CN107673418A - A kind of sanitary sewage disposal material and preparation method thereof - Google Patents
A kind of sanitary sewage disposal material and preparation method thereof Download PDFInfo
- Publication number
- CN107673418A CN107673418A CN201710948094.9A CN201710948094A CN107673418A CN 107673418 A CN107673418 A CN 107673418A CN 201710948094 A CN201710948094 A CN 201710948094A CN 107673418 A CN107673418 A CN 107673418A
- Authority
- CN
- China
- Prior art keywords
- parts
- oxide composite
- sanitary sewage
- chitosan
- sewage disposal
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The present invention relates to a kind of sanitary sewage disposal material and preparation method thereof, comprise the following steps A, measure raw material according to parts by weight, activated carbon, zeolite, ferrous sulfide, kaolin, montmorillonite, frerrous chloride are well mixed, it is crushed to 100 200 mesh powders, it is placed in deionized water, ultrasonic disperse is carried out, forms suspension；B, polyacrylic acid, polyvinyl alcohol, chitosan graphene oxide composite material, chitosan ferric oxide composite material, macroreticular resin concussion are uniformly mixed, carry out fusion plastification, and hot-forming a kind of sanitary sewage disposal material is prepared；Compared with prior art, sanitary sewage disposal material of the present invention has the characteristics of low cost, stable performance, high treating effect, and its preparation method is simple, easy operation control.
Description
Technical field
The present invention relates to sewage treatment area, more particularly to a kind of sanitary sewage disposal and preparation method thereof.
Background technology
Sanitary sewage is mainly various detergent and sewage, rubbish, excrement used in urban life etc., mostly nontoxic
Inorganic salts, more containing nitrogen phosphate and sulfur in sanitary sewage, malignant bacteria is more.Everyone sanitary sewage amount discharged daily of city is 150-
400L, its amount have substantial connection with living standard.Contain large amount of organic in sanitary sewage, such as cellulose, starch, carbohydrate and fat
Fat protein etc.；Also often pathogen, virus and parasitic ovum are contained；Chloride, sulfate, phosphate, the carbonic acid of inorganic salts
Hydrogen salt and sodium, potassium, calcium, magnesium etc..The characteristics of total is nitrogenous, sulfur-bearing and phosphorous height, and post-processing is relatively difficult.People should protect
Water resource, China's actual conditions are more special, and water resource occupancy volume per person is few, and spatial distribution is uneven.With Chinese Urbanization's, industry
The acceleration of change, the demand gap of water resource also increasingly increase.In this context, sewage treatment industry turns into new industry,
At present status of equal importance is in running water production, water supply, draining, Treated sewage reusing industry.
At present, it is domestic to be used in sanitary sewage disposal and the product of purification and have a lot, but the cost made is higher, and processing and
The technological process for purifying sewage is cumbersome.
The content of the invention
The purpose of the present invention is to provide a kind of low cost, stable performance, high treating effect in view of the shortcomings of the prior art
Sanitary sewage disposal material, its preparation method is simple, easy operation control.
The technical scheme that the present invention solves above-mentioned technical problem is as follows：
A kind of sanitary sewage disposal material, include the raw material of following parts by weight；Activated carbon 5-10 parts, zeolite 5-8 parts, poly- third
Olefin(e) acid 10-15 parts, polyvinyl alcohol 20-40 parts, ferrous sulfate 1-5 parts, chitosan-graphene oxide composite material 5-10 parts, height
Ridge soil 3-8 parts, -7 parts of montmorillonite 2, frerrous chloride 3-8 parts, chitosan-ferric oxide composite material 5-10 parts.
Compared with prior art, the beneficial effects of the invention are as follows：
The present invention provides a kind of low cost, stable performance, the sanitary sewage disposal material of high treating effect, its preparation method
Simply, easy operation control.
On the basis of above-mentioned technical proposal, the present invention can also do following improvement.
Further, the sewage treating material includes the raw material of following parts by weight；Activated carbon 5-8 parts, zeolite 5-8 parts, gather
Acrylic acid 11-15 parts, polyvinyl alcohol 30-40 parts, ferrous sulfate 2-5 parts, chitosan-graphene oxide composite material 6-10 parts,
Kaolin 5-8 parts, montmorillonite 5-7 parts, frerrous chloride 5-8 parts, chitosan-ferric oxide composite material 8-10 parts.
Further, the sewage treating material includes the raw material of following parts by weight；Activated carbon 6-8 parts, zeolite 7-8 parts, gather
Acrylic acid 13-15 parts, polyvinyl alcohol 30-35 parts, ferrous sulfate 4-5 parts, chitosan-graphene oxide composite material 8-10 parts,
Kaolin 5-8 parts, montmorillonite 6-7 parts, frerrous chloride 4-7 parts, chitosan-ferric oxide composite material 8-10 parts.
Further, the sewage treating material includes the raw material of following parts by weight；6 parts of activated carbon, 7 parts of zeolite, polypropylene
15 parts of acid, 30 parts of polyvinyl alcohol, 3 parts of ferrous sulfate, 8 parts of chitosan-graphene oxide composite material, 6 parts of kaolin, montmorillonite
5 parts, 5 parts of frerrous chloride, 8 parts of chitosan-ferric oxide composite material.
Further, the sanitary sewage disposal material also includes macroreticular resin 10-20 parts.
A kind of preparation method of sanitary sewage disposal material as described above, it comprises the following steps：
A, raw material is measured according to parts by weight, activated carbon, zeolite, ferrous sulfide, kaolin, montmorillonite, frerrous chloride is mixed
Close uniformly, be crushed to 100-200 mesh powders, be placed in deionized water, carry out ultrasonic disperse, form suspension；
B, by polyacrylic acid, polyvinyl alcohol, chitosan-graphene oxide composite material, chitosan-iron oxide composite wood
Material, macroreticular resin concussion are uniformly mixed, and carry out fusion plastification, and hot-forming a kind of sanitary sewage disposal material is prepared
Material.
Embodiment
The principles and features of the present invention are described below, and the given examples are served only to explain the present invention, is not intended to limit
Determine the scope of the present invention.
Embodiment 1
A, raw material is measured according to parts by weight, by 5 parts of activated carbon, 5 parts of zeolite, 1 part of ferrous sulfide, 3 parts of kaolin, montmorillonite
2 parts, 3 parts of frerrous chloride it is well mixed, be crushed to 100 mesh powders, be placed in deionized water, carry out ultrasonic disperse, formed outstanding
Supernatant liquid；
B, by 10 parts of polyacrylic acid, 20 parts of polyvinyl alcohol, 5 parts of chitosan-graphene oxide composite material, chitosan-oxygen
Change 10 parts of 5 parts of iron composite material, macroreticular resin concussions to be uniformly mixed, progress fusion plastification, and hot-forming be prepared
A kind of sanitary sewage disposal material.
Embodiment 2
A, raw material is measured according to parts by weight, by 8 parts of activated carbon, 6 parts of zeolite, 3 parts of ferrous sulfide, 6 parts of kaolin, montmorillonite
5 parts, 6 parts of frerrous chloride it is well mixed, be crushed to 150 mesh powders, be placed in deionized water, carry out ultrasonic disperse, formed outstanding
Supernatant liquid；
B, by 13 parts of polyacrylic acid, 30 parts of polyvinyl alcohol, 8 parts of chitosan-graphene oxide composite material, chitosan-oxygen
Change 15 parts of 8 parts of iron composite material, macroreticular resin concussions to be uniformly mixed, progress fusion plastification, and hot-forming be prepared
A kind of sanitary sewage disposal material.
Embodiment 3
A, raw material is measured according to parts by weight, 10 parts of activated carbon, 8 parts of zeolite, 5 parts of ferrous sulfide, 8 parts of kaolin, illiteracy is de-
7 parts of stone, 8 parts of frerrous chloride are well mixed, are crushed to 200 mesh powders, are placed in deionized water, carry out ultrasonic disperse, are formed
Suspension；
B, by 15 parts of polyacrylic acid, 40 parts of polyvinyl alcohol, 10 parts of chitosan-graphene oxide composite material, chitosan-oxygen
Change 20 parts of 10 parts of iron composite material, macroreticular resin concussions to be uniformly mixed, progress fusion plastification, and hot-forming be prepared
A kind of sanitary sewage disposal material.
Comparative example 1
A, raw material is measured according to parts by weight, 10 parts of activated carbon, 8 parts of zeolite, 5 parts of ferrous sulfide, 8 parts of kaolin, illiteracy is de-
7 parts of stone, 8 parts of frerrous chloride are well mixed, are crushed to 200 mesh powders, are placed in deionized water, carry out ultrasonic disperse, are formed
Suspension；
B, by 15 parts of polyacrylic acid, 40 parts of polyvinyl alcohol, 10 parts of chitosan-graphene oxide composite material, chitosan-oxygen
Change 10 parts of concussions of iron composite material to be uniformly mixed, progress fusion plastification, and hot-forming a kind of sanitary sewage is prepared
Handle material.
Comparative example 2
A, raw material is measured according to parts by weight, 10 parts of activated carbon, 8 parts of zeolite, 5 parts of ferrous sulfide, 8 parts of kaolin, illiteracy is de-
7 parts of stone, 8 parts of frerrous chloride are well mixed, are crushed to 200 mesh powders, are placed in deionized water, carry out ultrasonic disperse, are formed
Suspension；
B, by 15 parts of polyacrylic acid, 40 parts of polyvinyl alcohol, 10 parts of chitosan-graphene oxide composite material, macroreticular resin
20 parts of concussions are uniformly mixed, and carry out fusion plastification, and hot-forming a kind of sanitary sewage disposal material is prepared.
| Detection project | Embodiment 1 | Embodiment 2 | Embodiment 3 | Comparative example 1 | Comparative example 2 |
| COD clearances (%) | 94.5 | 93.5 | 92.4 | 76.2 | 77.7 |
| BOD clearances (%) | 96.4 | 95.4 | 96.8 | 66.9 | 89.5 |
| SS clearances (%) | 94.2 | 97.6 | 94.7 | 55.8 | 78.3 |
| NH3- N clearances (%) | 98.7 | 95.8 | 97.6 | 67.6 | 76.8 |
| Pb clearances (%) | 95.7 | 96.6 | 95.3 | 59.4 | 54.8 |
| pH | 7.2 | 7.1 | 7.2 | 6.8 | 6.5 |
From above table data, the material that the present invention is prepared can be effectively applied to sanitary sewage disposal.
It is obvious to a person skilled in the art that the invention is not restricted to the details of above-mentioned one exemplary embodiment, Er Qie
In the case of without departing substantially from spirit or essential attributes of the invention, the present invention can be realized in other specific forms.Therefore, no matter
From the point of view of which point, embodiment all should be regarded as exemplary, and be nonrestrictive, the scope of the present invention is by appended power
Profit requires rather than described above limits, it is intended that all in the implication and scope of the equivalency of claim by falling
Change is included in the present invention.
The foregoing is only presently preferred embodiments of the present invention, be not intended to limit the invention, it is all the present invention spirit and
Within principle, any modification, equivalent substitution and improvements made etc., it should be included in the scope of the protection.
Claims (6)
1. a kind of sanitary sewage disposal material, it is characterised in that include the raw material of following parts by weight；Activated carbon 5-10 parts, zeolite
5-8 parts, polyacrylic acid 10-15 parts, polyvinyl alcohol 20-40 parts, ferrous sulfate 1-5 parts, chitosan-graphene oxide composite material
5-10 parts, kaolin 3-8 parts, -7 parts of montmorillonite 2, frerrous chloride 3-8 parts, chitosan-ferric oxide composite material 5-10 parts.
2. sanitary sewage disposal material according to claim 1, it is characterised in that the sewage treating material includes following
The raw material of parts by weight；Activated carbon 5-8 parts, zeolite 5-8 parts, polyacrylic acid 11-15 parts, polyvinyl alcohol 30-40 parts, ferrous sulfate 2-
5 parts, chitosan-graphene oxide composite material 6-10 parts, kaolin 5-8 parts, montmorillonite 5-7 parts, frerrous chloride 5-8 parts, shell
Glycan-ferric oxide composite material 8-10 parts.
3. sanitary sewage disposal material according to claim 2, it is characterised in that the sewage treating material includes following
The raw material of parts by weight；Activated carbon 6-8 parts, zeolite 7-8 parts, polyacrylic acid 13-15 parts, polyvinyl alcohol 30-35 parts, ferrous sulfate 4-
5 parts, chitosan-graphene oxide composite material 8-10 parts, kaolin 5-8 parts, montmorillonite 6-7 parts, frerrous chloride 4-7 parts, shell
Glycan-ferric oxide composite material 8-10 parts.
4. sanitary sewage disposal material according to claim 1, it is characterised in that the sewage treating material includes following
The raw material of parts by weight；6 parts of activated carbon, 7 parts of zeolite, 15 parts of polyacrylic acid, 30 parts of polyvinyl alcohol, 3 parts of ferrous sulfate, chitosan-
8 parts of graphene oxide composite material, 6 parts of kaolin, 5 parts of montmorillonite, 5 parts of frerrous chloride, chitosan-ferric oxide composite material 8
Part.
5. sanitary sewage disposal material according to claim 1, it is characterised in that the sanitary sewage disposal material also wraps
Include macroreticular resin 10-20 parts.
6. the preparation method of the sanitary sewage disposal material described in a kind of claim 1-5 any one, it is characterised in that it is wrapped
Include following steps：
A, raw material is measured according to parts by weight, activated carbon, zeolite, ferrous sulfide, kaolin, montmorillonite, frerrous chloride is mixed equal
It is even, 100-200 mesh powders are crushed to, are placed in deionized water, carry out ultrasonic disperse, form suspension；
B, by polyacrylic acid, polyvinyl alcohol, chitosan-graphene oxide composite material, chitosan-ferric oxide composite material, big
Resin concussion in hole is uniformly mixed, and carries out fusion plastification, and hot-forming a kind of sanitary sewage disposal material is prepared.