CN107759202A - A kind of preparation method of culturing pool fragment of brick - Google Patents
A kind of preparation method of culturing pool fragment of brick Download PDFInfo
- Publication number
- CN107759202A CN107759202A CN201711149320.3A CN201711149320A CN107759202A CN 107759202 A CN107759202 A CN 107759202A CN 201711149320 A CN201711149320 A CN 201711149320A CN 107759202 A CN107759202 A CN 107759202A
- Authority
- CN
- China
- Prior art keywords
- brick
- fragment
- culturing pool
- preparation
- biogas residue
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention discloses a kind of preparation method of culturing pool fragment of brick, including following operating procedure：（1）According to mass ratio it is 18 22 by biogas residue and portland cement:After 7 ratio mixing, after adding portland cement 0.3 0.5 times of heavy water of weight thereto, stir, prepare biogas residue cement microballoon, the average grain diameter for controlling microballoon is 2 4mm；（2）After shale, flyash, melting silicon powder, basalt fibre, bamboo pulp fiber, sodium lignin sulfonate, biogas residue cement microballoon are well mixed, shale 0.4 0.6 times of heavy water of quality are added thereto, rear ripening is mixed evenly after 18 20 hours, add into mould, after compressing, it is dried, sinters obtained culturing pool fragment of brick.A kind of preparation method of culturing pool fragment of brick provided by the invention, simple to operate, cost is cheap, obtained fragment of brick, and intensity is high, and water absorption rate is low, has excellent water soak resistance energy, and safety and environmental protection, water body environment will not be damaged.
Description
Technical field
The invention belongs to fragment of brick technical field, and in particular to a kind of preparation method of culturing pool fragment of brick.
Background technology
With the rise of aquaculture, the scale of indoor culture is also increasing, and general indoor culturing pool is to use brick
Block is built into, but the fragment of brick produced in the prior art, is largely both used on building, to its water soak resistance can requirement compared with
It is low, therefore, after being built into culturing pool using commercially available common fragment of brick, there is the phenomenon that fragment of brick is decomposed in water, and city
Common fragment of brick is sold, gypsum component is more, and it can increase the pH value of water body, increases containing for the poisonous ammonia nitrogen compound in water body
Amount, and then it is unfavorable for the growth of aquatic biological.Therefore, the special fragment of brick of culturing pool is lacked at present.
The content of the invention
In order to solve the above-mentioned technical problem, the present invention provides a kind of preparation method of culturing pool fragment of brick.
The present invention is achieved by the following technical solutions.
A kind of preparation method of culturing pool fragment of brick, including following operating procedure：
（1）According to mass ratio it is 18-22 by biogas residue and portland cement:After 7 ratio mixing, portland cement is added thereto
After the water that 0.3-0.5 times of weight weighs, stir, prepare biogas residue cement microballoon, the average grain diameter for controlling microballoon is 2-4mm；
（2）By weight, 64-70 parts shale, 11-15 parts flyash, 3-6 parts are melted into silicon powder, 6-9 parts basalt fibre
After dimension, 0.5-0.8 parts bamboo pulp fiber, 1-2 parts sodium lignin sulfonate, 20-26 part biogas residue cement microballoon are well mixed, add thereto
Enter the water that 0.4-0.6 times of shale quality weighs, after rear ripening 18-20 hours are mixed evenly, add into mould, suppress
After shaping, it is dried, sinters obtained culturing pool fragment of brick.
Specifically, above-mentioned steps（1）In, the water content of biogas residue is 3-5%.
Specifically, above-mentioned steps（2）In, the Average Particle Diameters of shale are 0.6-1mm.
Specifically, above-mentioned steps（2）In, a diameter of 600-800 μm of basalt fibre, length 8-10mm, bamboo pulp is fine
The a diameter of 0.01-0.03mm, length 4-6mm of dimension.
Specifically, above-mentioned steps（2）In, the temperature of sintering is 800-850 DEG C, and the time of sintering is 2-4 hours.
Technical scheme more than, the beneficial effects of the invention are as follows：
A kind of preparation method of culturing pool fragment of brick provided by the invention, simple to operate, cost is cheap, obtained fragment of brick, intensity
Height, water absorption rate is low, has excellent water soak resistance energy, and safety and environmental protection, water body environment will not be damaged.Wherein, originally
Biogas residue cement microballoon made from invention, after sintering, the compactness of fragment of brick can be effectively lifted, reduces fragment of brick water absorption rate, and can
The effective hydrolysis for avoiding salt in cement, can effectively avoid the pH value of water body from uprising；Melting silicon powder can be lifted effectively
The compression strength of obtained fragment of brick；After basalt fibre and bamboo pulp fiber synergy, the water suction of fragment of brick can be further reduced
Rate, intensity of the lifting fragment of brick in water body, and then the effective water soak resistance energy for improving fragment of brick.
Embodiment
In order that those skilled in the art can be further understood that the feature and technology contents of the present invention, referring to following has
Close detailed description of the invention.
Embodiment 1
A kind of preparation method of culturing pool fragment of brick, including following operating procedure：
（1）According to mass ratio it is 18 by biogas residue and portland cement:After 7 ratio mixing, portland cement weight is added thereto
After measuring 0.3 times of heavy water, stir, prepare biogas residue cement microballoon, the average grain diameter for controlling microballoon is 2mm；
（2）By weight, by 64 parts of shale, 11 parts of flyash, 3 parts of melting silicon powders, 6 parts of basalt fibres, 0.5 part of bamboo pulp
After fiber, 1 part of sodium lignin sulfonate, 20 parts of biogas residue cement microballoons are well mixed, 0.4 times heavy of shale quality is added thereto
Water, rear ripening is mixed evenly after 18 hours, adds into mould, after compressing, be dried, sinter to be made and support
Grow pond fragment of brick.
Specifically, above-mentioned steps（1）In, the water content of biogas residue is 3%.
Specifically, above-mentioned steps（2）In, the Average Particle Diameters of shale are 0.6mm.
Specifically, above-mentioned steps（2）In, a diameter of 600 μm of basalt fibre, length 8mm, the diameter of bamboo pulp fiber
For 0.01mm, length 4mm.
Specifically, above-mentioned steps（2）In, the temperature of sintering is 800 DEG C, and the time of sintering is 2 hours.
Embodiment 2
A kind of preparation method of culturing pool fragment of brick, including following operating procedure：
（1）According to mass ratio it is 2 by biogas residue and portland cement:After 7 ratio mixing, portland cement weight is added thereto
After 0.4 times of heavy water, stir, prepare biogas residue cement microballoon, the average grain diameter for controlling microballoon is 3mm；
（2）By weight, by 66 parts of shale, 13 parts of flyash, 5 parts of melting silicon powders, 8 parts of basalt fibres, 0.7 part of bamboo pulp
After fiber, 1 part of sodium lignin sulfonate, 24 parts of biogas residue cement microballoons are well mixed, 0.5 times heavy of shale quality is added thereto
Water, rear ripening is mixed evenly after 19 hours, adds into mould, after compressing, be dried, sinter to be made and support
Grow pond fragment of brick.
Specifically, above-mentioned steps（1）In, the water content of biogas residue is 4%.
Specifically, above-mentioned steps（2）In, the Average Particle Diameters of shale are 0.8mm.
Specifically, above-mentioned steps（2）In, a diameter of 700 μm of basalt fibre, length 9mm, the diameter of bamboo pulp fiber
For 0.02mm, length 5mm.
Specifically, above-mentioned steps（2）In, the temperature of sintering is 830 DEG C, and the time of sintering is 3 hours.
Embodiment 3
A kind of preparation method of culturing pool fragment of brick, including following operating procedure：
（1）According to mass ratio it is 22 by biogas residue and portland cement:After 7 ratio mixing, portland cement weight is added thereto
After measuring 0.5 times of heavy water, stir, prepare biogas residue cement microballoon, the average grain diameter for controlling microballoon is 4mm；
（2）By weight, by 70 parts of shale, 15 parts of flyash, 6 parts of melting silicon powders, 9 parts of basalt fibres, 0.8 part of bamboo pulp
After fiber, 2 parts of sodium lignin sulfonates, 26 parts of biogas residue cement microballoons are well mixed, 0.6 times heavy of shale quality is added thereto
Water, rear ripening is mixed evenly after 20 hours, adds into mould, after compressing, be dried, sinter to be made and support
Grow pond fragment of brick.
Specifically, above-mentioned steps（1）In, the water content of biogas residue is 5%.
Specifically, above-mentioned steps（2）In, the Average Particle Diameters of shale are 1mm.
Specifically, above-mentioned steps（2）In, a diameter of 800 μm of basalt fibre, length 10mm, bamboo pulp fiber it is straight
Footpath is 0.03mm, length 6mm.
Specifically, above-mentioned steps（2）In, the temperature of sintering is 850 DEG C, and the time of sintering is 4 hours.
Comparative example 1
Step（2）In, biogas residue cement microballoon is changed into etc. to the portland cement of weight, remaining fragment of brick preparation method and embodiment 1
It is identical.
Fragment of brick is made with the method for each embodiment and comparative example respectively, the wherein fragment of brick of control group is commercially available common fragment of brick,
Then fragment of brick sample is placed in 5 times of heavy water of its weight, checks that the water absorption rate of fragment of brick and fragment of brick are put into water body pH after 20min
Change, result of the test is as shown in table 1：
| Project | Water absorption rate, % | Water body pH changes |
| Embodiment 1 | 6 | It is constant |
| Comparative example 1 | 13 | Rise 3 |
| Embodiment 2 | 5 | It is constant |
| Embodiment 3 | 5 | It is constant |
| Control group | 21 | Rise 3 |
As shown in Table 1, using fragment of brick produced by the present invention, not only water absorption rate is relatively low, and the pH value of water body will not be caused to raise,
It is suitable as piling up culturing pool use.
It should be appreciated that the application of the present invention is not limited to above-mentioned citing, for those of ordinary skills, can
To be improved or converted according to the above description, all these modifications and variations should all belong to the guarantor of appended claims of the present invention
Protect scope.
Claims (5)
1. a kind of preparation method of culturing pool fragment of brick, it is characterised in that including following operating procedure：
（1）According to mass ratio it is 18-22 by biogas residue and portland cement:After 7 ratio mixing, portland cement is added thereto
After the water that 0.3-0.5 times of weight weighs, stir, prepare biogas residue cement microballoon, the average grain diameter for controlling microballoon is 2-4mm；
（2）By weight, 64-70 parts shale, 11-15 parts flyash, 3-6 parts are melted into silicon powder, 6-9 parts basalt fibre
After dimension, 0.5-0.8 parts bamboo pulp fiber, 1-2 parts sodium lignin sulfonate, 20-26 part biogas residue cement microballoon are well mixed, add thereto
Enter the water that 0.4-0.6 times of shale quality weighs, after rear ripening 18-20 hours are mixed evenly, add into mould, suppress
After shaping, it is dried, sinters obtained culturing pool fragment of brick.
A kind of 2. preparation method of culturing pool fragment of brick according to claim 1, it is characterised in that above-mentioned steps（1）In,
The water content of biogas residue is 3-5%.
A kind of 3. preparation method of culturing pool fragment of brick according to claim 1, it is characterised in that above-mentioned steps（2）In,
The Average Particle Diameters of shale are 0.6-1mm.
A kind of 4. preparation method of culturing pool fragment of brick according to claim 1, it is characterised in that above-mentioned steps（2）In,
A diameter of 600-800 μm of basalt fibre, length 8-10mm, a diameter of 0.01-0.03mm of bamboo pulp fiber, length 4-
6mm。
A kind of 5. preparation method of culturing pool fragment of brick according to claim 1, it is characterised in that above-mentioned steps（2）In,
The temperature of sintering is 800-850 DEG C, and the time of sintering is 2-4 hours.