CN107757063A - A kind of glass-fiber-fabric and its processing technology - Google Patents
A kind of glass-fiber-fabric and its processing technology Download PDFInfo
- Publication number
- CN107757063A CN107757063A CN201711082078.2A CN201711082078A CN107757063A CN 107757063 A CN107757063 A CN 107757063A CN 201711082078 A CN201711082078 A CN 201711082078A CN 107757063 A CN107757063 A CN 107757063A
- Authority
- CN
- China
- Prior art keywords
- frame
- fabric
- fiber
- cloth
- glass
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a kind of glass-fiber-fabric and its processing technology, belongs to Strand Feeding Technique field.This glass-fiber-fabric, including fiberglass layer, described fiberglass layer uses thread count as 30X30 pieces/inch of woven fabric, the warp and weft of woven fabric use 1000D dacron thread, it is characterized in that, the both sides of described fiberglass layer are covered with PVC coatings one and PVC coatings two respectively, and the side of PVC coatings one is sequentially provided with waterproof layer one, flame-retardant layer one and PVC coatings three from inside to outside, and the side of PVC coatings two is sequentially provided with waterproof layer two, flame-retardant layer two and PVC coatings four from inside to outside.The present invention has the advantages of fire-retardant, waterproof, fold resistant rupture.
Description
Technical field
The invention belongs to fabric technical field, is related to a kind of glass-fiber-fabric and its production technology.
Background technology
Coating fabric is a kind of fabric handled through special process.It is exactly to utilize solvent or water by required coating micelle
(having PU glue, A/C glue, PVC, PE glue) etc. is dissolved into salivation shape, then (cylinder, scraper or roller) uniformly applies in one way
(there are the base materials such as cotton, terylene, polyamide fibre) on cloth, then pass through the set of oven temperature again, make to form one in web surface
The uniform covering sizing material of layer, windproof so as to reach waterproof, the function such as ventilative.
Due to the difference of coating fabric application field, the property indices required for coating fabric are also different.For mesh
Preceding coating fabric uses field, makes that fabric is provided simultaneously with fire-retardant, waterproof, fold resistant fracture is also a lack of, so, for
Those skilled in the art, it need that this coating fabric is researched and developed and produced and processed.
During being processed to this kind of coating fabric, that is, when coating is coated onto on coating fabric, it is necessary to using
Laminating equipment, after completion is laminating, it is also necessary to which, using drying plant etc., existing laminating equipment is laminating in the presence of two shell fabrics are merely able to
Deficiency the problems such as causing laminating efficiency low, and existing drying plant exists and is merely able to single drying and causes baking operation
The problems such as more and complicated, efficiency is low.
So for those skilled in the art, when needing to carry out laminating to this coating fabric and during drying
Equipment is researched and developed and produced and processed, and improves the laminating efficiency of fabric, to improve the quality of fabric.
The content of the invention
First purpose of the present invention is above mentioned problem be present for existing technology, it is proposed that a kind of glass-fiber-fabric, this hair
It is bright that there is the characteristics of fire-retardant, waterproof, fold resistant fracture.
First purpose of the present invention can be realized by following technical proposal:A kind of glass-fiber-fabric, including fiberglass layer, it is described
Fiberglass layer use thread count as 30X30 pieces/inch of woven fabric, the warp and weft of woven fabric use 1000D terylene
Silk, it is characterised in that the both sides of described fiberglass layer are covered with PVC coatings one and PVC coatings two, the side of PVC coatings one respectively
Waterproof layer one, flame-retardant layer one and PVC coatings three are sequentially provided with from inside to outside, and the side of PVC coatings two is sequentially provided with from inside to outside
Waterproof layer two, flame-retardant layer two and PVC coatings four.
This glass-fiber-fabric, by setting PVC coatings one and PVC coatings two, PVC coatings three and PVC coatings four to make coating fabric
Possesses performance not easy to break;By setting flame-retardant layer one and flame-retardant layer two coating fabric is possessed nonflammable performance;It is logical
Cross and set waterproof layer one and waterproof layer two coating fabric is possessed the performance being not easy into water, infiltration.
In above-mentioned glass-fiber-fabric, the thickness of described fiberglass layer is 0.2-0.3mm.
In above-mentioned glass-fiber-fabric, described PVC coatings one are equal with the thickness of PVC coatings two close, and are 0.05-
0.1mm, described PVC coatings three are equal with the thickness of PVC coatings four close, and are 0.08-0.13mm.
In above-mentioned glass-fiber-fabric, described flame-retardant layer one and flame-retardant layer two are polyurethane coating layer, the He of flame-retardant layer one
The thickness of flame-retardant layer two is 0.05-0.1mm.
In above-mentioned glass-fiber-fabric, described waterproof layer one and waterproof layer two are JS waterproof coating layers, the He of waterproof layer one
The thickness of waterproof layer two is 0.05-0.1mm
Second object of the present invention is above mentioned problem be present for existing technology, it is proposed that a kind of processing of glass-fiber-fabric
Technique, the present invention have the characteristics of PVC coatings can be combined on glass-fiber-fabric.
Second object of the present invention can be realized by following technical proposal:A kind of processing technology of glass-fiber-fabric, it is special
Sign is, comprises the following steps:
A, using washing method by the removing residues on glass-fiber-fabric surface;
B, cloth feeding;
C, using thermal composite machine that glass-fiber-fabric and PVC coatings one and PVC coatings two is compound, combined temp is 200 °;
D, first drying is carried out using dryer;
E, once cooled down;
F, using thermal composite machine by PVC coatings one and PVC coatings three and PVC coatings two and PVC coatings four compound, compound temperature
Spend for 200 °;
G, secondary drying is carried out using dryer;
H, secondary cooling is carried out;
I, impression;
J, wind.
In the processing technology of above-mentioned glass-fiber-fabric, the thermal composite machine in described c, f includes frame one, frame one it is upper
Side is provided with base fabric unreeling structure, and base fabric unreeling structure includes let off roll one, and let off roll one is to circumferentially rotate and the side of axial restraint
Formula is arranged in frame one, and the left and right sides of frame one is provided with face cloth unreeling structure one and face cloth unreeling structure two, and face cloth unreels
Mechanism one includes let off roll two, let off roll two by circumferentially rotate and axial restraint in a manner of be arranged in frame one, face cloth unreels
Mechanism two includes let off roll three, let off roll three by circumferentially rotate and axial restraint in a manner of be arranged in frame one, its feature exists
In the left and right sides of frame one is provided with can be respectively to the gumming mechanism of base fabric both sides gluing, and described gumming mechanism includes setting
Upper glue roller one in the side of frame one, upper glue roller one are connected with a regulation cylinder one, have cavity one, upper glue roller in upper glue roller one
One uniformly offers some plastic holes one, and plastic emitting shower nozzle one is mounted in plastic hole one, and the downside of upper glue roller one is provided with and can incited somebody to action
The spreading roller one that glue uniformly scratches, spreading roller one are arranged on by way of circumferentially rotating axial restraint in frame one, frictioning
Some frictioning brushes are uniformly provided with roller one, the both ends of frictioning brush one are equipped with bearing and bearing block, used between two bearing blocks
Link one connects, and described link one is connected with a regulation cylinder two;Described gumming mechanism also includes being arranged on frame
The upper glue roller two of one opposite side, upper glue roller two are connected with a regulation cylinder three, and upper glue roller two is interior to have a cavity two, and upper glue roller two is equal
It is even to offer some plastic holes two, plastic emitting shower nozzle two is mounted in plastic hole two, the downside of upper glue roller two is provided with can be by glue
The spreading roller two uniformly scratched, spreading roller two are arranged on by way of circumferentially rotating axial restraint in frame one, spreading roller two
On be uniformly provided with some frictioning brushes, the both ends of frictioning brush two are equipped with bearing and bearing block, using connection between two bearing blocks
Frame two connects, and described link two is connected with a regulation cylinder four;Being additionally provided with described frame one can be by base fabric and two pieces
The fit body of face cloth fitting, described fit body include composite roll one and composite roll two, and described composite roll one is with circumference
Rotate and the mode of axial restraint is arranged in frame one, composite roll two is provided with and can adjusted between composite roll one and composite roll two
The adjustment structure in gap.
Its operation principle is such:First, base fabric is carried out by base fabric unreeling structure unreeling feeding;Then, base fabric
Double spread is carried out in the presence of gumming mechanism, and is entered glue on the two sides of base fabric by frictioning brush one and frictioning brush two
Row smoothens;Then, the face cloth of base fabric once is unreeled by face cloth unreeling structure one, while passes through face cloth unreeling structure two
The base fabric face cloth of another time is unreeled;Finally, base fabric is bonded with the face cloth of its both sides in the presence of fit body,
So that the face cloth of base fabric and base fabric both sides carries out laminating simultaneously, cloth is set to reach laminating effect.
In the processing technology of above-mentioned glass-fiber-fabric, described adjustment structure includes being arranged on the bearing at the both ends of composite roll two
One and bearing two, one end of the inner ring and composite roll two of bearing one fix, the outer ring of bearing one is fixed with bearing block one, bearing block
One is slidably arranged in frame one, and the other end of the inner ring and composite roll two of bearing two is fixed, and the outer ring of bearing two is fixed with axle
Bearing two, bearing block two are slidably arranged in frame one.
In the processing technology of above-mentioned glass-fiber-fabric, chute one and chute two, bearing block are offered in described frame one
One is slidably arranged in chute one, and bearing block two is slidably arranged in chute two, passes through one between bearing block one and bearing block two
Connecting rod connects, and is further fixed on adjusting cylinder five in described frame one, the piston rod end of regulation cylinder five is consolidated with connecting rod
Even.
In the processing technology of above-mentioned glass-fiber-fabric, the dryer in described d, g includes frame two and is arranged on frame
There is the casing of cavity on two, offer a charging aperture in the lower wall of casing side, opened up on the upper side wall of casing opposite side
There is a discharging opening, it is characterised in that dividing plate one and dividing plate two setting up and down are laterally fixed with described cavity, at dividing plate one
In the lower section of dividing plate two, dividing plate one and dividing plate two divide the cavity into upper plenum, middle cavity, lower cavity, and punishment in advance is opened up on dividing plate one
Mouthful one, offered material mouth two on dividing plate two, if on lower cavity inner wall by circumferentially rotate and axial restraint in a manner of horizontal be provided with
A dry group heating roller group, heating roller group include two heating rollers setting up and down, between two heating rollers formation rolled for cloth logical
The gap crossed, in lower cavity one end away from charging aperture by circumferentially rotate and axial restraint in a manner of level supply cloth provided with one group
The guide roller one passed through;The drying mechanism that can be dried to cloth is provided with middle cavity, drying mechanism includes electric hot plate one
With electric hot plate two, electric hot plate one is fixed on by mobile cylinder one on the upper face of dividing plate one, and electric hot plate two passes through mobile cylinder
Two are fixed on the lower face of dividing plate two, and electric hot plate one and electric hot plate two are oppositely arranged, the both ends of middle cavity to circumferentially rotate and
The mode of axial restraint is horizontal to be provided with two groups of guide rollers two passed through for cloth;Being provided with upper plenum can be carried out quickly to cloth
Air-dried air-dried mechanism, air-drying mechanism includes hot gas production case, up-draught head and lower blowing head, and hot gas production case is fixed on casing
On, up-draught head, which is fixed on the roof of casing by mobile cylinder three and produces case with hot gas by snorkel one, to be connected,
Lower blowing head, which is fixed on the upper face of dividing plate two by mobile cylinder four and produces case with hot gas by snorkel two, to be connected,
Up-draught head and it is lower blowing head be oppositely arranged, in upper plenum away from discharging opening one end by circumferentially rotate and axial restraint in a manner of
Level is provided with one group of guide roller three.
Its operation principle is such:First, cloth in the presence of the feed roller from cavity under charging aperture entrance, some
In the presence of group heating roller, cloth is from upper and lower two corresponding heating rollers by carrying out tentatively rolling drying to cloth, together
When, in the presence of guide roller group one and one of which guide roller group two, guiding cloth enters middle cavity from lower cavity;So
Afterwards, when cavity in cloth entrance, in the presence of mobile cylinder one and mobile cylinder two, by driving electric hot plate one and electric heating
Plate two makes it dry cloth again close to cloth, meanwhile, in the presence of guide roller group two and guide roller group three, draw
Therefrom cavity enters upper plenum to selvage guide material;Finally, the hot blast of hot gas production case by snorkel one and snorkel two respectively from
Up-draught head and lower blowing head blowout, blow to the surface of cloth, the upper and lower surface of cloth are air-dried, finally going out
Cloth discharges from discharging opening in the presence of material roller, completes the drying of cloth.
In the processing technology of above-mentioned glass-fiber-fabric, two horizontally disposed feed rollers are provided with the outside of described charging aperture,
Two feed rollers by circumferentially rotate and axial restraint in a manner of be arranged in frame two.
In the processing technology of above-mentioned glass-fiber-fabric, two horizontally disposed discharge rollers are provided with the outside of described discharging opening,
Two discharge rollers by circumferentially rotate and axial restraint in a manner of be arranged in frame two.
Compared with prior art, the present invention has advantages below:
1st, this glass-fiber-fabric is by setting PVC coatings one and PVC coatings two, PVC coatings three and PVC coatings four to make coating fabric
Possesses performance not easy to break;By setting flame-retardant layer one and flame-retardant layer two coating fabric is possessed nonflammable performance;It is logical
Cross and set waterproof layer one and waterproof layer two coating fabric is possessed the performance being not easy into water, infiltration.
2nd, the thermal composite machine of this glass-fiber-fabric can carry out spraying glue simultaneously in the presence of gumming mechanism to the both sides of base fabric
Water, in the presence of spreading roller one and spreading roller two, the glue for being sprayed on scrim surfaces can be smoothened, in composite roll one and again
Three layers of direct laminating, efficiency high between base fabric, fabric one and fabric two is realized in the presence of conjunction roller two.
3rd, the dryer of this glass-fiber-fabric is in lower cavity in the presence of heating roller, it is possible to achieve cloth it is preliminary roll it is quick
Drying;In middle cavity in the presence of electric hot plate one and electric hot plate two, it is possible to achieve the drying again of cloth;Finally, in overhead
In chamber in the presence of up-draught head and lower blowing head, it is possible to achieve cloth is air-dried, and cloth drying is realized so as to reach quick
Purpose, treat that cloth comes out, can be packed.
Brief description of the drawings
Fig. 1 is the structural representation of this glass-fiber-fabric.
Fig. 2 is the structural representation of thermal composite machine in this processing technology.
Fig. 3 is the structural representation of dryer in this processing technology.
In figure, 1, fiberglass layer;1a, PVC coating one;1b, waterproof layer one;1c, flame-retardant layer one;1d, PVC coating three;1e、
PVC coatings two;1f, waterproof layer two;1g, flame-retardant layer two;1h, PVC coating four;2nd, let off roll one;3rd, let off roll two;4th, let off roll
Three;5th, upper glue roller one;6th, cylinder one is adjusted;7th, plastic emitting shower nozzle one;8th, spreading roller one;9th, cylinder two is adjusted;10th, upper glue roller two;
11st, cylinder three is adjusted;12nd, plastic emitting shower nozzle two;13rd, spreading roller two;14th, cylinder four is adjusted;15th, composite roll one;16th, composite roll
Two;17th, cylinder five is adjusted;18th, casing;19th, dividing plate one;20th, dividing plate two;21st, heating roller;22nd, guide roller one;23rd, electric hot plate
One;24th, electric hot plate two;25th, mobile cylinder one;26th, mobile cylinder two;27th, guide roller two;28th, hot gas production case;29th, blown on
Public attention;30th, lower blowing head;31st, mobile cylinder three;32nd, mobile cylinder four;33rd, guide roller three;34th, feed roller;35th, discharge roller.
Embodiment
It is the specific embodiment of the present invention and with reference to accompanying drawing below, technical scheme is further described,
But the present invention is not limited to these embodiments.
As shown in figure 1, a kind of glass-fiber-fabric, including fiberglass layer 1, fiberglass layer 1 use thread count as 30X30 pieces/inch
Woven fabric, the warp and weft of woven fabric use 1000D dacron thread, and the side of fiberglass layer 1 is covered with PVC coatings one 1a, PVC painting
One 1a of layer side is sequentially provided with the 1b of waterproof layer one, the 1d of one 1c and PVC coatings of flame-retardant layer three from inside to outside, fiberglass layer 1 it is another
The side that side is covered with the 1e of PVC coatings two 1e, PVC coating two is sequentially provided with the 1f of waterproof layer two, the 1g of flame-retardant layer two and PVC from inside to outside
The 1h of coating four.
In the present embodiment, the thickness of fiberglass layer 1 is 0.25mm, specifically, the thickness of the fiberglass layer 1 can be according to making
The actual situation of this coating fabric, is fluctuated between 0.2-0.3mm.
In the present embodiment, the 1e of one 1a and PVC coatings of PVC coatings two thickness is equal close, and is 0.07mm, and PVC is applied
Layer three 1d and PVC coatings four 1h thickness is equal close, and is 0.09mm.Specifically, the 1e of one 1a and PVC coatings of PVC coatings two
Thickness can be actual according to this fabric is made situation, fluctuated between 0.05-0.1mm, 1d the and PVC coatings of PVC coatings three
Four 1h thickness can fluctuate, by setting PVC coatings according to the situation for making this fabric reality between 0.08-0.13mm
The 1h of one 1a and PVC coatings, two 1e, PVC coating, three 1d and PVC coatings four makes coating fabric possess performance not easy to break.
In the present embodiment, the 1c of the flame-retardant layer one and 1g of flame-retardant layer two is polyurethane coating layer, the 1c of flame-retardant layer one and fire-retardant
Two 1g of layer thickness is 0.07mm.Specifically, the 1c of flame-retardant layer one and the 1g of flame-retardant layer two thickness can be real according to this fabric is made
The situation on border, is fluctuated between 0.05-0.1mm, by setting the 1c of flame-retardant layer one and the 1g of flame-retardant layer two coating fabric is possessed not
Incendive performance.
In the present embodiment, the 1b of the waterproof layer one and 1f of waterproof layer two is JS waterproof coating layers, the 1b of waterproof layer one and waterproof
Two 1f of layer thickness is 0.08mm.Specifically, the 1b of waterproof layer one and the 1f of waterproof layer two thickness can be real according to this fabric is made
The situation on border, is fluctuated between 0.05-0.1mm, by setting the 1b of waterproof layer one and the 1f of waterproof layer two coating fabric is possessed not
Easily intake, the performance of infiltration.
A kind of processing technology of glass-fiber-fabric, comprises the following steps:
A, using washing method by the removing residues on glass-fiber-fabric surface;
B, cloth feeding;
C, using thermal composite machine that glass-fiber-fabric and one 1a and PVC coatings of PVC coatings, two 1e is compound, combined temp is 200 °;
D, first drying is carried out using dryer;
E, once cooled down;
F, the 1h of three 1d and PVC coatings of the 1a of PVC coatings one and PVC coatings, two 1e and PVC coatings four is answered using thermal composite machine
Close, combined temp is 200 °;
G, secondary drying is carried out using dryer;
H, secondary cooling is carried out;
I, impression;
J, wind.
As shown in Fig. 2 thermal composite machine includes frame one, the top of frame one is provided with base fabric unreeling structure, base fabric unreeling machine
Structure includes let off roll 1, let off roll 1 by circumferentially rotate and axial restraint in a manner of be arranged in frame one, a left side for frame one
Right both sides are provided with face cloth unreeling structure one and face cloth unreeling structure two, and face cloth unreeling structure one includes let off roll 23, let off roll two
3 by circumferentially rotate and axial restraint in a manner of be arranged in frame one, face cloth unreeling structure two includes let off roll 34, let off roll
34 by circumferentially rotate and axial restraint in a manner of be arranged in frame one.
The left and right sides of frame one is provided with can be respectively to the gumming mechanism of base fabric both sides gluing.Gumming mechanism includes being arranged on
The upper glue roller 1 of the side of frame one, upper glue roller 1 are connected with a regulation cylinder 1, have cavity one in upper glue roller 1, glue
Roller 1 uniformly offers some plastic holes one, and plastic emitting shower nozzle 1 is mounted in plastic hole one, and the downside of upper glue roller 1 is provided with
The spreading roller 1 that glue uniformly scratches, spreading roller 1 can be arranged on frame one by way of circumferentially rotating axial restraint
On, some frictioning brushes are uniformly provided with spreading roller 1, the both ends of frictioning brush one are equipped with bearing and bearing block, two bearing blocks
Between connected using link one, described link one with one regulation cylinder 29 be connected;Described gumming mechanism also includes setting
The upper glue roller 2 10 in the opposite side of frame one is put, upper glue roller 2 10 is connected with a regulation cylinder 3 11, had in upper glue roller 2 10
Cavity two, upper glue roller 2 10 uniformly offer some plastic holes two, plastic emitting shower nozzle 2 12, upper glue roller are mounted in plastic hole two
2 10 downside is provided with can be by the spreading roller 2 13 that glue uniformly scratches, and spreading roller 2 13 is by circumferentially rotating the side of axial restraint
Formula is arranged in frame one, and some frictioning brushes are uniformly provided with spreading roller 2 13, and the both ends of frictioning brush two are equipped with bearing and axle
Bearing, connected using link two between two bearing blocks, described link two is connected with a regulation cylinder 4 14.
Composite roll 1 can be included by base fabric and the fit body of two pieces of face cloth fittings, fit body by being additionally provided with frame one
With composite roll 2 16, composite roll 1 by circumferentially rotate and axial restraint in a manner of be arranged in frame one, on composite roll 2 16
Provided with the adjustment structure that can adjust gap between composite roll 1 and composite roll 2 16.Adjustment structure includes being arranged on composite roll two
The bearing one and bearing two at 16 both ends, one end of the inner ring and composite roll 2 16 of bearing one are fixed, and the outer ring of bearing one is fixed with
Bearing block one, bearing block one are slidably arranged in frame one, and the other end of the inner ring and composite roll 2 16 of bearing two is fixed, bearing
Two outer ring is fixed with bearing block two, and bearing block two is slidably arranged in frame one.Chute one and chute are offered in frame one
Two, bearing block one is slidably arranged in chute one, and bearing block two is slidably arranged in chute two, bearing block one and bearing block two it
Between connected by a connecting rod, be further fixed in described frame one adjusting cylinder 5 17, adjust the tailpiece of the piston rod of cylinder 5 17
Portion is connected with connecting rod.
Its operation principle is such:First, base fabric is carried out by base fabric unreeling structure unreeling feeding;Then, base fabric
Double spread is carried out in the presence of gumming mechanism, and is entered glue on the two sides of base fabric by frictioning brush one and frictioning brush two
Row smoothens;Then, the face cloth of base fabric once is unreeled by face cloth unreeling structure one, while passes through face cloth unreeling structure two
The base fabric face cloth of another time is unreeled;Finally, base fabric is bonded with the face cloth of its both sides in the presence of fit body,
So that the face cloth of base fabric and base fabric both sides carries out laminating simultaneously, cloth is set to reach laminating effect.
As shown in figure 3, dryer includes frame two and is arranged on the casing 18 in frame two with cavity, the side of casing 18
Lower wall on offer a charging aperture, offer a discharging opening on the upper side wall of the opposite side of casing 18, be provided with the outside of charging aperture
Two horizontally disposed feed rollers 34, two feed rollers 34 by circumferentially rotate and axial restraint in a manner of be arranged on frame two
On.It is provided with two horizontally disposed discharge rollers 35 on the outside of discharging opening, two discharge rollers 35 are to circumferentially rotate and axial restraint
Mode is arranged in frame two.Dividing plate 1 and dividing plate 2 20 setting up and down are laterally fixed with cavity, dividing plate 1 is in
The lower section of dividing plate 2 20, dividing plate 1 and dividing plate 2 20 divide the cavity into upper plenum, middle cavity, lower cavity, are opened on dividing plate 1
If crossing material mouth one, material mouth two was offered on dividing plate 2 20.
On lower cavity inner wall by circumferentially rotate and axial restraint in a manner of horizontal be provided with some groups of 21 groups of heating rollers, heating roller
21 groups include two heating rollers 21 setting up and down, are formed between two heating rollers 21 and roll the gap passed through, lower sky for cloth
In chamber one end away from charging aperture by circumferentially rotate and axial restraint in a manner of horizontal be provided with one group of guide roller passed through for cloth
One 22.
The drying mechanism that can be dried to cloth is provided with middle cavity, drying mechanism includes electric hot plate 1 and electric heating
Plate 2 24, electric hot plate 1 are fixed on by mobile cylinder 1 on the upper face of dividing plate 1, and electric hot plate 2 24 passes through movement
Cylinder 2 26 is fixed on the lower face of dividing plate 2 20, and electric hot plate 1 and electric hot plate 2 24 are oppositely arranged, the both ends of middle cavity
By circumferentially rotate and axial restraint in a manner of horizontal be provided with two groups of guide rollers 2 27 passed through for cloth.
The air-dried mechanism of Quick-air-drying can be carried out to cloth by being provided with upper plenum, and air-drying mechanism includes hot gas production case
28th, up-draught first 29 and lower blowing first 30, hot gas production case 28 are fixed on casing 18, and up-draught first 29 passes through mobile cylinder three
31 are fixed on the roof of casing 18 and are connected by snorkel one with hot gas production case 28, and lower blowing first 30 passes through mobile gas
Cylinder 4 32, which is fixed on the upper face of dividing plate 2 20 and produces case 28 with hot gas by snorkel two, to be connected, first 29 He of up-draught
Lower blowing first 30 is oppositely arranged, in upper plenum one end away from discharging opening by circumferentially rotate and axial restraint in a manner of level be provided with
One group of guide roller 3 33.
Its operation principle is such:First, cloth in the presence of the feed roller 34 from cavity under charging aperture entrance, if
In the presence of dry group heating roller 21, cloth is from upper and lower two corresponding heating rollers 21 by carrying out tentatively rolling baking to cloth
It is dry, meanwhile, in the presence of guide roller group one and one of which guide roller group two, guiding cloth enters hollow from lower cavity
Chamber;Then, when cavity in cloth entrance, in the presence of mobile cylinder 1 and mobile cylinder 2 26, band electro kinetic potential is passed through
Plate 1 and electric hot plate 2 24 make it dry cloth again close to cloth, meanwhile, in guide roller group two and guide roller group
In the presence of three, therefrom cavity enters upper plenum to guiding cloth;Finally, the hot blast of hot gas production case 28 passes through the He of snorkel one
Snorkel two is blown out from up-draught first 29 and lower blowing first 30 respectively, blows to the surface of cloth, upper surface and following table to cloth
Face is air-dried, and finally cloth discharges from discharging opening in the presence of discharge roller 35, completes the drying of cloth.
Specific embodiment described herein is only to spirit explanation for example of the invention.Technology belonging to the present invention is led
The technical staff in domain can be made various modifications or supplement to described specific embodiment or be replaced using similar mode
Generation, but without departing from the spiritual of the present invention or surmount scope defined in appended claims.
Although 1, fiberglass layer has more been used herein;1a, PVC coating one;1b, waterproof layer one;1c, flame-retardant layer one;1d、
PVC coatings three;1e, PVC coating two;1f, waterproof layer two;1g, flame-retardant layer two;1h, PVC coating four;2nd, let off roll one;3rd, unreel
Roller two;4th, let off roll three;5th, upper glue roller one;6th, cylinder one is adjusted;7th, plastic emitting shower nozzle one;8th, spreading roller one;9th, cylinder two is adjusted;
10th, upper glue roller two;11st, cylinder three is adjusted;12nd, plastic emitting shower nozzle two;13rd, spreading roller two;14th, cylinder four is adjusted;15th, composite roll
One;16th, composite roll two;17th, cylinder five is adjusted;18th, casing;19th, dividing plate one;20th, dividing plate two;21st, heating roller;22nd, guide roller
One;23rd, electric hot plate one;24th, electric hot plate two;25th, mobile cylinder one;26th, mobile cylinder two;27th, guide roller two;28th, hot gas is given birth to
Produce case;29th, up-draught head;30th, lower blowing head;31st, mobile cylinder three;32nd, mobile cylinder four;33rd, guide roller three;34th, feed
Roller;35th, the term such as discharge roller, but it is not precluded from the possibility using other terms.Using these terms just for the sake of more square
Just the essence of the present invention is described and explained;Being construed as any additional limitation is disagreed with spirit of the present invention
The back of the body.
Claims (10)
1. a kind of glass-fiber-fabric, including fiberglass layer, described fiberglass layer uses thread count as 30X30 pieces/inch of woven fabric, shuttle
The warp and weft weaved cotton cloth use 1000D dacron thread, it is characterised in that the both sides of described fiberglass layer are covered with PVC paintings respectively
One and PVC of layer coatings two, the side of PVC coatings one is sequentially provided with waterproof layer one, flame-retardant layer one and PVC coatings three from inside to outside,
The side of PVC coatings two is sequentially provided with waterproof layer two, flame-retardant layer two and PVC coatings four from inside to outside.
2. glass-fiber-fabric according to claim 1, it is characterised in that the thickness of described fiberglass layer is 0.2-0.3mm.
3. glass-fiber-fabric according to claim 1, it is characterised in that described PVC coatings one and the thickness phase of PVC coatings two
Etc. close, and it is 0.05-0.1mm, described PVC coatings three are equal with the thickness of PVC coatings four close, and are 0.08-
0.13mm。
4. glass-fiber-fabric according to claim 1, it is characterised in that described flame-retardant layer one and flame-retardant layer two is polyurethane
The thickness of dope layer, flame-retardant layer one and flame-retardant layer two is 0.05-0.1mm.
5. glass-fiber-fabric according to claim 1, it is characterised in that described waterproof layer one and waterproof layer two is JS waterproofs
The thickness of dope layer, waterproof layer one and waterproof layer two is 0.05-0.1mm.
6. a kind of processing technology of glass-fiber-fabric, it is characterised in that comprise the following steps:
A, using washing method by the removing residues on glass-fiber-fabric surface;
B, cloth feeding;
C, using thermal composite machine that glass-fiber-fabric and PVC coatings one and PVC coatings two is compound, combined temp is 200 °;
D, first drying is carried out using dryer;
E, once cooled down;
F, using thermal composite machine that PVC coatings one and PVC coatings three and PVC coatings two and PVC coatings four is compound, combined temp is
200°;
G, secondary drying is carried out using dryer;
H, secondary cooling is carried out;
I, impression;
J, wind.
7. glass-fiber-fabric according to claim 6, it is characterised in that the thermal composite machine in described c, f includes frame one, machine
The top of frame one is provided with base fabric unreeling structure, and base fabric unreeling structure includes let off roll one, and let off roll one is to circumferentially rotate and axially
Fixed mode is arranged in frame one, and the left and right sides of frame one is provided with face cloth unreeling structure one and face cloth unreeling structure two,
Face cloth unreeling structure one includes let off roll two, let off roll two by circumferentially rotate and axial restraint in a manner of be arranged in frame one,
Face cloth unreeling structure two includes let off roll three, let off roll three by circumferentially rotate and axial restraint in a manner of be arranged in frame one,
Characterized in that, the left and right sides of frame one be provided with can be respectively to the gumming mechanism of base fabric both sides gluing, described gumming mechanism
Upper glue roller one including being arranged on the side of frame one, upper glue roller one are connected with a regulation cylinder one, have cavity in upper glue roller one
One, upper glue roller one uniformly offers some plastic holes one, and plastic emitting shower nozzle one, the downside of upper glue roller one are mounted in plastic hole one
Provided with the spreading roller one that glue uniformly scratches, spreading roller one being arranged on into frame one by way of circumferentially rotating axial restraint
On, be uniformly provided with some frictioning brushes on spreading roller one, the both ends of frictioning brush one are equipped with bearing and bearing block, two bearing blocks it
Between connected using link one, described link one with one regulation cylinder two be connected;Described gumming mechanism also includes setting
In the upper glue roller two of the opposite side of frame one, upper glue roller two is connected with a regulation cylinder three, has cavity two in upper glue roller two, glue
Roller two uniformly offers some plastic holes two, and plastic emitting shower nozzle two is mounted in plastic hole two, and the downside of upper glue roller two is provided with energy
The spreading roller two that glue is uniformly scratched, spreading roller two are arranged in frame one by way of circumferentially rotating axial restraint, scraped
Some frictioning brushes are uniformly provided with rubber roll two, the both ends of frictioning brush two are equipped with bearing and bearing block, adopted between two bearing blocks
Connected with link two, described link two is connected with a regulation cylinder four;Being additionally provided with described frame one can be by base fabric
With the fit body of two pieces of face cloth fittings, described fit body includes composite roll one and composite roll two, described composite roll one
By circumferentially rotate and axial restraint in a manner of be arranged in frame one, composite roll two be provided with can adjust composite roll one and composite roll
The adjustment structure in gap between two.
8. glass-fiber-fabric according to claim 7, it is characterised in that described adjustment structure includes being arranged on two liang of composite roll
The bearing one and bearing two at end, one end of the inner ring and composite roll two of bearing one are fixed, and the outer ring of bearing one is fixed with bearing block
One, bearing block one is slidably arranged in frame one, and the other end of the inner ring and composite roll two of bearing two is fixed, the outer ring of bearing two
Bearing block two is fixed with, bearing block two is slidably arranged in frame one.
9. glass-fiber-fabric according to claim 8, it is characterised in that offer chute one and chute in described frame one
Two, bearing block one is slidably arranged in chute one, and bearing block two is slidably arranged in chute two, bearing block one and bearing block two it
Between connected by a connecting rod, be further fixed in described frame one adjusting cylinder five, adjust the piston rod end of cylinder five with
Connecting rod is connected.
10. glass-fiber-fabric according to claim 6, it is characterised in that the dryer in described d, g includes frame two and set
Put has the casing of cavity in frame two, and a charging aperture, the upside of casing opposite side are offered in the lower wall of casing side
A discharging opening is offered on wall, it is characterised in that dividing plate one and dividing plate two setting up and down are laterally fixed with described cavity,
Dividing plate one is in the lower section of dividing plate two, and dividing plate one and dividing plate two divide the cavity into upper plenum, middle cavity, lower cavity, on dividing plate one
Opened up material mouth one, offered material mouth two on dividing plate two, on lower cavity inner wall by circumferentially rotate and axial restraint in a manner of water
Flat to be provided with some groups of heating roller groups, heating roller group includes two heating rollers setting up and down, is formed between two heating rollers and supply cloth
Material rolls the gap that passes through, in lower cavity one end away from charging aperture by circumferentially rotate and axial restraint in a manner of horizontal be provided with one
The guide roller one that group passes through for cloth;The drying mechanism that can be dried to cloth is provided with middle cavity, drying mechanism includes
Electric hot plate one and electric hot plate two, electric hot plate one are fixed on by mobile cylinder one on the upper face of dividing plate one, and electric hot plate two passes through
Mobile cylinder two is fixed on the lower face of dividing plate two, and electric hot plate one and electric hot plate two are oppositely arranged, and the both ends of middle cavity are with week
Two groups of guide rollers two passed through for cloth are provided with to the mode of rotation and axial restraint is horizontal;Being provided with upper plenum can be to cloth
The air-dried mechanism of Quick-air-drying is carried out, air-drying mechanism includes hot gas production case, up-draught head and lower blowing head, and hot gas production case is consolidated
It is scheduled on casing, up-draught head is fixed on the roof of casing by mobile cylinder three and produces case by snorkel one and hot gas
It is connected, lower blowing head is fixed on the upper face of dividing plate two by mobile cylinder four and produces case by snorkel two and hot gas
It is connected, up-draught head and lower blowing head are oppositely arranged, and one end away from discharging opening is to circumferentially rotate and axially solid in upper plenum
Fixed mode is horizontal to be provided with one group of guide roller three.