CN107695127A - A kind of production method of titanium tube - Google Patents
A kind of production method of titanium tube Download PDFInfo
- Publication number
- CN107695127A CN107695127A CN201710991041.5A CN201710991041A CN107695127A CN 107695127 A CN107695127 A CN 107695127A CN 201710991041 A CN201710991041 A CN 201710991041A CN 107695127 A CN107695127 A CN 107695127A
- Authority
- CN
- China
- Prior art keywords
- titanium
- titanium tube
- pipe
- production method
- annealing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of production method of titanium tube, specifically comprise the following steps:Step 1, it is raw material from TC4 titanium alloys;Step 2, TC4 titanium alloy raw materials are made by pipe using melting, forging and extruding;Step 3, pipe made of step 2 is rolled, drawing and annealing;Step 4, straightening processing is carried out to the titanium tube after step 3 processing.Titanium tube yield rate is higher made from this method.
Description
Technical field
The invention belongs to titanium and its alloy work technical field, is related to a kind of production method of titanium tube.
Background technology
Titanium or titanium alloy is a kind of important structural metal to grow up the 1950s, and titanium alloy is because having intensity
High, the features such as corrosion resistance is good, heat resistance is high, is widely used in every field, the production method of titanium tube is extruding, rolling, weldering
Connect-roll, although the application prospect of titanium alloy is preferable, current titanium alloy is easily broken in production and processing, causes pipe
Material yield rate is low.
The content of the invention
It is an object of the invention to provide a kind of production method of titanium tube, titanium tube yield rate is higher made from this method.
The technical solution adopted in the present invention is a kind of production method of titanium tube, to specifically comprise the following steps:
Step 1, it is raw material from TC4 titanium alloys;
Step 2, TC4 titanium alloy raw materials are made by pipe using melting, forging and extrusion process;
Step 3, pipe made of step 2 is rolled, drawing and annealing;
Step 4, straightening processing is carried out to the titanium tube after step 3 processing.
The features of the present invention also resides in,
Wherein pipe is preheated before step 3 is carried out, 200~300 DEG C of preheating temperature.
The passage wherein rolled in step 3 is 9~12 passages.
Annealing temperature is 350~400 DEG C wherein in step 3.
Wherein the operation of rolling is carried out in argon atmosphere in step 3.
The invention has the advantages that the present invention employs annealing when processing titanium tube, make crystal grain refinement, tissue
Arrangement is uniform, it is ensured that titanium tube has the performance of temperature, in addition, carried out in the operation of rolling in argon atmosphere, argon gas neither with gold
Category chemical reaction, is also not dissolved in metal, regardless of heat of desorption during high temperature.Titanium tube yield rate made from method provided by the invention compared with
It is high.
Embodiment
With reference to embodiment, the present invention is described in detail.
A kind of production method of titanium tube of the present invention, specifically comprises the following steps:
Step 1, it is raw material from TC4 titanium alloys;
Step 2, TC4 titanium alloy raw materials are made by pipe using melting, forging and extruding;
Step 3, pipe made of step 2 is rolled, drawing and annealing;
Pipe is preheated before step 3 is carried out, 200~300 DEG C of preheating temperature.
The passage wherein rolled in step 3 is 9~12 passages.
Annealing temperature is 350~400 DEG C wherein in step 3.
Wherein the operation of rolling is carried out in argon atmosphere in step 3.
Step 4, straightening processing is carried out to the titanium tube after step 3 processing.
Embodiment 1
It is raw material from TC4 titanium alloys;TC4 titanium alloy raw materials are made by pipe using melting, forging and extruding;To pipe
Preheated, 200 DEG C of preheating temperature, under the protection of argon gas, pipe is rolled, drawing and annealing;The road of rolling
Secondary is 9 passages;Annealing temperature is 350 DEG C, and straightening processing is carried out to the titanium tube after annealing.
Embodiment 2
It is raw material from TC4 titanium alloys;TC4 titanium alloy raw materials are made by pipe using melting, forging and extruding;To pipe
Preheated, 220 DEG C of preheating temperature, under the protection of argon gas, pipe is rolled, drawing and annealing;The road of rolling
Secondary is 10 passages;Annealing temperature is 360 DEG C, and straightening processing is carried out to the titanium tube after annealing.
Embodiment 3
It is raw material from TC4 titanium alloys;TC4 titanium alloy raw materials are made by pipe using melting, forging and extruding;To pipe
Preheated, 250 DEG C of preheating temperature, under the protection of argon gas, pipe is rolled, drawing and annealing;The road of rolling
Secondary is 10 passages;Annealing temperature is 380 DEG C, and straightening processing is carried out to the titanium tube after annealing.
Embodiment 4
It is raw material from TC4 titanium alloys;TC4 titanium alloy raw materials are made by pipe using melting, forging and extruding;To pipe
Preheated, 280 DEG C of preheating temperature, under the protection of argon gas, pipe is rolled, drawing and annealing;The road of rolling
Secondary is 12 passages;Annealing temperature is 400 DEG C, and straightening processing is carried out to the titanium tube after annealing.
Embodiment 5
It is raw material from TC4 titanium alloys;TC4 titanium alloy raw materials are made by pipe using melting, forging and extruding;To pipe
Preheated, 300 DEG C of preheating temperature, under the protection of argon gas, pipe is rolled, drawing and annealing;The road of rolling
Secondary is 12 passages;Annealing temperature is 400 DEG C, and straightening processing is carried out to the titanium tube after annealing.
Claims (5)
- A kind of 1. production method of titanium tube, it is characterised in that:Specifically comprise the following steps:Step 1, it is raw material from TC4 titanium alloys;Step 2, TC4 titanium alloy raw materials are made by pipe using melting, forging and extruding;Step 3, pipe made of step 2 is rolled, drawing and annealing;Step 4, straightening processing is carried out to the titanium tube after step 3 processing.
- A kind of 2. production method of titanium tube according to claim 1, it is characterised in that:To pipe before step 3 is carried out Preheated, 200~300 DEG C of preheating temperature.
- A kind of 3. production method of titanium tube according to claim 1, it is characterised in that:The passage rolled in the step 3 For 9~12 passages.
- A kind of 4. production method of titanium tube according to claim 1, it is characterised in that:Annealing temperature is in the step 3 350~400 DEG C.
- A kind of 5. production method of titanium tube according to claim 1, it is characterised in that:The operation of rolling exists in the step 3 Carried out in argon atmosphere.