40CrNiMo
Cheng Zhong, using the lonneal for being usually no more than 200 DEG C, in order to obtain higher hardness number and intensity level.This technique
In, by experiment repeatedly, hardening heat is chosen for improve 50 DEG C or so compared to prior art, mainly for closing in material
The solubility and homogenization degree of gold element；Compared to prior art, temperature multiplication, the material after being heat-treated may be such that
Material, although sacrificing part hardness number and intensity level, the low-temperature impact resistance ability of product has obtained significant raising.
By above Technology for Heating Processing, compared to prior art, when 40CrNiMo materials are as bearing pin purposes, compared to
The bearing pin of conventionally employed same material, although the performance decrease to some degree such as wearability and intensity, ring is used in low temperature
Under border, the shock loading under cryogenic conditions is the main reason for bearing pin destroys, therefore the bearing pin being thermally treated resulting in more than, is used
Life-span would generally reach more than the three times of prior art.
The Carburization Treatment process of arrangement above, it is easy to so that the bearing pin obtained by this Technology for Heating Processing, has well
Case hardness, so, gained bearing pin is while its good center toughness is played, also with good surface abrasion resistance.
Meanwhile the invention provides the specific processing technology for applying to low temperature environment bearing pin, can be high qualified by this technique
The completion of rate meets the bearing pin product of low temperature environment requirement.
Further technical scheme is：
Be easy to the slow cooling mode of control as a kind of specific cooling velocity, with avoid producing cool down in pressure crackle the defects of,
The slow cooling stage uses oil cooling.
As a kind of heat treatment mode beneficial to modulation effect, to reach in quenched preceding refiner material crystal grain, eliminate material
In internal stress concrete scheme, in addition to the normalized treatment before the Quenching Treatment.This programme is especially suitable for blank material
Expect the situation for forging.
As it is a kind of eliminate firing rate, furnace temperature decision, single stove piece count to be tempered influential effect technical side
Case, the soaking time of the drawing process are no less than 1.5h.
For this materials of 40CrNiMo, further to eliminate internal stress, the number of the temper is more than once.It is real
The bearing pin for low temperature environment bright, this material makes is verified, carries out the service life of bearing pin of double tempering compared to only adopting
The service life being tempered with a same parameter, extends about 0.5 times.Carry out tempering operation more than twice simultaneously, just return three times
Fire compared to there is certain service life lifting twice, it is but little for influence of the tempering three times to service life, as
It is preferred that for the benefit of production efficiency, this case use double tempering.
As the specific implementation of above Carburization Treatment process, the carbon potential concentration of the carburizing environment between 0.9% to
1.04%。
The Surface Machining is to carry out zinc-plated processing to the bearing pin obtained after finishing.Using zinc-plated processing bearing pin table
Face obtains one layer of zinc coat, can not only optimize the frost-cracking-preventing performance used under this bearing pin cold environment, while causes gained bearing pin
With good surface corrosion-resistant erosion ability and anti-wear performance.
The invention has the advantages that：
In above Technology for Heating Processing, for this materials of 40CrNiMo, the selection of conventional hardening heat is 800 DEG C or so, with master
Austenitizing is directed to, then in rapid cooling to realize martensite transfor mation；In the existing drawing process for 40CrNiMo, using one
As be no more than 200 DEG C of lonneal, in order to obtain higher hardness number and intensity level.In this technique, by repeatedly
Experiment, by hardening heat be chosen for compared to prior art improve 50 DEG C or so, mainly in material alloying element it is molten
Xie Du and homogenization degree；Compared to prior art, temperature multiplication, the material after being heat-treated is may be such that, although sacrificial
Domestic animal part hardness number and intensity level, but the low-temperature impact resistance ability of product obtained significant raising.
By above Technology for Heating Processing, compared to prior art, when 40CrNiMo materials are as bearing pin purposes, compared to
The bearing pin of conventionally employed same material, although the performance decrease to some degree such as wearability and intensity, ring is used in low temperature
Under border, the shock loading under cryogenic conditions is the main reason for bearing pin destroys, therefore the bearing pin being thermally treated resulting in more than, is used
Life-span would generally reach more than the three times of prior art.
The Carburization Treatment process of arrangement above, it is easy to so that the bearing pin obtained by this Technology for Heating Processing, has well
Case hardness, so, gained bearing pin is while its good center toughness is played, also with good surface abrasion resistance.
It is high using technique provided by the invention, product qualification rate.
Embodiment
With reference to embodiment, the present invention is described in further detail, but the present invention structure be not limited only to it is following
Embodiment.
Embodiment 1：
A kind of processing technology for low temperature environment bearing pin, including the following steps that order is carried out：Blanking, mechanical preliminary working, heat
Processing, machine finishing and Surface Machining, the material of the bearing pin is 40CrNiMo, and the heat treatment includes quenching for order progress
Fire processing and temper；
During the Quenching Treatment, including the holding stage of order progress and slow cooling stage, the temperature of the holding stage are situated between
Between 853 DEG C to 860 DEG C, soaking time is no less than 2.5h；
Heating-up temperature during the temper is between 580 DEG C to 600 DEG C；Also include being arranged at Quenching Treatment process
Carburization Treatment process before, the Carburization Treatment process are heated to 890 DEG C extremely for bearing pin blank is placed in carburizing environment
Insulation is no less than 5h between 900 DEG C.
Specifically, in above Technology for Heating Processing, for this materials of 40CrNiMo, the selection of conventional hardening heat is 800
DEG C or so, with mainly for austenitizing, then in rapid cooling to realize martensite transfor mation；The existing tempering for 40CrNiMo
Cheng Zhong, using the lonneal for being usually no more than 200 DEG C, in order to obtain higher hardness number and intensity level.This technique
In, by experiment repeatedly, hardening heat is chosen for improve 50 DEG C or so compared to prior art, mainly for closing in material
The solubility and homogenization degree of gold element；Compared to prior art, temperature multiplication, the material after being heat-treated may be such that
Material, although sacrificing part hardness number and intensity level, the low-temperature impact resistance ability of product has obtained significant raising.
By above Technology for Heating Processing, compared to prior art, when 40CrNiMo materials are as bearing pin purposes, compared to
The bearing pin of conventionally employed same material, although the performance decrease to some degree such as wearability and intensity, ring is used in low temperature
Under border, the shock loading under cryogenic conditions is the main reason for bearing pin destroys, therefore the bearing pin being thermally treated resulting in more than, is used
Life-span would generally reach more than the three times of prior art.
The Carburization Treatment process of arrangement above, it is easy to so that the bearing pin obtained by this Technology for Heating Processing, has well
Case hardness, so, gained bearing pin is while its good center toughness is played, also with good surface abrasion resistance.
Embodiment 2：
The present embodiment is further qualified on the basis of embodiment 1, is easy to the slow of control as a kind of specific cooling velocity
Cold mode, with avoid produce cool down in pressure crackle the defects of, the slow cooling stage uses oil cooling.
As a kind of heat treatment mode beneficial to modulation effect, to reach in quenched preceding refiner material crystal grain, eliminate material
In internal stress concrete scheme, in addition to the normalized treatment before the Quenching Treatment.This programme is especially suitable for blank material
Expect the situation for forging.
As it is a kind of eliminate firing rate, furnace temperature decision, single stove piece count to be tempered influential effect technical side
Case, the soaking time of the drawing process are no less than 1.5h.
For this materials of 40CrNiMo, further to eliminate internal stress, the number of the temper is more than once.It is real
The bearing pin for low temperature environment bright, this material makes is verified, carries out the service life of bearing pin of double tempering compared to only adopting
The service life being tempered with a same parameter, extends about 0.5 times.Carry out tempering operation more than twice simultaneously, just return three times
Fire compared to there is certain service life lifting twice, it is but little for influence of the tempering three times to service life, as
It is preferred that for the benefit of production efficiency, this case use double tempering.
860 DEG C of insulation 4h quenchings are used in the present embodiment, using 585 DEG C of insulation 3h tempering, and times of tempering is twice, together
When quenching using oil cooling by the way of, obtained bearing pin is tested suitable for -50 DEG C of working environment through stress loading, its use
Life-span is five times of identical material bearing pin in the prior art.
As the specific implementation of above Carburization Treatment process, the carbon potential concentration of the carburizing environment between 0.9% to
1.04%。
The Surface Machining is to carry out zinc-plated processing to the bearing pin obtained after finishing.Using zinc-plated processing bearing pin table
Face obtains one layer of zinc coat, can not only optimize the frost-cracking-preventing performance used under this bearing pin cold environment, while causes gained bearing pin
With good surface corrosion-resistant erosion ability and anti-wear performance.
Above content is to combine the further description that specific preferred embodiment is made to the present invention, it is impossible to assert this
The embodiment of invention is confined to these explanations.For general technical staff of the technical field of the invention,
The other embodiment drawn in the case where not departing from technical scheme, should be included within the scope of the present invention.
Claims (7)
1. a kind of processing technology for low temperature environment bearing pin, including the following steps that order is carried out：Blanking, mechanical preliminary working,
Heat treatment, machine finishing and Surface Machining, it is characterised in that the material of the bearing pin is 40CrNiMo, the heat treatment bag
Include Quenching Treatment and temper that order is carried out；
During the Quenching Treatment, including the holding stage of order progress and slow cooling stage, the temperature of the holding stage are situated between
Between 853 DEG C to 860 DEG C, soaking time is no less than 2.5h；
Heating-up temperature during the temper is between 580 DEG C to 600 DEG C；Also include being arranged at Quenching Treatment process
Carburization Treatment process before, the Carburization Treatment process are heated to 890 DEG C extremely for bearing pin blank is placed in carburizing environment
Insulation is no less than 5h between 900 DEG C.
A kind of 2. processing technology for low temperature environment bearing pin according to claim 1, it is characterised in that the slow cooling rank
Duan Caiyong oil coolings.
3. a kind of processing technology for low temperature environment bearing pin according to claim 1, it is characterised in that also include being located at
Normalized treatment before Quenching Treatment.
4. a kind of processing technology for low temperature environment bearing pin according to claim 1, it is characterised in that described to be tempered
The soaking time of journey is no less than 1.5h.
5. a kind of processing technology for low temperature environment bearing pin according to claim 1, it is characterised in that at the tempering
The number of reason is more than once.
A kind of 6. processing technology for low temperature environment bearing pin according to claim 1, it is characterised in that the carburizing ring
The carbon potential concentration in border is between 0.9% to 1.04%.
7. a kind of processing technology for low temperature environment bearing pin according to claim 1, it is characterised in that the surface adds
Work is to carry out zinc-plated processing to the bearing pin obtained after finishing.