CN107673740A - A kind of multi-functional tea set and preparation method thereof - Google Patents

A kind of multi-functional tea set and preparation method thereof Download PDF

Info

Publication number
CN107673740A
CN107673740A CN201711098425.0A CN201711098425A CN107673740A CN 107673740 A CN107673740 A CN 107673740A CN 201711098425 A CN201711098425 A CN 201711098425A CN 107673740 A CN107673740 A CN 107673740A
Authority
CN
China
Prior art keywords
mud
cash
base
walk
tea set
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201711098425.0A
Other languages
Chinese (zh)
Inventor
刘先勇
张宏亮
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Pingding County Hat Kiln Sand Device Pottery Art Co Ltd
Original Assignee
Pingding County Hat Kiln Sand Device Pottery Art Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Pingding County Hat Kiln Sand Device Pottery Art Co Ltd filed Critical Pingding County Hat Kiln Sand Device Pottery Art Co Ltd
Priority to CN201711098425.0A priority Critical patent/CN107673740A/en
Publication of CN107673740A publication Critical patent/CN107673740A/en
Pending legal-status Critical Current

Abstract

The present invention relates to a kind of multi-functional tea set, the raw material of its following weight percentage is prepared：Blue or green cash, viscous cash, gangue, bright stone, feldspar, quartz, clinker.Its preparation process：Dispensing：Blue or green cash, viscous cash, gangue, bright stone, feldspar, quartz and clinker are weighed by proportioning, and is well mixed；Grinding：Dispensing in upper step is put into ball mill be ground to 200 mesh go out mill, by the fine powder after grinding and water on demand soft durometer requirement matched；Clear mud：Mud is separated by the mud mixed in upper step in clear mud with water, base mud is made；Dry：Base mud in upper step is placed and dried in the cool, the water content for making base mud is 70%；Rub mud：The base mud dried in upper step is kneaded into walk repeatedly, walk requires pore-free, free from admixture, and shale is uniform；Shaping：The walk made in upper step is placed on throwing on mud platform required base substrate is made, and carry out shape and moulding and the modification of color；Drying；Form by a firing.

Description

A kind of multi-functional tea set and preparation method thereof
Technical field
The invention belongs to sand container field, and in particular to a kind of multi-functional tea set and preparation method thereof.
Background technology
At present, tea vessel have the manufacturing history of more than 2,000 years in China, because it is chiltern vessel, so with preferable Gas permeability and adsorptivity, by people extensively with as the vessel for boiling tea, because its used cost of material is low, and does not contain and appoint What noxious material, environmentally-friendly sanitary, thus be widely adopted, still, existing tea set causes because raw material and raw material proportioning are unreasonable It is poor physical property to be present in manufactured tea set, and it is easily fried, easily split, using it is dangerous the problems such as.
The content of the invention
It is an object of the invention to provide a kind of multi-functional tea set and preparation method thereof.Made of the present invention tea set environmental protection, Tea set is safe to use, and reasonable raw material proportioning.
The technical solution adopted by the present invention：A kind of multi-functional tea set, the raw material of its following weight percentage are prepared：
Blue or green cash 45-55% glues the bright stone 3-8% feldspars 3-14% quartz 3-8% clinkers 3-8% of cash 10-19% gangues 6-15%.
Preferentially, a kind of multi-functional tea set, the raw material of its following weight percentage are prepared：
Blue or green cash 50% glues 15% gangue of cash, 10% bright quartzy 5% clinker 5% of 5% feldspar of stone 10%.
In addition, present invention also offers a kind of preparation method of multi-functional tea set, it comprises the following steps：
（1）Dispensing：Blue or green cash, viscous cash, gangue, bright stone, feldspar, quartz and clinker are weighed by proportioning, and is well mixed；
（2）Grinding：Dispensing in upper step is put into ball mill and is ground to 200 mesh and goes out mill, by the fine powder after grinding and water on demand The soft durometer requirement wanted is matched；
（3）Clear mud：By step（2）In the mud that mixes mud is separated with water in clear mud, base mud is made；
（4）Dry：By step（3）In base mud place dry in the cool, make base mud water content be 70%；
（5）Rub mud：By step（4）In the base mud that has dried be kneaded into walk repeatedly, walk requires pore-free, free from admixture, and shale Uniformly；
（6）Shaping：By step（5）In the walk that makes be placed on throwing on mud platform required base substrate be made, and carry out shape and make The modification of type and color；
（7）Drying：By step（6）In the base substrate that makes dried at a temperature of 50-60 DEG C；
（8）Fire：By step（7）The base substrate made is placed in kiln, is fired 24 hours at a temperature of 1250-1300 DEG C, Naturally cool to kiln discharge after normal temperature.
Its advantage is the present invention compared with prior art：Manufacture craft of the present invention is simple, high yield rate, and color is pure Just, it is smooth to the touch, service life length, and tea set health environment-friendly is pollution-free, has very big market application foreground.
Embodiment
Embodiment 1
A kind of multi-functional tea set, the raw material of its following weight percentage are prepared：
Blue or green cash 45% glues 10% gangue of cash, 6% bright quartzy 3% clinker 3% of 3% feldspar of stone 3%.
A kind of preparation method of multi-functional tea set, it comprises the following steps：
（1）Dispensing：Blue or green cash, viscous cash, gangue, bright stone, feldspar, quartz and clinker are weighed by proportioning, and is well mixed；
（2）Grinding：Dispensing in upper step is put into ball mill and is ground to 200 mesh and goes out mill, by the fine powder after grinding and water on demand The soft durometer requirement wanted is matched；
（3）Clear mud：By step（2）In the mud that mixes mud is separated with water in clear mud, base mud is made；
（4）Dry：By step（3）In base mud place dry in the cool, make base mud water content be 70%；
（5）Rub mud：By step（4）In the base mud that has dried be kneaded into walk repeatedly, walk requires pore-free, free from admixture, and shale Uniformly；
（6）Shaping：By step（5）In the walk that makes be placed on throwing on mud platform required base substrate be made, and carry out shape and make The modification of type and color；
（7）Drying：By step（6）In the base substrate that makes dried at a temperature of 50-60 DEG C；
（8）Fire：By step（7）The base substrate made is placed in kiln, is fired 24 hours at a temperature of 1250-1300 DEG C, Naturally cool to kiln discharge after normal temperature.
Embodiment 2
A kind of multi-functional tea set, the raw material of its following weight percentage are prepared：
Blue or green cash 50% glues 15% gangue of cash, 10% bright quartzy 5% clinker 5% of 5% feldspar of stone 10%.
In addition, present invention also offers a kind of preparation method of multi-functional tea set, it comprises the following steps：
（1）Dispensing：Blue or green cash, viscous cash, gangue, bright stone, feldspar, quartz and clinker are weighed by proportioning, and is well mixed；
（2）Grinding：Dispensing in upper step is put into ball mill and is ground to 200 mesh and goes out mill, by the fine powder after grinding and water on demand The soft durometer requirement wanted is matched；
（3）Clear mud：By step（2）In the mud that mixes mud is separated with water in clear mud, base mud is made；
（4）Dry：By step（3）In base mud place dry in the cool, make base mud water content be 70%；
（5）Rub mud：By step（4）In the base mud that has dried be kneaded into walk repeatedly, walk requires pore-free, free from admixture, and shale Uniformly；
（6）Shaping：By step（5）In the walk that makes be placed on throwing on mud platform required base substrate be made, and carry out shape and make The modification of type and color；
（7）Drying：By step（6）In the base substrate that makes dried at a temperature of 50-60 DEG C；
（8）Fire：By step（7）The base substrate made is placed in kiln, is fired 24 hours at a temperature of 1250-1300 DEG C, Naturally cool to kiln discharge after normal temperature.
Embodiment 3
A kind of multi-functional tea set, the raw material of its following weight percentage are prepared：
Blue or green cash 55% glues 19% gangue of cash, 15% bright quartzy 8% clinker 8% of 8% feldspar of stone 14%.
A kind of preparation method of multi-functional tea set, it comprises the following steps：
（1）Dispensing：Blue or green cash, viscous cash, gangue, bright stone, feldspar, quartz and clinker are weighed by proportioning, and is well mixed；
（2）Grinding：Dispensing in upper step is put into ball mill and is ground to 200 mesh and goes out mill, by the fine powder after grinding and water on demand The soft durometer requirement wanted is matched；
（3）Clear mud：By step（2）In the mud that mixes mud is separated with water in clear mud, base mud is made；
（4）Dry：By step（3）In base mud place dry in the cool, make base mud water content be 70%；
（5）Rub mud：By step（4）In the base mud that has dried be kneaded into walk repeatedly, walk requires pore-free, free from admixture, and shale Uniformly；
（6）Shaping：By step（5）In the walk that makes be placed on throwing on mud platform required base substrate be made, and carry out shape and make The modification of type and color；
（7）Drying：By step（6）In the base substrate that makes dried at a temperature of 50-60 DEG C；
（8）Fire：By step（7）The base substrate made is placed in kiln, is fired 24 hours at a temperature of 1250-1300 DEG C, Naturally cool to kiln discharge after normal temperature.

Claims (3)

1. a kind of multi-functional tea set, it is characterised in that the raw material of its following weight percentage is prepared：
Blue or green cash 45-55% glues the bright stone 3-8% of cash 10-19% gangues 6-15%
Feldspar 3-14% quartz 3-8% clinkers 3-8%.
2. according to a kind of multi-functional tea set described in claim 1, it is characterised in that prepared by the raw material of its following weight percentage Form：
Blue or green cash 50% glues 15% gangue of cash, 10% bright quartzy 5% clinker 5% of 5% feldspar of stone 10%.
3. a kind of preparation method of multi-functional tea set as claimed in claim 1, it is characterised in that comprise the following steps：
（1）Dispensing：Blue or green cash, viscous cash, gangue, bright stone, feldspar, quartz and clinker are weighed by proportioning, and is well mixed；
（2）Grinding：Dispensing in upper step is put into ball mill and is ground to 200 mesh and goes out mill, by the fine powder after grinding and water on demand The soft durometer requirement wanted is matched；
（3）Clear mud：By step（2）In the mud that mixes mud is separated with water in clear mud, base mud is made；
（4）Dry：By step（3）In base mud place dry in the cool, make base mud water content be 70%；
（5）Rub mud：By step（4）In the base mud that has dried be kneaded into walk repeatedly, walk requires pore-free, free from admixture, and shale Uniformly；
（6）Shaping：By step（5）In the walk that makes be placed on throwing on mud platform required base substrate be made, and carry out shape and make The modification of type and color；
（7）Drying：By step（6）In the base substrate that makes dried at a temperature of 50-60 DEG C；
（8）Fire：By step（7）The base substrate made is placed in kiln, is fired 24 hours at a temperature of 1250-1300 DEG C, Naturally cool to kiln discharge after normal temperature.
CN201711098425.0A 2017-11-09 2017-11-09 A kind of multi-functional tea set and preparation method thereof Pending CN107673740A (en)