CN107663070A - A kind of antibacterial aerating brick block - Google Patents
A kind of antibacterial aerating brick block Download PDFInfo
- Publication number
- CN107663070A CN107663070A CN201711196109.7A CN201711196109A CN107663070A CN 107663070 A CN107663070 A CN 107663070A CN 201711196109 A CN201711196109 A CN 201711196109A CN 107663070 A CN107663070 A CN 107663070A
- Authority
- CN
- China
- Prior art keywords
- parts
- antibacterial
- brick block
- aerating brick
- clinker
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of antibacterial aerating brick block, comprising：150 160 parts of kaolin, 50 60 parts of river sand powder, 10 12 parts of cement, 20 40 parts of clinker, 15 18 parts of gypsum, 0.5 0.8 parts of aluminium powder, 0.1 0.2 parts of manganese carbonate, 15 18 parts of foaming agent, 34 parts of latex, 0.1 0.3 parts of Nano Silver.Kaolin, river sand powder, cement, clinker, gypsum, aluminium powder, manganese carbonate and foaming agent each component are prepared, manufactured aerated bricks external coating latex and nanometer silver coating by proportioning uniformly mixing by traditional aerated bricks technique.For this antibacterial aerating brick block through research experiment repeatedly, each component is reasonably combined, possess the insulation of excellent performance, antidetonation, processing characteristics etc., its external coating nanometer silver antimicrobial layer, bacterial micro-organism can be prevented to grow, antibacterial surface excellent performance.
Description
Technical field
The present invention relates to building materials technology field, specially a kind of antibacterial aerating brick block.
Background technology
Air-entrained concrete building block abbreviation aerated bricks, is to pass through autoclave at high temperature by steam pressurized manufactured concrete block
The air-entrained concrete building block of apparatus and process production." aerated bricks " can be understood as a simplified or general title.
Its product scope covered more greatly, that is, should will use the brick product of other various technique productions including steam pressure.Aerating
Brick has the characteristics that from heavy and light, thermal and insulating performance is good, shock resistance is strong, processing characteristics is good.
Traditional aerating brick block does not have fungistatic coating, is grown in moist local time one, its easy micro- life of breed bacteria volume
Thing, it is impossible to meet multiple demand.
The content of the invention
It is an object of the invention to strengthen the anti-microbial property of aerated bricks, there is provided a kind of antibacterial aerating brick block.
To reach above-mentioned purpose, the technical scheme that uses for：
A kind of antibacterial aerating brick block, it is made up of following parts by weight component：
Kaolin 150-160 parts,
River sand powder 50-60 parts,
Cement 10-12 parts,
Clinker 20-40 parts,
Gypsum 15-18 parts,
Aluminium powder 0.5-0.8 parts,
Manganese carbonate 0.1-0.2 parts,
Foaming agent 15-18 parts,
Latex 3-4 parts,
Nano Silver 0.1-0.3 parts.
Further, described antibacterial aerating brick block, is made up of following parts by weight component：
155 parts of kaolin,
55 parts of river sand powder,
11 parts of cement,
30 parts of clinker,
16 parts of gypsum,
0.7 part of aluminium powder,
0.2 part of manganese carbonate,
16 parts of foaming agent,
4 parts of latex,
0.2 part of Nano Silver.
Kaolin, river sand powder, cement, clinker, gypsum, aluminium powder, manganese carbonate and foaming agent each component are uniformly mixed by proportioning,
Prepared by traditional aerated bricks technique, manufactured aerated bricks external coating latex and nanometer silver coating.
Using having the beneficial effect that for such scheme：This antibacterial aerating brick block is reasonable through research experiment repeatedly, each component
Collocation, possess the insulation of excellent performance, antidetonation, processing characteristics etc., its external coating nanometer silver antimicrobial layer, can prevent
Bacterial micro-organism grows, antibacterial surface excellent performance.
Embodiment
The present invention is further described with reference to embodiment, but the present invention is not limited only to following embodiments, it is anticipated that this
Art personnel are in the case where combining prior art, and there may be many variations for performance.
Embodiment 1
A kind of antibacterial aerating brick block, it is made up of following parts by weight component：
Kaolin 150-160 parts,
River sand powder 50-60 parts,
Cement 10-12 parts,
Clinker 20-40 parts,
Gypsum 15-18 parts,
Aluminium powder 0.5-0.8 parts,
Manganese carbonate 0.1-0.2 parts,
Foaming agent 15-18 parts,
Latex 3-4 parts,
Nano Silver 0.1-0.3 parts.
Particle diameter is exactly accomplished nano level argent simple substance by Nano Silver.Nano Silver particle diameter is right mostly in 25 rans
The tens of kinds of pathogenic microorganisms such as Escherichia coli, gonococcus, chlamydia trachomatis have strong suppression and killing action, and will not
Produce drug resistance.The quilted stockings made of Nano Silver and combing cotton fibre, possesses the effect of good antibacterial deodourizing.Nano silver particles
Due to its good electric conductivity, it is set to occupy extremely important status in microelectronic.Skin effect, the amount of nano silver particles
Sub- dimensional effect etc., make it that also there are some special purposes, such as surface-enhanced Raman application, medical application.1. Nano Silver
It is powdered silver-colored simple substance, particle diameter is less than 100nm, typically between 25-50nm.2. the performance of Nano Silver has direct pass with its particle diameter
System.Research finds that particle diameter is smaller, and bactericidal property is stronger.
Embodiment 2
Antibacterial aerating brick block, it is made up of following parts by weight component：
155 parts of kaolin,
55 parts of river sand powder,
11 parts of cement,
30 parts of clinker,
16 parts of gypsum,
0.7 part of aluminium powder,
0.2 part of manganese carbonate,
06 part of foaming agent,
0.2 part of 4 parts of latex and Nano Silver.
Kaolin, river sand powder, cement, clinker, gypsum, aluminium powder, manganese carbonate and foaming agent each component are uniformly mixed by proportioning,
Prepared by traditional aerated bricks technique, manufactured aerated bricks external coating latex and nanometer silver coating.The antibacterial aerated bricks of the present invention
Through research experiment repeatedly, each component is reasonably combined for building block, possesses the insulation of excellent performance, antidetonation, processing characteristics etc., its
External coating nanometer silver antimicrobial layer, can prevent bacterial micro-organism from growing, antibacterial surface excellent performance.
Claims (2)
1. a kind of antibacterial aerating brick block, it is characterized in that, it is made up of following parts by weight component：
Kaolin 150-160 parts,
River sand powder 50-60 parts,
Cement 10-12 parts,
Clinker 20-40 parts,
Gypsum 15-18 parts,
Aluminium powder 0.5-0.8 parts,
Manganese carbonate 0.1-0.2 parts,
Foaming agent 15-18 parts,
Latex 3-4 parts,
Nano Silver 0.1-0.3 parts.
2. antibacterial aerating brick block according to claim 1, it is characterized in that, it is made up of following parts by weight component：
155 parts of kaolin,
55 parts of river sand powder,
11 parts of cement,
30 parts of clinker,
16 parts of gypsum,
0.7 part of aluminium powder,
0.2 part of manganese carbonate,
06 part of foaming agent,
4 parts of latex,
0.2 part of Nano Silver.