CN107718739A - Performance rational in infrastructure prevents tearing fabric well - Google Patents
Performance rational in infrastructure prevents tearing fabric well Download PDFInfo
- Publication number
- CN107718739A CN107718739A CN201610660978.XA CN201610660978A CN107718739A CN 107718739 A CN107718739 A CN 107718739A CN 201610660978 A CN201610660978 A CN 201610660978A CN 107718739 A CN107718739 A CN 107718739A
- Authority
- CN
- China
- Prior art keywords
- layer
- fiber
- weft yarn
- tear
- yarn
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Prevent well tearing fabric, including lining fibrous layer the present invention relates to a kind of performance rational in infrastructure(1), middle composite layer is sequentially provided with outside lining fibrous layer(2), tissue layer(3), basal layer(4)Layer is pulled with anti-tear(5);It is anti-tear to pull layer(5)It is made into using Du Pont's CORDURA fibers.The lining fibrous layer back side is provided with backing fabric layers, the backing fabric layers, warp uses casein fibre, and parallel uses a diameter of 18.62 μm of viscose rayon, wherein casein fibre, fiber number is 252dtex, a diameter of 8.29 μm of viscose rayon, fiber number 198dtex, it is 25.9/cm through density, weft density is 16.3/cm, using twill weaves institutional framework.The present invention, which has, dual wear-resisting anti-tear pulls function.Present invention performance rational in infrastructure is good.
Description
Technical field
The present invention relates to a kind of fabric, more particularly to one kind to prevent tearing fabric, belongs to textile fabric field.
Background technology
With the continuous development of economy, requirement more and more higher of the people to clothes, except possess it is comfortable it is warming in addition to, also to have
Standby specific function.The garment fabric of in the market is more based on frivolous, comfortable, but its deficiency of defencive function to human body, especially
Be when taking vigorous exercise, such as antagonism closely fought game, high load capacity, high intensity work in, used clothing
Should possess certain tension, prevent tearing function.Clothing made of most commonly seen use denim fabric in the market, it possesses
Certain abrasion resistant effect, but denim fabric is excessively abundant, and poor air permeability, weight are big, can not meet that people are both light to fabric
The anti-tear demand pulled again.
The content of the invention
It is an object of the invention to overcome above-mentioned deficiency, there is provided one kind is anti-to tear fabric, and the fabric possesses in light weight, anti-
Draw, be wear-resisting, it is anti-the function such as tear, meet consumer demand.
The object of the present invention is achieved like this:A kind of performance rational in infrastructure prevents tearing fabric, including lining fibre well
Tie up layer, be sequentially provided with outside the lining fibrous layer middle composite layer, tissue layer, basal layer and it is anti-tear pull layer, each layer passes through suture
It is fixed;The lining fibrous layer includes the first warp thread and the first weft yarn, and first warp thread is made into using cotton fiber, and described first
Weft yarn is made into using flax fiber;The middle composite layer includes the second warp thread and the second weft yarn, and second warp thread uses ox
Young yarn is made into, and second weft yarn is made into using wire spiral fiber;The tissue layer includes the 3rd warp thread and the 3rd latitude
Yarn, the 3rd warp thread are made into using Modal fibre, and the 3rd weft yarn is made into using cotton fiber;The basal layer uses
The ventilative polyester fiber of CoolMaX Du Ponts moisture absorption is made into;The anti-tear layer that pulls is made into using Du Pont's CORDURA fibers.The lining
The fibrous layer back side is provided with backing fabric layers, the backing fabric layers, and warp uses casein fibre, and parallel uses viscose rayon,
Wherein a diameter of 18.62 μm of casein fibre, fiber number 252dtex, a diameter of 8.29 μm of viscose rayon, fiber number is
198dtex, it is 25.9/cm through density, weft density is 16.3/cm, using twill weaves institutional framework.
Compared with prior art, the beneficial effects of the invention are as follows:
Du Pont's CORDURA fibers, possess high intensity, high abrasion, height and torn the performances such as anti-cut;Denim yarn and wire
Spiral fiber forms middle composite layer, with it is anti-tear pull layer and combine to form dual wear-resisting anti-tear pull function.
The present invention is rational in infrastructure, and performance is good, can meet the consumer of special requirement.
Brief description of the drawings
Fig. 1 is a kind of anti-structural representation for tearing fabric of the present invention.
Wherein:
Lining fibrous layer 1
Middle composite layer 2
Tissue layer 3
Basal layer 4
It is anti-tear to pull layer 5.
Embodiment
Referring to Fig. 1, a kind of performance rational in infrastructure prevents tearing fabric, including lining fibrous layer, the lining fiber well
Layer is outer be sequentially provided with middle composite layer, tissue layer, basal layer and it is anti-tear pull layer, each layer, which passes through to suture, to be fixed;The lining fiber
Layer includes the first warp thread and the first weft yarn, and first warp thread is made into using cotton fiber, and first weft yarn uses flax fiber
It is made into;The middle composite layer includes the second warp thread and the second weft yarn, and second warp thread is made into using denim yarn, and described
Two weft yarns are made into using wire spiral fiber;The tissue layer includes the 3rd warp thread and the 3rd weft yarn, and the 3rd warp thread is adopted
It is made into Modal fibre, the 3rd weft yarn is made into using cotton fiber;The basal layer is saturating using the moisture absorption of CoolMaX Du Ponts
Gas polyester fiber is made into;The anti-tear layer that pulls is made into using Du Pont's CORDURA fibers.
The lining fibrous layer back side is provided with backing fabric layers, the backing fabric layers, and warp uses casein fibre, latitude
Line uses a diameter of 18.62 μm of viscose rayon, wherein casein fibre, fiber number 252dtex, and a diameter of the 8.29 of viscose rayon
μm, fiber number 198dtex, it is 25.9/cm through density, weft density is 16.3/cm, using twill weaves institutional framework.
Claims (1)
1. a kind of performance rational in infrastructure prevents tearing fabric well, it is characterised in that:Including lining fibrous layer(1), the lining
Fibrous layer(1)It is sequentially provided with middle composite layer outside(2), tissue layer(3), basal layer(4)Layer is pulled with anti-tear(5), each layer passes through seam
Close and fix;The lining fibrous layer(1)Including the first warp thread and the first weft yarn, first warp thread is made into using cotton fiber, institute
The first weft yarn is stated to be made into using flax fiber;The middle composite layer(2)Including the second warp thread and the second weft yarn, second warp
Yarn is made into using denim yarn, and second weft yarn is made into using wire spiral fiber;The tissue layer(3)Including the 3rd warp
Yarn and the 3rd weft yarn, the 3rd warp thread are made into using Modal fibre, and the 3rd weft yarn is made into using cotton fiber;The base
Plinth layer(4)It is made into using the ventilative polyester fiber of CoolMaX Du Ponts moisture absorption;It is described anti-tear to pull layer(5)It is fine using Du Pont CORDURA
Dimension is made into;The lining fibrous layer back side is provided with backing fabric layers, the backing fabric layers, and warp uses casein fibre, latitude
Line uses a diameter of 18.62 μm of viscose rayon, wherein casein fibre, fiber number 252dtex, and a diameter of the 8.29 of viscose rayon
μm, fiber number 198dtex, it is 25.9/cm through density, weft density is 16.3/cm, using twill weaves institutional framework.