CN107649330A - A kind of preparation facilities and preparation technology of non-all standing formula coating barrier film - Google Patents
A kind of preparation facilities and preparation technology of non-all standing formula coating barrier film Download PDFInfo
- Publication number
- CN107649330A CN107649330A CN201710797489.3A CN201710797489A CN107649330A CN 107649330 A CN107649330 A CN 107649330A CN 201710797489 A CN201710797489 A CN 201710797489A CN 107649330 A CN107649330 A CN 107649330A
- Authority
- CN
- China
- Prior art keywords
- roller
- barrier film
- resilient
- formula coating
- standing formula
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention proposes a kind of preparation facilities and preparation technology of non-all standing formula coating barrier film, and the preparation facilities includes:Transfer roller;Surface has the resilient roller being left white, and the resilient roller rolls with the transfer roller to be coordinated;Hard bottom roller, the hard bottom roller rolls with the resilient roller to be coordinated.A kind of preparation facilities of non-all standing formula coating barrier film according to embodiments of the present invention, can form localised application structure smooth, of the same size on barrier film.
Description
Technical field
The present invention relates to a kind of preparation facilities and preparation technology of non-all standing formula coating barrier film.
Background technology
In order to improve the security of lithium battery, prior art is mostly using the coating on polypropylene or polyethene microporous membrane
Inorganic nano-particle that can be stable improves the heat endurance of microporous barrier, and coats all standing formula Polymer Tie-layer, improves
The heat resistance of barrier film and its cohesive force (such as Application No. CN201210000157.5) between lithium battery pole slice.But it polymerize
After thing and electrolyte form gel layer, electrolytic conductivity drops to 10%, is unfavorable for the conduction of lithium ion, increases lithium battery
Internal resistance, influence the multiplying power discharging and cycle performance of lithium battery.
Nowadays lithium battery not only needs the good thermal stability and bonding force between barrier film and electrode, and needs quickly to fill
Electrical property, therefore occur by way of non-all standing formula coats glue-line, non-polymer glue point perforated can realize lithium
Effective transmission of ion, the lithium ion conduction ability of barrier film is improved, so as to improve the charge-discharge performance of lithium battery, extend lithium electricity
The cycle life (such as Application No. CN201710039461.3) in pond.It is to be based on traditional coating method that this kind of technique, which is still, is led to
Cross the appropriate proportioning of polymer and binding agent in glue-line, protect to be formed on glue-line and be randomly distributed but total certain hole of area coverage
Hole, non-all standing formula glue-line is formed, reduce barrier film ventilative loss caused by thickness increase.But it can not be precisely controlled every
The state of the size of individual glue point, the distance of glue point and reunion, therefore the adhesive film of the discrete shape formed, no matter to the quality of production
Control and follow-up coiling quality, all exist influence.
The content of the invention
Present inventors appreciate that in printing technology, ink layer is filled on transfer roller, then printing ink transfer to roller
The upper layer of ink so that roller oils have and be left white, paper makes have what is be left white in roller by the extruding of roller and hard bottom roller
Ink layer is transferred on paper, can form localised application structure smooth, of the same size.Inspired by this, present invention
If people is coated in the preparation of barrier film, it is realized that printing technology is converted into non-all standing formula, can solve above-mentioned prior art
Present in problem, form localised application structure smooth, of the same size.
It is contemplated that at least solves one of technical problem in correlation technique to a certain extent.
Therefore, it is an object of the present invention to propose a kind of preparation facilities of non-all standing formula coating barrier film.
Another object of the present invention is to propose a kind of preparation technology of non-all standing formula coating barrier film.
The preparation facilities of non-all standing formula coating barrier film according to embodiments of the present invention, including:
Transfer roller;
Surface has the resilient roller being left white, and the resilient roller rolls with the transfer roller to be coordinated;
Hard bottom roller, the hard bottom roller rolls with the resilient roller to be coordinated.
Advantageously, when the transfer roller is anilox roll, the resilient roller is the block roller that surface has salient point.
Advantageously, the preparation facilities of described non-all standing formula coating barrier film also includes hopper, the hopper and the net
Line roller is connected.
Advantageously, the salient point corrodes to be formed using photosensitive resin, or the salient point is formed using rubber laser engraving.
Advantageously, when the transfer roller is smooth roll, the resilient roller is that surface has reeded gravure printing roller.
Advantageously, the preparation facilities of described non-all standing formula coating barrier film also includes flushing roller or gap scraper, institute
State flushing roller or gap scraper and the smooth roll is combined.
Advantageously, the groove corrodes to be formed using photosensitive resin, or the groove is formed using rubber laser engraving.
Advantageously, the hard bottom roller is vulcanie bottom roller or metal bottom roller.
The preparation technology of non-all standing formula coating barrier film according to embodiments of the present invention, using according to any of the above-described
Non- all standing formula coating barrier film preparation facilities carry out, comprise the following steps:
Transfer roller is driven to roll, so that the surface of transfer roller forms adhesive film;
Make resilient roller roll with transfer roller to coordinate, so that adhesive film is transferred to the non-blank space of resilient roll surface;
Extruding by the barrier film of pre- coated nano ceramic material by resilient roller and hard bottom roller, makes on resilient roll surface
Adhesive film is transferred to the surface of barrier film, forms localised application structure smooth, of the same size.
Advantageously, when the transfer roller is anilox roll, the resilient roller is the block roller that surface has salient point;Work as institute
When to state transfer roller be smooth roll, the resilient roller is that surface has reeded gravure printing roller.
The additional aspect and advantage of the present invention will be set forth in part in the description, and will partly become from the following description
Obtain substantially, or recognized by the practice of the present invention.
Brief description of the drawings
Fig. 1 is the schematic diagram of the preparation facilities of non-all standing formula coating barrier film according to an embodiment of the invention;
Fig. 2 is the schematic diagram of the preparation facilities of non-all standing formula coating barrier film according to another embodiment of the present invention.
Embodiment
Embodiments of the invention are described below in detail, the example of the embodiment is shown in the drawings, wherein from beginning to end
Same or similar label represents same or similar element or the element with same or like function.Below with reference to attached
The embodiment of figure description is exemplary, it is intended to for explaining the present invention, and is not considered as limiting the invention.
Below with reference to the accompanying drawings it is described in detail a kind of preparation of non-all standing formula coating barrier film according to embodiments of the present invention
Device.
Present inventors appreciate that in printing technology, ink layer is filled on transfer roller, then printing ink transfer to roller
The upper layer of ink so that roller oils have and be left white, paper makes have what is be left white in roller by the extruding of roller and hard bottom roller
Ink layer is transferred on paper, can form localised application structure smooth, of the same size.Inspired by this, present invention
If people is coated in the preparation of barrier film, it is realized that printing technology is converted into non-all standing formula, can solve above-mentioned prior art
Present in problem, form localised application structure smooth, of the same size.
As depicted in figs. 1 and 2, the preparation facilities of a kind of non-all standing formula coating barrier film according to embodiments of the present invention, bag
Include:Transfer roller, resilient roller, hard bottom roller 300.
Specifically, the surface of the resilient roller has and is left white, and the resilient roller rolls with the transfer roller to be coordinated.
Hard bottom roller 300 rolls with the resilient roller to be coordinated.Advantageously, hard bottom roller 300 can be vulcanie bottom
Roller or metal bottom roller.
As shown in figure 1, when the transfer roller is anilox roll 110, the resilient roller is the convex print that surface has salient point 211
Roller 210.Advantageously, salient point 211 corrodes to be formed using photosensitive resin, or salient point 211 is formed using rubber laser engraving.This
When, the surface of block roller 210 is left white as the part positioned at salient point below 211.
Advantageously, the preparation facilities of described non-all standing formula coating barrier film also includes hopper 400, hopper 400 and reticulate pattern
Roller 210 is connected.
As shown in Fig. 2 when the transfer roller is smooth roll 120, the resilient roller is the gravure that surface has groove 221
Roller 220.Advantageously, groove 221 corrodes to be formed using photosensitive resin, or groove 221 is formed using rubber laser engraving.Now,
The surface of gravure printing roller 220 is left white as the part beyond groove 221.
Advantageously, the preparation facilities of described non-all standing formula coating barrier film also includes flushing roller 600 or gap scraper
700, flushing roller 600 or gap scraper 700 and smooth roll 120 are combined.
The preparation technology of non-all standing formula coating barrier film according to embodiments of the present invention, comprises the following steps:
Transfer roller is driven to roll, so that the surface of transfer roller forms adhesive film;
Make resilient roller roll with transfer roller to coordinate, so that adhesive film is transferred to the non-blank space of resilient roll surface;
Extruding by the barrier film of pre- coated nano ceramic material by resilient roller and hard bottom roller, makes on resilient roll surface
Adhesive film is transferred to the surface of barrier film, forms localised application structure smooth, of the same size.
More specifically, when the transfer roller is anilox roll 110, the resilient roller is the convex print that surface has salient point 211
Roller 210.Driving anilox roll 110 rolls, so that the surface of anilox roll 110 forms adhesive film.Make block roller 210 and anilox roll
110 roll cooperation, so that adhesive film is transferred on the salient point 211 on the surface of block roller 210, and the surface of block roller 210 is located at
Part (i.e. the blank space of block roller 210) of the salient point below 211 does not have adhesive film then.By pre- coated nano ceramic material every
Film 500 makes the adhesive film on the salient point 211 on the surface of block roller 210 by the extruding of block roller 210 and hard bottom roller 300
The surface of barrier film 500 is transferred to, forms localised application structure smooth, of the same size.Such a mode, suitable for adhesive film thickness
Relatively thin situation.
In other words, using anilox roll material transfer structure, one layer of uniform glued membrane (thinner thickness) is formed.By adjusting anilox roll
Line number, mesh depth, can have the function that adjust film thickness.
On anilox roll opposite, there is the resilient roller that a surface has seamless bump structure.The rollers can pass through sense
Photopolymer resin corrodes to form salient point, or rubber laser direct engraving forms salient point.The highly controllable of salient point, point-like size are controllable.
Contacted by anilox roll with resilient roller, uniform adhesive film in anilox roll is transferred on the salient point of resilient roller.
On resilient roller opposite, there are a vulcanie bottom roller or metal bottom roller.By pre- coated nano ceramic material every
Film can uniformly be transferred to membrane surface by the extruding of resilient roller and bottom roller, the adhesive film of the bump surface of resilient roller, be formed
Localised application structure smooth, of the same size.
And when the transfer roller is smooth roll 120, the resilient roller is the gravure printing roller 220 that surface has groove 221.Drive
Dynamic smooth roll 120 rolls, so that the surface of smooth roll 120 forms adhesive film.Make gravure printing roller 220 roll with smooth roll 120 to coordinate, so that
Adhesive film is transferred in the groove 221 on the surface of gravure printing roller 220, and the surface of gravure printing roller 220 is located at the part beyond groove 221
(i.e. the blank space of gravure printing roller 220 does not have adhesive film then).The barrier film 500 of pre- coated nano ceramic material is passed through into gravure printing roller
220 with the extruding of hard bottom roller 300, the adhesive film in the groove 221 on the surface of gravure printing roller 220 is transferred to the table of barrier film 500
Face, form localised application structure smooth, of the same size.Such a mode, suitable for the thicker situation of adhesive film thickness.
In other words, using smooth roll material transfer structure, form one layer of uniform glued membrane (thickness is thicker).
On smooth roll opposite, there is the resilient roller that a surface has seamless groove structure.The rollers can be by photosensitive
Resin erosion forms groove, or rubber laser direct engraving forms groove.The depth of groove is controllable, point-like size is controllable.It is logical
Cross smooth roll to contact with resilient roller, uniform adhesive film on smooth roll is transferred on the groove of resilient roller.
On resilient roller opposite, there are a vulcanie bottom roller or metal bottom roller.By pre- coated nano ceramic material every
For film by the extruding of resilient roller and bottom roller, the adhesive film in the groove of resilient roller can uniformly be transferred to membrane surface, be formed flat
Localised application structure whole, of the same size.
The present invention substitutes the modes such as existing coating, spraying by the structure of flexible printing, forms uniform, smooth, coated side
Product at any time can quick-adjustsing non-all standing formula glue-line.Production cost is greatly reduced, improves product quality.
In the description of the invention, it is to be understood that term " " center ", " longitudinal direction ", " transverse direction ", " length ", " width ",
" thickness ", " on ", " under ", "front", "rear", "left", "right", " vertical ", " level ", " top ", " bottom " " interior ", " outer ", " up time
The orientation or position relationship of the instruction such as pin ", " counterclockwise ", " axial direction ", " radial direction ", " circumference " be based on orientation shown in the drawings or
Position relationship, it is for only for ease of and describes the present invention and simplify description, rather than indicates or imply that signified device or element must
There must be specific orientation, with specific azimuth configuration and operation, therefore be not considered as limiting the invention.
In addition, term " first ", " second " are only used for describing purpose, and it is not intended that instruction or hint relative importance
Or the implicit quantity for indicating indicated technical characteristic.Thus, define " first ", the feature of " second " can be expressed or
Implicitly include one or more this feature.In the description of the invention, " multiple " are meant that two or more, unless separately
There is clearly specific limit.
In the present invention, unless otherwise clearly defined and limited, term " installation ", " connected ", " connection ", " fixation " etc.
Term should be interpreted broadly, for example, it may be fixedly connected or be detachably connected, or integrally;Can be that machinery connects
Connect or electrically connect;Can be joined directly together, can also be indirectly connected by intermediary, can be in two elements
The connection in portion or the interaction relationship of two elements.For the ordinary skill in the art, can be according to specific feelings
Condition understands the concrete meaning of above-mentioned term in the present invention.
In the present invention, unless otherwise clearly defined and limited, fisrt feature can be with "above" or "below" second feature
It is that the first and second features directly contact, or the first and second features pass through intermediary mediate contact.Moreover, fisrt feature exists
Second feature " on ", " top " and " above " but fisrt feature are directly over second feature or oblique upper, or be merely representative of
Fisrt feature level height is higher than second feature.Fisrt feature second feature " under ", " lower section " and " below " can be
One feature is immediately below second feature or obliquely downward, or is merely representative of fisrt feature level height and is less than second feature.
In the description of this specification, reference term " one embodiment ", " some embodiments ", " example ", " specifically show
The description of example " or " some examples " etc. means specific features, structure, material or the spy for combining the embodiment or example description
Point is contained at least one embodiment or example of the present invention.In this manual, to the schematic representation of above-mentioned term not
Identical embodiment or example must be directed to.Moreover, specific features, structure, material or the feature of description can be with office
Combined in an appropriate manner in one or more embodiments or example.In addition, in the case of not conflicting, the skill of this area
Art personnel can be tied the different embodiments or example and the feature of different embodiments or example described in this specification
Close and combine.
Although embodiments of the invention have been shown and described above, it is to be understood that above-described embodiment is example
Property, it is impossible to limitation of the present invention is interpreted as, one of ordinary skill in the art is within the scope of the invention to above-mentioned implementation
Example is changed, changed, replacing and modification, each falls within protection scope of the present invention.
Claims (10)
- A kind of 1. preparation facilities of non-all standing formula coating barrier film, it is characterised in that including:Transfer roller;Surface has the resilient roller being left white, and the resilient roller rolls with the transfer roller to be coordinated;Hard bottom roller, the hard bottom roller rolls with the resilient roller to be coordinated.
- 2. the preparation facilities of non-all standing formula coating barrier film according to claim 1, it is characterised in that when the transfer roller For anilox roll when, the resilient roller is that surface has the block roller of salient point.
- 3. the preparation facilities of non-all standing formula coating barrier film according to claim 2, it is characterised in that also including hopper, The hopper is connected with the anilox roll.
- 4. the preparation facilities of non-all standing formula coating barrier film according to claim 2, it is characterised in that the salient point uses Photosensitive resin corrodes to be formed, or the salient point is formed using rubber laser engraving.
- 5. the preparation facilities of non-all standing formula coating barrier film according to claim 1, it is characterised in that when the transfer roller For smooth roll when, the resilient roller is that surface has reeded gravure printing roller.
- 6. the preparation facilities of non-all standing formula coating barrier film according to claim 5, it is characterised in that also including flushing roller Or gap scraper, the flushing roller or gap scraper and the smooth roll are combined.
- 7. the preparation facilities of non-all standing formula coating barrier film according to claim 5, it is characterised in that the groove uses Photosensitive resin corrodes to be formed, or the groove is formed using rubber laser engraving.
- 8. the preparation facilities of the non-all standing formula coating barrier film according to any one of claim 1-7, it is characterised in that institute It is vulcanie bottom roller or metal bottom roller to state hard bottom roller.
- 9. a kind of preparation technology of non-all standing formula coating barrier film, it is characterised in that using according to any one of claim 1-8 The preparation facilities of described non-all standing formula coating barrier film is carried out, and is comprised the following steps:Transfer roller is driven to roll, so that the surface of transfer roller forms adhesive film;Make resilient roller roll with transfer roller to coordinate, so that adhesive film is transferred to the non-blank space of resilient roll surface;Extruding by the barrier film of pre- coated nano ceramic material by resilient roller and hard bottom roller, makes the glued membrane on resilient roll surface Layer is transferred to the surface of barrier film, forms localised application structure smooth, of the same size.
- 10. the preparation technology of non-all standing formula coating barrier film according to claim 9, it is characterised in that when the material transfer When roller is anilox roll, the resilient roller is the block roller that surface has salient point;When the transfer roller is smooth roll, the elasticity Roller is that surface has reeded gravure printing roller.