CN106183197A - Special requirement can be met prevent tearing fabric - Google Patents
Special requirement can be met prevent tearing fabric Download PDFInfo
- Publication number
- CN106183197A CN106183197A CN201610655716.4A CN201610655716A CN106183197A CN 106183197 A CN106183197 A CN 106183197A CN 201610655716 A CN201610655716 A CN 201610655716A CN 106183197 A CN106183197 A CN 106183197A
- Authority
- CN
- China
- Prior art keywords
- layer
- fiber
- warp thread
- weft yarn
- tear
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to one and can meet that special requirement is anti-tears fabric, including fibrous layer inside (1), be sequentially provided with inside middle composite layer (2), tissue layer (3), basal layer (4) outside fibrous layer and anti-tear pull layer (5);The anti-tear layer (5) that pulls uses Du Pont's CORDURA fiber to be made into.The described back side of fibrous layer inside is provided with backing fabric layers, described backing fabric layers, it is respectively adopted cotton fiber and silk tussah fibre through parallel, wherein a diameter of 16.3 μm of cotton fiber, fiber number is 278dtex, a diameter of 13.9 μm of silk tussah fibre, and fiber number is 263dtex, being 35.1/cm through density, weft density is 18.3/cm.The present invention has and dual wear-resisting anti-tear pulls function.The present invention can meet special requirement.
Description
Technical field
The present invention relates to a kind of fabric, particularly relate to one and prevent tearing fabric, belong to textile fabric field.
Background technology
Along with economic development, people are more and more higher to the requirement of clothing, except possess comfortable warming in addition to, also to have
Standby specific function.Garment fabric on market is many based on frivolous, comfortable, but it is not enough, especially to the defencive function of human body
Taking vigorous exercise when, such as antagonism closely fought game, high load capacity, high intensity work in, the medicated clothing used
Should possess certain tension, anti-tear function.The most most commonly seen medicated clothing using denim fabric to make, it possesses
Certain abrasion resistant effect, but denim fabric is the most abundant, and poor air permeability, weight are big, it is impossible to meet people the lightest to fabric
The most anti-tear demand pulled.
Summary of the invention
It is an object of the invention to overcome above-mentioned deficiency, it is provided that one is anti-tears fabric, and this fabric has possessed lightweight, anti-
Draw, the function such as tear wear-resisting, anti-, meet consumer demand.
The object of the present invention is achieved like this: one can meet special requirement and prevent tearing fabric, including fibrous layer inside,
Being sequentially provided with middle composite layer, tissue layer, basal layer and the anti-tear layer that pulls outside described fibrous layer inside, each layer is fixing by sewing up;
Described fibrous layer inside includes that the first warp thread and the first weft yarn, described first warp thread use cotton fiber to be made into, described first weft yarn
Employing flax fiber is made into;Described middle composite layer includes that the second warp thread and the second weft yarn, described second warp thread use jean yarn
Line is made into, and described second weft yarn uses tinsel spiral fiber to be made into;Described tissue layer includes the 3rd warp thread and the 3rd weft yarn, institute
Stating the 3rd warp thread uses Modal fibre to be made into, and described 3rd weft yarn uses cotton fiber to be made into;Described basal layer uses CoolMaX
Du Pont's moisture absorption polyster fibre of breathing freely is made into;The described anti-tear layer that pulls uses Du Pont's CORDURA fiber to be made into.Described fibrous layer inside is carried on the back
Face is provided with backing fabric layers, described backing fabric layers, and it is respectively adopted cotton fiber and silk tussah fibre through parallel, wherein cotton fine
A diameter of 16.3 μm of dimension, fiber number is 278dtex, and a diameter of 13.9 μm of silk tussah fibre, fiber number is 263dtex, through density
Being 35.1/cm, weft density is 18.3/cm.
Compared with prior art, the invention has the beneficial effects as follows:
Du Pont's CORDURA fiber, possesses high intensity, high abrasion, high has torn the anti-cut performance such as cut;Denim yarn and tinsel
Spiral fiber forms middle composite layer, is combined to be formed dual wear-resisting anti-tear pulls function with the anti-tear layer that pulls.
Present configuration is reasonable, and serviceability is good, can meet the consumer of special requirement.
Accompanying drawing explanation
Fig. 1 is a kind of anti-structural representation tearing fabric of the present invention.
Wherein:
Fibrous layer 1 inside
Middle composite layer 2
Tissue layer 3
Basal layer 4
Anti-tear pull layer 5.
Detailed description of the invention
Seeing Fig. 1, one can meet special requirement and prevent tearing fabric, including fibrous layer inside, outside described fibrous layer inside
Being sequentially provided with middle composite layer, tissue layer, basal layer and the anti-tear layer that pulls, each layer is fixing by sewing up;Described fibrous layer bag inside
Including the first warp thread and the first weft yarn, described first warp thread uses cotton fiber to be made into, and described first weft yarn uses flax fiber to be made into;
Described middle composite layer includes that the second warp thread and the second weft yarn, described second warp thread use denim yarn to be made into, described second latitude
Yarn uses tinsel spiral fiber to be made into;Described tissue layer includes that the 3rd warp thread and the 3rd weft yarn, described 3rd warp thread use not
Dai Er fiber is made into, and described 3rd weft yarn uses cotton fiber to be made into;Described basal layer uses the moisture absorption of CoolMaX Du Pont to breathe freely and washs
Synthetic fibre fiber is made into;The described anti-tear layer that pulls uses Du Pont's CORDURA fiber to be made into.
The described back side of fibrous layer inside is provided with backing fabric layers, described backing fabric layers, and it is respectively adopted cotton through parallel
Fiber and silk tussah fibre, wherein a diameter of 16.3 μm of cotton fiber, fiber number is 278dtex, silk tussah fibre a diameter of
13.9 μm, fiber number is 263dtex, is 35.1/cm through density, and weft density is 18.3/cm.
Claims (1)
1. one kind can meet that special requirement is anti-tears fabric, it is characterised in that: include fibrous layer (1) inside, described fiber inside
Being sequentially provided with middle composite layer (2), tissue layer (3), basal layer (4) outside layer (1) and anti-tear pull layer (5), each layer is consolidated by sewing up
Fixed;Described fibrous layer inside (1) includes the first warp thread and the first weft yarn, and described first warp thread uses cotton fiber to be made into, described the
One weft yarn uses flax fiber to be made into;Described middle composite layer (2) includes that the second warp thread and the second weft yarn, described second warp thread are adopted
Being made into by denim yarn, described second weft yarn uses tinsel spiral fiber to be made into;Described tissue layer (3) include the 3rd warp thread and
3rd weft yarn, described 3rd warp thread uses Modal fibre to be made into, and described 3rd weft yarn uses cotton fiber to be made into;Described basal layer
(4) CoolMaX Du Pont moisture absorption polyster fibre of breathing freely is used to be made into;The described anti-tear layer (5) that pulls uses Du Pont's CORDURA fiber to knit
Become;The described back side of fibrous layer inside is provided with backing fabric layers, described backing fabric layers, its through parallel be respectively adopted cotton fiber and
Silk tussah fibre, wherein a diameter of 16.3 μm of cotton fiber, fiber number is 278dtex, a diameter of 13.9 μm of silk tussah fibre, fine
Degree is 263dtex, is 35.1/cm through density, and weft density is 18.3/cm.