CN107675334A - Utilize the method for viscose staple fibre and the viscose filament yarn production cellular cloth of 3 D stereo - Google Patents
Utilize the method for viscose staple fibre and the viscose filament yarn production cellular cloth of 3 D stereo Download PDFInfo
- Publication number
- CN107675334A CN107675334A CN201710773654.1A CN201710773654A CN107675334A CN 107675334 A CN107675334 A CN 107675334A CN 201710773654 A CN201710773654 A CN 201710773654A CN 107675334 A CN107675334 A CN 107675334A
- Authority
- CN
- China
- Prior art keywords
- viscose
- cloth
- filament yarn
- staple fibre
- stereo
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The method that the present invention relates to the use of viscose staple fibre and the viscose filament yarn production cellular cloth of 3 D stereo, belongs to Strand Feeding Technique field, including warping, four big step of weaving, dyeing and finishing and finished product.The present invention selects viscose rayon first, and two kinds of different viscose rayons are combined, different beneficial to its shrinkage, cloth of the production with stronger cleaning capacity.The washing shrinkage of viscose staple fibre is 15%, and the washing shrinkage for having the flat viscose filament yarn of light is 2%, and the difference of the shrinkage after water is entered by two kinds of fibers, reaches 3 D stereo honeycomb type structure, and then the purpose of strength cleaning.Moistening cleaning tissue produced by the invention is than traditional fibre cloth moistening cleaning tissue, and the stronger cleaning effect of detergency is more preferably；Compared with steel wire lump, to vessel without scuffing, do not fall bits.Bath towel produced by the invention is more stronger than cleaning force with traditional towel, and self-cleaning power is stronger；Compared with traditional bathing towel without pain, it is easy to foaming, be more suitable for shower clean skin.
Description
Technical field
The invention belongs to Strand Feeding Technique field, especially relates to one kind using viscose staple fibre and viscose filament yarn production three
The method of the three-dimensional cellular cloth of dimension.
Background technology
Traditional handicraft manufactures walf checks mainly only with a kind of material, and more using cotton and the preferable yarn of ultra-fine equal strength as
Main, materials limitation is big, and the cloth produced is mostly plane-shaped structure, and cleaning force is poor.Three-dimensional cleaning supplies such as steel wire
Ball, cleaning force is big, but scuffing can be produced on vessel, and easily falls bits.
During traditional bathing, body top layer dirt typically is removed with wash towel, but because traditional bathing cloth weave patterns are thick
It is rough, extremely strong easily injury skin of keenly feeling；After dirt removal, general to smear body lotion using tradition bath flower, tradition bath flower is plastics system
Product, easy to aging, non-natural.The bathing mode that this two step is walked, it is lot more time to have the epoch of a bath in past people, also
There is certain applicability.But the enhancing with personal hygiene consciousness, bathing have changed into the improvement of people ' s living standards
Allegro daily cleaning.Therefore needed badly among prior art and want a kind of new technical scheme, be on the one hand by two steps conjunction two
One improves efficiency, on the one hand improves performance, improves bathing experience sense.
The content of the invention
The technical problems to be solved by the invention are：There is provided a kind of three-dimensional vertical using viscose staple fibre and viscose filament yarn production
The method of the cellular cloth of body, for solving a kind of traditional handicraft manufacture walf checks mainly big, the work(only with material materials limitation
Energy property is poor, and feature is few, use range limitation；Traditional bathing cloth has been no longer suitable for now allegro daily bathing cleaning etc.
Technical problem.
Using viscose staple fibre and viscose filament yarn production the cellular cloth of 3 D stereo method, comprise the following steps and with
Lower step is sequentially carried out,
Step 1: warping
Viscose staple fibre is chosen as warp thread, has light abnormal shape viscose filament yarn as weft yarn, it is described to have light abnormal shape viscose filament yarn
Cross section be pancake structure；
Step 2: weaving
Warp thread in step 1 and weft yarn are made into light and dark starlike cloth using rapier loom；
Step 3: dyeing and finishing
The cloth obtained in step 2 is subjected to dyeing and finishing, forms concavo-convex honeycomb cloth；
Step 4: finished product
The honeycomb cloth of step 3 is sheared, sew, is packaged into finished product.
Viscose staple fibre in the step 1 is the viscose staple fibre of 20 bifilar 18 twists.
Light abnormal shape viscose filament yarn in the step 1 has the flat viscose filament yarn of light for 333.3dtex/30f, and flatness is
5mm compares 1mm.
In the step 2 warp thread through it is close be 56/it is right；The filling density of weft yarn be 43/it is right.
Rapier loom uses 8 heald frames, No. 25 steel buttons, 28 plumages in the step 2.
By above-mentioned design, the present invention can bring following beneficial effect：
The present invention selects viscose rayon first, and two kinds of different viscose rayons are combined, different beneficial to its shrinkage, raw
Cloth of the production with stronger cleaning capacity.The washing shrinkage of viscose staple fibre is 15%, and the washing shrinkage for having the flat viscose filament yarn of light is
2%, the difference of the shrinkage after water is entered by two kinds of fibers, reaches 3 D stereo honeycomb type structure, and then the mesh of strength cleaning
's.Can also be as the bath towel of personal bathing as household cleaning towel by the use of cloth produced by the invention.
In terms of household cleaning, moistening cleaning tissue produced by the invention is than traditional fibre cloth moistening cleaning tissue, the stronger cleaning effect of detergency
More preferably；Compared with steel wire lump, to vessel without scuffing, do not fall bits.
In terms of personal bathing, bath towel produced by the invention is more stronger than cleaning force with traditional towel, and self-cleaning power is stronger；With biography
Unite bathing towel compare without pain, it is easy to foaming, be more suitable for shower clean skin.
Brief description of the drawings
Below in conjunction with the drawings and specific embodiments, the present invention is further illustrated：
Fig. 1 is to utilize the structural representation before the cellular cloth water suction of 3 D stereo produced by the invention.
Fig. 2 is to utilize the state diagram after the cellular cloth water suction of 3 D stereo produced by the invention.
1- warp thread, 2- weft yarns in figure.
Embodiment
As illustrated, from 20 bifilar 18 twists viscose staple fibre yarn as warp thread 1, warp thread 1 is unglazed；From
333.3dtex/30f has the flat viscose filament yarn of light to have light as weft yarn 2, weft yarn 2.
Rapier loom uses 5 heald frames, the light and dark starlike cloth that No. 25 steel buttons are made into, bright (latitude is produced on a cloth
Point) the dark starlike characteristic alternate (through point).In weaving the density of warp thread be 56/it is right；The density of weft yarn is 43/right, heald frame
Quantity is 8, and its institutional framework is as follows：
The cloth woven passes through dyeing and finishing, is cut according to different purposes, sews, is packaged into finished product.
Warp thread 1 is no twisting filament to have sth. made by twisting glue yarn and weft yarn 2, and the two washing shrinkage is widely different so that cloth enters group after water
Knit structure to change, i.e., be changed into concavo-convex alternately honeycomb from starlike between light and shade.Warp thread 1 is that string has again with weft yarn 2
Viscose water-oil separating characteristic so that cloth has significant grease resistance, oily dirt free.Weft yarn 2 is super soft, super because its is flat abnormally-structured
Water suction make it that cloth water imbibition is high.
Utilize cloth suitable for making cleaning cloth produced by the invention and bath towel.Cleaning cloth includes kitchen towel, a dishcloth, clearly
Clean cloth, moistening cleaning tissue；Bath towel includes wash towel, wash gloves, facial tissue, beautification glove etc..
Claims (5)
1. using the method for viscose staple fibre and the viscose filament yarn production cellular cloth of 3 D stereo, it is characterized in that：Including following step
Rapid and following steps are sequentially carried out,
Step 1: warping
Viscose staple fibre is chosen as warp thread, has light abnormal shape viscose filament yarn as weft yarn, the horizontal stroke for having light abnormal shape viscose filament yarn
Section is pancake structure；
Step 2: weaving
Warp thread in step 1 and weft yarn are made into light and dark starlike cloth using rapier loom；
Step 3: dyeing and finishing
The cloth obtained in step 2 is subjected to dyeing and finishing, forms concavo-convex honeycomb cloth；
Step 4: finished product
The honeycomb cloth of step 3 is sheared, sew, is packaged into finished product.
2. the method according to claim 1 for producing the cellular cloth of 3 D stereo using viscose staple fibre and viscose filament yarn,
It is characterized in that：Viscose staple fibre in the step 1 is the viscose staple fibre of 20 bifilar 18 twists.
3. the method according to claim 1 for producing the cellular cloth of 3 D stereo using viscose staple fibre and viscose filament yarn,
It is characterized in that：Light abnormal shape viscose filament yarn in the step 1 has the flat viscose filament yarn of light for 333.3dtex/30f, and flatness is
5mm compares 1mm.
4. the method according to claim 1 for producing the cellular cloth of 3 D stereo using viscose staple fibre and viscose filament yarn,
It is characterized in that：In the step 2 warp thread through it is close be 56/it is right；The filling density of weft yarn be 43/it is right.
5. the method according to claim 1 for producing the cellular cloth of 3 D stereo using viscose staple fibre and viscose filament yarn,
It is characterized in that：Rapier loom uses 8 heald frames, No. 25 steel buttons, 28 plumages in the step 2.