CN107738491A - A kind of leaching membrane paper with good resistance to elevated temperatures - Google Patents
A kind of leaching membrane paper with good resistance to elevated temperatures Download PDFInfo
- Publication number
- CN107738491A CN107738491A CN201711085756.0A CN201711085756A CN107738491A CN 107738491 A CN107738491 A CN 107738491A CN 201711085756 A CN201711085756 A CN 201711085756A CN 107738491 A CN107738491 A CN 107738491A
- Authority
- CN
- China
- Prior art keywords
- layer
- leaching membrane
- elevated temperatures
- good resistance
- thickness
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a kind of leaching membrane paper with good resistance to elevated temperatures.It includes film paper substrate, the side of film paper substrate is disposed with waterproof breathable membrane layer, absorption resin of sodium polyacrylate layer, aluminium foil layer and polyimide layer from the inside to the outside, aluminium foil layer offers aperture, and the opposite side of film paper substrate is disposed with silicon layer, ventilated membrane and leaching membrane layer from the inside to the outside.Leaching membrane paper of the invention with good resistance to elevated temperatures is with good high temperature resistant and fire resistance.
Description
Technical field
The present invention relates to leaching membrane paper technical field, more particularly to a kind of leaching membrane paper with good resistance to elevated temperatures.
Background technology
Leaching membrane paper is exactly the composite that plastic pellet is coated in paper surface by casting machine, and main feature is exactly this
Composite can with grease proofing, waterproof (relative), can be with heat seal.The production of current domestic leaching membrane paper, especially high temperature resistant film
The production technology of paper is immature, and leaching membrane paper has the problem of heat-resisting quantity difference.
Therefore it provides a kind of leaching membrane paper with good resistance to elevated temperatures, it is urgently to be resolved hurrily to turn into leaching membrane paper technical field
Problem.
The content of the invention
It is an object of the invention to provide a kind of leaching membrane paper with good resistance to elevated temperatures, the resistance to height of leaching membrane paper is which solved
The problem of warm nature can be with fire resistance deficiency.
To use following technical scheme up to this purpose, the present invention：
A kind of leaching membrane paper with good resistance to elevated temperatures, including film paper substrate, the side of film paper substrate by it is interior extremely
It is disposed with waterproof breathable membrane layer, absorption resin of sodium polyacrylate layer, aluminium foil layer and polyimide layer, the aluminium foil outside
Layer offers aperture, and the opposite side of the film paper substrate is disposed with silicon layer, ventilated membrane and leaching membrane layer from the inside to the outside.
Wherein, the thickness of the film paper substrate be 200~400 μm, such as can be 200 μm, 220 μm, 250 μm, 280
μm, 300 μm, 320 μm, 350 μm or 400 μm.
Wherein, the waterproof breathable membrane layer is TPUE film layer, the waterproof breathable membrane layer
Thickness be 10~30 μm, such as can be 10 μm, 12 μm, 15 μm, 18 μm, 20 μm, 25 μm, 28 μm or 30 μm.
Wherein, the absorption resin of sodium polyacrylate layer offers several hemispherical dimples arranged in arrays, described
The thickness of absorption resin of sodium polyacrylate layer be 40~60 μm, such as can be 40 μm, 42 μm, 45 μm, 50 μm, 52 μm, 55 μm,
58 μm or 60 μm.
Wherein, the aluminium foil layer is 10~30 μm, such as can be 10 μm, 15 μm, 18 μm, 20 μm, 25 μm, 28 μm or 30
μm。
Wherein, the thickness of the polyimide layer is 30~50 μm, such as can be 30 μm, 32 μm, 35 μm, 40 μm, 42 μ
M, 45 μm, 48 μm or 50 μm, the thickness of the silicon layer are 10~30 μm, for example, can be 10 μm, 12 μm, 15 μm, 20 μm, 22
μm, 25 μm, 28 μm or 30 μm.
The thickness of the ventilated membrane is 8~15 μm, such as can be 8 μm, 9 μm, 10 μm, 11 μm, 12 μm, 13 μm or 15 μ
M, the thickness of the leaching membrane layer is 20~40 μm, such as can be 20 μm, 25 μm, 28 μm, 30 μm, 35 μm, 38 μm or 40 μm.
Beneficial effects of the present invention：Leaching membrane paper provided by the invention with good resistance to elevated temperatures, including film paper substrate
Layer, the side of the film paper substrate be disposed with from the inside to the outside waterproof breathable membrane layer, absorption resin of sodium polyacrylate layer,
Aluminium foil layer and polyimide layer, the aluminium foil layer offer aperture, and the opposite side of the film paper substrate is from the inside to the outside successively
It is provided with silicon layer, ventilated membrane and leaching membrane layer.Polyimide layer has good high temperature resistant and fire resistance, forms and prevents height
The first line of defence of the invasion and attack of temperature, aluminium foil layer have the performance of heat-insulating flame-retardant, heat can be blocked in outside, in addition, poly- third
Olefin(e) acid absorption resin of sodium layer has good water absorbing properties, can adsorb substantial amounts of moisture, and when running into high temperature, moisture can be from aluminium
Substantial amounts of heat is taken away in evaporation in the aperture of layers of foil, further prevents the invasion and attack of high temperature, and waterproof breathable membrane layer has good
Waterproof and breathable performance, can prevent absorption resin of sodium polyacrylate layer adsorb moisture enter in film paper substrate, in addition,
Silicon layer has good hydrophobic, water resistance, and ventilated membrane ensure that gas permeability.The present invention's has good resistance to elevated temperatures
Leaching membrane paper has good high temperature resistant and fire resistance.
Brief description of the drawings
Fig. 1 is the structural representation of the leaching membrane paper with good resistance to elevated temperatures of the present invention.
Reference is as follows：1- films paper substrate, 2- waterproof breathable membranes layer, 3- absorption resin of sodium polyacrylate layer, 4-
Aluminium foil layer, 5- polyimide layers, 6- silicon layers, 7- ventilated membranes, 8- leaching membrane layers.
Embodiment
The leaching membrane paper with good resistance to elevated temperatures of the present invention is applied to make high temperature resistant packaging material.
Technical scheme is further illustrated below in conjunction with Fig. 1 and by specific embodiment.
The leaching membrane paper with good resistance to elevated temperatures provided in the present embodiment, including film paper substrate 1, film paper substrate
1 side is disposed with waterproof breathable membrane layer 2, absorption resin of sodium polyacrylate layer 3, aluminium foil layer 4 and gathered from the inside to the outside
Imide layer 5, the opposite side of film paper substrate 1 are disposed with silicon layer 6, ventilated membrane 7 and leaching membrane layer 8 from the inside to the outside.
Polyimide layer 5 has good high temperature resistant and fire resistance, forms the first line of defence for the invasion and attack for preventing high temperature,
Aluminium foil layer 4 has the performance of heat-insulating flame-retardant, heat can be blocked in outside, in addition, absorption resin of sodium polyacrylate layer 3 has
Good water absorbing properties, substantial amounts of moisture can be adsorbed, when running into high temperature, moisture can from the aperture of aluminium foil layer 4 evaporator strip
Substantial amounts of heat is walked, further prevents the invasion and attack of high temperature, waterproof breathable membrane layer 2 has good waterproof and breathable performance, energy
The moisture of the absorption of absorption resin of sodium polyacrylate layer 3 is enough prevented to enter in film paper substrate 1, in addition, silicon layer 6 has well
Hydrophobic, water resistance, ventilated membrane 7 ensure that gas permeability.The leaching membrane paper with good resistance to elevated temperatures of the present invention is with good
Good high temperature resistant and fire resistance.
The thickness of film paper substrate 1 is 200~400 μm, such as can be 200 μm, 220 μm, 250 μm, 280 μm, 300 μ
M, 320 μm, 350 μm or 400 μm.
Waterproof breathable membrane layer 2 is TPUE film layer or polytetrafluoroethylene film layer, waterproof and breathable
The thickness of film layer 2 is 20~60 μm.TPUE film layer has good ventilative, moisture-inhibiting and water pressure resistance
Performance, polytetrafluoroethylene film is in addition to good breathable and waterproof performance, also with good high temperature resistant and anticorrosion
Performance, using operating temperature up to 250 DEG C, there is good mechanical tenacity, that is, drop temperature to -196 DEG C, can also keep
5% elongation；To most of chemicals and solvent, inertia, energy strong alkali-acid resistance, water and various organic solvents are shown,
There is aging life-span optimal in plastics.The thickness of waterproof breathable membrane layer 2 be 20 μm, 25 μm, 30 μm, 35 μm, 40 μm, 45 μm,
50 μm or 60 μm.
Absorption resin of sodium polyacrylate layer 3 offers several hemispherical dimples arranged in arrays, and Sodium Polyacrylate is inhaled
The thickness of water tree lipid layer 3 is 40~60 μm, such as can be 40 μm, 42 μm, 45 μm, 50 μm, 52 μm, 55 μm, 58 μm or 60 μm.
Absorption resin of sodium polyacrylate layer 3 offers several hemispherical dimples arranged in arrays, on the one hand can be in order to polypropylene
Sour absorption resin of sodium layer 3 is absorbed water and stored water in absorption resin of sodium polyacrylate layer 3 and in hemispherical dimples, by high temperature
When, water in hemispherical dimples from the aperture infiltration of aluminium foil layer 4 and can be evaporated rapidly, take away substantial amounts of heat, the opposing party
The hemispherical dimples that face absorption resin of sodium polyacrylate layer 3 is set, bubble is produced when avoiding adhered aluminium foil layer 4.
The thickness of aluminium foil layer 4 is 10~30 μm, such as can be 10 μm, 15 μm, 18 μm, 20 μm, 25 μm, 28 μm or 30 μ
m.The thickness of polyimide layer 5 be 30~50 μm, such as can be 30 μm, 32 μm, 35 μm, 40 μm, 42 μm, 45 μm, 48 μm or
50 μm, the thickness of silicon layer 6 is 10~30 μm, such as can be 10 μm, 12 μm, 15 μm, 20 μm, 22 μm, 25 μm, 28 μm or 30
μm。
The thickness of the ventilated membrane 7 is 8~15 μm, such as can be 8 μm, 9 μm, 10 μm, 11 μm, 12 μm, 13 μm or 15 μ
M, the thickness of the leaching membrane layer 8 is 20~40 μm, such as can be 20 μm, 25 μm, 28 μm, 30 μm, 35 μm, 38 μm or 40 μm.
Above content is only presently preferred embodiments of the present invention, for one of ordinary skill in the art, according to the present invention's
Thought, there will be changes, this specification content should not be construed as to the present invention in specific embodiments and applications
Limitation.
Claims (10)
1. a kind of leaching membrane paper with good resistance to elevated temperatures, it is characterised in that including film paper substrate (1), the leaching membrane paper
The side of basic unit (1) is disposed with waterproof breathable membrane layer (2), absorption resin of sodium polyacrylate layer (3), aluminium foil from the inside to the outside
Layer (4) and polyimide layer (5), the aluminium foil layer (4) offer aperture, and the opposite side of the film paper substrate (1) is by interior
To being disposed with silicon layer (6), ventilated membrane (7) and leaching membrane layer (8) outside.
2. the leaching membrane paper according to claim 1 with good resistance to elevated temperatures, it is characterised in that the film paper substrate
(1) thickness is 200~400 μm.
3. the leaching membrane paper according to claim 1 with good resistance to elevated temperatures, it is characterised in that the waterproof and breathable is thin
Film layer (2) is TPUE film layer.
4. the leaching membrane paper according to claim 1 with good resistance to elevated temperatures, it is characterised in that the waterproof and breathable is thin
The thickness of film layer (2) is 10~30 μm.
5. the leaching membrane paper according to claim 1 with good resistance to elevated temperatures, it is characterised in that the Sodium Polyacrylate
Water-absorbing resin layer (3) offers several hemispherical dimples arranged in arrays, the absorption resin of sodium polyacrylate layer (3)
Thickness is 40~60 μm.
6. the leaching membrane paper according to claim 1 with good resistance to elevated temperatures, it is characterised in that the aluminium foil layer (4)
Thickness be 10~30 μm.
7. the leaching membrane paper according to claim 1 with good resistance to elevated temperatures, it is characterised in that the polyimide layer
(5) thickness is 30~50 μm.
8. the leaching membrane paper according to claim 1 with good resistance to elevated temperatures, it is characterised in that the silicon layer (6)
Thickness be 10~30 μm.
9. the leaching membrane paper according to claim 1 with good resistance to elevated temperatures, it is characterised in that the ventilated membrane (7)
Thickness be 8~15 μm.
10. the leaching membrane paper according to claim 1 with good resistance to elevated temperatures, it is characterised in that the leaching membrane layer (8)
Thickness be 20~40 μm.