CN107747211A - A kind of preparation method of antibacterial silk elasticity fabric - Google Patents
A kind of preparation method of antibacterial silk elasticity fabric Download PDFInfo
- Publication number
- CN107747211A CN107747211A CN201710756334.5A CN201710756334A CN107747211A CN 107747211 A CN107747211 A CN 107747211A CN 201710756334 A CN201710756334 A CN 201710756334A CN 107747211 A CN107747211 A CN 107747211A
- Authority
- CN
- China
- Prior art keywords
- parts
- fabric
- antibacterial
- silk
- degree
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of preparation method of antibacterial silk elasticity fabric, belong to field of textile.The preparation method of this kind of antibacterial silk elasticity fabric, during fabric is made, technique simply and readily controls this method.The antibacterial silk elasticity fabric that this method manufactures assigns chemical fiber plus material with soft and smooth elastic feel as silk.The immersion of weaving Antibacterial accessory ingredient is added during preparation so that fabric has stronger antibiotic property, while has both the warming and cold-resistant performance of anti-suede, and the fabric also has the characteristics of tearing toughness is good in addition.The fabric be particularly suitable for use in feather dress fabric and directly contact skin clothing fabric.
Description
Technical field
The present invention relates to a kind of preparation method of antibacterial silk elasticity fabric, belong to field of textile.
Background technology
With the continuous improvement of people's living standards, requirement of the people to clothing performance improves constantly.Fabric is to clothes
It can be played an important role with the quality of quality.Elasticity, antibiotic property, feel and the warmth retention property of fabric are increasingly by the weight of people
Depending on.
A kind of preparation method of antibacterial silk elasticity fabric of the present invention, this method is during fabric is made, technique
Simply and readily control.The antibacterial silk elasticity fabric that this method manufactures assigns chemical fiber plus material with soft and smooth elastic hand as silk
Sense.The immersion of weaving Antibacterial accessory ingredient is added during preparation so that fabric has stronger antibiotic property, has both simultaneously
The warming and cold-resistant performance of anti-suede, in addition the fabric also there is the characteristics of tearing toughness is good.The fabric is particularly suitable for use in eider down
Take fabric and directly the clothing fabric of contact skin.
The content of the invention
In order to overcome defect present in background technology, the technical solution adopted for the present invention to solve the technical problems is：
A kind of preparation method of antibacterial silk elasticity fabric, its step are：
（1）Cloth is connect, cloth machine margin to seam, upper A cabinet frames package are connect using flatcar；
（2）Pad, padded using forming machine, the composition of padding liquid is according to parts by weight：
Water 80-120 parts, silk bullet glue 5-15 parts, bridging agent 3-8 parts, accelerator 1-4 parts；During padding, temperature control exists
135-155 degree, the fabric speed of service are that 55-65 rice is per minute, and pressure is 0.3-0.5 MPas；
（3）Add antiseptic, cloth is immersed in the solution for the weaving Antibacterial accessory ingredient that mass concentration is 5%, the temperature of solution is
65-85 degree, soak time are 15 minutes, and immersion is taken out later, is air-dried under normal temperature；
（4）Upper coating, using coating machine, the composition of coating is according to parts by weight：
Anti-chiseling down glue 30-100 parts, silk bullet glue 30-100 parts, bridging agent 3-8 parts, accelerator 1-4 parts, antiplastering aid 5-15 parts are soft
Agent 5-15 parts, anti-chiseling down glue 5-15 parts；In upper coating procedure, for temperature control in 140-160 degree, the fabric speed of service is 30-
35 meters per minute；
（5）Calendering, using calender, temperature control is 28-38 in 75-85 degree, 800-1000 MPas of pressure, the fabric speed of service
Rice is per minute；
（6）By step（5）Treated fabric clot, packaging prepare antibacterial silk elasticity fabric.
A kind of preparation method of antibacterial silk elasticity fabric of the present invention, this method is during fabric is made, technique
Simply and readily control.The antibacterial silk elasticity fabric that this method manufactures assigns chemical fiber plus material with soft and smooth elastic hand as silk
Sense.The immersion of weaving Antibacterial accessory ingredient is added during preparation so that fabric has stronger antibiotic property, has both simultaneously
The warming and cold-resistant performance of anti-suede, in addition the fabric also there is the characteristics of tearing toughness is good.The fabric is particularly suitable for use in eider down
Take fabric and directly the clothing fabric of contact skin.
Embodiment
Specific embodiment one：A kind of preparation method of antibacterial silk elasticity fabric, its step are：
（1）Cloth is connect, cloth machine margin to seam, upper A cabinet frames package are connect using flatcar；
（2）Pad, padded using forming machine, the composition of padding liquid is according to parts by weight：
80 parts of water, 5 parts of silk bullet glue, 3 parts of bridging agent, 1 part of accelerator；During padding, temperature control at 135 degree, transport by fabric
Scanning frequency degree is 55 meters per minute, and pressure is 0.3 MPa；
（3）Add antiseptic, cloth is immersed in the solution for the weaving Antibacterial accessory ingredient that mass concentration is 5%, the temperature of solution is 65
Degree, soak time are 15 minutes, and immersion is taken out later, is air-dried under normal temperature；
（4）Upper coating, using coating machine, the composition of coating is according to parts by weight：
30 parts of anti-chiseling down glue, 30 parts of silk bullet glue, 3 parts of bridging agent, 1 part of accelerator, 5 parts of antiplastering aid, 5 parts of softening agent, anti-chiseling down glue 5
Part；In upper coating procedure, for temperature control at 140 degree, the fabric speed of service is 30 meters per minute；
（5）Calendering, using calender, for temperature control at 75 degree, 800 MPas of pressure, the fabric speed of service is 28 meters per minute；
（6）By step（5）Treated fabric clot, packaging prepare antibacterial silk elasticity fabric.
Specific embodiment two：A kind of preparation method of antibacterial silk elasticity fabric, its step are：
（1）Cloth is connect, cloth machine margin to seam, upper A cabinet frames package are connect using flatcar；
（2）Pad, padded using forming machine, the composition of padding liquid is according to parts by weight：
110 parts of water, 12 parts of silk bullet glue, 6 parts of bridging agent, 3 parts of accelerator；During padding, temperature control is at 145 degree, fabric
The speed of service is 60 meters per minute, and pressure is 0.4 MPa；
（3）Add antiseptic, cloth is immersed in the solution for the weaving Antibacterial accessory ingredient that mass concentration is 5%, the temperature of solution is 75
Degree, soak time are 15 minutes, and immersion is taken out later, is air-dried under normal temperature；
（4）Upper coating, using coating machine, the composition of coating is according to parts by weight：
65 parts of anti-chiseling down glue, 70 parts of silk bullet glue, 6 parts of bridging agent, 3 parts of accelerator, 8 parts of antiplastering aid, 8 parts of softening agent, anti-chiseling down glue 9
Part；In upper coating procedure, for temperature control at 150 degree, the fabric speed of service is 33 meters per minute；
（5）Calendering, using calender, for temperature control at 80 degree, 900 MPas of pressure, the fabric speed of service is 35 meters per minute；
（6）By step（5）Treated fabric clot, packaging prepare antibacterial silk elasticity fabric.
Specific embodiment three：A kind of preparation method of antibacterial silk elasticity fabric, its step are：
（1）Cloth is connect, cloth machine margin to seam, upper A cabinet frames package are connect using flatcar；
（2）Pad, padded using forming machine, the composition of padding liquid is according to parts by weight：
120 parts of water, 15 parts of silk bullet glue, 8 parts of bridging agent, 4 parts of accelerator；During padding, temperature control is at 155 degree, fabric
The speed of service is 65 meters per minute, and pressure is 0.5 MPa；
（3）Add antiseptic, cloth is immersed in the solution for the weaving Antibacterial accessory ingredient that mass concentration is 5%, the temperature of solution is 85
Degree, soak time are 15 minutes, and immersion is taken out later, is air-dried under normal temperature；
（4）Upper coating, using coating machine, the composition of coating is according to parts by weight：
100 parts of anti-chiseling down glue, 100 parts of silk bullet glue, 8 parts of bridging agent, 4 parts of accelerator, 15 parts of antiplastering aid, 15 parts of softening agent are anti-drilling
15 parts of suede glue；In upper coating procedure, for temperature control at 160 degree, the fabric speed of service is 35 meters per minute；
（5）Calendering, using calender, for temperature control at 85 degree, 1000 MPas of pressure, the fabric speed of service is 38 meters per minute；
（6）By step（5）Treated fabric clot, packaging prepare antibacterial silk elasticity fabric.
A kind of preparation method of antibacterial silk elasticity fabric of the present invention, this method is during fabric is made, technique
Simply and readily control.The antibacterial silk elasticity fabric that this method manufactures assigns chemical fiber plus material with soft and smooth elastic hand as silk
Sense.The immersion of weaving Antibacterial accessory ingredient is added during preparation so that fabric has stronger antibiotic property, has both simultaneously
The warming and cold-resistant performance of anti-suede, in addition the fabric also there is the characteristics of tearing toughness is good.The fabric is particularly suitable for use in eider down
Take fabric and directly the clothing fabric of contact skin.
Embodiments of the invention are the foregoing is only, are not intended to limit the scope of the invention, it is every to utilize this hair
The equivalent structure or equivalent flow conversion that bright description is made, or directly or indirectly it is used in other related technology necks
Domain, it is included within the scope of the present invention.
Claims (1)
1. a kind of preparation method of antibacterial silk elasticity fabric, it is characterised in that its step is：
（1）Cloth is connect, cloth machine margin to seam, upper A cabinet frames package are connect using flatcar；
（2）Pad, padded using forming machine, the composition of padding liquid is according to parts by weight：
Water 80-120 parts, silk bullet glue 5-15 parts, bridging agent 3-8 parts, accelerator 1-4 parts；During padding, temperature control exists
135-155 degree, the fabric speed of service are that 55-65 rice is per minute, and pressure is 0.3-0.5 MPas；
（3）Add antiseptic, cloth is immersed in the solution for the weaving Antibacterial accessory ingredient that mass concentration is 5%, the temperature of solution is
65-85 degree, soak time are 15 minutes, and immersion is taken out later, is air-dried under normal temperature；
（4）Upper coating, using coating machine, the composition of coating is according to parts by weight：
Anti-chiseling down glue 30-100 parts, silk bullet glue 30-100 parts, bridging agent 3-8 parts, accelerator 1-4 parts, antiplastering aid 5-15 parts are soft
Soft dose of 5-15 part, anti-chiseling down glue 5-15 parts；In upper coating procedure, temperature control is in 140-160 degree, the fabric speed of service
30-35 rice is per minute；
（5）Calendering, using calender, temperature control is 28-38 in 75-85 degree, 800-1000 MPas of pressure, the fabric speed of service
Rice is per minute；
（6）By step（5）Treated fabric clot, packaging prepare antibacterial silk elasticity fabric.