CN107698218A - A kind of insulation leakproofing material - Google Patents
A kind of insulation leakproofing material Download PDFInfo
- Publication number
- CN107698218A CN107698218A CN201711112418.1A CN201711112418A CN107698218A CN 107698218 A CN107698218 A CN 107698218A CN 201711112418 A CN201711112418 A CN 201711112418A CN 107698218 A CN107698218 A CN 107698218A
- Authority
- CN
- China
- Prior art keywords
- parts
- insulation
- leakproofing material
- heat
- weight
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of insulation leakproofing material, it is made up of the component of following parts by weight:45 60 parts of portland cement;65 80 parts of diatomite;12 25 parts of heat stabilizer;25 35 parts of polyurethanes:10 20 parts of negative ion powder for building;21 33 parts of silicon ash;10 15 parts of high aluminum fiber;15 parts of modifying agent.The insulation leakproofing material of the present invention, using the main body framework of portland cement and diatomite as insulation leakproofing material, heat-barrier material can be made to possess preferable mechanical performance, such as shock-absorbing capacity, it is auxiliary in people's stabilizer as heat-insulated upgrade materials, heat insulating effect can be greatly enhanced, anion can persistently be discharged by negative ion powder for building.The material of the present invention integrates heat-proof quality and leak resistance, and anti-pressure ability is stronger, service life length, and resistance to elevated temperatures is splendid;With certain elongation percentage, crack resistance is strong, adhesive force is strong, can form one layer of waterproof layer in body surface, effectively avoid object from aoxidizing.
Description
Technical field
The present invention relates to technical field of buildings, more particularly to a kind of insulation leakproofing material.
Background technology
With continuing deeply for national propulsion energy-saving environmental protection, the implementation of Regulation of building energy-saving, future architecture energy-saving heat preserving material
Wide market development space be present in material.Now, global heat preserving and insulating material is just towards efficient, energy-conservation, thin layer, heat-insulated, waterproof
The outer integrated direction of shield is developed, and in Development of Novel heat preserving and insulating material and meets structural thermal insulation power-saving technology simultaneously, has more emphasized
Specific aim uses heat-insulation material, by standard criterion design and construction, makes great efforts to improve insulating efficiency and reduces cost.
Existing construction material, after used a period of time mostly inevitably occur heat insulating effect compared with
Difference, or even situations such as leak occur, especially skyscraper, once there is water leakage situation, it is very troublesome, or even influence whether
Resident family's relation of lower floor.
The content of the invention
The technical problems to be solved by the invention are to be directed to above-mentioned the deficiencies in the prior art, there is provided a kind of insulation leakproof
Material.
The technical scheme that the present invention solves above-mentioned technical problem is as follows:A kind of insulation leakproofing material, by following weight
The component of part is made:
The beneficial effects of the invention are as follows:The insulation leakproofing material of the present invention, made using portland cement and diatomite
For the main body framework of insulation leakproofing material, heat-barrier material can be made to possess preferable mechanical performance, such as shock-absorbing capacity, it is auxiliary
In people's stabilizer as heat-insulated upgrade materials, heat insulating effect can be greatly enhanced, meanwhile, pass through negative ion powder for building
Anion can persistently be discharged.The insulation leakproofing material of the present invention integrates heat-proof quality and leak resistance, anti-pressure ability
Stronger, service life is grown, and resistance to elevated temperatures is splendid;With certain elongation percentage, crack resistance is strong, adhesive force is strong, can be in object
Surface forms one layer of waterproof layer, effectively avoids object from aoxidizing.
On the basis of above-mentioned technical proposal, the present invention can also do following improvement:
Further:Described insulation leakproofing material, is made up of the component of following parts by weight:
Further:The modifying agent is the mixture of flakey aluminium flake and magnesia, and the flakey aluminium flake and oxidation
The weight ratio of magnesium is (1-3):(3-5).
Further:Described filler is the mixture of talcum powder, expanded perlite and tourmaline powder, and talcum powder, expansion are precious
The weight of Zhu Yan and tourmaline powder ratio is (1-5):(2-7):1.
Further:The negative ion powder for building is made up of following weight parts raw material:70 parts of tourmaline, neodymia 10-20
Part, terbium peroxide 10-20 parts.
Further:The particle diameter of the silicon ash is 50-90mm.
Further:The heat stabilizer is the mixture of zinc stearate, potassium stearate, zinc laurate and beta-diketon, and institute
The weight ratio for stating zinc stearate, potassium stearate, zinc laurate and beta-diketon is (1~1.5):(1~1.2):(0.7~0.9):(1
~1.1).
Further:The insulation leakproofing material also includes swelling perlite powder, and the weight of the swelling perlite powder
Amount part is 8-10 parts.
The above-mentioned further beneficial effect of scheme is:Using swelling perlite powder as filling palliative, can subtract significantly
The quality of light material, plays a part of filler and expansion.
Further:The insulation leakproofing material also includes adhesive aid, and the parts by weight of the adhesive aid are 5-9
Part.
The above-mentioned further beneficial effect of scheme is:Use adhesive aid can be with the structural strength of reinforcing material, especially
Strengthen the adhesive property on surface, raising waterproof effect can be beaten.
Further:The adhesive aid is any of magnesium phosphate, aluminum phosphate and aluminium borate.
Embodiment
The principles and features of the present invention are described below, and the given examples are served only to explain the present invention, is not intended to limit
Determine the scope of the present invention.
A kind of insulation leakproofing material, is made up of the component of following parts by weight:
The insulation leakproofing material of the present invention, using portland cement and diatomite as insulation leakproofing material
Main body framework, heat-barrier material can be made to possess preferable mechanical performance, such as shock-absorbing capacity, it is auxiliary to change in people's stabilizer as heat-insulated
Good material, heat insulating effect can be greatly enhanced, meanwhile, anion can persistently be discharged by negative ion powder for building.This
The insulation leakproofing material of invention integrates heat-proof quality and leak resistance, and anti-pressure ability is stronger, service life length, resistance to
High-temperature behavior is splendid;With certain elongation percentage, crack resistance is strong, adhesive force is strong, can form one layer of waterproof layer in body surface, have
Effect avoids object from aoxidizing.
Embodiment 1
A kind of insulation leakproofing material, is made up of the component of following parts by weight:
In the present embodiment, the weight of flakey aluminium flake and magnesia ratio is 2 in the modifying agent:5, it is sliding in the filler
The weight ratio of stone flour, expanded perlite and tourmaline powder is 3:4:1, the parts by weight of each raw material in the negative ion powder for building
For:70 parts of tourmaline, 15 parts of neodymia, 12 parts of terbium peroxide, the particle diameter of the silicon ash are 76mm, hard in the heat stabilizer
Resin acid zinc, potassium stearate, the weight ratio of zinc laurate and beta-diketon are 1.2:1.0:0.8:1.1.
It is in the present embodiment, 70 parts of tourmaline, 15 parts of neodymia, 12 parts of terbium peroxide is well mixed, crush, set system
The negative ion powder for building, then by portland cement, diatomite, polyurethanes, negative ion powder for building, silicon ash and
High aluminum fiber is uniformly mixed, and is eventually adding modifying agent, you can the insulation leakproofing material is made.
Embodiment 2
A kind of insulation leakproofing material, is made up of the component of following parts by weight:
In the present embodiment, the weight of flakey aluminium flake and magnesia ratio is 3 in the modifying agent:5, it is sliding in the filler
The weight ratio of stone flour, expanded perlite and tourmaline powder is 2:4:1, the parts by weight of each raw material in the negative ion powder for building
For:70 parts of tourmaline, 16 parts of neodymia, 14 parts of terbium peroxide, the particle diameter of the silicon ash are 68mm, hard in the heat stabilizer
Resin acid zinc, potassium stearate, the weight ratio of zinc laurate and beta-diketon are 1.4:1.1:0.7:1.0.
It is in the present embodiment, 70 parts of tourmaline, 16 parts of neodymia, 14 parts of terbium peroxide is well mixed, crush, set system
The negative ion powder for building, then by portland cement, diatomite, polyurethanes, negative ion powder for building, silicon ash and
High aluminum fiber is uniformly mixed, and is eventually adding modifying agent, you can the insulation leakproofing material is made.
Embodiment 3
A kind of insulation leakproofing material, is made up of the component of following parts by weight:
In the present embodiment, the weight of flakey aluminium flake and magnesia ratio is 2.5 in the modifying agent:4.5, the filler
The weight ratio of middle talcum powder, expanded perlite and tourmaline powder is 2.5:3.6:1, each raw material in the negative ion powder for building
Parts by weight are:70 parts of tourmaline, 13 parts of neodymia, 17 parts of terbium peroxide, the particle diameter of the silicon ash are 85mm, the thermostabilization
Zinc stearate in agent, potassium stearate, the weight ratio of zinc laurate and beta-diketon are 1.35:1.15:0.85:1.05.
It is in the present embodiment, 70 parts of tourmaline, 13 parts of neodymia, 17 parts of terbium peroxide is well mixed, crush, set system
The negative ion powder for building, then by portland cement, diatomite, polyurethanes, negative ion powder for building, silicon ash and
High aluminum fiber is uniformly mixed, and is eventually adding modifying agent, you can the insulation leakproofing material is made.
Embodiment 4
A kind of insulation leakproofing material, is made up of the component of following parts by weight:
In the present embodiment, the weight of flakey aluminium flake and magnesia ratio is 1.5 in the modifying agent:3.5, the filler
The weight ratio of middle talcum powder, expanded perlite and tourmaline powder is 2.25:4.25:1, each raw material in the negative ion powder for building
Parts by weight be:70 parts of tourmaline, 15 parts of neodymia, 15 parts of terbium peroxide, the particle diameter of the silicon ash is 62mm, and the heat is steady
The weight ratio for determining zinc stearate in agent, potassium stearate, zinc laurate and beta-diketon is 1.15:1.20:0.90:1.10.
It is in the present embodiment, 70 parts of tourmaline, 15 parts of neodymia, 15 parts of terbium peroxide is well mixed, crush, set system
The negative ion powder for building, then by portland cement, diatomite, polyurethanes, negative ion powder for building, silicon ash,
Swelling perlite powder and high aluminum fiber are uniformly mixed, and are eventually adding modifying agent, you can the insulation leakproof material is made
Material.
Embodiment 5
A kind of insulation leakproofing material, is made up of the component of following parts by weight:
In the present embodiment, the weight of flakey aluminium flake and magnesia ratio is 2.5 in the modifying agent:4.5, the filler
The weight ratio of middle talcum powder, expanded perlite and tourmaline powder is 3.45:5.65:1, each raw material in the negative ion powder for building
Parts by weight be:70 parts of tourmaline, 12 parts of neodymia, 18 parts of terbium peroxide, the particle diameter of the silicon ash is 85mm, and the heat is steady
The weight ratio for determining zinc stearate in agent, potassium stearate, zinc laurate and beta-diketon is 1.45:1.15:0.85:1.05.
It is in the present embodiment, 70 parts of tourmaline, 12 parts of neodymia, 18 parts of terbium peroxide is well mixed, crush, set system
The negative ion powder for building, then by portland cement, diatomite, polyurethanes, negative ion powder for building, silicon ash,
Swelling perlite powder and high aluminum fiber are uniformly mixed, and are eventually adding modifying agent and adhesive aid is uniformly mixed, you can
The insulation leakproofing material is made.
Heat conduction, insulation and waterproof test, test knot are carried out to the heat-insulation and heat-preservation leakproofing material according to made from above-described embodiment
Fruit such as table 1 below:
Table 1
Thermal conductivity factor (W 〃 m-1〃k-1) | Classification of waterproof | |
Embodiment 1 | 0.75 | IPX8 |
Embodiment 2 | 0.78 | IPX7 |
Embodiment 3 | 0.76 | IPX8 |
Embodiment 4 | 0.80 | IPX8 |
Embodiment 5 | 0.79 | IPX8 |
As can be seen here, the heat insulating effect of heat-insulation and heat-preservation leakproofing material of the invention is preferable, and leak preventing effect is splendid, effectively
Solve that heat insulation for building material heat insulation effect of the prior art is poor, technological deficiency of leak, suit large area to popularize use.
Uniformly spread out in addition, taking 1000 grams of heat preserving and insulating materials produced by the present invention to be placed in seal box, closed 24 hours,
Detected once every 1 hour with the AIC-1000 anionic textiles instrument that Alphalab companies of the U.S. produce, take 20 data every time,
The average value for trying to achieve each data is shown in Table 2 as final detection result, test data.
Anion-generating capacity (individual 〃 cm-3) | |
Embodiment 1 | 670 |
Embodiment 2 | 645 |
Embodiment 3 | 706 |
Embodiment 4 | 685 |
Embodiment 5 | 693 |
As can be seen here, heat-insulation and heat-preservation leakproofing material of the invention, anion can be persistently discharged, improves air quality, optimization
Environment, it is green.
The foregoing is only presently preferred embodiments of the present invention, be not intended to limit the invention, it is all the present invention spirit and
Within principle, any modification, equivalent substitution and improvements made etc., it should be included in the scope of the protection.
Claims (10)
1. a kind of insulation leakproofing material, it is characterised in that be made up of the component of following parts by weight:
2. insulation leakproofing material according to claim 1, it is characterised in that be made up of the component of following parts by weight:
3. insulation leakproofing material according to claim 1, it is characterised in that:The modifying agent be flakey aluminium flake and
The mixture of magnesia, and the weight ratio of the flakey aluminium flake and magnesia is (1-3):(3-5).
4. insulation leakproofing material according to claim 1, it is characterised in that:Described filler is talcum powder, expansion
The mixture of perlite and tourmaline powder, the weight ratio of talcum powder, expanded perlite and tourmaline powder is (1-5):(2-7):1.
5. insulation leakproofing material according to claim 1, it is characterised in that:The negative ion powder for building is by following
Raw material forms:70 parts of tourmaline, neodymia 10-20 parts, terbium peroxide 10-20 parts.
6. insulation leakproofing material according to claim 1, it is characterised in that:The particle diameter of the silicon ash is 50-90mm.
7. insulation leakproofing material according to claim 1, it is characterised in that:The heat stabilizer be zinc stearate,
The mixture of potassium stearate, zinc laurate and beta-diketon, and the zinc stearate, potassium stearate, zinc laurate and beta-diketon
Weight ratio is (1~1.5):(1~1.2):(0.7~0.9):(1~1.1).
8. the insulation leakproofing material according to any one of claim 1 to 7, it is characterised in that:Also include expanded pearlite
Rock dust, and the parts by weight of the swelling perlite powder are 8-10 parts.
9. the insulation leakproofing material according to any one of claim 1 to 7, it is characterised in that:Also include adhesive aid,
The parts by weight of the adhesive aid are 5-9 parts.
10. insulation leakproofing material according to claim 9, it is characterised in that:The adhesive aid be magnesium phosphate,
Any of aluminum phosphate and aluminium borate.