CN107652541A - A kind of polypropylene medical Transfusion device material - Google Patents
A kind of polypropylene medical Transfusion device material Download PDFInfo
- Publication number
- CN107652541A CN107652541A CN201710916992.6A CN201710916992A CN107652541A CN 107652541 A CN107652541 A CN 107652541A CN 201710916992 A CN201710916992 A CN 201710916992A CN 107652541 A CN107652541 A CN 107652541A
- Authority
- CN
- China
- Prior art keywords
- parts
- transfusion device
- device material
- medical transfusion
- antioxidant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of polypropylene medical Transfusion device material, it is made by the raw material of following parts by weight:50-100 parts of acrylic resin, 5-9 parts of nucleator, 2-4 parts of antistatic additive, 2-8 parts of toughener, 0.2-0.7 part of antioxidant, 0.5-1 part of lubricant, 0.2-0.5 part of antiseptic.The raw material that the present invention uses has good toughness, and mobility is high, and transparency is high, and has added nanometer Ag TiO in raw material2Antiseptic, the effect of making it have antibacterial, use is safer.
Description
Technical field
The present invention relates to transfusion device preparing technical field, and in particular to a kind of polypropylene medical Transfusion device material.
Background technology
With the progress of medical technology, the operation of medical treatment aspect is more and more stricter, and the basis as medical procedure of infusing,
Most of medical procedures are required for using transfusion.At present, the material that the disposable transfusion device used is commonly used is polypropylene, its cost
Low, the preferable transparent polymer material of combination property, but limit it the shortcomings that toughness is poor under its toughness especially low temperature and enter one
Step application and development.How reasonably to prepare high tenacity, the high grade of transparency and the transfusion device material with antibacterial functions has turned into
The study hotspot of modern medical material.
The content of the invention
In view of the above-mentioned problems of the prior art, the present invention provides a kind of polypropylene medical Transfusion device material.
To achieve these goals, the technical solution adopted by the present invention is:
A kind of polypropylene medical Transfusion device material, is made by the raw material of following parts by weight:50-100 parts of acrylic resin, into
5-9 parts of core agent, 2-4 parts of antistatic additive, 2-8 parts of toughener, 0.2-0.7 part of antioxidant, lubricant 0.5-1
Part, 0.2-0.5 part of antiseptic.
Further, the toughener is polycaprolactone.
Further, the antioxidant is phosphite ester kind antioxidant(2,4- di-tert-butyl-phenyls)Tris phosphite.
Further, the lubricant is stearic acid.
Further, the antistatic additive is ethoxy fatty amine.
Further, the nucleator is two (3,4- dimethylbenzylidene) sorbierites.
Further, the antiseptic is nanometer Ag-TiO2。
After said structure, the present invention has the beneficial effect that:
The raw material that the present invention uses has good toughness, and mobility is high, and transparency is high, and has added nanometer Ag-TiO in raw material2
Antiseptic, the effect of making it have antibacterial, use is safer.
Embodiment
Example of the present invention is the description of the invention and can not limit the present invention, in the implication suitable with the present invention
Any change and adjustment with scope, are all considered as within the scope of the invention.
Embodiment 1
A kind of polypropylene medical Transfusion device material, is made by the raw material of following parts by weight:50-100 parts of acrylic resin, into
5-9 parts of core agent, 2-4 parts of antistatic additive, 2-8 parts of toughener, 0.2-0.7 part of antioxidant, lubricant 0.5-1
Part, 0.2-0.5 part of antiseptic.
Wherein, the toughener is polycaprolactone, and the antioxidant is phosphite ester kind antioxidant(2,4- di-t-butyls
Phenyl)Tris phosphite, the lubricant are stearic acid, and the antistatic additive is ethoxy fatty amine, and the nucleator is two
(3,4- dimethylbenzylidene) sorbierite, the antiseptic are nanometer Ag-TiO2。
Embodiment 2
A kind of polypropylene medical Transfusion device material, is made by the raw material of following parts by weight:50-100 parts of acrylic resin, into
5-9 parts of core agent, 2-4 parts of antistatic additive, 2-8 parts of toughener, 0.2-0.7 part of antioxidant, lubricant 0.5-1
Part, 0.2-0.5 part of antiseptic.
Wherein, the toughener is polycaprolactone, and the antioxidant is phosphite ester kind antioxidant(2,4- di-t-butyls
Phenyl)Tris phosphite, the lubricant are stearic acid, and the antistatic additive is ethoxy fatty amine, and the nucleator is two
(3,4- dimethylbenzylidene) sorbierite, the antiseptic are nanometer Ag-TiO2。
Embodiment 3
A kind of polypropylene medical Transfusion device material, is made by the raw material of following parts by weight:50-100 parts of acrylic resin, into
5-9 parts of core agent, 2-4 parts of antistatic additive, 2-8 parts of toughener, 0.2-0.7 part of antioxidant, lubricant 0.5-1
Part, 0.2-0.5 part of antiseptic.
Wherein, the toughener is polycaprolactone, and the antioxidant is phosphite ester kind antioxidant(2,4- di-t-butyls
Phenyl)Tris phosphite, the lubricant are stearic acid, and the antistatic additive is ethoxy fatty amine, and the nucleator is two
(3,4- dimethylbenzylidene) sorbierite, the antiseptic are nanometer Ag-TiO2。
Particular embodiments described above, the purpose of the present invention, technical scheme and beneficial effect are carried out further in detail
Describe in detail it is bright, should be understood that the foregoing is only the present invention specific embodiment, be not intended to limit the invention.This
Invention expands to any new feature disclosed in this manual or any new combination, and any new method for disclosing or
The step of process or any new combination.
Claims (7)
1. a kind of polypropylene medical Transfusion device material, it is characterised in that be made by the raw material of following parts by weight:Acrylic resin
50-100 parts, 5-9 parts of nucleator, 2-4 parts of antistatic additive, 2-8 parts of toughener, 0.2-0.7 part of antioxidant, lubricant
0.5-1 part, 0.2-0.5 part of antiseptic.
2. polypropylene medical Transfusion device material according to claim 1, it is characterised in that the toughener is to gather in oneself
Ester.
3. polypropylene medical Transfusion device material according to claim 1, it is characterised in that the antioxidant is phosphite ester
Kind antioxidant (2,4- di-tert-butyl-phenyl) tris phosphite.
4. polypropylene medical Transfusion device material according to claim 1, it is characterised in that the lubricant is stearic acid.
5. polypropylene medical Transfusion device material according to claim 1, it is characterised in that the antistatic additive is ethoxy
Fatty amine.
6. polypropylene medical Transfusion device material according to claim 1, it is characterised in that the nucleator is two (3,4-
Dimethylbenzylidene) sorbierite.
7. polypropylene medical Transfusion device material according to claim 1, it is characterised in that the antiseptic be nanometer Ag-
TiO2。