CN107747110A - A kind of steel electro-plating method - Google Patents
A kind of steel electro-plating method Download PDFInfo
- Publication number
- CN107747110A CN107747110A CN201711182320.3A CN201711182320A CN107747110A CN 107747110 A CN107747110 A CN 107747110A CN 201711182320 A CN201711182320 A CN 201711182320A CN 107747110 A CN107747110 A CN 107747110A
- Authority
- CN
- China
- Prior art keywords
- parts
- electroplate liquid
- steel
- plating method
- nano
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of steel electro-plating method, belong to electroplating technology, including herein below：A. oil removing, derusting are carried out to steel surface, cleans up and polishes；B. electroplate liquid is prepared, electroplate liquid includes the component of following parts by weight：15~40 parts of nano chromium oxide, 15~30 parts of fluoboric acid, 5~10 parts of lauryl sodium sulfate, 5~10 parts of nano aluminum nitride, 30~50 parts of sodium phosphate, 1~5 part of dibutyltin diacetate, 1~5 part of complexing agent, 1~5 part of complexant, 1~5 part of buffer, 1~5 part of ethane, 80~100 parts of deionized water；C. electroplate liquid is stirred after 1~2 hour, and steel immerse electroplate liquid, and temperature of electroplating solution is 30~40 DEG C.The adhesion of coating and steel is strong, enhances the wearability and corrosion resistance of coating, improves service life and performance.
Description
Technical field
The present invention relates to electroplating technology, in particular to a kind of steel electro-plating method.
Background technology
Steel can carry out electroplating processes generally for antirust is wear-resisting on surface, have high rigidity, excellent anti-wear performance, resistance to
Corrosion and decorative surface, to improve the corrosion resistance of steel substrate, wearability, case hardness and dicoration.But current plating
Method all need to be improved for the wearability and corrosion resistance of coating, therefore needs to study new electroplating surface processing method and plating
Liquid, the adhesion of coating and steel is improved, strengthen the wearability and corrosion resistance of coating.
The content of the invention
It is an object of the invention to provide a kind of steel electro-plating method, to solve the above problems.
To realize the object of the invention, the technical scheme that uses for：A kind of steel electro-plating method, including herein below：A. it is right
Steel surface carries out oil removing, derusting, cleans up and polishes；B. electroplate liquid is prepared, electroplate liquid includes the component of following parts by weight：
15~40 parts of nano chromium oxide, 15~30 parts of fluoboric acid, 5~10 parts of lauryl sodium sulfate, 5~10 parts of nano aluminum nitride, phosphorus
Sour 30~50 parts of sodium, 1~5 part of dibutyltin diacetate, 1~5 part of complexing agent, 1~5 part of complexant, 1~5 part of buffer, ethane
1~5 part, 80~100 parts of deionized water；C. electroplate liquid is stirred after 1~2 hour, and steel immerse electroplate liquid, temperature of electroplating solution 30
~40 DEG C.
Further, the electroplate liquid includes the component of following parts by weight：35 parts of nano chromium oxide, 20 parts of fluoboric acid, ten
8 parts of sodium dialkyl sulfate, 8 parts of nano aluminum nitride, 45 parts of sodium phosphate, 3 parts of dibutyltin diacetate, 2 parts of complexing agent, complexant 2
Part, 1 part of buffer, 2 parts of ethane, 85 parts of deionized water.
Further, electroplate liquid mixing time is 2 hours in content c.
The invention has the advantages that by the above method, electroplate liquid stirs after mixing in proportion, is made wear-resistant
Electroplate liquid, and by the way that the electroplate liquid is plated on into steel surface, so that steel effectively prevent from wearing in actual use, plate
Layer is strong with the adhesion of steel, enhances the wearability and corrosion resistance of coating, improves service life and performance.
Embodiment
The present invention is described in further detail below by specific examples of the implementation.
Steel electro-plating method provided by the invention, including herein below：A. oil removing, derusting, cleaning are carried out to steel surface
Totally and polish；B. electroplate liquid is prepared, electroplate liquid includes the component of following parts by weight：15~40 parts of nano chromium oxide, fluoboric acid
15~30 parts, 5~10 parts of lauryl sodium sulfate, 5~10 parts of nano aluminum nitride, 30~50 parts of sodium phosphate, oxalic acid dibutyl
1~5 part of tin, 1~5 part of complexing agent, 1~5 part of complexant, 1~5 part of buffer, 1~5 part of ethane, 80~100 parts of deionized water；
C. electroplate liquid is stirred after 1~2 hour, and steel immerse electroplate liquid, and temperature of electroplating solution is 30~40 DEG C.
Electroplate liquid includes the component of following parts by weight：35 parts of nano chromium oxide, 20 parts of fluoboric acid, lauryl sodium sulfate 8
Part, 8 parts of nano aluminum nitride, 45 parts of sodium phosphate, 3 parts of dibutyltin diacetate, 2 parts of complexing agent, 2 parts of complexant, 1 part of buffer,
2 parts of ethane, 85 parts of deionized water.Electroplate liquid mixing time is 2 hours in content c.In content c, temperature of electroplating solution is 35 DEG C.
By the above method, electroplate liquid stirs after mixing in proportion, and wear-resistant electroplate liquid is made, and by by the electricity
Plating solution is plated on steel surface, so that steel effectively prevent from wearing in actual use, the adhesion of coating and steel is strong,
The wearability and corrosion resistance of coating are enhanced, improves service life and performance.
Electroplate liquid may include the component of following parts by weight：15 parts of nano chromium oxide, 15 parts of fluoboric acid, lauryl sodium sulfate
5 parts, 5 parts of nano aluminum nitride, 30 parts of sodium phosphate, 1 part of dibutyltin diacetate, 1 part of complexing agent, 1 part of complexant, 1 part of buffer,
1 part of ethane, 80 parts of deionized water.Electroplate liquid may also comprise the component of following parts by weight：40 parts of nano chromium oxide, fluoboric acid 30
Part, 10 parts of lauryl sodium sulfate, 10 parts of nano aluminum nitride, 50 parts of sodium phosphate, 5 parts of dibutyltin diacetate, 5 parts of complexing agent,
5 parts of complexant, 5 parts of buffer, 5 parts of ethane, 100 parts of deionized water.
The preferred embodiments of the present invention are the foregoing is only, are not intended to limit the invention, for the skill of this area
For art personnel, there can be various modifications and variations in the spirit and principles in the present invention, these equivalent modifications or replacement etc.,
It is all contained within protection scope of the present invention.
Claims (3)
1. a kind of steel electro-plating method, it is characterised in that including herein below：A. oil removing, derusting, cleaning are carried out to steel surface
Totally and polish；B. electroplate liquid is prepared, electroplate liquid includes the component of following parts by weight：15~40 parts of nano chromium oxide, fluoboric acid
15~30 parts, 5~10 parts of lauryl sodium sulfate, 5~10 parts of nano aluminum nitride, 30~50 parts of sodium phosphate, oxalic acid dibutyl
1~5 part of tin, 1~5 part of complexing agent, 1~5 part of complexant, 1~5 part of buffer, 1~5 part of ethane, 80~100 parts of deionized water；
C. electroplate liquid is stirred after 1~2 hour, and steel immerse electroplate liquid, and temperature of electroplating solution is 30~40 DEG C.
2. steel electro-plating method according to claim 1, it is characterised in that the electroplate liquid includes the group of following parts by weight
Point：35 parts of nano chromium oxide, 20 parts of fluoboric acid, 8 parts of lauryl sodium sulfate, 8 parts of nano aluminum nitride, 45 parts of sodium phosphate, diethyl
Sour 3 parts of dibutyl tin, 2 parts of complexing agent, 2 parts of complexant, 1 part of buffer, 2 parts of ethane, 85 parts of deionized water.
3. steel electro-plating method according to claim 1, it is characterised in that electroplate liquid mixing time is 2 small in content c
When.