CN107672270A - Can double-deck or multiple layer combination combination enhancing film - Google Patents
Can double-deck or multiple layer combination combination enhancing film Download PDFInfo
- Publication number
- CN107672270A CN107672270A CN201710946038.1A CN201710946038A CN107672270A CN 107672270 A CN107672270 A CN 107672270A CN 201710946038 A CN201710946038 A CN 201710946038A CN 107672270 A CN107672270 A CN 107672270A
- Authority
- CN
- China
- Prior art keywords
- layer
- obstruct membrane
- combination
- deck
- thickness
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses it is a kind of can double-deck or multiple layer combination combination strengthen film, it combine to pasting or multiple first Obstruct membranes and second Obstruct membrane after patch successively to forming by first Obstruct membrane and second Obstruct membrane;First Obstruct membrane is made up of oxide skin(coating), substrate layer, glue layer and easy following layer successively;Second Obstruct membrane is made up of oxide skin(coating), substrate layer, glue layer, easy following layer and atomizing layer successively;Resin bed is provided between first Obstruct membrane and the second Obstruct membrane;The thickness of the resin bed is 0.1 5 μm, and the thickness of glue layer is 0.5 10 μm.The invention provides it is a kind of can double-deck or multiple layer combination combination strengthen film, by the way that the first relatively low Obstruct membrane of manufacturing cost and the second Obstruct membrane are bonded according to demand, realize any requirement of the market to Obstruct membrane barrier property, compared with prior art, not only cost is substantially reduced, and production efficiency is improved.
Description
Technical field
Present invention relates particularly to it is a kind of can double-deck or multiple layer combination combination strengthen film.
Background technology
Obstruct membrane quantum dot is shown, solar energy, OLED are shown etc., more and more applied by field, in order to increase resistance
Separating performance, especially block-water performance, Obstruct membrane uses the Obstruct membrane coated with oxide skin(coating), in order to further increase barrier
Can, the thickness of oxide skin(coating) can be relatively large, causes the adhesive force between oxide skin(coating) and quantum dot glue poor, causes to encapsulate
Caudacoria product peeling force is poor, and then influences the use of its product.It is usually in oxygen in the prior art to solve this technical problem
Compound layer surface increases protective coating, causes the cost of product high and easily damages the surface of oxide skin(coating).
The content of the invention
For above-mentioned technical problem, the invention provides it is a kind of can double-deck or multiple layer combination combination strengthen film.
It is a kind of can double-deck or multiple layer combination combination enhancing film, it is by first Obstruct membrane and a second Obstruct membrane group
Close to patch or multiple first Obstruct membranes and second Obstruct membrane successively to being formed after patch;
First Obstruct membrane is made up of oxide skin(coating), substrate layer, glue layer and easy following layer successively;Second Obstruct membrane according to
It is secondary to be made up of oxide skin(coating), substrate layer, glue layer, easy following layer and atomizing layer;
Resin bed is provided between first Obstruct membrane and the second Obstruct membrane;
The thickness of the resin bed is 0.1-5 μm, and the thickness of glue layer is 0.5-10 μm.
Preferably, the substrate layer is PET, and thickness is 6-50 μm.
Preferably, the glue layer is in polyester, epoxy resin, acrylic resin, organosilicon or polyurethane
One kind, the thickness of glue layer is 1-3 μm;The easily following layer choice of material is polyurethane, polyacrylate or petchem
One kind, thickness be 20-50 μm.
Preferably, the resin is selected from epoxy resin, polyurethane, one kind of polyacrylic resin.
Preferably, the mist degree of the atomizing layer is between 0.1-90%, and fog surface layer hardness is between 3B-6H.
Preferably, the oxide skin(coating) is silicon-base oxide or aluminium base oxide;Oxide layer thicknesses are 20-100 nm.
The invention provides it is a kind of can double-deck or multiple layer combination combination strengthen film, by by manufacturing cost it is relatively low first
Obstruct membrane and the second Obstruct membrane are bonded according to demand, any requirement of the market to Obstruct membrane barrier property are realized, compared to existing skill
Art, not only cost is substantially reduced, and production efficiency is improved.
Brief description of the drawings
Technical scheme in order to illustrate the embodiments of the present invention more clearly, make required in being described below to embodiment
Accompanying drawing is briefly described.
Fig. 1 is the structure chart of the first Obstruct membrane;
Fig. 2 is the structure chart of the second Obstruct membrane;
Fig. 3 is the bilayer combination structure chart of the present invention;
Fig. 4 is three layers of combination assumption diagram of the present invention.
Numeral represents in figure:
1st, substrate layer 2, oxide skin(coating) 3, glue layer 4, easy following layer 5, atomizing layer 6, resin bed.
Embodiment
Below in conjunction with the accompanying drawing in the embodiment of the present invention, the technical scheme in the embodiment of the present invention is carried out clear, complete
Site preparation describes.
Embodiment 1:
Shown in Fig. 1 to 3, it is proposed by the present invention it is a kind of can double-deck or multiple layer combination combination enhancing film, it is by one first barrier
Film and second Obstruct membrane combine to be formed;
First Obstruct membrane is made up of oxide skin(coating) 2, substrate layer 1, glue layer 3 and easily following layer 4 successively;Second Obstruct membrane successively by
Oxide skin(coating) 2, substrate layer 1, glue layer 3, easy following layer 4 and atomizing layer 5 form;
It is resin bed 6 between first Obstruct membrane and the second Obstruct membrane;
Wherein, oxide skin(coating) 2 selects silica, and thickness is 50 nm, and substrate layer 1 is PET, and thickness is 25 μm, and glue layer 3 is ring
Oxygen tree fat, thickness are 5 μm, and easy following layer 4 is polyurethane, and thickness is 30 μm;Atomizing layer 5 uses normal optical atomization method, mist
Spend for 50%, hardness 2H;Resin bed 6 is epoxy resin, and thickness is 2 μm.
Embodiment 2:Shown in Fig. 1 to 3, it is proposed by the present invention it is a kind of can double-deck or multiple layer combination combination enhancing film, its by
One the first Obstruct membrane and second Obstruct membrane combine to be formed;
First Obstruct membrane is made up of oxide skin(coating) 2, substrate layer 1, glue layer 3 and easily following layer 4 successively;Second Obstruct membrane successively by
Oxide skin(coating) 2, substrate layer 1, glue layer 3, easy following layer 4 and atomizing layer 5 form;
It is resin bed 6 between first Obstruct membrane and the second Obstruct membrane;
Wherein, oxide skin(coating) 2 selects aluminum oxide, and thickness is 25 nm, and substrate layer 1 is PET, and thickness is 15 μm, and glue layer 3 is ring
Oxygen tree fat, thickness are 5 μm, and easy following layer 4 is polyurethane, and thickness is 30 μm;Atomizing layer 5 uses normal optical atomization method, mist
Spend for 50%, hardness 3H;Lipid layer is epoxy resin, and thickness is 2 μm.
Embodiment 3:Shown in Fig. 1, Fig. 2 and Fig. 4, it is made up of two the first Obstruct membranes and second Obstruct membrane;First resistance
Barrier film is made up of oxide skin(coating) 2, substrate layer 1, glue layer 3 and easily following layer 4 successively;Second Obstruct membrane successively by oxide skin(coating) 2,
Substrate layer 1, glue layer 3, easy following layer 4 and atomizing layer 5 form;
It is resin bed 6 between first Obstruct membrane and the second Obstruct membrane;
Wherein, oxide skin(coating) 2 selects silica, thickness 50nm, and substrate layer 1 is PET, and thickness is 25 μm, and glue layer 3 is epoxy
Resin, thickness are 5 μm, and easy following layer 4 is polyurethane, and thickness is 30 μm;Atomizing layer 5 uses normal optical atomization method, mist degree
For 50%, hardness 2H;Resin bed 6 is epoxy resin, and thickness is 2 μm.
Embodiment 4:Shown in Fig. 1, Fig. 2 and Fig. 4, the first Obstruct membrane is successively by oxide skin(coating) 2, substrate layer 1, the and of glue layer 3
Easy following layer 4 forms;Second Obstruct membrane is successively by 5 groups of oxide skin(coating) 2, substrate layer 1, glue layer 3, easy following layer 4 and atomizing layer
Into;
It is resin bed 6 between first Obstruct membrane and the second Obstruct membrane;
Wherein, oxide skin(coating) 2 selects silica, and thickness is 50 nm, and substrate layer 1 is PET, and thickness is 25 μm, and glue layer 3 is ring
Oxygen tree fat, thickness are 5 μm, and easy following layer 4 is polyurethane, and thickness is 30 μm;Atomizing layer 5 uses normal optical atomization method, mist
Spend for 50%, hardness 2H;Resin bed 6 is epoxy resin, and thickness is 2 μm.
The barrier transmitance to steam and oxygen of the Obstruct membrane of prior art is generally 10-1-10-2g/m2.day;
The bilayer combination mode of embodiment 1 and embodiment 2, can reach 10-2-10-3g/m2.day;Embodiment 3 and embodiment 4
Three layers of combination, 10 can be reached-3-10-4g/m2.day;Further, if four layers or five layers even more layers when,
10 can be reached-5-10-7g/m2.day, any demand in market is fully met;And production efficiency is substantially increased, reduction is produced into
This.
A variety of modifications to these embodiments will be apparent for those skilled in the art, herein
Defined General Principle can be realized in other embodiments without departing from the spirit or scope of the present invention.
Claims (6)
1. a kind of can double-deck or multiple layer combination combination enhancing film, it is characterised in that it is by first Obstruct membrane and one the
The combination of two Obstruct membranes is to patch or multiple first Obstruct membranes and second Obstruct membrane successively to being formed after patch;
First Obstruct membrane is made up of oxide skin(coating), substrate layer, glue layer and easy following layer successively;Second Obstruct membrane according to
It is secondary to be made up of oxide skin(coating), substrate layer, glue layer, easy following layer and atomizing layer;
Resin bed is provided between first Obstruct membrane and the second Obstruct membrane;
The thickness of the resin bed is 0.1-5 μm, and the thickness of glue layer is 0.5-10 μm.
2. according to claim 1 can double-deck or multiple layer combination combination enhancing film, it is characterised in that the substrate layer is
PET, thickness are 6-50 μm.
3. according to claim 1 can double-deck or multiple layer combination combination enhancing film, it is characterised in that the glue layer is
One kind in polyester, epoxy resin, acrylic resin, organosilicon or polyurethane, the thickness of glue layer is 1-3 μm;Institute
One kind that easy following layer choice of material is polyurethane, polyacrylate or petchem is stated, thickness is 20-50 μm.
4. according to claim 1 can double-deck or multiple layer combination combination enhancing film, it is characterised in that the resin is selected from
In epoxy resin, polyurethane, polyacrylic resin one kind.
5. according to claim 1 can double-deck or multiple layer combination combination enhancing film, it is characterised in that the atomizing layer
Mist degree is between 0.1-90%, and fog surface layer hardness is between 3B-6H.
6. according to claim 1 can double-deck or multiple layer combination combination enhancing film, it is characterised in that the oxide skin(coating)
For silicon-base oxide or aluminium base oxide;Oxide layer thicknesses are 20-100nm.