CN107675215A - A kind of gear electroplating solution - Google Patents
A kind of gear electroplating solution Download PDFInfo
- Publication number
- CN107675215A CN107675215A CN201710742807.6A CN201710742807A CN107675215A CN 107675215 A CN107675215 A CN 107675215A CN 201710742807 A CN201710742807 A CN 201710742807A CN 107675215 A CN107675215 A CN 107675215A
- Authority
- CN
- China
- Prior art keywords
- parts
- gear
- solution
- electroplating solution
- acid
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of gear electroplating solution, the proportioning of the solution each component is as follows:15 ~ 25 parts of chromium trichloride, 15 ~ 20 parts of sodium sulphate, 5 ~ 10 parts of ammonium bromide, 12 ~ 18 parts of boric acid, 5 ~ 10 parts of nickel sulfate, 5 ~ 8 parts of citric acid, 3 ~ 5 parts of glycerine, 10 ~ 15 parts of lauryl sodium sulfate, 3 ~ 4 parts of nitrilotriacetic acid, 85 ~ 95 parts of deionized water;Total, the present invention has the advantages of good plated film stable and uniform, compactness, increase gear wearability and service life.
Description
Technical field
The present invention relates to electroplating technology, and in particular to a kind of gear electroplating solution.
Background technology
Chromium has the wearability that hardness is high, corrosion-resistant and excellent, is widely used in decoration, the surface treatment of wear-resisting part
Deng industry-by-industry;Gear is with teeth on wheel rim, can continuously engage the mechanical organ for transmitting motion and power, and gear rises in the industry
Irreplaceable effect;And because hard contact easily caused impact shock, increase between existing gear and miscellaneous part
Noise during gear drive so that gear wear is accelerated, and shortens the service life of gear, substantially reduces the reliable of working gear
Property, the wearability that plating is greatly improved gear is carried out to gear, improves its service life;Therefore, to solve the above problems, originally
Invention provides a kind of gear electroplating solution.
The content of the invention
It is a primary object of the present invention to provide a kind of to have that plated film stable and uniform, compactness be good, increase gear wearability
With the gear electroplating solution of service life.
To achieve the above object, the present invention provides a kind of gear electroplating solution, and the proportioning of the solution each component is as follows:
15 ~ 25 parts of chromium trichloride, 15 ~ 20 parts of sodium sulphate, 5 ~ 10 parts of ammonium bromide, 12 ~ 18 parts of boric acid, 5 ~ 10 parts of nickel sulfate, citric acid 5 ~ 8
Part, 3 ~ 5 parts of glycerine, 10 ~ 15 parts of lauryl sodium sulfate, 3 ~ 4 parts of nitrilotriacetic acid, 85 ~ 95 parts of deionized water.
A kind of gear electroplating solution, the proportioning of the solution each component are as follows:20 parts of chromium trichloride, 16 parts of sodium sulphate,
8 parts of ammonium bromide, 15 parts of boric acid, 8 parts of nickel sulfate, 7 parts of citric acid, 3 parts of glycerine, 11 parts of lauryl sodium sulfate, nitrilotriacetic acid 4
Part, 88 parts of deionized water.
A kind of preparation method of gear electroplating solution, its preparation process are as follows:
Step 1:It is static after stirring after adding sodium sulphate, ammonium bromide and deionized water in chromium trichloride, fill three
Divide mixing, mixed solution A is made;
Step 2:Boric acid, nickel sulfate, citric acid, glycerine, lauryl sodium sulfate, nitrilotriacetic acid are added in mixed solution A
And remaining deionized water, it is then heated to 38 ~ 40 DEG C and stirs, each component is fully dissolved and mixed solution B is made;
Step 3:It will be placed under mixed solution B natures 8 ~ 10 hours and can be made into required electroplating solution.
The beneficial effects of the present invention are:The compounding ingredient of sodium sulphate, citric acid as chromium in the present invention;Nitrilotriacetic acid be with
Position agent, ammonium bromide is as conducting salt, and for boric acid as buffer, glycerine is organic additive;The effect of ammonium bromide is suppression six
The generation of valency chromium and the effusion of chlorine;Reduce the discharge of pernicious gas and the pollution to environment;Total, the present invention has plated film
Stable and uniform, compactness are good, increase the advantages of gear wearability and service life.
Embodiment
With reference to embodiment, the present invention is described further.
Embodiment 1:
A kind of gear electroplating solution, the proportioning of the solution each component are as follows:15 parts of chromium trichloride, 15 parts of sodium sulphate, bromination
5 parts of ammonium, 12 parts of boric acid, 5 parts of nickel sulfate, 5 parts of citric acid, 3 parts of glycerine, 10 parts of lauryl sodium sulfate, 3 parts of nitrilotriacetic acid,
85 parts of deionized water.
A kind of preparation method of gear electroplating solution, its preparation process are as follows:
Step 1:After 15 sodium sulphate, 5 parts of ammonium bromides and 20 parts of deionized waters are added in 15 parts of chromium trichlorides, after stirring
It is static, three is sufficiently mixed, mixed solution A is made;
Step 2:12 parts of boric acid, 5 parts of nickel sulfates, 5 parts of citric acids, 3 parts of glycerine, 10 parts of dodecanes are added in mixed solution A
Base sodium sulphate, 3 parts of nitrilotriacetic acids and 65 parts of deionized waters, are then heated to 38 DEG C and stir, each component is fully dissolved system
Into mixed solution B;
Step 3:Required electroplating solution is made by being placed 8.5 hours under mixed solution B natures.
Embodiment 2:
A kind of gear electroplating solution, the proportioning of the solution each component are as follows:25 parts of chromium trichloride, 20 parts of sodium sulphate, bromination
10 parts of ammonium, 18 parts of boric acid, 10 parts of nickel sulfate, 8 parts of citric acid, 5 parts of glycerine, 15 parts of lauryl sodium sulfate, nitrilotriacetic acid 4
Part, 95 parts of deionized water.
Embodiment 3:
A kind of gear electroplating solution, the proportioning of the solution each component are as follows:18 parts of chromium trichloride, 17 parts of sodium sulphate, bromination
8 parts of ammonium, 14 parts of boric acid, 7 parts of nickel sulfate, 6 parts of citric acid, 3 parts of glycerine, 12 parts of lauryl sodium sulfate, 4 parts of nitrilotriacetic acid,
92 parts of deionized water.
Embodiment 4:
A kind of gear electroplating solution, the proportioning of the solution each component are as follows:20 parts of chromium trichloride, 16 parts of sodium sulphate, bromination
8 parts of ammonium, 15 parts of boric acid, 8 parts of nickel sulfate, 7 parts of citric acid, 3 parts of glycerine, 11 parts of lauryl sodium sulfate, 4 parts of nitrilotriacetic acid,
88 parts of deionized water.
Compared with Example 1, its each component ratio is different, and preparation method is identical for embodiment 2, embodiment 3, embodiment 4;
Using the solution made by above-described embodiment, its coating film thickness is:Embodiment 1 is 40 μm, and embodiment 2 is 42 μm, and embodiment 3 is
45 μm, embodiment 4 is 46 μm;Total, the gear after being electroplated using electroplating solution of the present invention, plated film is uniform and stable, compactness is good,
And wearability and service life are greatly improved.
Although an embodiment of the present invention has been shown and described, for the ordinary skill in the art, can be with
A variety of changes, modification can be carried out to these embodiments, replace without departing from the principles and spirit of the present invention by understanding
And modification, the scope of the present invention is defined by the appended.
Claims (3)
- A kind of 1. gear electroplating solution, it is characterised in that:The proportioning of the solution each component is as follows:15 ~ 25 parts of chromium trichloride, 15 ~ 20 parts of sodium sulphate, 5 ~ 10 parts of ammonium bromide, 12 ~ 18 parts of boric acid, 5 ~ 10 parts of nickel sulfate, 5 ~ 8 parts of citric acid, 3 ~ 5 parts of glycerine, 10 ~ 15 parts of lauryl sodium sulfate, 3 ~ 4 parts of nitrilotriacetic acid, 85 ~ 95 parts of deionized water.
- A kind of 2. gear electroplating solution according to claim 1, it is characterised in that:The solution each component is matched somebody with somebody such as Under:20 parts of chromium trichloride, 16 parts of sodium sulphate, 8 parts of ammonium bromide, 15 parts of boric acid, 8 parts of nickel sulfate, 7 parts of citric acid, 3 parts of glycerine, 11 parts of lauryl sodium sulfate, 4 parts of nitrilotriacetic acid, 88 parts of deionized water.
- A kind of 3. preparation method of gear electroplating solution according to claim 1, it is characterised in that:Its preparation process is such as Under:Step 1:It is static after stirring after adding sodium sulphate, ammonium bromide and deionized water in chromium trichloride, fill three Divide mixing, mixed solution A is made;Step 2:Boric acid, nickel sulfate, citric acid, glycerine, lauryl sodium sulfate, nitrilotriacetic acid are added in mixed solution A And remaining deionized water, it is then heated to 35 ~ 40 DEG C and stirs, each component is fully dissolved and mixed solution B is made;Step 3:It will be placed under mixed solution B natures 8 ~ 10 hours and can be made into required electroplating solution.