CN107692396A - A kind of cack and its 3D printing method - Google Patents
A kind of cack and its 3D printing method Download PDFInfo
- Publication number
- CN107692396A CN107692396A CN201710935927.8A CN201710935927A CN107692396A CN 107692396 A CN107692396 A CN 107692396A CN 201710935927 A CN201710935927 A CN 201710935927A CN 107692396 A CN107692396 A CN 107692396A
- Authority
- CN
- China
- Prior art keywords
- vamp
- parts
- cack
- sole
- printing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of cack and its 3D printing method.The cack includes sole and vamp, the vamp includes forefoot portion and heel portion, and the heel portion is divided into symmetrical two pieces, and every piece of antetheca is connected as a single entity with forefoot portion, two pieces of rear wall region is superposed, and the fastener by being arranged on rear wall is closed together.The 3D printing method includes first establishing vamp and sole model, then prints inboard vamp, fixed thread gluing, printing outside vamp, the inboard sole of printing, securing footwear upper edge, printing lateral shoe bottom according to model, that is, the cack of the present invention is made.The cack of the present invention wear off conveniently, one-hand operation, usage time length, the 3D printing method that uses of the present invention, technique is simple, non junction, seamless, is integrally formed, obtained cack is comfortable and easy to wear, firm.
Description
Technical field
The invention belongs to the technical field of shoemaking, more particularly to a kind of cack and its 3D printing method.
Background technology
The bound feet of baby is sufficiently flexible, and most more fat, without heel, shoes especially easily fall.In order to prevent baby from rubbing
Small footwear, Chinese invention patent application CN1032126180A (publication date on June 5th, 2013) discloses a kind of cack, in the leg of a boot
Top edge is provided with cohesive cloth, the cohesive cloth and trousers sticks together so as to play fixation during use.Though its energy
Solve the technical problem that cack is not easy, but be easily damaged trousers, it is impossible to singlehanded wear shoes.Chinese invention patent
101600363B (publication date on December 21st, 2011) discloses a kind of cack with pivoting heel portion, and it includes sole
And inclined-plane, vamp are formed by forefoot portion and heel portion, after the pin of baby inserts forefoot portion, heel portion being capable of pivot
The position closed substantially is gone to, and the forefoot portion is fastened to by fixing device.The patent can effectively solve the problem that one hand is worn
The technical problem of footwear, but its sole will undergo bending repeatedly, and perishable, heel also easily falls in the process of walking, and comfort level is low.
The requirement that cack is not only worn off to comfort level and easily is higher, also requires higher to the aesthetics of shoes.It is existing
Cack, usually formed by the sewing of a variety of fabrics spliced togethers, ornamental pattern flower is pasted or be sewed with to vamp.Usually,
The pattern flower of stickup easily falls, and the pattern flower sewed easily leaves the tender bound feet of the protrusions such as the end of a thread injury baby, and whole
The processing of individual vamp and sole is, it is necessary to carry out the cutting of multiple fabrics, sewing etc., and complex procedures, shoe size is small, operating space
Narrow, manufacture difficulty is big, cost is high.
The content of the invention
The present invention is intended to provide a kind of attractive in appearance, comfortable, cack for easily wearing off, while provide that a kind of process is simple, makes
The 3D printing method of convenient cack, to solve the problems, such as to propose in background technology.
In order to solve the above problems, present invention employs following technical scheme:
A kind of cack, including sole and vamp, the vamp include forefoot portion and heel portion, the heel portion
It is divided into symmetrical two pieces, every piece of antetheca is connected as a single entity with forefoot portion, and two pieces of rear wall region is superposed, and passes through setting
It is closed together in the fastener of rear wall.
As the improved technical scheme of the present invention, the fastener is thread gluing.
A kind of 3D printing method of cack, comprises the following steps:(1) three-dimensional software design vamp and sole mould are utilized
The heel portion of type, wherein vamp is divided into two pieces, and every piece of antetheca is connected as a single entity with forefoot portion, and two pieces of rear wall region is in footwear
Heel part is superposed when closing, and overlay area is provided with fastening area;(2) nexine vamp is printed;(3) thread gluing is fixed
To fastening area;(4) outer layer vamp is printed so that outer layer vamp covers the fringe region of thread gluing;(5) nexine sole is printed;
(6) shoe upper edge is fixed to nexine sole edge region;(7) outer shoe is printed.
As the improved technical scheme of the present invention, step (2)-(4) can use two printers same with step (5)
Shi Jinhang;Or step (5) is first carried out, then step (2)-(4) are carried out, finally carry out step (6)-(7);Or sequentially carry out step
(1)-(7)
As the improved technical scheme of the present invention, the nexine vamp and nexine sole are printed upon soft moisture-wicking textile table
Face.
As the improved technical scheme of the present invention, when printing outer layer vamp, in vamp printout surface three-dimensional pattern.
It is anti-skidding in sole surface printing 3 D stereo when printing outer shoe as the improved technical scheme of the present invention
Strangle bar or 3 D stereo non-slip patterns.
As the improved technical scheme of the present invention, the printed material that vamp and the nexine sole uses is mainly by PLA
50~67 parts, 20~38 parts of bamboo fibre, 3~5.6 parts of glycidyl trimethylammonium chloride, β-TiO20.1~3 part, aromatic series resists
0.1~2 part of oxidant, 0.1~2 part of acid amides class lubricating oil, 0.1~1 part of Nano Silver, 0.1~3 part of silane coupler, pigment 0~
4 parts of compositions.Further, the printed material that vamp and the nexine sole uses is mainly by 56~64 parts of PLA, bamboo fibre
25~35 parts, 3.7~5.2 parts of glycidyl trimethylammonium chloride, β-TiO21~2.5 part, aromatic series antioxidant 0.5~1.5
0~2 part of part, 0.5~1.5 part of acid amides class lubricating oil, 0.3~0.8 part of Nano Silver, 0.5~2 part of silane coupler, pigment composition.
Preferably, the printed material that vamp and the nexine sole uses is mainly by 60 parts of PLA, 28 parts of bamboo fibre, glycidol three
4.5 parts of ammonio methacrylate, β-TiO22 parts, 1 part of aromatic series antioxidant, 1 part of acid amides class lubricating oil, 0.5 part of Nano Silver, silane
2 parts of 1 part of coupling agent, pigment compositions.
As the improved technical scheme of the present invention, the printed material that the outer shoe uses is mainly by PLA 50~67
Part, 15~28 parts of bamboo fibre, 5~10 parts of carbon fiber, 3~5.6 parts of glycidyl trimethylammonium chloride, β-TiO20.1~3 part,
0.1~2 part of aromatic series antioxidant, 0.1~2 part of acid amides class lubricating oil, 0.1~1 part of Nano Silver, silane coupler 0.1~3
0~4 part of part, pigment composition.Further, the printed material that vamp and the nexine sole uses is mainly by PLA 56~64
Part, 19~26 parts of bamboo fibre, 6~9 parts of carbon fiber, 3.7~5.2 parts of glycidyl trimethylammonium chloride, β-TiO21~2.5
It is part, 0.5~1.5 part of aromatic series antioxidant, 0.5~1.5 part of acid amides class lubricating oil, 0.3~0.8 part of Nano Silver, silane coupled
0~2 part of 0.5~2 part of agent, pigment composition.Preferably, the printed material that vamp and the nexine sole uses is mainly by PLA
60 parts, 20.5 parts of bamboo fibre, 7.5 parts of carbon fiber, 4.5 parts of glycidyl trimethylammonium chloride, β-TiO22 parts, aromatic series antioxygen
2 parts of 1 part of agent, 1 part of acid amides class lubricating oil, 0.5 part of Nano Silver, 1 part of silane coupler, pigment compositions.
As further improved technical scheme of the present invention, the thickness of vamp and the nexine sole is 0.5~3mm, institute
The thickness for stating outer shoe is 1.5~10mm.
Beneficial effect:
Baby's heel of a shoe of the present invention can be opened, and facilitate wearing off for baby, one-hand operation.In addition, the cack may be used also
To adjust the size of overlay area according to the size of infant's foot, so that when the cack of the present invention possesses more long use
Between.The 3D printing method that the present invention uses, is integrally formed cack, and each several part is seamlessly connected, and no the end of a thread will not hinder without projection
The tender both feet of evil baby.The present invention additionally uses the 3D printing material of uniqueness, and it has the function such as absorbing sweat, antibacterial, ventilative, will
Within the specific limits, material possesses good flexibility and hardness to its thickness limit.The 3D printing material that vamp uses with inner side sole
Material, it is flexible, gas permeability is strong;The 3D printing material that lateral shoe bottom uses, flexible and hardness is moderate, wearability is good.
Brief description of the drawings
Fig. 1 is the schematic diagram of the vamp sole of cack of the present invention;
Fig. 2 is the cack structural representation of the present invention;
Embodiment
In order that it will be apparent to those skilled in that legibly understand the present invention, it is right in conjunction with the drawings and specific embodiments
The present invention is described in detail.
As shown in Figure 1-2, cack of the invention includes sole 1 and vamp 2, and the vamp includes forefoot portion and heel
Part, the heel portion are divided into symmetrical two pieces (22,23), and every piece of antetheca is connected as a single entity with forefoot portion, after two pieces
Wall region is superposed, and the fastener 25 by being arranged on rear wall is closed together.The fastener 25 is preferably viscous
Button.For the cack of the present invention compared with existing shoes, its main distinction is that the heel portion of vamp 2 is stacked by thread gluing
Together, it can be opened and closed, therefore very convenient when worn off to baby, can be with one-handed performance.When infant's foot compared with
Hour, overlay area can be increased, so that shoes are close to the heel of baby;After infant's foot is grown up, it can reduce stacked
Region, so as to expand the capacity of shoes.It possesses with baby development and the function of dilatation, and usage time interval is longer, practicality
It is stronger.
In order that cack is more firm, dress is more comfortable, the present invention additionally uses new technique --- 3D printing method is come
Make cack.The 3D printing method mainly includes following seven steps:(1) three-dimensional software design vamp 2 and the mould of sole 1 are utilized
Type, the heel portion of wherein vamp 2 are divided into two pieces (22,23), and every piece of antetheca is connected as a single entity with forefoot portion, two pieces of rear wall
Region is superposed when heel portion closes, and overlay area is provided with fastening area;(2) nexine vamp is printed;(3) will
Thread gluing is fixed to fastening area;(4) outer layer vamp is printed so that outer layer vamp covers the fringe region of thread gluing;(5) in printing
Layer sole;(6) shoe upper edge 21 is fixed to the region of nexine sole edge 11;(7) outer shoe is printed.Wherein, step (2)-
(4) operation order with step (5) can be changed, and can also carry out simultaneously.According to client's needs, when printing outer layer vamp,
In the printout surface three-dimensional pattern of vamp 2;When printing outer shoe, the anti-skidding Le bar of 3 D stereo is printed in sole surface 1
Or 3 D stereo non-slip patterns.Preferably, the nexine vamp and nexine sole are printed upon soft moisture-wicking textile surface, baby's
Foot is in contact with soft moisture-wicking textile, and dress is more comfortable.
According to the difference of vamp 2 and sole 1 to material pliability and hardness, present invention also offers a kind of brand-new baby
Footwear printed material.Wherein, nexine vamp, outer layer vamp and nexine sole are mainly made of following material:PLA 50~
67 parts, 20~38 parts of bamboo fibre, 3~5.6 parts of glycidyl trimethylammonium chloride, β-TiO20.1~3 part, aromatic series it is anti-oxidant
0.1~2 part of agent, 0.1~2 part of acid amides class lubricating oil, 0.1~1 part of Nano Silver, 0.1~3 part of silane coupler, 0~4 part of pigment.
Its pliability is good, gas permeability is high, and foot is contacted more comfortably, also with antibacterial function.The outer shoe utilizes carbon
Fiber substituted for part bamboo fibre, and its gas permeability reduces, the comfort level reduction with skin contact, but its wearability and hardness are purer
Bamboo fibre is high.In the present invention, outer shoe is mainly using 50~67 parts of PLA, 15~28 parts of bamboo fibre, carbon fiber 5~10
Part, 3~5.6 parts of glycidyl trimethylammonium chloride, β-TiO20.1~3 part, 0.1~2 part of aromatic series antioxidant, amide-type
0~4 part of 0.1~2 part of lubricating oil, 0.1~1 part of Nano Silver, 0.1~3 part of silane coupler, pigment printing form.In order that footwear
The flexibility and hardness of face and sole meet baby's needs comfortable and easy to wear, and the thickness of vamp and nexine sole is preferably defined 0.5
~3mm, the thickness of outer shoe are preferably defined in 1.5~10mm.
Embodiment 1
Weigh in proportion:50 parts of PLA, 38 parts of bamboo fibre, 5.6 parts of glycidyl trimethylammonium chloride, β-TiO20.1
Part, 0.1 part of aromatic series antioxidant, 2 parts of acid amides class lubricating oil, 0.1 part of Nano Silver, 0.1 part of silane coupler, 4 parts of pigment, mix
Close it is uniform, then add in double screw extruder carry out melt blending, extrusion, tie rod, cooling and and dry, obtain bamboo fibre
Modified particles of polylactic acid.Drum winding after particles of polylactic acid is added to wire drawing in single screw extrusion machine, water cooling, air-dried, is obtained
To a diameter of 0.5~3mm 3D printing wire rod.Print parameters are set:Printing head temperature is 200 DEG C, and print platform temperature is
40~60 DEG C, nozzle printing speed is 60mm/s, and it is 90mm/s that shower nozzle sky, which walks speed, designs vamp model according to three-dimensional software and beats
Nexine vamp, outer layer vamp and nexine sole are printed, nexine vamp, outer layer vamp and nexine sole thickness are 1.5mm.
Weigh in proportion:50 parts of PLA, 28 parts of bamboo fibre, 10 parts of carbon fiber, 5.6 parts of glycidyl trimethylammonium chloride,
β-TiO20.1 part, 0.1 part of aromatic series antioxidant, 2 parts of acid amides class lubricating oil, 0.1 part of Nano Silver, 0.1 part of silane coupler,
4 parts of pigment, be well mixed, then add double screw extruder in carry out melt blending, extrusion, tie rod, cooling and and dry,
Obtain the particles of polylactic acid of bamboo fibre modification.By particles of polylactic acid be added to wire drawing in single screw extrusion machine, water cooling, air-dry after around
Disk is wound, and obtains a diameter of 0.5~3mm 3D printing wire rod.Print parameters are set:Printing head temperature is 200 DEG C, and printing is flat
Platform temperature is 40~60 DEG C, and nozzle printing speed is 60mm/s, and it is 90mm/s that shower nozzle sky, which walks speed, and footwear are designed according to three-dimensional software
Surface model prints outer shoe, and outer shoe thickness is 5mm.
Embodiment 2
Weigh in proportion:56 parts of PLA, 35 parts of bamboo fibre, 5.2 parts of glycidyl trimethylammonium chloride, β-TiO21 part,
0.5 part of aromatic series antioxidant, 1.5 parts of acid amides class lubricating oil, 0.3 part of Nano Silver, 0.5 part of silane coupler, 0 part of pigment, mix
Close it is uniform, then add in double screw extruder carry out melt blending, extrusion, tie rod, cooling and and dry, obtain bamboo fibre
Modified particles of polylactic acid.Drum winding after particles of polylactic acid is added to wire drawing in single screw extrusion machine, water cooling, air-dried, is obtained
To a diameter of 0.5~3mm 3D printing wire rod.Print parameters are set:Printing head temperature is 200 DEG C, and print platform temperature is
40~60 DEG C, nozzle printing speed is 60mm/s, and it is 90mm/s that shower nozzle sky, which walks speed, designs vamp model according to three-dimensional software and beats
Nexine vamp, outer layer vamp and nexine sole are printed, nexine vamp, outer layer vamp and nexine sole thickness are 0.5mm.
Weigh in proportion:56 parts of PLA, 26 parts of bamboo fibre, 9 parts of carbon fiber, 5.2 parts of glycidyl trimethylammonium chloride,
β-TiO21 part, 0.5 part of aromatic series antioxidant, 1.5 parts of acid amides class lubricating oil, 0.3 part of Nano Silver, 0.5 part of silane coupler,
It is well mixed, then add in double screw extruder carry out melt blending, extrusion, tie rod, cooling and and dry, obtain bamboo fibre
Tie up modified particles of polylactic acid.Drum winding after particles of polylactic acid is added to wire drawing in single screw extrusion machine, water cooling, air-dried,
Obtain a diameter of 0.5~3mm 3D printing wire rod.Print parameters are set:Printing head temperature is 200 DEG C, print platform temperature
For 40~60 DEG C, nozzle printing speed is 60mm/s, and it is 90mm/s that shower nozzle sky, which walks speed, and vamp model is designed according to three-dimensional software
Outer shoe is printed, outer shoe thickness is 1.5mm.
Embodiment 3
Weigh in proportion:60 parts of PLA, 28 parts of bamboo fibre, 4.5 parts of glycidyl trimethylammonium chloride, β-TiO22 parts,
1 part of aromatic series antioxidant, 1 part of acid amides class lubricating oil, 0.5 part of Nano Silver, 1 part of silane coupler, 2 parts of pigment, it is well mixed,
Then add in double screw extruder carry out melt blending, extrusion, tie rod, cooling and and dry, obtain the poly- of bamboo fibre modification
Lactic acid particles.Drum winding after particles of polylactic acid is added to wire drawing in single screw extrusion machine, water cooling, air-dried, is obtained a diameter of
0.5~3mm 3D printing wire rod.Print parameters are set:Printing head temperature is 200 DEG C, and print platform temperature is 40~60 DEG C,
Nozzle printing speed is 60mm/s, and it is 90mm/s that shower nozzle sky, which walks speed, and vamp model printing nexine footwear are designed according to three-dimensional software
Face, outer layer vamp and nexine sole, nexine vamp, outer layer vamp and nexine sole thickness are 1.5mm.
Weigh in proportion:56 parts of PLA, 26 parts of bamboo fibre, 9 parts of carbon fiber, 5.2 parts of glycidyl trimethylammonium chloride,
β-TiO21 part, 0.5 part of aromatic series antioxidant, 1.5 parts of acid amides class lubricating oil, 0.3 part of Nano Silver, 0.5 part of silane coupler,
0 part of pigment, be well mixed, then add double screw extruder in carry out melt blending, extrusion, tie rod, cooling and and dry,
Obtain the particles of polylactic acid of bamboo fibre modification.By particles of polylactic acid be added to wire drawing in single screw extrusion machine, water cooling, air-dry after around
Disk is wound, and obtains a diameter of 0.5~3mm 3D printing wire rod.Print parameters are set:Printing head temperature is 200 DEG C, and printing is flat
Platform temperature is 40~60 DEG C, and nozzle printing speed is 60mm/s, and it is 90mm/s that shower nozzle sky, which walks speed, and footwear are designed according to three-dimensional software
Surface model prints outer shoe, and outer shoe thickness is 5mm.
Embodiment 4
Weigh in proportion:64 parts of PLA, 25 parts of bamboo fibre, 3.7 parts of glycidyl trimethylammonium chloride, β-TiO22.5
Part, 1.5 parts of aromatic series antioxidant, 0.5 part of acid amides class lubricating oil, 0.8 part of Nano Silver, 2 parts of silane coupler, it is well mixed,
Then add in double screw extruder carry out melt blending, extrusion, tie rod, cooling and and dry, obtain the poly- of bamboo fibre modification
Lactic acid particles.Drum winding after particles of polylactic acid is added to wire drawing in single screw extrusion machine, water cooling, air-dried, is obtained a diameter of
0.5~3mm 3D printing wire rod.Print parameters are set:Printing head temperature is 200 DEG C, and print platform temperature is 40~60 DEG C,
Nozzle printing speed is 60mm/s, and it is 90mm/s that shower nozzle sky, which walks speed, and vamp model printing nexine footwear are designed according to three-dimensional software
Face, outer layer vamp and nexine sole, nexine vamp, outer layer vamp and nexine sole thickness are 3mm.
Weigh in proportion:56 parts of PLA, 26 parts of bamboo fibre, 9 parts of carbon fiber, 5.2 parts of glycidyl trimethylammonium chloride,
β-TiO21 part, 0.5 part of aromatic series antioxidant, 1.5 parts of acid amides class lubricating oil, 0.3 part of Nano Silver, 0.5 part of silane coupler,
0 part of pigment, be well mixed, then add double screw extruder in carry out melt blending, extrusion, tie rod, cooling and and dry,
Obtain the particles of polylactic acid of bamboo fibre modification.By particles of polylactic acid be added to wire drawing in single screw extrusion machine, water cooling, air-dry after around
Disk is wound, and obtains a diameter of 0.5~3mm 3D printing wire rod.Print parameters are set:Printing head temperature is 200 DEG C, and printing is flat
Platform temperature is 40~60 DEG C, and nozzle printing speed is 60mm/s, and it is 90mm/s that shower nozzle sky, which walks speed, and footwear are designed according to three-dimensional software
Surface model prints outer shoe, and outer shoe thickness is 10mm.
Embodiment 5
Weigh in proportion:67 parts of PLA, 20 parts of bamboo fibre, 3 parts of glycidyl trimethylammonium chloride, β-TiO23 parts, virtue
Fragrant 2 parts of race's antioxidant, 0.1 part of acid amides class lubricating oil, 1 part of Nano Silver, 3 parts of silane coupler, 0.9 part of pigment, it is well mixed,
Then add in double screw extruder carry out melt blending, extrusion, tie rod, cooling and and dry, obtain the poly- of bamboo fibre modification
Lactic acid particles.Drum winding after particles of polylactic acid is added to wire drawing in single screw extrusion machine, water cooling, air-dried, is obtained a diameter of
0.5~3mm 3D printing wire rod.Print parameters are set:Printing head temperature is 200 DEG C, and print platform temperature is 40~60 DEG C,
Nozzle printing speed is 60mm/s, and it is 90mm/s that shower nozzle sky, which walks speed, and vamp model printing nexine footwear are designed according to three-dimensional software
Face, outer layer vamp and nexine sole, nexine vamp, outer layer vamp and nexine sole thickness are 1.5mm.
Weigh in proportion:56 parts of PLA, 26 parts of bamboo fibre, 9 parts of carbon fiber, 5.2 parts of glycidyl trimethylammonium chloride,
β-TiO21 part, 0.5 part of aromatic series antioxidant, 1.5 parts of acid amides class lubricating oil, 0.3 part of Nano Silver, 0.5 part of silane coupler,
0 part of pigment, be well mixed, then add double screw extruder in carry out melt blending, extrusion, tie rod, cooling and and dry,
Obtain the particles of polylactic acid of bamboo fibre modification.By particles of polylactic acid be added to wire drawing in single screw extrusion machine, water cooling, air-dry after around
Disk is wound, and obtains a diameter of 0.5~3mm 3D printing wire rod.Print parameters are set:Printing head temperature is 200 DEG C, and printing is flat
Platform temperature is 40~60 DEG C, and nozzle printing speed is 60mm/s, and it is 90mm/s that shower nozzle sky, which walks speed, and footwear are designed according to three-dimensional software
Surface model prints outer shoe, and outer shoe thickness is 5mm.
The pigment used in embodiment 1-5 can be organic pigment, or inorganic pigment.Use in the present invention
Pigment is phthalocyanine color.
Nexine vamp, top layer vamp, nexine sole and outer shoe test result as shown in Table 1 and Table 2
The nexine vamp of table 1, top layer vamp, the test result of nexine sole
The test result of the outer shoe of table 2
The announcement and teaching of book according to the above description, those skilled in the art in the invention can also be to above-mentioned embodiment party
Formula carries out appropriate change and modification.Therefore, the invention is not limited in embodiment disclosed and described above, to this
Some modifications and changes of invention should also be as falling into the scope of the claims of the present invention.In addition, although this specification
In used some specific terms, but these terms are merely for convenience of description, do not form any restrictions to the present invention.
Claims (10)
1. a kind of cack, including sole and vamp, the vamp includes forefoot portion and heel portion, it is characterised in that:Institute
To state heel portion and be divided into symmetrical two pieces, every piece of antetheca is connected as a single entity with forefoot portion, and two pieces of rear wall region is superposed,
And the fastener by being arranged on rear wall is closed together.
2. cack according to claim 1, it is characterised in that:The fastener is thread gluing.
3. a kind of 3D printing method of cack, comprises the following steps:(1) vamp and sole model are designed using three-dimensional software,
The heel portion of wherein vamp is divided into two pieces, and every piece of antetheca is connected as a single entity with forefoot portion, and two pieces of rear wall region is in heel
Part is superposed when closing, and overlay area is provided with fastening area;(2) nexine vamp is printed;(3) thread gluing is fixed to
Fastening area;(4) outer layer vamp is printed so that outer layer vamp covers the fringe region of thread gluing;(5) nexine sole is printed;(6)
Shoe upper edge is fixed to nexine sole edge region;(7) outer shoe is printed.
4. the 3D printing method of cack according to claim 3, it is characterised in that:Step (2)-(4) can with step (5)
To be carried out using two printers simultaneously;Or first carry out step (5), then carry out step (2)-(4), finally carry out step (6)-
(7);Or sequentially carry out step (1)-(7).
5. the 3D printing method of cack according to claim 3, it is characterised in that:The nexine vamp and nexine sole
It is printed upon soft moisture-wicking textile surface.
6. the 3D printing method of cack according to claim 3, it is characterised in that:When printing outer layer vamp, in footwear
Face printout surface three-dimensional pattern.
7. the 3D printing method of cack according to claim 3, it is characterised in that:When printing outer shoe, in footwear
Basal surface printing 3 D stereo is anti-skidding to strangle bar or 3 D stereo non-slip patterns.
8. the 3D printing method of cack according to claim 3, it is characterised in that:Vamp and the nexine sole uses
Printed material mainly by 50~67 parts of PLA, 20~38 parts of bamboo fibre, 3~5.6 parts of glycidyl trimethylammonium chloride, β-
TiO20.1~3 part, 0.1~2 part of aromatic series antioxidant, 0.1~2 part of acid amides class lubricating oil, 0.1~1 part of Nano Silver, silane
0~4 part of 0.1~3 part of coupling agent, pigment composition.
9. the 3D printing method of cack according to claim 3, it is characterised in that:The printing that the outer shoe uses
Material mainly by 50~67 parts of PLA, 15~28 parts of bamboo fibre, 5~10 parts of carbon fiber, glycidyl trimethylammonium chloride 3~
5.6 parts, β-TiO20.1~3 part, 0.1~2 part of aromatic series antioxidant, 0.1~2 part of acid amides class lubricating oil, Nano Silver 0.1~1
0~4 part of part, 0.1~3 part of silane coupler, pigment composition.
10. the 3D printing method of cack according to claim 8 or claim 9, it is characterised in that:Vamp and the nexine sole
Thickness be 0.5~3mm, the thickness of the outer shoe is 1.5~10mm.