CN107699150A - A kind of environmentally friendly cold-pressed adhesive tape - Google Patents
A kind of environmentally friendly cold-pressed adhesive tape Download PDFInfo
- Publication number
- CN107699150A CN107699150A CN201610645135.2A CN201610645135A CN107699150A CN 107699150 A CN107699150 A CN 107699150A CN 201610645135 A CN201610645135 A CN 201610645135A CN 107699150 A CN107699150 A CN 107699150A
- Authority
- CN
- China
- Prior art keywords
- adhesive tape
- environmentally friendly
- paper
- pressed
- friendly cold
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of environmentally friendly cold-pressed adhesive tape, including adhesive tape layer and adhesive linkage, adhesive linkage is arranged at the upper surface of adhesive tape layer, and the component of adhesive linkage is mainly made up of latex, ammoniacal liquor, filler, antioxidant and mixed aid.The environmentally friendly cold-pressed adhesive tape composition of the present invention is simple, and production process is few, and cost is cheap, and the raw materials for production of use are environment friendly and pollution-free, not cull, and tack and stability are stronger.
Description
Technical field
The application belongs to adhesive tape area, specifically, is related to a kind of environmentally friendly cold-pressed adhesive tape.
Background technology
In electric capacity industrialized production, electric capacity carries out needing to cover by adhesive tape during metal spraying, and electric capacity is used when producing
Cold-pressed adhesive tape, composition are mostly noxious material, and formula is complicated, and manufacturing process is more, less stable, and easy cull needs on electric capacity
Electric capacity is subsequently cleared up, influence the production efficiency and product quality of electric capacity.
The content of the invention
For deficiency of the prior art, it is an object of the invention to provide a kind of environmentally friendly cold-pressed adhesive tape.
In order to solve the above-mentioned technical problem, this application discloses a kind of environmentally friendly cold-pressed adhesive tape, including adhesive tape layer and adhesive linkage,
Adhesive linkage is arranged at the upper surface of adhesive tape layer, and the component of adhesive linkage is mainly helped by latex, ammoniacal liquor, filler, antioxidant and mixing
Agent forms, and wherein percentage by weight corresponding to each component is
Latex 55%~70%
Ammoniacal liquor 25%~40%
Filler 0.1%~1.0%
Antioxidant 0.1%~1.0% and
Mixed aid 0.1%~5.0%.
According to the embodiment of the application, above-mentioned adhesive tape layer includes upper strengthening course, ply of paper and lower strengthening course, upper strengthening course
It is arranged at the upper surface of ply of paper, lower strengthening course is arranged at the lower surface of ply of paper, and the component of upper strengthening course and lower strengthening course is surface
Inorganic agent.
According to the embodiment of the application, above-mentioned adhesive tape layer includes ply of paper.
According to the embodiment of the application, above-mentioned latex is natural emulsion.
According to the embodiment of the application, the thickness of above-mentioned adhesive linkage is 20 μm~27 μm.
According to the embodiment of the application, the thickness of above-mentioned upper strengthening course and lower strengthening course is respectively 0.1 μm~0.5 μ
m。
According to the embodiment of the application, the thickness of above-mentioned ply of paper is 60 μm~70 μm.
According to the embodiment of the application, above-mentioned ply of paper is brown paper, U.S. line paper, Micron Technology's paper or other environment protecting papers.
According to the embodiment of the application, above-mentioned filler is calcium hydroxide or magnesium hydroxide.
According to the embodiment of the application, above-mentioned antioxidant is paracresol and dicyclopentadiene copolymer.
The environmentally friendly cold-pressed adhesive tape composition of the present invention is simple, and production process is few, and cost is cheap, the raw materials for production environmental protection nothing of use
Pollute, not cull, tack and stability are stronger, not cull.
Brief description of the drawings
Accompanying drawing described herein is used for providing further understanding of the present application, forms the part of the application, this Shen
Schematic description and description please is used to explain the application, does not form the improper restriction to the application.In the accompanying drawings:
Fig. 1 is the environmentally friendly cold-pressed adhesive tape structure chart of the embodiment of the application.
Fig. 2 is the adhesive tape layer structure chart of the embodiment of the application.
Embodiment
Multiple embodiments of the application will be disclosed with schema below, as clearly stated, the details on many material objects
It will be explained in the following description.It should be appreciated, however, that the details on these material objects is not applied to limit the application.Also
It is to say, in some embodiments of the application, the details in these practices is non-essential.In addition, for the sake of simplifying schema,
Some known usual structures will illustrate it in a manner of simply illustrative in the drawings with component.
Referring to Fig. 1, Fig. 1 is the environmentally friendly cold-pressed adhesive tape structure chart of the embodiment of the application.As shown in figure 1, this hair
Bright environmentally friendly cold-pressed adhesive tape, including adhesive tape layer 2 and adhesive linkage 1, adhesive linkage 1 are arranged at the upper surface of adhesive tape layer 2, adhesive linkage 1
Component is mainly made up of latex, ammoniacal liquor, filler, antioxidant and mixed aid.Percentage by weight corresponding to each component is
Latex 55%~70%
Ammoniacal liquor 25%~40%
Filler 0.1%~1.0%
Antioxidant 0.1%~1.0%
Mixed aid 0.1%~5.0%.
The adhesive linkage 1 of the present invention uses and method is produced by below.At normal temperatures, latex and ammoniacal liquor are inserted into high speed dispersor
In, latex is natural emulsion, is stirred 30 minutes by high speed dispersor, cools down mixture to normal temperature, then successively to mixing
Filler, antioxidant and mixed aid are added in thing, it is preferable that filler is calcium hydroxide or magnesium hydroxide, and filler has
Sterilization and the effect for suppressing bacterial putrefaction, antioxidant is paracresol and dicyclopentadiene copolymer, then is stirred by high speed dispersor
Glue is formed after mixing uniformly, is stored being stood in glue injection storage glue tank, glue is finally applied to adhesive tape by rolling technology
The upper surface of layer 2 forms adhesive linkage 1, and adhesive linkage 1 and adhesive tape layer 2 form the environmentally friendly cold-pressed adhesive tape of the application.Referring to Fig. 2, its
The structure chart of adhesive tape layer 2 of the embodiment of real the application.As illustrated, wherein adhesive tape layer 2 includes ply of paper 21, ply of paper 21 can be adopted
With brown paper, U.S. line paper, Micron Technology's paper or other environment protecting papers.Selectively, for strengthen ply of paper 21 tensile resistence and glue into
The adhesive force of product therewith, in the upper and lower surface coating surface inorganic agent of ply of paper 21, and in the upper surface of ply of paper 21 and under
Surface forms strengthening course 22 and lower strengthening course 23 respectively.The thickness of the adhesive linkage 1 of the application is 20 μm~27 μm, upper strengthening course
22 and lower strengthening course 23 be respectively 0.1 μm~0.5 μm, the thickness of ply of paper 21 is 60 μm~70 μm.
Embodiment 1:
As shown in figure 1, the environmentally friendly cold-pressed adhesive tape that the application provides, is followed successively by adhesive linkage 1 and adhesive tape layer 2 from top to bottom.Its
The component of middle adhesive linkage 1 is mainly made up of latex, ammoniacal liquor, filler, antioxidant and mixed aid, weight hundred corresponding to each component
Point ratio is:Weight ratio shared by latex is 55%, and weight ratio shared by ammoniacal liquor is 40%, and weight ratio shared by filler is 0.3%, antioxygen
Weight ratio shared by agent is 0.3%, and weight ratio shared by mixed aid is 4.4%, and mixing preparation is formed each component according to the method described above
Glue, the upper surface that adhesive tape layer 2 is applied to finally by rolling technology form adhesive linkage 1.Further, adhesive tape layer 2 includes paper
Layer, ply of paper use the brown paper of high intensity, and adhesive linkage 1 and adhesive tape layer 2 form the environmentally friendly cold-pressed adhesive tape of the application.Adhesive linkage 1
Thickness is 23 μm, and the thickness of adhesive tape layer 2 is 65 μm.
Embodiment 2:
As shown in figure 1, the environmentally friendly cold-pressed adhesive tape that the application provides, is followed successively by adhesive linkage 1 and adhesive tape layer 2 from top to bottom.Its
The component of middle adhesive linkage 1 is mainly made up of latex, ammoniacal liquor, filler, antioxidant and mixed aid, weight hundred corresponding to each component
Point ratio is:Weight ratio shared by latex is 60%, and weight ratio shared by ammoniacal liquor is 37.5%, and weight ratio shared by filler is 0.5%, is resisted
Weight ratio shared by oxygen agent is 0.5%, and weight ratio shared by mixed aid is 1.5%, each component mixing preparation shape according to the method described above
Into glue, the upper surface that adhesive tape layer 2 is applied to finally by rolling technology forms adhesive linkage 1.Further, adhesive tape layer 2 includes
Ply of paper, ply of paper use the brown paper of high intensity, and adhesive linkage 1 and adhesive tape layer 2 form the environmentally friendly cold-pressed adhesive tape of the application.Adhesive linkage 1
Thickness be 25 μm, the thickness of adhesive tape layer 2 is 65 μm.
Embodiment 3:
As shown in figure 1, the environmentally friendly cold-pressed adhesive tape that the application provides, is followed successively by adhesive linkage 1 and adhesive tape layer 2 from top to bottom.Its
The component of middle adhesive linkage 1 is mainly made up of latex, ammoniacal liquor, filler, antioxidant and mixed aid, weight hundred corresponding to each component
Point ratio is:Weight ratio shared by latex is 70%, and weight ratio shared by ammoniacal liquor is 27%, and weight ratio shared by filler is 1.0%, antioxygen
Weight ratio shared by agent is 1.0%, and weight ratio shared by mixed aid is 1.0%, and mixing preparation is formed each component according to the method described above
Glue, the upper surface that adhesive tape layer 2 is applied to finally by rolling technology form adhesive linkage 1, and further, adhesive tape layer 2 includes paper
Layer, ply of paper use the brown paper of high intensity, and adhesive linkage 1 and adhesive tape layer 2 form the environmentally friendly cold-pressed adhesive tape of the application.Adhesive linkage 1
Thickness is 27 μm, and the thickness of adhesive tape layer 2 is 65 μm.
In summary, in one or more embodiments of the application, the environmentally friendly cold-pressed adhesive tape composition of the application is simple, makes work
Sequence is few, and cost is cheap, and the raw materials for production of use are environment friendly and pollution-free, not cull, and tack and stability are stronger.
Some preferred embodiments of the present invention have shown and described in described above, but as previously described, it should be understood that the present invention
Be not limited to form disclosed herein, be not to be taken as the exclusion to other embodiment, and available for various other combinations,
Modification and environment, and above-mentioned teaching or the technology or knowledge of association area can be passed through in the scope of the invention is set forth herein
It is modified., then all should be in this hair and the change and change that those skilled in the art are carried out do not depart from the spirit and scope of the present invention
The protection domain of bright appended claims.
Claims (10)
1. a kind of environmentally friendly cold-pressed adhesive tape, it is characterised in that including adhesive tape layer and adhesive linkage, the adhesive linkage is arranged at the adhesive tape
The upper surface of layer, the component of the adhesive linkage is mainly made up of latex, ammoniacal liquor, filler, antioxidant and mixed aid, wherein respectively
Component corresponds to percentage by weight
2. environmentally friendly cold-pressed adhesive tape according to claim 1, it is characterised in that the adhesive tape layer includes upper strengthening course, ply of paper
And lower strengthening course, the upper strengthening course are arranged at the upper surface of the ply of paper, the lower strengthening course is arranged under the ply of paper
The component of surface, the upper strengthening course and lower strengthening course is surface conditioning agent.
3. environmentally friendly cold-pressed adhesive tape according to claim 1, it is characterised in that the adhesive tape layer includes ply of paper.
4. environmentally friendly cold-pressed adhesive tape according to claim 1, it is characterised in that the latex is natural emulsion.
5. environmentally friendly cold-pressed adhesive tape according to claim 1, it is characterised in that the thickness of the adhesive linkage is 20 μm~27 μ
m。
6. environmentally friendly cold-pressed adhesive tape according to claim 2, it is characterised in that the thickness of the upper strengthening course and lower strengthening course
Respectively 0.1 μm~0.5 μm.
7. the environmentally friendly cold-pressed adhesive tape according to Claims 2 or 3, it is characterised in that the thickness of the ply of paper is 60 μm~70 μ
m。
8. environmentally friendly cold-pressed adhesive tape according to claim 7, it is characterised in that the material of the ply of paper is brown paper, U.S. line
Paper, Micron Technology's paper or other environment protecting papers.
9. environmentally friendly cold-pressed adhesive tape according to claim 1, it is characterised in that the filler is calcium hydroxide or hydroxide
Magnesium.
10. environmentally friendly cold-pressed adhesive tape according to claim 1, it is characterised in that the antioxidant is paracresol and bicyclic penta
Diene copolymers.