CN107759879A - A kind of manufacture method of Plastic Drum - Google Patents
A kind of manufacture method of Plastic Drum Download PDFInfo
- Publication number
- CN107759879A CN107759879A CN201610703505.3A CN201610703505A CN107759879A CN 107759879 A CN107759879 A CN 107759879A CN 201610703505 A CN201610703505 A CN 201610703505A CN 107759879 A CN107759879 A CN 107759879A
- Authority
- CN
- China
- Prior art keywords
- plastic drum
- manufacture method
- raw material
- stearamides
- toughener
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of manufacture method of Plastic Drum belongs to plastic product technical field, more particularly to a kind of manufacture method of Plastic Drum.The present invention provides a kind of manufacture method of high, good flame resistance the Plastic Drum of intensity.The present invention comprises the following steps：1）Raw material is chosen, and configures by weight：Polyvinyl resin 75~85, polyvinyl chloride 30~40, calcium carbonate 10~15, burn kaolin 10~15, metal-rare-earth 15~20, polyaniline 4~7, zirconium oxide 4~7, adipic acid propanediol polyester 1.5~2.5, cumyl peroxide alcohol 2~4, calcium zinc stabilizer 3~5, ethylidine bis-stearamides 4~7, vinyl acetate 10~20, plasticizer 1~2, antioxidant 1~2, toughener 1~2.
Description
Technical field
The invention belongs to plastic product technical field, more particularly to a kind of manufacture method of Plastic Drum.
Background technology
Plastic Drum has the advantages that light, cheap, unsuitable seepage when containing liquid, compared to other materials, but
Common Plastic Drum there is also some it is obvious the shortcomings that., bucket be present in the problem of Plastic Drum is due to its composition of raw materials and manufacture craft
Body low intensity, easily it is damaged, inflammable the problems such as.
The content of the invention
The present invention is aiming above mentioned problem, there is provided a kind of intensity is high, the manufacture method of the Plastic Drum of good flame resistance.
To achieve the above object, the present invention adopts the following technical scheme that, the present invention comprises the following steps.
1）Raw material is chosen, and configures by weight：Polyvinyl resin 75~85, polyvinyl chloride 30~40, calcium carbonate 10~15,
Burn kaolin 10~15, metal-rare-earth 15~20, polyaniline 4~7, zirconium oxide 4~7, and adipic acid propanediol polyester 1.5~
2.5, cumyl peroxide alcohol 2~4, calcium zinc stabilizer 3~5, ethylidine bis-stearamides 4~7, vinyl acetate 10~20,
Plasticizer 1~2, antioxidant 1~2, toughener 1~2.
2）Raw material is put into mixer and is stirred, stirring environment temperature be 80 DEG C~90 DEG C, mixing time be 5min~
10min。
3）Raw material after stirring is put into extruder, sets extruder barrel temperature as 120 DEG C~140 DEG C, extrusion plasticizing
Grain.
4）Particle is put into blow moulding machine, sets blow moulding machine barrel temperature as 130 DEG C~150 DEG C, extrudes blank.
5）Blank is put into blow molding machine mould, Plastic Drum is made.
As a kind of preferred scheme, antibiotic layer is scribbled inside Plastic Drum of the present invention.
As another preferred scheme, raw material of the present invention is chosen, and configures by weight：Polyvinyl resin 75, polychlorostyrene
Ethene 30, calcium carbonate 10, burn kaolin 10, metal-rare-earth 15, polyaniline 4, zirconium oxide 4, adipic acid propanediol polyester 1.5,
Cumyl peroxide alcohol 2, calcium zinc stabilizer 3, ethylidine bis-stearamides 4, vinyl acetate 10, plasticizer 1, antioxidant 1,
Toughener 1.
Secondly, raw material of the present invention is chosen, and configures by weight：Polyvinyl resin 85, polyvinyl chloride 40, calcium carbonate
15, burn kaolin 15, metal-rare-earth 20, polyaniline 7, zirconium oxide 7, adipic acid propanediol polyester 2.5, cumyl peroxide
Alcohol 4, calcium zinc stabilizer 5, ethylidine bis-stearamides 7, vinyl acetate 20, plasticizer 2, antioxidant 2, toughener 2.
In addition, raw material of the present invention is chosen, configure by weight：Polyvinyl resin 80, polyvinyl chloride 35, calcium carbonate
12, burn kaolin 13, metal-rare-earth 17, polyaniline 5, zirconium oxide 6, adipic acid propanediol polyester 2, cumyl peroxide alcohol
3, calcium zinc stabilizer 4, ethylidine bis-stearamides 5, vinyl acetate 15, plasticizer 1.5, antioxidant 2, toughener 1.
Beneficial effect of the present invention.
Being used cooperatively by each component of the invention, intensity, abrasivity and the toughness of Plastic Drum are significantly enhanced, is solved
The plasticiser toxicity problem of original Plastic Drum.
The present invention uses raw material as common industrial chemicals, and cheap, and production cost is low.
Embodiment
The present invention comprises the following steps.
1）Raw material is chosen, and configures by weight：Polyvinyl resin 75~85, polyvinyl chloride 30~40, calcium carbonate 10~15,
Burn kaolin 10~15, metal-rare-earth 15~20, polyaniline 4~7, zirconium oxide 4~7, and adipic acid propanediol polyester 1.5~
2.5, cumyl peroxide alcohol 2~4, calcium zinc stabilizer 3~5, ethylidine bis-stearamides 4~7, vinyl acetate 10~20,
Plasticizer 1~2, antioxidant 1~2, toughener 1~2.
2）Raw material is put into mixer and is stirred, stirring environment temperature be 80 DEG C~90 DEG C, mixing time be 5min~
10min。
3）Raw material after stirring is put into extruder, sets extruder barrel temperature as 120 DEG C~140 DEG C, extrusion plasticizing
Grain.
4）Particle is put into blow moulding machine, sets blow moulding machine barrel temperature as 130 DEG C~150 DEG C, extrudes blank.
5）Blank is put into blow molding machine mould, Plastic Drum is made.
Antibiotic layer is scribbled inside the Plastic Drum.The antibiotic layer of application, significantly enhances Plastic Drum inside Plastic Drum
Safe and healthy coefficient.
The raw material is chosen, and configures by weight：Polyvinyl resin 75, polyvinyl chloride 30, calcium carbonate 10, burn kaolin
10, metal-rare-earth 15, polyaniline 4, zirconium oxide 4, adipic acid propanediol polyester 1.5, cumyl peroxide alcohol 2, calcium zinc stabilization
Agent 3, ethylidine bis-stearamides 4, vinyl acetate 10, plasticizer 1, antioxidant 1, toughener 1.
The raw material is chosen, and configures by weight：Polyvinyl resin 85, polyvinyl chloride 40, calcium carbonate 15, burn kaolin
15, metal-rare-earth 20, polyaniline 7, zirconium oxide 7, adipic acid propanediol polyester 2.5, cumyl peroxide alcohol 4, calcium zinc stabilization
Agent 5, ethylidine bis-stearamides 7, vinyl acetate 20, plasticizer 2, antioxidant 2, toughener 2.
The raw material is chosen, and configures by weight：Polyvinyl resin 80, polyvinyl chloride 35, calcium carbonate 12, burn kaolin
13, metal-rare-earth 17, polyaniline 5, zirconium oxide 6, adipic acid propanediol polyester 2, cumyl peroxide alcohol 3, calcium zinc stabilizer
4, ethylidine bis-stearamides 5, vinyl acetate 15, plasticizer 1.5, antioxidant 2, toughener 1.
It is understood that above with respect to the specific descriptions of the present invention, it is merely to illustrate the present invention and is not limited to this
Technical scheme described by inventive embodiments, it will be understood by those within the art that, still the present invention can be carried out
Modification or equivalent substitution, to reach identical technique effect；As long as meet use needs, all protection scope of the present invention it
It is interior.
Claims (5)
1. a kind of manufacture method of Plastic Drum, it is characterised in that comprise the following steps：
1）Raw material is chosen, and configures by weight：Polyvinyl resin 75~85, polyvinyl chloride 30~40, calcium carbonate 10~15, burning
Kaolin 10~15, metal-rare-earth 15~20, polyaniline 4~7, zirconium oxide 4~7, adipic acid propanediol polyester 1.5~2.5, mistake
Aoxidize diisopropylbenzene (DIPB) alcohol 2~4, calcium zinc stabilizer 3~5, ethylidine bis-stearamides 4~7, vinyl acetate 10~20, plasticizer 1
~2, antioxidant 1~2, toughener 1~2；
2）Raw material is put into mixer and is stirred, stirring environment temperature be 80 DEG C~90 DEG C, mixing time be 5min~
10min；
3）Raw material after stirring is put into extruder, sets extruder barrel temperature as 120 DEG C~140 DEG C, extrusion plasticizing particle；
4）Particle is put into blow moulding machine, sets blow moulding machine barrel temperature as 130 DEG C~150 DEG C, extrudes blank；
5）Blank is put into blow molding machine mould, Plastic Drum is made.
2. a kind of manufacture method of Plastic Drum according to claim 1, it is characterised in that scribble antibacterial inside the Plastic Drum
Layer.
3. a kind of manufacture method of Plastic Drum according to claim 2, it is characterised in that the raw material is chosen, and matches somebody with somebody by weight
Put：Polyvinyl resin 75, polyvinyl chloride 30, calcium carbonate 10, burn kaolin 10, metal-rare-earth 15, polyaniline 4, zirconium oxide 4,
Adipic acid propanediol polyester 1.5, cumyl peroxide alcohol 2, calcium zinc stabilizer 3, ethylidine bis-stearamides 4, vinyl acetate
10, plasticizer 1, antioxidant 1, toughener 1.
4. a kind of manufacture method of Plastic Drum according to claim 3, it is characterised in that the raw material is chosen, and matches somebody with somebody by weight
Put：Polyvinyl resin 85, polyvinyl chloride 40, calcium carbonate 15, burn kaolin 15, metal-rare-earth 20, polyaniline 7, zirconium oxide 7,
Adipic acid propanediol polyester 2.5, cumyl peroxide alcohol 4, calcium zinc stabilizer 5, ethylidine bis-stearamides 7, vinyl acetate
20, plasticizer 2, antioxidant 2, toughener 2.
5. a kind of manufacture method of Plastic Drum according to claim 4, it is characterised in that the raw material is chosen, and matches somebody with somebody by weight
Put：Polyvinyl resin 80, polyvinyl chloride 35, calcium carbonate 12, burn kaolin 13, metal-rare-earth 17, polyaniline 5, zirconium oxide 6,
Adipic acid propanediol polyester 2, cumyl peroxide alcohol 3, calcium zinc stabilizer 4, ethylidine bis-stearamides 5, vinyl acetate 15,
Plasticizer 1.5, antioxidant 2, toughener 1.