CN107699128A - A kind of alcohol-soluble zinc-rich coating and its production method - Google Patents
A kind of alcohol-soluble zinc-rich coating and its production method Download PDFInfo
- Publication number
- CN107699128A CN107699128A CN201710961384.7A CN201710961384A CN107699128A CN 107699128 A CN107699128 A CN 107699128A CN 201710961384 A CN201710961384 A CN 201710961384A CN 107699128 A CN107699128 A CN 107699128A
- Authority
- CN
- China
- Prior art keywords
- parts
- alcohol
- zinc
- rich coating
- soluble zinc
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of alcohol-soluble zinc-rich coating, it is made up of following raw material according to parts by weight：Alkyl silicic acids ester polymer：30 40 parts；Zinc powder:40 50 parts；Solvent:20 30 parts；Auxiliary agent：25 parts；A kind of production method of alcohol-soluble zinc-rich coating, the production method of the alcohol-soluble zinc-rich coating comprise the following steps：S1；Stirred under normal pressure；S2 is packed.Alcohol-soluble zinc-rich coating is made up of alkyl silicic acids ester polymer, zinc powder, auxiliary agent and solvent etc..
Description
Technical field
The present invention relates to alcohol-soluble zinc-rich coating technical field, specially a kind of alcohol-soluble zinc-rich coating and its
Production method.
Background technology
The priming paint that alcohol-soluble zinc-rich coating makees high-performance painting design uses, available for industrial antisepsis coating, machinery
Product coating, anticorrosion of steel structure coating, bridge anti-corrosion primer, ocean and offshore installation anti-corrosion primer etc..Alcohol-soluble inorganic zinc-rich
The cathodic protection effect of priming paint zinc powder makes coating have fabulous rustless property.Drying rapid, workpiece is in a short period of time
Stackable, carrying.400 DEG C of high temperature can be subjected to for a long time with prominent heat resistance, paint film.Solvent resistance is good, impact resistance
And excellent wear-resisting property.Excellent low temperature curing properties (can also solidify in the case of -20 DEG C).
The content of the invention
The invention aims to solve shortcoming present in prior art, and a kind of alcohol-soluble inorganic zinc-rich proposed
Priming paint and its production method.
To achieve the above object, the present invention provides following technical scheme：
A kind of alcohol-soluble zinc-rich coating, is made up of following raw material according to parts by weight：
Alkyl silicic acids ester polymer：30 parts；
Zinc powder：40 parts；
Solvent：20 parts；
Auxiliary agent：2 parts；
Preferably, the alkyl silicic acids ester polymer.
Preferably, the zinc powder particle diameter is 400 mesh.
Preferably, a kind of production method of alcohol-soluble zinc-rich coating, the producer of the alcohol-soluble zinc-rich coating
Method comprises the following steps：
S1：Stirred under normal pressure：Alkyl silicic acids ester polymer：30 parts；Zinc powder：40 parts；Solvent：20 parts；Auxiliary agent：2 parts；Stirring
30 minutes to 50 minutes；
S2：Packaging：S1 product is packed according to specification requirement.
A kind of alcohol-soluble zinc-rich coating provided by the invention, the alcohol-soluble zinc-rich coating not only have preferable
Antiseptic property, and be that a kind of cost is cheap, excellent performance, full-featured alcohol-soluble zinc-rich coating.
Embodiment
Based on the embodiment in the present invention, those of ordinary skill in the art are obtained under the premise of creative work is not made
The every other embodiment obtained, belongs to the scope of protection of the invention.
Embodiment 1
A kind of alcohol-soluble zinc-rich coating, is made up of following raw material according to parts by weight：
Alkyl silicic acids ester polymer：32 parts；
Zinc powder：41 parts；
Solvent：21 parts；
Auxiliary agent：2 parts；
Preferably, the alkyl silicic acids ester polymer.
Preferably, the zinc powder particle diameter is 400 mesh.
A kind of production method of alcohol-soluble zinc-rich coating, the production method of the alcohol-soluble zinc-rich coating include with
Lower step：
S1：Alkyl silicic acids ester polymer is stirred under normal pressure：32 parts；Zinc powder:41 parts；Solvent:21 parts；Auxiliary agent：2 parts；Stirring
30 minutes to 50 minutes；
S2：Packaging：S1 product is packed according to specification requirement.
Embodiment 2
A kind of alcohol-soluble zinc-rich coating, is made up of following raw material according to parts by weight：
Alkyl silicic acids ester polymer：33 parts；
Zinc powder：44 parts；
Solvent：25 parts；
Auxiliary agent：3 parts；
Preferably, the alkyl silicic acids ester polymer.
Preferably, the zinc powder particle diameter is 400 mesh.
A kind of production method of alcohol-soluble zinc-rich coating, the production method of the alcohol-soluble zinc-rich coating include with
Lower step：
S1：Stirred under normal pressure：Alkyl silicic acids ester polymer：33 parts；Zinc powder:44 parts；
Solvent:25 parts；Auxiliary agent：3 parts；Stir 30 minutes to 50 minutes；
S2：Packaging：S1 product is packed according to specification requirement.
Embodiment 3
A kind of alcohol-soluble zinc-rich coating, the formula of the alcohol-soluble zinc-rich coating is by including the groups of following parts by weight
Divide and be made：
Alkyl silicic acids ester polymer：40 parts；
Zinc powder：50 parts；
Solvent：30 parts；
Auxiliary agent：5 parts；
Preferably, the alkyl silicic acids ester polymer.
Preferably, the zinc powder particle diameter is 400 mesh.
A kind of production method of alcohol-soluble zinc-rich coating, the production method of the alcohol-soluble zinc-rich coating include with
Lower step：
S1：Stirred under normal pressure：Alkyl silicic acids ester polymer：40 parts；Zinc powder:50 parts；
Solvent：30 parts；Auxiliary agent：5 parts；Stir 30 minutes to 50 minutes；
S2：Packaging：S1 product is packed according to specification requirement.
Although an embodiment of the present invention has been shown and described, for the ordinary skill in the art, can be with
A variety of changes, modification can be carried out to these embodiments, replace without departing from the principles and spirit of the present invention by understanding
And modification, the scope of the present invention is defined by the appended.
Claims (6)
- A kind of 1. alcohol-soluble zinc-rich coating, it is characterised in that：It is made up of following raw material according to parts by weight：Alkyl silicic acids ester polymer：30-40 parts；Zinc powder：40-50 parts；Solvent：20-30 parts；Auxiliary agent：2-5 parts.
- A kind of 2. alcohol-soluble zinc-rich coating according to claim 1, it is characterised in that：By following raw material according to weight Part composition：Alkyl silicic acids ester polymer：30 parts；Zinc powder：40 parts；Solvent：20 parts；Auxiliary agent：2 parts.
- A kind of 3. alcohol-soluble zinc-rich coating according to claim 1, it is characterised in that：The alkyl silicic acids polyisocyanate polyaddition Thing.
- A kind of 4. alcohol-soluble zinc-rich coating according to claim 1, it is characterised in that：The zinc powder particle diameter is 400 Mesh.
- A kind of 5. alcohol-soluble zinc-rich coating according to claim 1, it is characterised in that：Auxiliary agent is anti-sag agent.
- A kind of 6. production method of alcohol-soluble zinc-rich coating as claimed in claim 1, it is characterised in that：The alcohol-soluble is inorganic The production method of zinc rich primer comprises the following steps：S1：Stirred under normal pressure：Alkyl silicic acids ester polymer：30 parts；Zinc powder：40 parts；Solvent：20 parts；Auxiliary agent：2 parts；Stir 30 Minute was by 50 minutes；S2：Packaging：S1 product is packed according to specification requirement.