CN107718984A - A kind of preparation method that I asks pottery handicraft - Google Patents
A kind of preparation method that I asks pottery handicraft Download PDFInfo
- Publication number
- CN107718984A CN107718984A CN201710907476.7A CN201710907476A CN107718984A CN 107718984 A CN107718984 A CN 107718984A CN 201710907476 A CN201710907476 A CN 201710907476A CN 107718984 A CN107718984 A CN 107718984A
- Authority
- CN
- China
- Prior art keywords
- glaze
- glazing
- ball milling
- pottery
- asks
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
A kind of preparation method that I asks pottery handicraft, belong to pottery ornameutal handiwork field, comprise the following steps, 1, engraving model;2nd, make mould, 3, choose clay;4th, slurrying;5th, slip casting;6th, it is molded;7th, biscuiting;8th, glazing;9th, fire;Described glaze material is by including melilite 50 60%, white feldspar 8 15%, calcite 10 15%, Copper Ores 3 5%, zinc chloride 3 5%, barium carbonate 0.1 0.4%, tin oxide 0.1 0.8%, the glaze material of kieselguhr 3 8% are crushed, mixing, ball milling, it is 420 targeted fine powders to become fineness, adds water that glaze slip is made after being stirred ball milling, includes 3% iron oxide, with the characteristics of design philosophy that can fully demonstrate works, dark red is presented in body color.
Description
Technical field
The invention belongs to industrial art field, what more particularly to a kind of title implied meaning for using pottery to make asked for me
The preparation method of handicraft.
Background technology
Ceramics are one of important components of Chinese culture, and pottery is one in Chinese Ceramics Culture bright bright
Pearl;Pottery has unique characteristics such as " entering that kiln is of the same colour, kiln discharge ten thousand is color ", is that other ceramics can not be realized and compare;
I asks, is a legend in Chinese tradition Taoism, designer utilizes the peculiar characteristic of pottery, by my people's matter-element
Element, Tai Ji female and male fish element are designed as rotation upwards, ask that, for content, such as Fig. 1, global design holds head high to endure for me with me
Chest, ask the feature image in day;Embody the wisdom of my Classic of the Virtue of the Tao, and negative and positive Tai Ji, the harmony between man and nature, the think of of studying from nature
Think elite;Wherein roomy robe sleeve is front and rear to form the concept with the rotation of Tai Ji female and male fish, and long beard is the boundary of female and male fish
Limit, both hands are respectively pitch attitude, also represent the concept of negative and positive;Bottom rotates up line with three, and statue is positioned over and turned
Rotated on platform, have the concept for ramping up and rising, overall implied meaning, signify that I is asked in day, and after attaining the Way, establish Tai Ji the moon
Sun, school of Taoist school basis of studying from nature, and derivative form school of Taoist school wisdom and thought.
The content of the invention
The design style and thought of pottery handicraft are asked in order to more preferably embody me, the present invention proposes one kind, and I asks
The preparation method of pottery handicraft;Comprise the following steps, 1, engraving model;2nd, make mould, 3, choose clay;4th, slurrying;5、
Slip casting;6th, it is molded;7th, biscuiting;8th, glazing;9th, fire;Described step 1 refers to whole handicraft being divided into some difference
Engraving;Wherein head, beard, chignon, left hand portion, right hand portion, foot add right robe sleeve as master plus robe pendulum plus left robe sleeve
Body, independently engraving shaping;Described step 2 refers to the head that will be carved respectively, beard, chignon, left hand portion, right hand portion,
Main body makes gypsum mold respectively;Described step 3 is to choose injecting paste material;Described injecting paste material includes blue clay 65-75%,
Sandstone 8-12%, lead powder 8-12%, mullite 8-12%, iron ore 1-2%, cobalt oxide 0.2-0.4%, dietary alkali 0.3-0.5%;It is described
Step 4 be to mix injecting paste material that step 3 is chosen to grind, its fineness of grinding be 230-250 mesh, adds ball milling after water mixing,
Pulpous state is made;Described step 5 is that the slurry in step 4 is injected separately into each mould in step 2;Described step 6
It is that will solidify the base type of generation in multiple moulds after slip casting, is bonded together according to design requirement, by finishing, is formed whole
The bodily form as;Described step 7 is that the base type after step 6 is molded is put into biscuit kiln, and 5-6 are fired at a temperature of 1000 °C
Hour;Described step 8 is that the base type after biscuiting is carried out into surface to apply glaze material, wherein head, beard, chignon, left hand portion, the right hand
Portion, foot part do not apply glaze, and main part either glaze spraying or is dipped in the method for glaze and carry out glazing using brushing glazing;Described glaze material is
Will be including melilite 50-60%, white feldspar 8-15%, calcite 10-15%, Copper Ores 3-5%, zinc chloride 3-5%, barium carbonate 0.1-
0.4%, tin oxide 0.1-0.8%, kieselguhr 3-8% glaze material are crushed, and mixing, ball milling, it is 420 purposes to become fineness
Fine powder, add water that glaze slip is made after being stirred ball milling;Described step 9 be by after glazing and dry base type be put into kiln
1300 °C of temperature fires 12-15 hour.
Beneficial effect
The beneficial effects of the present invention are can preferably embody me and ask the intention and artistic effect of works.
Brief description of the drawings
Fig. 1 is that I asks the schematic diagram of pottery handicraft
1. foot, 2. robes pendulum, 3. left robe sleeves, 4. beards, 5. heads, 6. right robe sleeves, 7. left hand portions.
Fig. 2 is that I asks the schematic rear view of pottery handicraft
6. right robe sleeve, 8. right hand portions, 9. chignons.
Embodiment
In order to further illustrate technical scheme, in conjunction with example, illustrate embodiment of the invention;Such as
Fig. 1, Fig. 2, embodiment one, the color in this example from main body be the chicken blood in pottery it is red exemplified by;It is first general from the industry
Model engraving process, foot 1 and the main body of robe pendulum 2 and left robe sleeve 3 and the composition of right robe sleeve 6 are carved into shaping, led to using the industry
Method makes the gypsum mold of main part;And head 5 is carved out respectively, and beard 4, chignon 9, left hand portion 7, right hand portion 8,
And gypsum mold is made respectively;The injecting paste material selected in this example includes blue clay 71%, sandstone 11%, lead powder 9%, mullite 10%,
Iron ore 1.5%, cobalt oxide 0.2%, dietary alkali 0.4%;So it is in order to which handicraft in the present invention can be embodied when base type is molded
Fine and smooth details;The injecting paste material of selection is mixed and ground, its fineness of grinding is 235 mesh, adds ball milling after water mixing, slurry is made
Shape;Above-mentioned slurry is injected separately into each mould in step 2, layering solidification, deflated profile is made with carving the outer of shaping
Shape is identical, the local base type of internal cavities;Foregoing local base type is bonded together according to design requirement, by finishing, formed
Overall image;It is put into after drying in biscuit kiln, 6 hours is fired at a temperature of 900-1000 °C;By the base after biscuiting
Type carries out surface and applies glaze material, and wherein head 5, beard 4, chignon 9, left hand portion 7, right hand portion 8, the part of foot 1 does not apply glaze, such energy
Enough embody the vivid of these parts;And glazing is carried out using the method for brushing glazing in main part this example;Glaze material is in this example
From including melilite 55%, white feldspar 10%, calcite 12%, Copper Ores 4%, zinc chloride 4%, barium carbonate 0.3%, tin oxide
0.5%, the glaze material of kieselguhr 5%, crushed, mixed, ball milling, it is 420 targeted fine powders to become fineness, adds water to stir
Glaze slip is made after mixing and ball milling;Surface of the glaze slip coated in main part is dried;By after glazing and dry base type be put into kiln
In 1300 °C temperature fire 13 hours, it becomes possible to obtain meeting design philosophy, and this hair of features above can be embodied
Bright signified I asks pottery handicraft.
Embodiment two, the character of artwork of pottery handicraft is asked in order to enrich me, the main part of works is selected in this example
Divide with dark red, the iron oxide of addition 3% in glaze material, other are identical with embodiment one, it becomes possible to which it is black to obtain body color
I ask pottery handicraft.
In embodiment more than it should be noted that in main part glazing, it shall be guaranteed that the glazed thickness of glazing is little
In 1 millimeter, to ensure to reduce the cracking of glaze layer, the solemnity of this works is influenceed.
Claims (1)
1. a kind of preparation method that I asks pottery handicraft, comprises the following steps, 1, engraving model;2nd, making mould, 3,
Choose clay;4th, slurrying;5th, slip casting;6th, it is molded;7th, biscuiting;8th, glazing;9th, fire;Described step 8 is by the base after biscuiting
Type carries out surface and applies glaze material, wherein head, and beard, chignon, left hand portion, right hand portion, foot part does not apply glaze, main part use
Brushing glazing either glaze spraying or dip in glaze method carry out glazing;Described glaze material is by including melilite 50-60%, white feldspar 8-
15%, calcite 10-15%, Copper Ores 3-5%, zinc chloride 3-5%, barium carbonate 0.1-0.4%, tin oxide 0.1-0.8%, kieselguhr 3-
8% glaze material is crushed, and mixing, ball milling, it is 420 targeted fine powders to become fineness, adds water that glaze is made after being stirred ball milling
Slurry, it is characterised in that:Also include iron oxide 3%.