CN107737706A - Imitation wood line spraying aluminum profile technique - Google Patents
Imitation wood line spraying aluminum profile technique Download PDFInfo
- Publication number
- CN107737706A CN107737706A CN201710808672.9A CN201710808672A CN107737706A CN 107737706 A CN107737706 A CN 107737706A CN 201710808672 A CN201710808672 A CN 201710808672A CN 107737706 A CN107737706 A CN 107737706A
- Authority
- CN
- China
- Prior art keywords
- section bar
- aluminium
- parts
- aluminium section
- shape surface
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to aluminium section bar technical field, and in particular to imitation wood line spraying aluminum profile technique, comprises the following steps:Aluminium section bar is placed in 43% sodium hydroxide and soaks 20 40min, then be put into potassium dihydrogen phosphate and soak;Aluminium shape surface is irradiated with ultraviolet;Take out aluminium section bar and put into passivating solution and soak 25 hours;Taking-up aluminium section bar, which is placed in the concentrated sulfuric acid solution of concentration 88%, is used as anode, makes anodic oxidation with impressed current, is passivated aluminium shape surface;In aluminium shape surface even application anti-fouling paint, thickness is 5 20 μm;Microwave treatment 40min under microwave frequency 350MHz, power 410W is first used under anti-fouling paint leather hard.Spraying coating process of the present invention can form such as the similar structure of wood surface in aluminium shape surface, it appears and it is attractive in appearance, and also passivating solution can be firmly attached to aluminium shape surface after anodic oxidation, improve the decay resistance of aluminium section bar.
Description
Technical field:
The present invention relates to aluminium section bar technical field, and in particular to imitation wood line spraying aluminum profile technique.
Background technology:
Aluminium and aluminium alloy density are small, specific strength is high, corrosion resistance, inoxidizability, conduction and it is hot be only second to silver and copper,
Nontoxic and processability is good, also good low temperature reflecting properties, it is nonmagnetic, produce no spark, lustrous surface is attractive in appearance, can surface painting
A variety of properties such as decorations.It is widely used in building, transports, industry and the daily life field such as national defence, packaging.China is
The production and consumption big country of aluminum products, however, the bauxite resource in China is but very deficient, bauxite can exploit the time limit not at present
Foot 30 years.Therefore, the market demand constantly expanded has turned into the bottle of China's Aluminum future development with relatively poor bauxite resource
Neck ring section, this contradiction promote developing rapidly for China Aluminum Recycling Industry.Aluminium section bar is because of its special property and by wide
General use.
The content of the invention:
The technical problems to be solved by the invention are to overcome existing technological deficiency, there is provided imitation wood line spraying aluminum profile
Technique.
The technical problems to be solved by the invention are realized using following technical scheme:
Imitation wood line spraying aluminum profile technique, comprises the following steps:
(1) aluminium section bar is placed in the sodium hydroxide that temperature is 46-55 DEG C, mass fraction is 43% and soaks 20-40min,
It is put into again in 0.6mol/L potassium dihydrogen phosphates and soaks 5-10min;
(2) aluminium section bar is taken out, irradiates aluminium shape surface with ultraviolet;
(3) aluminium section bar after irradiation is placed in pickling 10 minutes in 45% concentration salpeter solution, then takes out aluminium profiles in time
Material simultaneously puts into immersion 2-5 hours in passivating solution;
(4) taking-up aluminium section bar, which is placed in the concentrated sulfuric acid solution of concentration 88%, is used as anode, makes anodic oxygen with impressed current
Change, be passivated aluminium shape surface, form the oxide-film of 5-20 μ m thicks;
(5) aluminium section bar is taken out, aluminium shape surface is rinsed with water;
(6) after drying, in aluminium shape surface even application anti-fouling paint, thickness is 5-20 μm;
(7) microwave treatment 40min, Ran Houzai under microwave frequency 350MHz, power 410W are first used under anti-fouling paint leather hard
1 is pressed to aluminium shape surface sprinkling turpentine oil, ATBC, water is added:1:The mixed liquor of 4 ratios mixing, continues at microwave
Manage 30min;
(8) after aluminium section bar being toasted into 20-30min in the baking oven that temperature is 220-225 DEG C, natural cooling.
The passivating solution is made up of the component of following parts by weight:5.6 parts of maleic anhydride, 4.4 parts of calgon, sea
1.3 parts of alginic acid, 0.3 part of cystine, 2.2 parts of polyvinyl alcohol, 4.3 parts of D-sorbite, 100 parts of purified water.
Beneficial effects of the present invention are:Spraying coating process of the present invention can be formed as wood surface is similar in aluminium shape surface
Structure, it appears it is attractive in appearance, and passivating solution can be firmly attached to aluminium shape surface after anodic oxidation, improve aluminium section bar
Decay resistance.
Embodiment:
Below in conjunction with the embodiment of the present invention, the technical scheme in the embodiment of the present invention is clearly and completely retouched
State, it is clear that described embodiment is only part of the embodiment of the present invention, rather than whole embodiments.Based on the present invention
In embodiment, the every other implementation that those of ordinary skill in the art are obtained under the premise of creative work is not made
Example, belongs to the scope of protection of the invention.
In description of the invention, it is necessary to explanation, the orientation of the instruction such as term " vertical ", " on ", " under ", " level "
Or position relationship, be for only for ease of describe this practicality and simplify describe, rather than instruction or imply meaning device or
Person's element must have specific orientation, with specific azimuth configuration and operation, therefore it is not intended that to limit of the invention
System.In addition, " first ", " second ", " the 3rd ", " the 4th " are only used for describing purpose, and it is not intended that instruction or implying phase
To importance.
In description of the invention, it is also necessary to explanation, unless otherwise clear and definite regulation and limit, term " setting ",
" installation ", " connected ", " connection " should be interpreted broadly, for example, it may be fixedly connected or be detachably connected, or one
Connect body, can be mechanical connection or electrical connection, can be directly connected to or by intermediary phase
Even, can be the connection of two element internals.For the ordinary skill in the art, can manage as the case may be
Solve the concrete meaning of above-mentioned term in the present invention.
Embodiment one
Imitation wood line spraying aluminum profile technique, comprises the following steps:
(1) aluminium section bar is placed in the sodium hydroxide that temperature is 46-55 DEG C, mass fraction is 43% and soaks 20-40min,
It is put into again in 0.6mol/L potassium dihydrogen phosphates and soaks 5-10min;
(2) aluminium section bar is taken out, irradiates aluminium shape surface with ultraviolet;
(3) aluminium section bar after irradiation is placed in pickling 10 minutes in 45% concentration salpeter solution, then takes out aluminium profiles in time
Material simultaneously puts into immersion 2-5 hours in passivating solution;
(4) taking-up aluminium section bar, which is placed in the concentrated sulfuric acid solution of concentration 88%, is used as anode, makes anodic oxygen with impressed current
Change, be passivated aluminium shape surface, form the oxide-film of 5-20 μ m thicks;
(5) aluminium section bar is taken out, aluminium shape surface is rinsed with water;
(6) after drying, in aluminium shape surface even application anti-fouling paint, thickness is 5-20 μm;
(7) microwave treatment 40min, Ran Houzai under microwave frequency 350MHz, power 410W are first used under anti-fouling paint leather hard
1 is pressed to aluminium shape surface sprinkling turpentine oil, ATBC, water is added:1:The mixed liquor of 4 ratios mixing, continues at microwave
Manage 30min;
(8) after aluminium section bar being toasted into 20-30min in the baking oven that temperature is 220-225 DEG C, natural cooling.
Passivating solution is made up of the component of following parts by weight:5.6 parts of maleic anhydride, 4.4 parts of calgon, alginic acid
1.3 parts, 0.3 part of cystine, 2.2 parts of polyvinyl alcohol, 4.3 parts of D-sorbite, 100 parts of purified water.
Embodiment two
Imitation wood line spraying aluminum profile technique, comprises the following steps:
(1) aluminium section bar is placed in the sodium hydroxide that temperature is 46-55 DEG C, mass fraction is 43% and soaks 20-40min,
It is put into again in 0.6mol/L potassium dihydrogen phosphates and soaks 5-10min;
(2) aluminium section bar is taken out, irradiates aluminium shape surface with ultraviolet;
(3) aluminium section bar after irradiation is placed in pickling 10 minutes in 45% concentration salpeter solution, then takes out aluminium profiles in time
Material simultaneously puts into immersion 2-5 hours in passivating solution;
(4) taking-up aluminium section bar, which is placed in the concentrated sulfuric acid solution of concentration 88%, is used as anode, makes anodic oxygen with impressed current
Change, be passivated aluminium shape surface, form the oxide-film of 5-20 μ m thicks;
(5) aluminium section bar is taken out, aluminium shape surface is rinsed with water;
(6) after drying, in aluminium shape surface even application anti-fouling paint, thickness is 5-20 μm;
(7) microwave treatment 40min, Ran Houzai under microwave frequency 350MHz, power 410W are first used under anti-fouling paint leather hard
1 is pressed to aluminium shape surface sprinkling turpentine oil, ATBC, water is added:1:The mixed liquor of 4 ratios mixing, continues at microwave
Manage 30min;
(8) after aluminium section bar being toasted into 20-30min in the baking oven that temperature is 220-225 DEG C, natural cooling.
Passivating solution is made up of the component of following parts by weight:5.6 parts of maleic anhydride, 4.4 parts of calgon, alginic acid
1.3 parts, 0.3 part of cystine, 2.2 parts of polyvinyl alcohol, 4.3 parts of D-sorbite, 100 parts of purified water.
Anti-fouling paint is made up of the component of following parts by weight:60 parts of cycloaliphatic epoxy resin, 4.2 parts of polyester acrylate,
15.3 parts of dibutyltin dilaurate, 5.6 parts of diethylene glycol dibenzoate, 3.2 parts of polyvinyl alcohol, hydroxypropyl methyl fiber
4.3 parts of element, 6.2 parts of borax, 4.2 parts of adipic acid, 0.8 part of Lenzin viscose glue, 0.6 part of Dipyridamole, didecyl Dimethy chlorination
1.1 parts of ammonium, 1.3 parts of Ergol, 1.3 parts of antiager, 1.3 parts of rubber solvent, 1.3 parts of hydroquinones, acetyl citrate
0.9 part.
Embodiment three
Imitation wood line spraying aluminum profile technique, comprises the following steps:
(1) aluminium section bar is placed in the sodium hydroxide that temperature is 46-55 DEG C, mass fraction is 43% and soaks 20-40min,
It is put into again in 0.6mol/L potassium dihydrogen phosphates and soaks 5-10min;
(2) aluminium section bar is taken out, irradiates aluminium shape surface with ultraviolet;
(3) aluminium section bar after irradiation is placed in pickling 10 minutes in 45% concentration salpeter solution, then takes out aluminium profiles in time
Material simultaneously puts into immersion 2-5 hours in passivating solution;
(4) taking-up aluminium section bar, which is placed in the concentrated sulfuric acid solution of concentration 88%, is used as anode, makes anodic oxygen with impressed current
Change, be passivated aluminium shape surface, form the oxide-film of 5-20 μ m thicks;
(5) aluminium section bar is taken out, aluminium shape surface is rinsed with water;
(6) after drying, in aluminium shape surface even application anti-fouling paint, thickness is 5-20 μm;
(7) microwave treatment 40min, Ran Houzai under microwave frequency 350MHz, power 410W are first used under anti-fouling paint leather hard
1 is pressed to aluminium shape surface sprinkling turpentine oil, ATBC, water is added:1:The mixed liquor of 4 ratios mixing, continues at microwave
Manage 30min;
(8) after aluminium section bar being toasted into 20-30min in the baking oven that temperature is 220-225 DEG C, natural cooling.
Passivating solution is made up of the component of following parts by weight:5.6 parts of maleic anhydride, 4.4 parts of calgon, alginic acid
1.3 parts, 0.3 part of cystine, 2.2 parts of polyvinyl alcohol, 4.3 parts of D-sorbite, 100 parts of purified water.
Anti-fouling paint is made up of the component of following parts by weight:60 parts of cycloaliphatic epoxy resin, 4.2 parts of polyester acrylate,
15.3 parts of dibutyltin dilaurate, 5.6 parts of diethylene glycol dibenzoate, 3.2 parts of polyvinyl alcohol, hydroxypropyl methyl cellulose
4.3 parts, 6.2 parts of borax, 4.2 parts of adipic acid, 0.8 part of Lenzin viscose glue, 0.6 part of Dipyridamole, didecyl Dimethy ammonium chloride
1.1 parts, 1.3 parts of Ergol, 1.3 parts of antiager, 1.3 parts of rubber solvent, 1.3 parts of hydroquinones, acetyl citrate
0.9 part, 0.6 part of epoxidized soybean oil, 2.2 parts of modified fibre.
Antiager is styrenated phenol, and the rubber solvent is neoprene toluene solvant.
Wherein, modified fibre is made up of the component of following parts by weight:It is 17 parts of bamboo-carbon fibre, 10.6 parts of linoleic acid, different pungent
5.6 parts of ester, 9.6 parts of hydrogen peroxide, 18 parts of polyisocyanates;Each raw material is mixed at 45-50 DEG C.
Glue preparation method, each raw material of composition glue is weighed, is sequentially added in mixer, it is evacuated to -0.04~-
Mixed under 0.03MPa 0.5~2 hour, speed of agitator is 1500~2000 revs/min and stirred, and hangs naturally to room temperature, sealing
Packaging.
Experiment
The aluminium section bar of embodiment one, two, three carries out verification experimental verification, and (insulation material generally refers to heat conduction with insulation material
Coefficient is less than or equal to 0.12 material.) be compared, it is as a result as follows:
It can be seen that spraying coating process of the present invention causes aluminium section bar to have preferable heat-insulating property, and it is not easy to be oxidized.
The general principle and principal character and advantages of the present invention of the present invention has been shown and described above.The skill of the industry
For art personnel it should be appreciated that the present invention is not limited to the above embodiments, described in above-described embodiment and specification is explanation
The principle of the present invention, without departing from the spirit and scope of the present invention, various changes and modifications of the present invention are possible, this
A little changes and improvements all fall within the protetion scope of the claimed invention.The claimed scope of the invention is by appended claim
Book and its equivalent thereof.
Claims (2)
1. imitation wood line spraying aluminum profile technique, it is characterised in that comprise the following steps:
(1) aluminium section bar is placed in the sodium hydroxide that temperature is 46-55 DEG C, mass fraction is 43% and soaks 20-40min, then will
It, which is inserted in 0.6mol/L potassium dihydrogen phosphates, soaks 5-10min;
(2) aluminium section bar is taken out, irradiates aluminium shape surface with ultraviolet;
(3) aluminium section bar after irradiation is placed in pickling 10 minutes in 45% concentration salpeter solution, then takes out aluminium section bar simultaneously in time
Put into and 2-5 hours are soaked in passivating solution;
(4) taking-up aluminium section bar, which is placed in the concentrated sulfuric acid solution of concentration 88%, is used as anode, makes anodic oxidation with impressed current, makes aluminium
Surface of profile is passivated, and forms the oxide-film of 5-20 μ m thicks;
(5) aluminium section bar is taken out, aluminium shape surface is rinsed with water;
(6) after drying, in aluminium shape surface even application anti-fouling paint, thickness is 5-20 μm;
(7) microwave treatment 40min under microwave frequency 350MHz, power 410W is first used under anti-fouling paint leather hard, then again to adding
Enter aluminium shape surface sprinkling turpentine oil, ATBC, water by 1:1:The mixed liquor of 4 ratios mixing, continues microwave treatment
30min;
(8) after aluminium section bar being toasted into 20-30min in the baking oven that temperature is 220-225 DEG C, natural cooling.
2. imitation wood line spraying aluminum profile technique according to claim 1, it is characterised in that the passivating solution is by following weight
The component of number is made:5.6 parts of maleic anhydride, 4.4 parts of calgon, 1.3 parts of alginic acid, 0.3 part of cystine, polyvinyl alcohol
2.2 parts, 4.3 parts of D-sorbite, 100 parts of purified water.