CN107722809A - A kind of ecological wall finiss for preventing that metope is mouldy, coming off and preparation method thereof - Google Patents
A kind of ecological wall finiss for preventing that metope is mouldy, coming off and preparation method thereof Download PDFInfo
- Publication number
- CN107722809A CN107722809A CN201711015600.5A CN201711015600A CN107722809A CN 107722809 A CN107722809 A CN 107722809A CN 201711015600 A CN201711015600 A CN 201711015600A CN 107722809 A CN107722809 A CN 107722809A
- Authority
- CN
- China
- Prior art keywords
- parts
- metope
- wall finiss
- mouldy
- coming
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of ecological wall finiss for preventing that metope is mouldy, coming off, including following components, as mass fraction：50 60 parts of 30 40 parts of aqueous polyurethane dispersion, 20 35 parts of modification infusorial earth, 10 15 parts of microporous calcium silicate, 10 15 parts of calcium stearate, 35 parts of silicone emulsion, 25 parts of composite assistant, 35 parts of surfactant, 35 parts of antioxidant, 5 10 parts of UV absorbers and deionized water.The invention also discloses a kind of preparation method for the ecological wall finiss for preventing that metope is mouldy, coming off.The wall finiss has oleophobic hydrophobic function, avoid water droplet and greasy dirt is attached to metope, improve the clean performance of wall finiss, and the wall finiss brushing is after metope, because porous material content is high, the sound absorption qualities of metope are substantially increased, there is good soundproof effect, improve the comfortableness of people's living environment.
Description
Technical field
The present invention relates to wall finiss to produce and process field, specifically a kind of ecological wall finiss for preventing that metope is mouldy, coming off
And preparation method thereof.
Background technology
Wall finiss is using extensively in the life and work of people, and especially in finishing field, the use of wall finiss increases
Add the aesthetic measure in house, it is welcomed by the people.
As people are to environmental protection and the attention of own health, used emulsion paint need to have the spy of environmental protection in fitment process
Do not require, first choice need to meet HJ2537-2014《Environmental labelling product technical requirements water paint》And GB18582-2008《Room
Limits of harmful substances in interior trim finishing material interior wall coating》Requirement, but existing wall finiss is after use, is passed through on metope
Water droplet and greasy dirt often are attached with, causes metope easily dirty, have impact on the living environment of people.
The content of the invention
It is an object of the invention to provide a kind of ecological wall finiss for preventing that metope is mouldy, coming off and preparation method thereof, with
Solve the problems, such as to propose in above-mentioned background technology.
To achieve the above object, the present invention provides following technical scheme：
A kind of ecological wall finiss for preventing that metope is mouldy, coming off, including following components, as mass fraction：Water-based poly- ammonia
Ester dispersion 30-40 parts, modification infusorial earth 20-35 parts, microporous calcium silicate 10-15 parts, calcium stearate 10-15 parts, silicone emulsion
3-5 parts, composite assistant 2-5 parts, surfactant 3-5 parts, antioxidant 3-5 parts, UV absorbers 5-10 parts and deionization
Water 50-60 parts.
As the further scheme of the present invention：The above-mentioned ecological wall finiss for preventing that metope is mouldy, coming off, including with the following group
Point, as mass fraction：Aqueous polyurethane dispersion 33-37 parts, modification infusorial earth 23-28 parts, microporous calcium silicate 11-13 parts,
Calcium stearate 12-14 parts, silicone emulsion 4-5 parts, composite assistant 2-3 parts, surfactant 3-4 parts, antioxidant 3-5 parts, purple
Outer light absorber 8-9 parts and deionized water 50-60 parts.
As further scheme of the invention：The above-mentioned ecological wall finiss for preventing that metope is mouldy, coming off, including with the following group
Point, as mass fraction：25 parts of aqueous polyurethane dispersion, 35 parts of modification infusorial earth, 12 parts of microporous calcium silicate, calcium stearate 13
Part, 4 parts of silicone emulsion, 3 parts of composite assistant, 4 parts of surfactant, 4 parts of antioxidant, 8 parts of UV absorbers and deionization
55 parts of water.
As further scheme of the invention：Described modification infusorial earth is that diatomite powder passes through faintly acid copper sulphate
Solution is prepared through concussion.
As further scheme of the invention：Described antioxidant is 2,2,6,6- tetramethylpiperidinols, antioxidant
For；One kind in 2,6- three-level butyl -4- methylphenols, pentaerythritol ester.
As further scheme of the invention：Described UV absorbers are septichen phenyl ester, 2- (2
ˊ-the ˊ of hydroxyl-5-aminomethyl phenyl) one or more of mixtures in BTA or ESCALOL 567.
The preparation method of the above-mentioned ecological wall finiss for preventing that metope is mouldy, coming off, is concretely comprised the following steps：
S1, diatomite modified：Diatomite addition is entered in copper-bath, is positioned in oscillator and shakes, during concussion
Between be 2h, filtering drying grind into powder, vacuum preserves.
S2, modification infusorial earth, microporous calcium silicate and calcium stearate be mixed evenly, cross 300 mesh sieves, pulverize
End, prepare intermediate blend A.
S3, intermediate blend A prepared by step S2 is added in deionized water, add aqueous polyurethane dispersion, heating
Stirring, heating-up temperature are 40-50 DEG C, stir, prepare solvent.
S4, silicone emulsion, composite assistant and surfactant, mistake after stirring are added in solvent prepared by step S3
Filter, prepares wall finiss crude product.
S5, after addition UV absorbers stir in wall finiss crude product prepared by step S4, it is sealed, produces
Finished product.
Compared with prior art, the beneficial effects of the invention are as follows：The wall finiss has oleophobic hydrophobic function, avoids water droplet
And greasy dirt is attached to metope, the clean performance of wall finiss is improved, and the wall finiss brushing is after metope, due to porous material
Expect that content is high, substantially increase the sound absorption qualities of metope, there is good soundproof effect, improve the comfortable of people's living environment
Property.
Embodiment
Technical scheme is described in more detail with reference to embodiment.
Embodiment 1
A kind of ecological wall finiss for preventing that metope is mouldy, coming off, including following components, as mass fraction：Water-based poly- ammonia
30 parts of ester dispersion, 20 parts of modification infusorial earth, 10 parts of microporous calcium silicate, 10 parts of calcium stearate, 3 parts of silicone emulsion, composite assistant 2
Part, 3 parts of surfactant, 3 parts of antioxidant, 5 parts of UV absorbers and 50 parts of deionized water.
Described modification infusorial earth is that diatomite powder is prepared by faintly acid copper-bath through concussion.
Described antioxidant is 2,2,6,6- tetramethylpiperidinols, and antioxidant is；2,6- three-level butyl -4- methylbenzenes
One kind in phenol, pentaerythritol ester.
Described UV absorbers are septichen phenyl ester, 2- (the 2 ˊ-ˊ of hydroxyl-5-aminomethyl phenyl) benzo three
One or more of mixtures in nitrogen azoles or ESCALOL 567.
A kind of preparation method for the ecological wall finiss for preventing that metope is mouldy described above, coming off, is comprised the following steps that：
S1, diatomite modified：Diatomite addition is entered in copper-bath, is positioned in oscillator and shakes, during concussion
Between be 2h, filtering drying grind into powder, vacuum preserves.
S2, modification infusorial earth, microporous calcium silicate and calcium stearate be mixed evenly, cross 300 mesh sieves, pulverize
End, prepare intermediate blend A.
S3, intermediate blend A prepared by step S2 is added in deionized water, add aqueous polyurethane dispersion, heating
Stirring, heating-up temperature are 40-50 DEG C, stir, prepare solvent.
S4, silicone emulsion, composite assistant and surfactant, mistake after stirring are added in solvent prepared by step S3
Filter, prepares wall finiss crude product.
S5, after addition UV absorbers stir in wall finiss crude product prepared by step S4, it is sealed, produces
Finished product.
Embodiment 2
A kind of ecological wall finiss for preventing that metope is mouldy, coming off, including following components, as mass fraction：Water-based poly- ammonia
35 parts of ester dispersion, 25 parts of modification infusorial earth, 12 parts of microporous calcium silicate, 13 parts of calcium stearate, 4 parts of silicone emulsion, composite assistant 3
Part, 4 parts of surfactant, 4 parts of antioxidant, 8 parts of UV absorbers and 55 parts of deionized water.
Described modification infusorial earth is that diatomite powder is prepared by faintly acid copper-bath through concussion.
Described antioxidant is 2,2,6,6- tetramethylpiperidinols, and antioxidant is；2,6- three-level butyl -4- methylbenzenes
One kind in phenol, pentaerythritol ester.
Described UV absorbers are septichen phenyl ester, 2- (the 2 ˊ-ˊ of hydroxyl-5-aminomethyl phenyl) benzo three
One or more of mixtures in nitrogen azoles or ESCALOL 567.
A kind of preparation method for the ecological wall finiss for preventing that metope is mouldy described above, coming off, is comprised the following steps that：
S1, diatomite modified：Diatomite addition is entered in copper-bath, is positioned in oscillator and shakes, during concussion
Between be 2h, filtering drying grind into powder, vacuum preserves.
S2, modification infusorial earth, microporous calcium silicate and calcium stearate be mixed evenly, cross 300 mesh sieves, pulverize
End, prepare intermediate blend A.
S3, intermediate blend A prepared by step S2 is added in deionized water, add aqueous polyurethane dispersion, heating
Stirring, heating-up temperature are 40-50 DEG C, stir, prepare solvent.
S4, silicone emulsion, composite assistant and surfactant, mistake after stirring are added in solvent prepared by step S3
Filter, prepares wall finiss crude product.
S5, after addition UV absorbers stir in wall finiss crude product prepared by step S4, it is sealed, produces
Finished product.
Embodiment 3
A kind of ecological wall finiss for preventing that metope is mouldy, coming off, including following components, as mass fraction：Water-based poly- ammonia
40 parts of ester dispersion, 40 parts of modification infusorial earth, 15 parts of microporous calcium silicate, 15 parts of calcium stearate, 5 parts of silicone emulsion, composite assistant 5
Part, 5 parts of surfactant, 5 parts of antioxidant, 10 parts of UV absorbers and 60 parts of deionized water.
Described modification infusorial earth is that diatomite powder is prepared by faintly acid copper-bath through concussion.
Described antioxidant is 2,2,6,6- tetramethylpiperidinols, and antioxidant is；2,6- three-level butyl -4- methylbenzenes
One kind in phenol, pentaerythritol ester.
Described UV absorbers are septichen phenyl ester, 2- (the 2 ˊ-ˊ of hydroxyl-5-aminomethyl phenyl) benzo three
One or more of mixtures in nitrogen azoles or ESCALOL 567.
A kind of preparation method for the ecological wall finiss for preventing that metope is mouldy described above, coming off, is comprised the following steps that：
S1, diatomite modified：Diatomite addition is entered in copper-bath, is positioned in oscillator and shakes, during concussion
Between be 2h, filtering drying grind into powder, vacuum preserves.
S2, modification infusorial earth, microporous calcium silicate and calcium stearate be mixed evenly, cross 300 mesh sieves, pulverize
End, prepare intermediate blend A.
S3, intermediate blend A prepared by step S2 is added in deionized water, add aqueous polyurethane dispersion, heating
Stirring, heating-up temperature are 40-50 DEG C, stir, prepare solvent.
S4, silicone emulsion, composite assistant and surfactant, mistake after stirring are added in solvent prepared by step S3
Filter, prepares wall finiss crude product.
S5, after addition UV absorbers stir in wall finiss crude product prepared by step S4, it is sealed, produces
Finished product.
The better embodiment of the present invention is explained in detail above, but the present invention is not limited to above-mentioned embodiment party
Formula, can also be on the premise of present inventive concept not be departed from one skilled in the relevant art's possessed knowledge
Various changes can be made.
Claims (7)
1. a kind of ecological wall finiss for preventing that metope is mouldy, coming off, it is characterised in that including following components, as mass fraction：
Aqueous polyurethane dispersion 30-40 parts, modification infusorial earth 20-35 parts, microporous calcium silicate 10-15 parts, calcium stearate 10-15 parts,
Silicone emulsion 3-5 parts, composite assistant 2-5 parts, surfactant 3-5 parts, antioxidant 3-5 parts, UV absorbers 5-10 parts
With deionized water 50-60 parts.
A kind of 2. ecological wall finiss for preventing that metope is mouldy, coming off according to claim 1, it is characterised in that including with
Lower component, as mass fraction：Aqueous polyurethane dispersion 33-37 parts, modification infusorial earth 23-28 parts, microporous calcium silicate 11-13
Part, calcium stearate 12-14 parts, silicone emulsion 4-5 parts, composite assistant 2-3 parts, surfactant 3-4 parts, antioxidant 3-5 parts,
UV absorbers 8-9 parts and deionized water 50-60 parts.
A kind of 3. ecological wall finiss for preventing that metope is mouldy, coming off according to claim 1, it is characterised in that including with
Lower component, as mass fraction：25 parts of aqueous polyurethane dispersion, 35 parts of modification infusorial earth, 12 parts of microporous calcium silicate, stearic acid
13 parts of calcium, 4 parts of silicone emulsion, 3 parts of composite assistant, 4 parts of surfactant, 4 parts of antioxidant, 8 parts of UV absorbers and go
55 parts of ionized water.
4. according to a kind of any described ecological wall finisses for preventing that metope is mouldy, coming off of claim 1-3, it is characterised in that
Described modification infusorial earth is that diatomite powder is prepared by faintly acid copper-bath through concussion.
5. a kind of ecological wall finiss for preventing that metope is mouldy, coming off according to claim 4, it is characterised in that described
Antioxidant is 2,2,6,6- tetramethylpiperidinols, and antioxidant is；In 2,6- three-level butyl -4- methylphenols, pentaerythritol ester
One kind.
6. a kind of ecological wall finiss for preventing that metope is mouldy, coming off according to claim 5, it is characterised in that described
UV absorbers are septichen phenyl ester, 2- (the 2 ˊ-ˊ of hydroxyl-5-aminomethyl phenyl) BTAs or 2- hydroxyls-4-
One or more of mixtures in methoxy benzophenone.
7. a kind of a kind of preparation method of ecological wall finiss for preventing that metope is mouldy, coming off as described in claim 1-3 is any,
Characterized in that, concretely comprise the following steps：
S1, diatomite modified：By diatomite addition enter copper-bath in, be positioned in oscillator and shake, concussion the time be
2h, filtering drying grind into powder, vacuum preserve.
S2, modification infusorial earth, microporous calcium silicate and calcium stearate be mixed evenly, cross 300 mesh sieves, grind into powder, system
Standby intermediate blend A.
S3, the intermediate blend A for adding step S2 preparations in deionized water, addition aqueous polyurethane dispersion, heating stirring,
Heating-up temperature is 40-50 DEG C, stirs, prepares solvent.
S4, silicone emulsion, composite assistant and surfactant are added in solvent prepared by step S3, are filtered after stirring,
Prepare wall finiss crude product.
S5, after addition UV absorbers stir in wall finiss crude product prepared by step S4, it is sealed, produces into
Product.