CN107722706A - A kind of moist putty paste and preparation method thereof - Google Patents
A kind of moist putty paste and preparation method thereof Download PDFInfo
- Publication number
- CN107722706A CN107722706A CN201711104787.6A CN201711104787A CN107722706A CN 107722706 A CN107722706 A CN 107722706A CN 201711104787 A CN201711104787 A CN 201711104787A CN 107722706 A CN107722706 A CN 107722706A
- Authority
- CN
- China
- Prior art keywords
- parts
- water
- putty paste
- moist
- coalescents
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of moist putty paste and preparation method thereof.The moist putty paste is in terms of parts by weight including following component：60 90 parts of filler；0 20 parts of water-proofing agent；5 30 parts of coalescents；15 parts of thickener；Also include water, the percentage by weight of the water and above-mentioned material total amount is 2:5；By filler, water, water-proofing agent and coalescents successively by stirring 30min to uniform under 1000r/min ~ 1200r/min in formula input mixer；The thickener of formula ratio is added, 3000r/min ~ 4000r/min is stirred 10 minutes ~ 15 minutes, to substantially uniformity, obtains finished product；Packaging：Finished product is weighed to put into Plastic Drum after measuring and packed.Moist putty paste provided by the present invention, its water resistance, sanding property, whiteness, caking property etc., can substitute brushing gypsum, dry-powder putty, imitation porcelain coating etc..
Description
Technical field
The present invention relates to putty paste, more particularly to a kind of moist putty paste and preparation method thereof.
Background technology
A large amount of sludge can be produced during artificial quartz stone plate wet tumbling, its composition is mainly silica, belongs to general discarded
Thing；But because it contains substantial amounts of moisture, limit utilization of the sludge in other industry.
Putty paste is a kind of decoration gel material of smooth surface of wall, is a kind of paste coating, and being must not before coating paints
A kind of product that can lack.Painting is imposed on priming paint or directly applied and imposes on object, rugged on coated article surface to remove
Defect.
Substantial amounts of brushing gypsum, inner wall putty etc. can be used in view of building trade inner wall decoration and paints alignment material, be
This, the product of research and utilization polished waste material production inner wall decoration putty paste is necessary.
The content of the invention
In view of this, it is an object of the invention to provide a kind of moist putty paste and preparation method thereof.
In order to reach above-mentioned purpose, the invention provides a kind of moist putty paste, including such as the following group in terms of parts by weight
Point：
Filler 60-90 parts；
Water-proofing agent 0-20 parts；
Coalescents 5-30 parts；
Thickener 1-5 parts.
Further, wherein including following component in terms of parts by weight：
60 parts of filler；
15 parts of water-proofing agent；
20 parts of coalescents；
5 parts of thickener；
40 parts of running water.
Further, wherein including following component in terms of parts by weight：
70 parts of filler；
20 parts of water-proofing agent；
9 parts of coalescents；
1 part of thickener；
40 parts of running water.
Further, wherein including following component in terms of parts by weight：
80 parts of filler；
10 parts of water-proofing agent；
5 parts of coalescents；
5 parts of thickener；
40 parts of running water.
Further, wherein including following component in terms of parts by weight：
90 parts of filler；
0 part of water-proofing agent；
6 parts of coalescents；
4 parts of thickener；
40 parts of running water.
Further, wherein also including water, the water and the weight of filler, water-proofing agent, coalescents and thickener total amount
Percentage is 2:5.
Further, wherein the filler is quartz polished waste material.
Further, wherein the water-proofing agent is sierozem power.
Further, wherein the coalescents are acrylic emulsion.
Further, wherein the thickener is methyl cellulose ether.
Further, wherein the water is running water.
Invention further provides a kind of preparation method of above-mentioned moist putty paste, comprise the following steps：
1）Filler, water, water-proofing agent and coalescents are put into mixer under 1000r/min ~ 1200r/min by formula successively
30min is stirred to uniform；
2）The thickener of formula ratio is added, 100r/min ~ 200r/min is stirred 10 minutes ~ 15 minutes, to substantially uniformity, obtained into
Product；
3）Packaging：Finished product is weighed to put into Plastic Drum after measuring and packed.
, should be first by the oil of matrix surface before construction invention further provides the application method of above-mentioned moist putty paste
The material such as stain, floating ash, dirt is disposed, it is ensured that the cleaning of matrix surface, to avoid matrix surface too dry from causing to scrape to criticizing
Putty paste cause to absorb water, matrix surface is soaked using water-based boundary material simple process or with water before batch scraping, Ran Houzai
Criticize Puttying cream.
Construction technical requirement：Putty paste batch, which is scraped to criticize by several times, to be scraped, and each batch is scraped thickness and should keep 0.5-1mm, and-secondary batch is scraped
It is blocked up easily dry shrinkage and cracking occur.Putty paste should be finished in 2h, can be polished before if desired being done solid work after surface drying.
The invention has the advantages that：
1st, moist putty paste provided by the present invention, its be pre-add water mixing all should body of paste, more on the market dry powder need to add water
Mix, will not airborne dust and more environmentally-friendly, in factory mechanical automation mixing can more all should, quality is more guaranteed；
2nd, moist putty paste provided by the present invention, which solve artificial quartz in lump polished waste material this disposition of solid waste and deposit
The problem put, turns waste into wealth；
3rd, moist putty paste provided by the present invention, its water resistance, sanding property, whiteness, caking property etc., can substitute powder
Brush gypsum, dry-powder putty, imitation porcelain coating etc.；
4th, preparation method provided by the present invention, due to the characteristics of make use of shearing force difference under the conditions of different speeds of agitator, make
Obtain preparation time to shorten, the effect of being adapted to rapid, high volume production, and can reach reduction Production Time and manpower operation's cost.
Embodiment
The present invention is explained with reference to embodiment, case study on implementation is merely to illustrate the present invention.Unless stated otherwise, it is of the invention
In used technological means be method known in those skilled in the art.In addition, embodiment be interpreted as it is illustrative,
The scope being not intended to limit the present invention, the spirit and scope of the invention are limited only by the claims that follow.
Following various raw materials are typically commercially available unless stated otherwise.
Embodiment 1：
A kind of moist putty paste is present embodiments provided, including following component in terms of parts by weight：
60 parts of quartz polished waste material；
15 parts of sierozem power；
20 parts of acrylic emulsion；
5 parts of methyl cellulose ether；
40 parts of running water.
The preparation method of above-mentioned moist putty paste, comprises the following steps：
1）60 parts of quartz polished waste materials, 40 parts of running water, 15 parts of sierozem powers and 20 parts of acrylic emulsions are thrown by formula successively
Enter in mixer to stir 30min under 100r/min ~ 200r/min to uniform；
2）5 parts of methyl cellulose ethers are added, 100r/min ~ 200r/min is stirred 10 minutes, to substantially uniformity, obtains finished product；
3）Packaging：Finished product is weighed to put into Plastic Drum after measuring and packed.
Embodiment 2：
A kind of moist putty paste is present embodiments provided, including following component in terms of parts by weight：
70 parts of quartz polished waste material；
20 parts of sierozem power；
9 parts of acrylic emulsion；
1 part of methyl cellulose ether；
40 parts of running water.
The preparation method of above-mentioned moist putty paste, comprises the following steps：
1）By 70 parts of quartz polished waste materials, 40 parts of running water, 20 parts of sierozem powers and 9 parts of acrylic emulsions successively by formula input
30min is stirred to uniform under 100r/min ~ 200r/min in mixer；
2）1 part of methyl cellulose ether is added, 100r/min ~ 200r/min is stirred 10 minutes, to substantially uniformity, obtains finished product；
3）Packaging：Finished product is weighed to put into Plastic Drum after measuring and packed.
Embodiment 3：
A kind of moist putty paste is present embodiments provided, including following component in terms of parts by weight：
80 parts of quartz polished waste material；
10 parts of sierozem power；
5 parts of acrylic emulsion；
5 parts of methyl cellulose ether；
40 parts of running water.
The preparation method of above-mentioned moist putty paste, comprises the following steps：
1）By 80 parts of quartz polished waste materials, 40 parts of running water, 10 parts of sierozem powers and 5 parts of acrylic emulsions successively by formula input
30min is stirred to uniform under 100r/min ~ 200r/min in mixer；
2）5 parts of methyl cellulose ethers are added, 100r/min ~ 200r/min is stirred 15 minutes, to substantially uniformity, obtains finished product；
3）Packaging：Finished product is weighed to put into Plastic Drum after measuring and packed.
Embodiment 4：
A kind of moist putty paste is present embodiments provided, including following component in terms of parts by weight：
90 parts of quartz polished waste material；
0 part of sierozem power；
6 parts of acrylic emulsion；
4 parts of methyl cellulose ether；
40 parts of running water.
The preparation method of above-mentioned moist putty paste, comprises the following steps：
1）By 90 parts of quartz polished waste materials, 40 parts of running water and 6 parts of acrylic emulsions successively by formula input mixer in
30min is stirred under 100r/min ~ 200r/min to uniform；
2）4 parts of methyl cellulose ethers are added, 100r/min ~ 200r/min is stirred 12 minutes, to substantially uniformity, obtains finished product；
3）Packaging：Finished product is weighed to put into Plastic Drum after measuring and packed.
First the material such as the oil stain of matrix surface, floating ash, dirt should be disposed before construction, it is ensured that the cleaning of matrix surface,
It is simple using water-based boundary material before batch scraping to avoid matrix surface too dry from causing to cause to absorb water to the putty paste batch scraped
Processing is soaked matrix surface with water, moisture content ＜ 8%, pH value ＜ 10, is then again applied putty paste and is scraped matrix surface, applies
More than 5 DEG C of work temperature, less than 35 DEG C, relative air humidity is less than 75%.
Construction technical requirement：Putty paste batch scrapes thickness more than 2mm, should by several times criticize and scrape, each batch is scraped thickness and should kept
0.5-1mm, scrape for-secondary batch and blocked up easily dry shrinkage and cracking occur.Putty paste should be finished in 2h, be beaten before should being done solid work after surface drying
Mill.
In order to test the performance of the moist putty paste of the present invention, the standard according to correlation prepares test specimen, to embodiment 1-
Releasing agent described in 4 carries out performance test.Test data is as shown in table 1.
Table 1
As it can be seen from table 1 the various aspects of performance of the putty paste described in 1-4 of the embodiment of the present invention is more excellent, can substitute
Brushing gypsum, dry-powder putty, imitation porcelain coating etc..
Although above the present invention is described in detail with a general description of the specific embodiments,
On the basis of the present invention, it can be made some modifications or improvements, this will be apparent to those skilled in the art.Cause
This, these modifications or improvements, belong to the scope of protection of present invention without departing from theon the basis of the spirit of the present invention.
Claims (10)
1. a kind of moist putty paste, it is characterised in that including following component in terms of parts by weight：
Filler 60-90 parts；
Water-proofing agent 0-20 parts；
Coalescents 5-30 parts；
Thickener 1-5 parts；
Also include water, the percentage by weight of the water and above-mentioned material total amount is 2:5.
2. moist putty paste as claimed in claim 1, it is characterised in that including following component in terms of parts by weight：
60 parts of filler；
15 parts of water-proofing agent；
20 parts of coalescents；
5 parts of thickener；
40 parts of running water.
3. moist putty paste as claimed in claim 1, it is characterised in that including following component in terms of parts by weight：
70 parts of filler；
20 parts of water-proofing agent；
9 parts of coalescents；
1 part of thickener；
40 parts of running water.
4. moist putty paste as claimed in claim 1, it is characterised in that including following component in terms of parts by weight：
80 parts of filler；
10 parts of water-proofing agent；
5 parts of coalescents；
5 parts of thickener；
40 parts of running water.
5. moist putty paste as claimed in claim 1, it is characterised in that including following component in terms of parts by weight：
90 parts of filler；
0 part of water-proofing agent；
6 parts of coalescents；
4 parts of thickener；
40 parts of running water.
6. the moist putty paste as described in claim any one of 1-5, it is characterised in that the filler is that quartz polishing is useless
Material.
7. moist putty paste as claimed in claim 6, it is characterised in that the water-proofing agent is sierozem power.
8. moist putty paste as claimed in claim 7, it is characterised in that the coalescents are acrylic emulsion.
9. moist putty paste as claimed in claim 8, it is characterised in that the thickener is methyl cellulose ether；The water
For running water.
10. the preparation method of the moist putty paste described in a kind of claim 9, it is characterised in that comprise the following steps：
1）Filler, water, water-proofing agent and coalescents are pressed successively and stirred in formula input mixer under 100r/min ~ 200r/min
30min is mixed to uniform；
2）The thickener of formula ratio is added, 100r/min ~ 200r/min is stirred 10 minutes ~ 15 minutes, to substantially uniformity, obtained into
Product；
3）Packaging：Finished product is weighed to put into Plastic Drum after measuring and packed.