CN107674736A - A kind of lubricant composition and preparation method thereof - Google Patents
A kind of lubricant composition and preparation method thereof Download PDFInfo
- Publication number
- CN107674736A CN107674736A CN201710994521.7A CN201710994521A CN107674736A CN 107674736 A CN107674736 A CN 107674736A CN 201710994521 A CN201710994521 A CN 201710994521A CN 107674736 A CN107674736 A CN 107674736A
- Authority
- CN
- China
- Prior art keywords
- lubricant composition
- ptfe
- ptfe composite
- composition according
- kollag
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides a kind of lubricant composition, includes the component of following mass fraction:Compound soap:6~10%;Polyalphaolefin:70~80%;Antioxidant:0.2~1%;Extreme pressure anti-wear additives:1~3%;Anticorrosive:0.2~1%;Kollag:10~20%;The kollag includes one or both of ptfe composite micro mist, ptfe micropowder and melamine cyanurate;The ptfe composite micro mist is polybenzoate PTFE composite micro-powders.Lubricant composition in the present invention with the addition of ptfe composite (PTFE) micropowder material, it can be used in 40 DEG C~150 DEG C temperature ranges, possesses excellent abrasion resistance, it is suitable for high stress lower slider friction pair or the friction lubricating of skid mixing, be particularly suitable for use in angle regulating device for seat of vehicle, the lubrication at steering camshaft rack position.Present invention also offers a kind of preparation method of lubricant composition.
Description
Technical field
The invention belongs to technical field of lubricating grease, more particularly to a kind of lubricant composition and preparation method thereof.
Background technology
The many driving members of automobile are slided or containing the friction pair partly slided, such as recliner slip ring, steering gear scroll bar
Rack etc..Sliding friction is harsher with respect to rolling friction condition, and vehicle transmission part typically has to fit precision and life-span
Strict requirements, this just needs lubricating grease to have long-acting anti-wear performance.Common recliner lubricating grease can meet in a short time
Wear-resistant requirement, but wear extent is bigger than normal after endurancing.
The content of the invention
It is an object of the invention to provide a kind of lubricant composition and preparation method thereof, the grease composition in the present invention
Thing has long-acting anti-wear performance.
The present invention provides a kind of lubricant composition, includes the component of following mass fraction:
Compound soap:6~10%;Poly alpha olefin:70~80%;Antioxidant:0.2~1%;Extreme pressure anti-wear additives:1~3%;It is anti-
Corrosive agent:0.2~1%;Kollag:10~20%;
The kollag includes ptfe composite micro mist, ptfe micropowder and melamine cyanurate
One or both of;
The ptfe composite micro mist is polybenzoate PTFE composite micro-powders.
Preferably, mass fraction of the ptfe composite in the lubricant composition is 5~10%.
Preferably, the kollag is ptfe composite micro mist and ptfe micropowder.
Preferably, viscosity of the poly alpha olefin at 100 DEG C is 6~20mm2/s。
Preferably, the poly alpha olefin includes PAO8 and PAO10;
The mass ratio of the PAO8 and PAO10 are (4~6):(6~4).
Preferably, the antioxidant is one kind or more in diphenylamines, di-iso-octyldiphenylamine and N- phenyl-α-aniline
Kind.
Preferably, the extreme pressure anti-wear additives are sulphur phosphorus fourth octyl group zinc salt, aminothio ester, tri o cresyl thiophosphate alizarinic acid and acidity
One or more in dibutyl phosphite.
Preferably, the anticorrosive is one or two kinds of in thiadiazoles derivative and benzotriazole.
The present invention provides a kind of preparation method of lubricant composition, including lower step:
The alkali difference of the quality such as two parts is soluble in water, obtain alkali lye A and alkali lye B;
After the poly alpha olefin of 1/2 amount is mixed with 12- hydroxy stearic acids, 85 DEG C are warming up to, alkali lye A is added, is reacted;
React and be warming up to 135~140 DEG C, added decanedioic acid, stir, then added alkali lye B, reacted;
160 DEG C are continuously heating to, adds the poly alpha olefin of remaining 1/2 amount, 210 DEG C is warming up to and stops heating;
160 DEG C of addition kollags are naturally cooled to, 100 DEG C is cooled to and adds antioxidant, the extreme pressure of 10~15% amounts
The anticorrosive of antiwear additive and 3~4% amounts, the extreme pressure anti-wear additives and anticorrosive of 70 DEG C of addition surpluses are cooled to, are moistened
Grease composition.
The present invention provides a kind of lubricant composition, includes the component of following mass fraction:Compound soap:6~10%;Poly- α-
Alkene:70~80%;Antioxidant:0.2~1%;Extreme pressure anti-wear additives:1~3%;Anticorrosive:0.2~1%;Kollag:
10~20%;The kollag includes ptfe composite micro mist, ptfe micropowder and melamine cyanurate
One or both of ester;The ptfe composite micro mist is polybenzoate PTFE composite micro-powders.Lubricating grease in the present invention
Composition with the addition of ptfe composite (PTFE) micropowder material, can use, possess in -40 DEG C~150 DEG C temperature ranges
Excellent abrasion resistance, it is suitable for high stress lower slider friction pair or the friction lubricating of skid mixing, be particularly suitable for use in automotive seats
Chair recliner, the lubrication at steering camshaft rack position.
Embodiment
The invention provides a kind of lubricant composition, include the component of following mass fraction:
Compound soap:6~10%;Poly alpha olefin:70~80%;Antioxidant:0.2~1%;Extreme pressure anti-wear additives:1~3%;It is anti-
Corrosive agent:0.2~1%;Kollag:10~20%;
The kollag includes ptfe composite micro mist, ptfe micropowder and melamine cyanurate
One or both of;
The ptfe composite micro mist is polybenzoate PTFE composite micro-powders.
In the present invention, the compound soap is preferably the combination product of 12- hydroxy lithium stearates and decanedioic acid lithium;It is described multiple
The mass fraction for closing soap is preferably 6~10%, more preferably 7~9%, most preferably 8%.
In the present invention, it is oily based on the poly alpha olefin, preferably PAO8 and PAO10 mixture, the PAO8 and
PAO10 mass ratio is preferably (4~6):(6~4), more preferably 5:5;The mass fraction of the poly alpha olefin is preferably 70~
80%, more preferably 75~76%.The viscosity at 100 DEG C of the poly alpha olefin is preferably 6~20mm2/ s, more preferably 8
~15mm2/ s, most preferably 10~12mm2/s。
In the present invention, the antioxidant is preferably one in diphenylamines, di-iso-octyldiphenylamine and N- phenyl-α-aniline
Kind is a variety of;The mass fraction of the antioxidant is preferably 0.2~1%, more preferably 0.5~0.8%, most preferably 0.6~
0.7%.
In the present invention, the extreme pressure anti-wear additives are preferably sulphur phosphorus fourth octyl group zinc salt, aminothio ester, tri o cresyl thiophosphate madder
One or more in sour and acid dibutyl phosphite;The mass fraction of the extreme pressure anti-wear additives is preferably 1~3%, more excellent
Elect 1.5~2.5%, most preferably 2% as.
In the present invention, the anticorrosive is preferably one or two kinds of in thiadiazoles derivative and benzotriazole;Institute
The mass fraction for stating anticorrosive is preferably 0.2~1%, more preferably 0.5~0.8%, most preferably 0.6~0.7%.
In the present invention, the kollag includes ptfe composite micro mist (compound PTFE), polytetrafluoroethylene (PTFE)
One or both of micro mist and melamine cyanurate;Preferably ptfe composite micro mist and polytetrafluoroethylene (PTFE) are micro-
Powder;The ptfe composite micro mist is polybenzoate PTFE composite micro-powders;The particle diameter of the ptfe composite micro mist is excellent
Elect 3~8 μm as;The particle diameter of the ptfe micropowder is preferably 3 μm~8 μm;The ptfe composite described
Mass fraction in lubricant composition is preferably 5~10%, more preferably 6~9%, most preferably 7~8%.
Present invention also offers a kind of preparation method of lubricant composition, including lower step:
The alkali difference of the quality such as two parts is soluble in water, obtain alkali lye A and alkali lye B;
After the poly alpha olefin of 1/2 amount is mixed with 12- hydroxy stearic acids, 85 DEG C are warming up to, alkali lye A is added, is reacted;
React and be warming up to 135~140 DEG C, added decanedioic acid, stir, then added alkali lye B, reacted;
160 DEG C are continuously heating to, adds the poly alpha olefin of remaining 1/2 amount, 210 DEG C is warming up to and stops heating;
160 DEG C of addition kollags are naturally cooled to, 100 DEG C is cooled to and adds antioxidant, the extreme pressure of 10~15% amounts
The anticorrosive of antiwear additive and 3~4% amounts, the extreme pressure anti-wear additives and anticorrosive of 70 DEG C of addition surpluses are cooled to, are moistened
Grease composition.
The present invention provides a kind of lubricant composition, includes the component of following mass fraction:Compound soap:6~10%;Poly- α-
Alkene:70~80%;Antioxidant:0.2~1%;Extreme pressure anti-wear additives:1~3%;Anticorrosive:0.2~1%;Kollag:
10~20%;The kollag includes ptfe composite micro mist, ptfe micropowder and melamine cyanurate
One or both of ester;The ptfe composite micro mist is polybenzoate PTFE composite micro-powders.Lubricating grease in the present invention
Composition with the addition of ptfe composite (PTFE) micropowder material, can use, possess in -40 DEG C~150 DEG C temperature ranges
Excellent abrasion resistance, it is suitable for high stress lower slider friction pair or the friction lubricating of skid mixing, be particularly suitable for use in automotive seats
Chair recliner, the lubrication at steering camshaft rack position.
In order to further illustrate the present invention, with reference to embodiments to a kind of lubricant composition provided by the invention and its
Preparation method is described in detail, but can not be understood as limiting the scope of the present invention.
Embodiment 1
It is standby alkali lye A to be made into 10.99g lithium hydroxides with 6 times of distilled water, with the 6 times of steamings of 11.03g lithium hydroxides in advance
It is standby that distilled water is made into alkali lye B;
By 400g base oils (PAO8:PAO10=4:6), 12- hydroxyls stearic acid 75g is added in fat kettle processed, heating;
Stirring is warming up to 85 DEG C, is slowly added to alkali lye A, constant temperature stirring reaction 20min.
React and be warming up to 135~140 DEG C, stopped heating, added decanedioic acid 25g, constant temperature stirring 5min.
It is slowly added to alkali lye B, stirring reaction 20min.
Continue to heat up, 160 DEG C add 400g base oils (PAO8:PAO10=4:6)
Stop heating to 210 DEG C, stir natural cooling.
It is cooled to 160 DEG C and adds compound PTFE micro mists 80g, PTFE micro mist 120g, continues stirring cooling
Di-iso-octyldiphenylamine 2g, benzotriazole 3g, tri o cresyl thiophosphate alizarinic acid 1g are added after being cooled to 100 DEG C, is added
Stirring cooling afterwards
It is cooled to 70 DEG C and adds sulphur phosphorus fourth octyl group zinc salt 20g, thiadiazoles derivative 5g, it is quick to stir 5 minutes to lubricating grease
Homogenizing post processing, makes the smooth exquisiteness of lubricating grease.
Embodiment 2
It is standby alkali lye A to be made into 10.99g lithium hydroxides with 6 times of distilled water, with the 6 times of steamings of 11.03g lithium hydroxides in advance
It is standby that distilled water is made into alkali lye B
By 400g base oils (PAO8:PAO10=5:5), 12- hydroxyls stearic acid 75g is added in fat kettle processed, heating
Stirring is warming up to 85 DEG C, is slowly added to alkali lye A, constant temperature stirring reaction 20min.
React and be warming up to 135~140 DEG C, stopped heating, added decanedioic acid 25g, constant temperature stirring 5min.
It is slowly added to alkali lye B, stirring reaction 20min.
Continue to heat up, 160 DEG C add 400g base oils (PAO8:PAO10=5:5)
Stop heating to 210 DEG C, stir natural cooling.
It is cooled to 160 DEG C and adds compound PTFE micro mists 80g, PTFE micro mist 100g, continues stirring cooling
Di-iso-octyldiphenylamine 2g, benzotriazole 3g, tri o cresyl thiophosphate alizarinic acid 1g are added after being cooled to 100 DEG C, is added
Stirring cooling afterwards
It is cooled to 70 DEG C and adds sulphur phosphorus fourth octyl group zinc salt 20g, thiadiazoles derivative 5g, it is quick to stir 5 minutes to lubricating grease
Homogenizing post processing, makes the smooth exquisiteness of lubricating grease.
Embodiment 3
It is standby alkali lye A to be made into 10.99g lithium hydroxides with 6 times of distilled water, with the 6 times of steamings of 11.03g lithium hydroxides in advance
It is standby that distilled water is made into alkali lye B
By 400g base oils (PAO8:PAO10=6:4), 12- hydroxyls stearic acid 75g is added in fat kettle processed, heating
Stirring is warming up to 85 DEG C, is slowly added to alkali lye A, constant temperature stirring reaction 20min.
React and be warming up to 135~140 DEG C, stopped heating, added decanedioic acid 25g, constant temperature stirring 5min.
It is slowly added to alkali lye B, stirring reaction 20min.
Continue to heat up, 160 DEG C add 400g base oils (PAO8:PAO10=6:4)
Stop heating to 210 DEG C, stir natural cooling.
It is cooled to 160 DEG C and adds compound PTFE micro mists 80g, PTFE micro mist 80g, continues stirring cooling
Di-iso-octyldiphenylamine 2g, benzotriazole 3g, tri o cresyl thiophosphate alizarinic acid 1g are added after being cooled to 100 DEG C, is added
Stirring cooling afterwards
It is cooled to 70 DEG C and adds sulphur phosphorus fourth octyl group zinc salt 20g, thiadiazoles derivative 5g, it is quick to stir 5 minutes to lubricating grease
Homogenizing post processing, makes the smooth exquisiteness of lubricating grease.
The lubricating grease that the present invention obtains to embodiment 1~3 carries out performance detection, as a result as shown in table 1.
The performance data of lubricating grease in the embodiment of the present invention 1~3 of table 1
Wherein, the method for testing of wear extent is as follows:
Lubricating grease SRV (face contact) wear extent method of testing
Method:See the lubricating grease friction and wear behavior test method(s)s of SH/T 0721 (high frequency linearity vibration rig method);
Condition:Normal temperature, 10h, 50Hz, 1.0mm, 400N, face contact;
Testpieces specification:Test board:See SH/T 0,721 7.2;
Proving ring:52100 steel, hardness RC are 60 ± 2, and roughness is identical with test board, external diameter 20mm, internal diameter 17mm, high
Spend 5.5mm.
Method is summarized:1. by the requirement of SH/T0721 methods by test board and proving ring wiped clean, and dried with dry silk,
Weigh;
2nd, friction test is carried out after testpieces being smeared into lubricating grease by the experimental conditions of SH/T 0721 and step;
3rd, after off-test, lubricating grease unnecessary on testpieces is washed with solvent, and is dried with dry silk, is weighed.
4th, the difference of former and later two testpieces weight and as wear extent are tested.
Described above is only the preferred embodiment of the present invention, it is noted that for the ordinary skill people of the art
For member, under the premise without departing from the principles of the invention, some improvements and modifications can also be made, these improvements and modifications also should
It is considered as protection scope of the present invention.
Claims (9)
1. a kind of lubricant composition, include the component of following mass fraction:
Compound soap:6~10%;Poly alpha olefin:70~80%;Antioxidant:0.2~1%;Extreme pressure anti-wear additives:1~3%;Anticorrosion
Agent:0.2~1%;Kollag:10~20%;
The kollag is included in ptfe composite micro mist, ptfe micropowder and melamine cyanurate
It is one or two kinds of;
The ptfe composite micro mist is polybenzoate PTFE composite micro-powders.
2. lubricant composition according to claim 1, it is characterised in that the ptfe composite is in the lubrication
Mass fraction in oil/fat composition is 5~10%.
3. lubricant composition according to claim 1, it is characterised in that the kollag is compound polytetrafluoroethyl-ne
Alkene micro mist and ptfe micropowder.
4. lubricant composition according to claim 1, it is characterised in that viscosity of the poly alpha olefin at 100 DEG C
For 6~20mm2/s。
5. lubricant composition according to claim 1, it is characterised in that the poly alpha olefin includes PAO8 and PAO10;
The mass ratio of the PAO8 and PAO10 are (4~6):(6~4).
6. lubricant composition according to claim 1, it is characterised in that the antioxidant is diphenylamines, diisooctyl
One or more in diphenylamines and N- phenyl-α-aniline.
7. lubricant composition according to claim 1, it is characterised in that the extreme pressure anti-wear additives are sulphur phosphorus fourth octyl group zinc
One or more in salt, aminothio ester, tri o cresyl thiophosphate alizarinic acid and acid dibutyl phosphite.
8. lubricant composition according to claim 1, it is characterised in that the anticorrosive be thiadiazoles derivative and
It is one or two kinds of in benzotriazole.
9. a kind of preparation method of lubricant composition, including lower step:
The alkali difference of the quality such as two parts is soluble in water, obtain alkali lye A and alkali lye B;
After the poly alpha olefin of 1/2 amount is mixed with 12- hydroxy stearic acids, 85 DEG C are warming up to, alkali lye A is added, is reacted;
React and be warming up to 135~140 DEG C, added decanedioic acid, stir, then added alkali lye B, reacted;
160 DEG C are continuously heating to, adds the poly alpha olefin of remaining 1/2 amount, 210 DEG C is warming up to and stops heating;
160 DEG C of addition kollags are naturally cooled to, 100 DEG C is cooled to and adds antioxidant, the extreme-pressure anti-wear of 10~15% amounts
Agent and the anticorrosive of 3~4% amounts, the extreme pressure anti-wear additives and anticorrosive of 70 DEG C of addition surpluses are cooled to, obtain lubricating grease
Composition.