CN107732530A - The manufacture method of the connector of temperature sensing color changing, new temperature sensing color changing data wire and temperature sensing color changing material - Google Patents
The manufacture method of the connector of temperature sensing color changing, new temperature sensing color changing data wire and temperature sensing color changing material Download PDFInfo
- Publication number
- CN107732530A CN107732530A CN201711024735.8A CN201711024735A CN107732530A CN 107732530 A CN107732530 A CN 107732530A CN 201711024735 A CN201711024735 A CN 201711024735A CN 107732530 A CN107732530 A CN 107732530A
- Authority
- CN
- China
- Prior art keywords
- temperature
- color changing
- temperature sensing
- sensing color
- connector
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to the manufacture method of a kind of connector of temperature sensing color changing, new temperature sensing color changing data wire and temperature sensing color changing material.The connector of the temperature sensing color changing includes shell and is installed to the terminal of the shell, and the shell is made up of following steps：Pre-treatment step, it is stirred step, extruding pelletization step and injection-moulding step.The connector of the present invention can be realized to be monitored to temperature, so as to remind the temperature regime of user connector in time, can effectively be ensured the normal use of data wire, be improved the security used.
Description
【Technical field】
The present invention relates to data wire technical field, more particularly, to a kind of connector of temperature sensing color changing, new temperature sensing color changing
The manufacture method of data wire and temperature sensing color changing material.
【Background technology】
Data wire be used for electric room data transfer or electron equipment charge, be mobile terminal device can not
The accessory lacked, data wire generally comprise the connector being connected with electronic equipment.The function of existing connector is mostly relatively more single
One, the function of temperature conditions is not monitored, once temperature is too high, it is possible to trigger safety problem.
【The content of the invention】
It is an object of the invention to realize to be monitored temperature conditions.
The first aspect of the present invention provides a kind of connector of temperature sensing color changing, including shell and the end for being installed to the shell
Son, the shell are made up of following steps：
Pre-treatment step, specifically include：Temperature sensing color changing toner, antioxidant, heat stabilizer are ground, is obtained pretreated
Temperature sensing color changing toner, antioxidant, heat stabilizer；
Step is stirred, is specifically included：Take 100 parts of unit of weight PVC plastic particles, 0.1~10 part of unit of weight institute
State pretreated temperature sensing color changing toner, 20~50 parts of unit of weight plasticizer, 10~50 parts of unit of weight dispersing agent for wax, 0.1
Pretreated antioxidant described in~5 parts of unit of weights, pretreated heat stabilizer described in 0.1~5 part of unit of weight are put
Mixed 4 to 7 minutes within the temperature range of 40 to 60 degrees Celsius in mixer, obtain compound；
Extruding pelletization step, is specifically included：The compound is placed in the torque rheometer of single screw rod, taken the photograph 160 to 180
Extruding pelletization within the temperature range of family name's degree, obtains Masterbatch；
Injection-moulding step, specifically include：The Masterbatch and soft pvc plastic are stirred and at 160 to 180 degrees Celsius
Within the temperature range of injection molding.
Further, the temperature sensing color changing toner can make the color of the shell be higher than the first pre- constant temperature in the temperature of shell
Changed when spending.
Further, the connector also includes the warm change portion for covering the shell, and the temperature change portion is in the shell
Temperature color change occurs when being higher than the second predetermined temperature.
Further, the temperature change portion is printed onto the shell so as to have shape corresponding with silk-screen in a manner of silk-screen
Shape.
Further, the connector also includes the fluorescence portion for being arranged on the temperature change portion.
Further, the temperature change portion is housed in the space that the fluorescence portion fences up.
Further, described to be stirred in step, the time of mixing is 5 minutes.
Further, in the extruding pelletization step, the temperature of extruding pelletization is 170 degrees Celsius.
The second aspect of the present invention provides a kind of new temperature sensing color changing data wire, including cable, includes of the invention the
On the one hand the connector of the temperature sensing color changing provided, the terminal of the connector electrically connect with the cable.
The third aspect of the present invention provides a kind of manufacture method of temperature sensing color changing material, comprises the following steps：
Pre-treatment step, specifically include：Temperature sensing color changing toner, antioxidant, heat stabilizer are ground, is obtained pretreated
Temperature sensing color changing toner, antioxidant, heat stabilizer；
Step is stirred, is specifically included：Take 100 parts of unit of weight PVC plastic particles, 0.1~10 part of unit of weight institute
State pretreated temperature sensing color changing toner, 20~50 parts of unit of weight plasticizer, 10~50 parts of unit of weight dispersing agent for wax, 0.1
Pretreated antioxidant described in~5 parts of unit of weights, pretreated heat stabilizer described in 0.1~5 part of unit of weight are put
Mixed 4 to 7 minutes within the temperature range of 40 to 60 degrees Celsius in mixer, obtain compound；
Extruding pelletization step, is specifically included：The compound is placed in the torque rheometer of single screw rod, taken the photograph 160 to 180
Extruding pelletization within the temperature range of family name's degree, obtains Masterbatch；
Injection-moulding step, specifically include：The Masterbatch and soft pvc plastic are stirred and at 160 to 180 degrees Celsius
Within the temperature range of injection molding.
Implement the present invention, the temperature sensing color changing toner contained by shell, can be achieved to be monitored temperature, so as to timely
The temperature regime of user connector is reminded, the normal use of data wire can be effectively ensured, improve the security used, prevent not
Necessary accident occurs.
【Brief description of the drawings】
Fig. 1 is a kind of schematic diagram of the connector for temperature sensing color changing that one embodiment of the invention provides；
Fig. 2 is the flow chart of the making of shell shown in Fig. 1；
Fig. 3 is the data wire schematic diagram of application Fig. 1 of the present invention connector.
【Embodiment】
The invention will be further described with reference to the accompanying drawings and examples.
With reference to figure 1, a kind of connector 10 for temperature sensing color changing that one embodiment of the invention provides, data wire is mainly used in,
Input terminal adapter or output terminal adapter can be used as.The connector 10 includes shell 11 and is installed to the terminal 12 of shell 11.
Terminal 12 is USB2.0 terminals, Mini-USB terminals, Micro-USB terminals or type-c terminals etc..
Shell 11 contains temperature sensing color changing toner.Temperature sensing color changing toner can be such that the color of shell 11 is higher than in the temperature of shell 11
Changed during the first predetermined temperature.Shell 11 is molded by Shooting Technique, as shown in Fig. 2 specific injection-moulding step is as follows：
S1, pre-treatment step, are specifically included：Temperature sensing color changing toner, antioxidant, heat stabilizer are ground, is pre-processed
Temperature sensing color changing toner, antioxidant, heat stabilizer afterwards.
S2, step is stirred, specifically included：Take 100 parts of unit of weight PVC (Polyvinyl chloride, polychlorostyrene second
Alkene) plastic pellet, the above-mentioned pretreated temperature sensing color changing toner of 0.1~10 part of unit of weight, 20~50 parts of unit of weight DOP
(Dioctyl Phthalate, dioctyl phthalate) plasticizer, 10~50 parts of unit of weight EVA (ethylene-vinyl
Acetate copolymer, ethylene-vinyl acetate copolymer) dispersing agent for wax, after 0.1~5 part of above-mentioned pretreatment of unit of weight
Antioxidant, the above-mentioned pretreated heat stabilizer of 0.1~5 part of unit of weight is placed in mixer at 40 to 60 degrees Celsius
Mixing 4 to 7 minutes, obtain compound in temperature range.Wherein, DOP plasticizer, EVA dispersing agent for wax, antioxidant, thermostabilization
Agent is all auxiliary agent.Preferably, processing temperature is 50 degrees Celsius, and incorporation time is 5 minutes.
S3, extruding pelletization step, are specifically included：Above-mentioned compound is placed in the torque rheometer of single screw rod, 160 to
Extruding pelletization within the temperature range of 180 degrees Celsius, obtains Masterbatch.Wherein, processing temperature is preferably 170 degrees Celsius.
S4, injection-moulding step, are specifically included：Above-mentioned Masterbatch is stirred with soft pvc plastic and taken the photograph 170 to 200
Injection molding within the temperature range of family name's degree.Wherein, processing temperature is preferably 170 degrees Celsius.
Being merged by the injection molding process, in shell 11 has temperature sensing color changing toner, when the temperature of shell 11 is higher than first
During predetermined temperature, temperature sensing color changing toner can make the color of shell 11 change, while be easy to manufacture, and can reduce production cost.
When the temperature of shell 11 is higher than the first predetermined temperature, the color of shell 11 changes into predetermined face by priming color
Color.
The connector 10 also includes the warm change portion 13 for covering the top surface of shell 11.Warm change portion 13 can be in the temperature height of shell 11
Color change occurs when the second predetermined temperature.In the present embodiment, warm change portion 13 is printed onto shell 11 in a manner of silk-screen, so as to
With shape corresponding with silk-screen, manufacturing procedure is easy, is easy to produce.Warm change portion 13 can also be by works such as spraying, pad pastings
Skill covers shell 11.Preferably, warm change portion 13 is shaped as sleeve configuration.It is to be appreciated that the shape in warm change portion 13 can also
It is such as oblateness, ellipse, rectangle, round rectangle or rhombus.
When the temperature of shell 11 is higher than the second predetermined temperature, the color in warm change portion 13 changes into predetermined face by priming color
Color.
Color change in order to help to observe warm change portion 13 at night is provided with glimmering with reminding user in warm change portion 13
Light portion 14.Fluorescence portion 14 can be in night self-luminous, for example from emitting white light, the spontaneous light color in fluorescence portion 14 is first with warm change portion 13
Beginning color, predetermined color are different.Preferably, warm change portion 13 is housed in the space that fluorescence portion 14 fences up.It is glimmering in the present embodiment
Light portion 14 forms some discrete shapes, the combination of word, pattern or the word and pattern that are for example, arranged in warm change portion 13,
Such as logo, decorative pattern etc., the color change in the more convenient warm change portion 13 of observation.It is to be appreciated that fluorescence portion 14 can also
The position in the close temperature change portion 13 being provided on shell 11, similarly help to the color change in the warm change portion 13 of night observation.
In the present embodiment, the priming color in warm change portion 13, predetermined color respectively with the shell 11 containing temperature sensing color changing toner
Priming color, predetermined color it is identical.If priming color is black, predetermined color is orange.When the temperature of shell 11 is higher than
During the first predetermined temperature, temperature sensing color changing toner makes the color of shell 11 change into orange by black.When the temperature of shell 11 is higher than
During the second predetermined temperature, the color in warm change portion 13 changes into orange by black.Now whole shell 11 is all in orange.It is appreciated that
Ground, priming color, predetermined color can also be other colors, priming color, the species not enough present invention in pairs of predetermined color
Limitation.In other embodiments, the priming color of the shell 11 containing temperature sensing color changing toner, predetermined color and warm change portion 13
Priming color, predetermined color are respectively different.
First predetermined temperature is generally the heat-resisting warning temperature of shell 11 in normal use of connector 10.Second pre- constant temperature
Degree is generally the heat-resisting warning temperature of shell 11 in non-normal use of connector 10.If the shell when in use of connector 10
11 color changes, then shows the warning temperature when temperature of shell 11 has met or exceeded 10 normal use of connector,
Reminding effect is played to user.If the color in warm change portion 13 changes, show that the temperature of shell 11 has reached or surpassed
Warning temperature during 10 non-normal use of connector is crossed, plays high temperature warning function, now user should stop using, to prevent going out
Existing security incident, it is ensured that the normal use of connector 10.In the present embodiment, the first predetermined temperature is 35 degrees Celsius, and second is predetermined
Temperature is 60 degrees Celsius.
The difference to connector 10 can be realized by the color change of the shell 11 containing temperature sensing color changing toner, warm change portion 13
The temperature conditions in stage is warned, and reminding effect is played to user.User only need to be by observing shell 11, warm change portion 13
Color change be the current temperature conditions of can be known connector 10, can effectively ensure the normal use of connector 10, to prevent
There is safety problem.And connector 10 at night in use, the color change in warm change portion 13 can be by the spontaneous of fluorescence portion 14
Light is observed, and observation is convenient, and being not required to turn on light to be observed.
With reference to figure 3, for the schematic diagram of the data wire of application Fig. 1 of the present invention connector 10.The data wire includes connector
10 and cable 30.In the present embodiment, connector 10 is the input terminal adapter of data wire.The terminal 12 of connector 10 and cable 30
Electrical connection.In the present embodiment, it can be realized by the connector 10 and warning monitoring is carried out to the temperature conditions of the input of data wire,
Reminding effect is played to user, it can be ensured that the normal use of data wire, extend the service life of data wire.
Data wire also includes output terminal adapter 20, and the shell 21 of output terminal adapter 20 inputs using with connector 10
The same structure of the shell 11 of terminal adapter, so as to which data wire can realize the temperature conditions progress to input, output end simultaneously
Monitoring, further improve the security that data wire uses.
The present invention also provides a kind of manufacture method of temperature sensing color changing material, the manufacturing step and the temperature sensing color changing described in Fig. 1
Connector 10 shell 11 manufacturing step it is essentially identical, as shown in Fig. 2 mainly include pre-treatment step, be stirred step
Suddenly, extruding pelletization step and injection-moulding step, are repeated no more here.
By the material that the manufacture method produces due to containing temperature sensing color changing toner, making a reservation for when the temperature of the material is higher than
Color change can occur during temperature, so as to play supervisory function bit to temperature.
Above example only expresses the preferred embodiment of the present invention, and its description is more specific and detailed, but can not
Therefore it is interpreted as the limitation to the scope of the claims of the present invention.It should be pointed out that for the person of ordinary skill of the art,
Without departing from the inventive concept of the premise, various modifications and improvements can be made, it is such as special to the difference in each embodiment
Sign is combined, and these belong to protection scope of the present invention.
Claims (10)
1. a kind of connector of temperature sensing color changing, including shell and the terminal for being installed to the shell, it is characterised in that the shell
It is made up of following steps：
Pre-treatment step, specifically include：Temperature sensing color changing toner, antioxidant, heat stabilizer are ground, obtains pretreated warming
Change colour toner, antioxidant, heat stabilizer；
Step is stirred, is specifically included：Take 100 parts of unit of weight PVC plastic particles, pre- described in 0.1~10 part of unit of weight
Temperature sensing color changing toner, 20~50 parts of unit of weight plasticizer, 10~50 parts of unit of weight dispersing agent for wax after processing, 0.1~5 part
Pretreated antioxidant described in unit of weight, pretreated heat stabilizer described in 0.1~5 part of unit of weight are placed in stirring
Mixed 4 to 7 minutes within the temperature range of 40 to 60 degrees Celsius in machine, obtain compound；
Extruding pelletization step, is specifically included：The compound is placed in the torque rheometer of single screw rod, at 160 to 180 degrees Celsius
Within the temperature range of extruding pelletization, obtain Masterbatch；
Injection-moulding step, specifically include：The Masterbatch and soft pvc plastic are stirred and in 160 to 180 degrees Celsius of temperature
Injection molding in the range of degree.
2. the connector of temperature sensing color changing according to claim 1, it is characterised in that the temperature sensing color changing toner can make described
The color of shell changes when the temperature of shell is higher than the first predetermined temperature.
3. the connector of temperature sensing color changing according to claim 1, it is characterised in that the connector also includes covering institute
The warm change portion of shell is stated, when the temperature of the shell is higher than the second predetermined temperature color change occurs for the temperature change portion.
4. the connector of temperature sensing color changing according to claim 3, it is characterised in that the temperature change portion is printed in a manner of silk-screen
The shell is brushed so as to have shape corresponding with silk-screen.
5. the connector of temperature sensing color changing according to claim 3, it is characterised in that the connector also includes being arranged on institute
State the fluorescence portion in warm change portion.
6. the connector of temperature sensing color changing according to claim 5, it is characterised in that the temperature change portion is housed in the fluorescence
In the space that portion fences up.
7. a kind of new temperature sensing color changing data wire, including cable, it is characterised in that also including warming as claimed in claim 1
The connector of discoloration, the terminal of the connector electrically connect with the cable.
8. a kind of manufacture method of temperature sensing color changing material, it is characterised in that comprise the following steps：
Pre-treatment step, specifically include：Temperature sensing color changing toner, antioxidant, heat stabilizer are ground, obtains pretreated warming
Change colour toner, antioxidant, heat stabilizer；
Step is stirred, is specifically included：Take 100 parts of unit of weight PVC plastic particles, pre- described in 0.1~10 part of unit of weight
Temperature sensing color changing toner, 20~50 parts of unit of weight plasticizer, 10~50 parts of unit of weight dispersing agent for wax after processing, 0.1~5 part
Pretreated antioxidant described in unit of weight, pretreated heat stabilizer described in 0.1~5 part of unit of weight are placed in stirring
Mixed 4 to 7 minutes within the temperature range of 40 to 60 degrees Celsius in machine, obtain compound；
Extruding pelletization step, is specifically included：The compound is placed in the torque rheometer of single screw rod, at 160 to 180 degrees Celsius
Within the temperature range of extruding pelletization, obtain Masterbatch；
Injection-moulding step, specifically include：The Masterbatch and soft pvc plastic are stirred and in 160 to 180 degrees Celsius of temperature
Injection molding in the range of degree.
9. manufacture method according to claim 8, it is characterised in that described to be stirred in step, the time of mixing is 5
To 6 minutes.
10. manufacture method according to claim 8, it is characterised in that in the extruding pelletization step, the temperature of extruding pelletization
Spend for 160 to 180 degrees Celsius.