CN107652879A - A kind of long-acting cold galvanizing fire-resistant anticorrosion paint - Google Patents
A kind of long-acting cold galvanizing fire-resistant anticorrosion paint Download PDFInfo
- Publication number
- CN107652879A CN107652879A CN201710988659.6A CN201710988659A CN107652879A CN 107652879 A CN107652879 A CN 107652879A CN 201710988659 A CN201710988659 A CN 201710988659A CN 107652879 A CN107652879 A CN 107652879A
- Authority
- CN
- China
- Prior art keywords
- long
- fire
- acting
- anticorrosion paint
- cold galvanizing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention discloses a kind of long-acting cold galvanizing fire-resistant anticorrosion paint, by weight percentage, is made up of following material：The resins of FR 28, anti-settling agent, defoamer, dispersant, organobentonite, high-purity zinc powder.The present invention is produced by following technical process：In kettle of the liquid material input with stirring, stirring is opened, then solid-state material is slowly put into and is dispersed with stirring uniform (about 10 20 minutes), is packaged as finished product.The present invention is resistant to 400 DEG C of high temperature, to steel component, can carry out long-effective protection.
Description
Technical field
The invention belongs to inorganic modified organic matter technical field, and in particular to a kind of long-acting cold galvanizing high-temperature resistant anti-corrosive applies
Material.
Background technology
Coating is commonly called as painting, and is main film forming substance generally by grease and organic synthetic resin.Because it is organic matter, therefore
Its heat-resisting quantity is poor, easy aging, therefore can not accomplish long-acting durable.The present invention be directed to problem above, and the new production researched and developed
Product.
The content of the invention
The present invention by using fluosilicic acid be modified silester generation fluorination ethyl polysilicate (FR-28 resins) its have it is organic
Thing holds easy working strong point, has inorganic material long-acting (UV resistant, anti-aging) resistant to elevated temperatures speciality again, therefore ensure that this
The performance and feature of invention.
The purpose of invention is realized in：A kind of long-acting cold galvanizing fire-resistant anticorrosion paint by weight percentage, by one
Lower component composition：
A kind of preparation of long-acting cold galvanizing fire-resistant anticorrosion paint, comprises the steps：Liquid material is put into band
In the kettle of stirring, stirring is opened, then solid-state material is slowly put into and is dispersed with stirring uniform (about 10-20 minutes), is packaged as into
Product.
Preferably, the FR-28 resins are fluorination ethyl polysilicate, are the Special Resins of our company's research and development, it was both
Flexibility with organic matter, have the characteristics of inorganic heat-resisting heatproof is long-acting durable concurrently again, be the main film forming substance of the present invention, it
Assign product of the present invention long-acting resistant to elevated temperatures effect.It is made by following steps：Take parts by weight 30-80 part silester (dioxies
SiClx content opens stirring, then slowly puts into 2-25 parts for 28%), and in parts by weight 15-30 parts isopropanol input reactor
Concentration is 35% fluosilicic acid, and 1-5 hours are reacted in 25-80 DEG C of range temperature, forms fluorination ethyl polysilicate (FR-28 trees
Fat).
Preferably, the anti-settling agent is the anti-settling agent of BYK companies 411.
Preferably, the dispersant is 122 wetting dispersing agents that BYK companies produce.
Preferably, the defoamer is 145 defoamers that BYK companies produce.
Preferably, the anti-settling agent is that De Qian companies produce E202P anti-settling agents
Preferably, the zinc powder is high-purity micro-fine zinc powder, the mesh of fineness≤3000, purity >=99%.
A kind of long-acting cold galvanizing fire-resistant anticorrosion paint of the present invention is the zinc content pole using silicate as main film forming substance
Height, high temperature resistant, antirust function is strong, anti-ultraviolet aging, has long-acting heatproof antiseptic effect.
Embodiment
With reference to embodiment, the invention will be further described：
Embodiment 1
A kind of preparation of long-acting cold galvanizing fire-resistant anticorrosion paint, comprises the steps：Liquid material is put into band
In the kettle of stirring, stirring is opened, then solid-state material is slowly put into and is dispersed with stirring uniform (about 10-20 minutes), is packaged as into
Product.
Embodiment 2
A kind of preparation of long-acting cold galvanizing fire-resistant anticorrosion paint, comprises the steps：Liquid material is put into band
In the kettle of stirring, stirring is opened, then solid-state material is slowly put into and is dispersed with stirring uniform (about 10-20 minutes), is packaged as into
Product.
Embodiment 3
A kind of preparation of long-acting cold galvanizing fire-resistant anticorrosion paint, comprises the steps：Liquid material is put into band
In the kettle of stirring, stirring is opened, then solid-state material is slowly put into and is dispersed with stirring uniform (about 10-20 minutes), is packaged as into
Product.
Embodiment 4
A kind of preparation of long-acting cold galvanizing fire-resistant anticorrosion paint, comprises the steps：Liquid material is put into band
In the kettle of stirring, stirring is opened, then solid-state material is slowly put into and is dispersed with stirring uniform (about 10-20 minutes), is packaged as into
Product.
Embodiment 5
A kind of preparation of long-acting cold galvanizing fire-resistant anticorrosion paint, comprises the steps：Liquid material is put into band
In the kettle of stirring, stirring is opened, then solid-state material is slowly put into and is dispersed with stirring uniform (about 10-20 minutes), is packaged as into
Product.
Described above is only the preferred embodiments of the present invention, it is noted that for the ordinary skill people of this area
For member, without departing from the principles of the present invention, some improved modifications can also be made, this is also considered as the guarantor of the present invention
Protect scope.
Claims (7)
1. a kind of long-acting cold galvanizing fire-resistant anticorrosion paint is by weight percentage, it is made up of following material：
A kind of preparation of long-acting cold galvanizing fire-resistant anticorrosion paint, comprises the steps：Liquid material is put into band stirring
Kettle in, open stirring, then solid-state material slowly put into and is dispersed with stirring uniform (about 10-20 minutes), is packaged as finished product.
A kind of 2. long-acting cold galvanizing fire-resistant anticorrosion paint according to claim 1, it is characterised in that：The FR-28 trees
Fat is fluorination ethyl polysilicate, is the Special Resin of our company's research and development, and it had both had the flexibility of organic matter, and had concurrently again inorganic
Heat-resisting heatproof it is long-acting durable the characteristics of, be the present invention main film forming substance, it is long-acting resistant to elevated temperatures that it assigns product of the present invention
Performance.It is made by following steps：Take parts by weight 30-80 parts silester (dioxide-containing silica 28%), and parts by weight 15-
In 30 parts of isopropanol input reactors, stirring is opened, it is 35% fluosilicic acid then slowly to put into 2-25 parts concentration, at 25-80 DEG C
Reaction 1-5 hours in range temperature, form fluorination ethyl polysilicate (FR-28 resins).
A kind of 3. long-acting cold galvanizing fire-resistant anticorrosion paint according to claim 1, it is characterised in that：The anti-settling agent is
The anti-settling agent of BYK companies 411.
A kind of 4. long-acting cold galvanizing fire-resistant anticorrosion paint according to claim 1, it is characterised in that：The dispersant is
122 wetting dispersing agents that BYK companies produce.
A kind of 5. long-acting cold galvanizing fire-resistant anticorrosion paint according to claim 1, it is characterised in that：The defoamer is
145 defoamers that BYK companies produce.
A kind of 6. long-acting cold galvanizing fire-resistant anticorrosion paint according to claim 1, it is characterised in that：The anti-settling agent is
De Qian companies produce E202P anti-settling agents.
A kind of 7. long efficiency high temperature resistance cold galvanizing coating according to claim 1, it is characterised in that：The zinc powder is high-purity
Ultra tiny zinc powder, the mesh of fineness≤3000, purity >=99%.