CN107640934A - A kind of wall heat insulation material and preparation method thereof - Google Patents
A kind of wall heat insulation material and preparation method thereof Download PDFInfo
- Publication number
- CN107640934A CN107640934A CN201710906837.6A CN201710906837A CN107640934A CN 107640934 A CN107640934 A CN 107640934A CN 201710906837 A CN201710906837 A CN 201710906837A CN 107640934 A CN107640934 A CN 107640934A
- Authority
- CN
- China
- Prior art keywords
- parts
- stirred
- thickener
- insulation material
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of wall heat insulation material and preparation method thereof, is mainly made up of following raw material：15 30 parts of bentonite, 10 20 parts of cement, 10 20 parts of flyash, 5 10 parts of talcum powder, 20 30 parts of kaolin, 5 10 parts of glass fibre, 25 parts of thickener, 25 parts of curing agent, 13 parts of environment-friendlyadhesive adhesive, 13 parts of foaming agent, 24 parts of potassium permanganate.The present invention is advantageous in that：Formula is reasonable, safety, and green, environmental protection, manufacture craft is simple, lighter in weight, alternative traditional insulation material, and raw material sources are very extensive, has huge market potential.
Description
Technical field
The present invention relates to construction material applied technical field, and in particular to a kind of wall heat insulation material and preparation method thereof.
Background technology
With the progress of science and technology and the raising year by year of living standard, insulation material has become in people's production, life not
One of articles for use that can lack.And the material used at present is not ideal enough in various performances, especially insulation, acid and alkali-resistance,
Weatherability etc. can not meet the needs of people.Traditional building thermal insulation material is disadvantageous in that in the market, proportion
Greatly, thermal conductivity factor is big, and intensity is relatively low, not resistance to compression, easy to aging, is not durable, and easily comes off, and integrated cost is high.
The content of the invention
It is an object of the invention to provide a kind of wall heat insulation material and preparation method thereof, count in parts by weight, mainly by with
Lower raw material is made：Bentonite 15-30 parts, cement 10-20 parts, flyash 10-20 parts, talcum powder 5-10 parts, kaolin 20-30
Part, glass fibre 5-10 parts, thickener 2-5 parts, curing agent 2-5 parts, environment-friendlyadhesive adhesive 1-3 parts, foaming agent 1-3 parts, potassium permanganate 2-4
Part.
It is further preferred that counting in parts by weight, mainly it is made up of following raw material：15 parts of bentonite, 20 parts of cement, fine coal
10 parts of ash, 10 parts of talcum powder, 25 parts of kaolin, 8 parts of glass fibre, 3 parts of thickener, 2 parts of curing agent, 2 parts of environment-friendlyadhesive adhesive, foaming agent
2 parts, 2 parts of potassium permanganate.
Comprise the following steps：
1) bentonite, cement, flyash, talcum powder, kaolin, glass fibre, thickener is weighed by the proportioning to add
It is mixed and stirred for uniformly, being subsequently added into water, stirring and be well mixed in mixer；
2) potassium permanganate and water are converted into mixed liquor；
3) foaming agent is poured into step 1) after being stirred 10-20min, stands 2h；
4) step 3) pours into step 1), is stirred；
5) thickener, curing agent, environment-friendlyadhesive adhesive that the proportioning is added into step 4) mixture are stirred and are well mixed；
6) mixed liquor pours into step 5) and stirred in step 2)；
7) slurry being stirred is poured into mould, compaction moulding；
8) it is stripped after placing 50-80min, dries, produce.
The present invention is advantageous in that：Formula is reasonable, safety, and green, environmental protection, manufacture craft is simple, lighter in weight, can
Traditional insulation material is substituted, and raw material sources are very extensive, have huge market potential.
Embodiment
In order to deepen the understanding of the present invention and understanding, the present invention is made further with reference to embodiment
Illustrate and introduce.
Embodiment 1
A kind of wall heat insulation material and preparation method thereof, is counted in parts by weight, is mainly made up of following raw material：Bentonite 15
Part, 20 parts of cement, 10 parts of flyash, 10 parts of talcum powder, 25 parts of kaolin, 8 parts of glass fibre, 3 parts of thickener, 2 parts of curing agent,
2 parts of environment-friendlyadhesive adhesive, 2 parts of foaming agent, 2 parts of potassium permanganate.
Comprise the following steps：
1) bentonite, cement, flyash, talcum powder, kaolin, glass fibre, thickener is weighed by the proportioning to add
It is mixed and stirred for uniformly, being subsequently added into water, stirring and be well mixed in mixer；
2) potassium permanganate and water are converted into mixed liquor；
3) foaming agent is poured into step 1) after being stirred 10min, stands 2h；
4) step 3) pours into step 1), is stirred；
5) thickener, curing agent, environment-friendlyadhesive adhesive that the proportioning is added into step 4) mixture are stirred and are well mixed；
6) mixed liquor pours into step 5) and stirred in step 2)；
7) slurry being stirred is poured into mould, compaction moulding；
8) it is stripped after placing 50min, dries, produce.
Embodiment 2
A kind of wall heat insulation material and preparation method thereof, is counted in parts by weight, is mainly made up of following raw material：Bentonite 30
Part, 10 parts of cement, 15 parts of flyash, 5 parts of talcum powder, 20 parts of kaolin, 8 parts of glass fibre, 2 parts of thickener, 2 parts of curing agent,
3 parts of environment-friendlyadhesive adhesive, 3 parts of foaming agent, 2 parts of potassium permanganate.
Comprise the following steps：
1) bentonite, cement, flyash, talcum powder, kaolin, glass fibre, thickener is weighed by the proportioning to add
It is mixed and stirred for uniformly, being subsequently added into water, stirring and be well mixed in mixer；
2) potassium permanganate and water are converted into mixed liquor；
3) foaming agent is poured into step 1) after being stirred 20min, stands 2h；
4) step 3) pours into step 1), is stirred；
5) thickener, curing agent, environment-friendlyadhesive adhesive that the proportioning is added into step 4) mixture are stirred and are well mixed；
6) mixed liquor pours into step 5) and stirred in step 2)；
7) slurry being stirred is poured into mould, compaction moulding；
8) it is stripped after placing 80min, dries, produce.
Claims (3)
1. a kind of wall heat insulation material and preparation method thereof, it is characterised in that count in parts by weight, mainly by following raw material system
Into：Bentonite 15-30 parts, cement 10-20 parts, flyash 10-20 parts, talcum powder 5-10 parts, kaolin 20-30 parts, glass fibers
Tie up 5-10 parts, thickener 2-5 parts, curing agent 2-5 parts, environment-friendlyadhesive adhesive 1-3 parts, foaming agent 1-3 parts, potassium permanganate 2-4 parts.
2. a kind of wall heat insulation material according to claim 1 and preparation method thereof, it is characterised in that in parts by weight
Meter, is mainly made up of following raw material：15 parts of bentonite, 20 parts of cement, 10 parts of flyash, 10 parts of talcum powder, 25 parts of kaolin, glass
8 parts of glass fiber, 3 parts of thickener, 2 parts of curing agent, 2 parts of environment-friendlyadhesive adhesive, 2 parts of foaming agent, 2 parts of potassium permanganate.
3. a kind of wall heat insulation material according to claim 1 and preparation method thereof, it is characterised in that including following step
Suddenly：
1) bentonite, cement, flyash, talcum powder, kaolin, glass fibre, thickener are weighed by the proportioning and adds stirring
It is mixed and stirred for uniformly, being subsequently added into water, stirring and be well mixed in machine；
2) potassium permanganate and water are converted into mixed liquor；
3) foaming agent is poured into step 1) after being stirred 10-20min, stands 2h；
4) step 3) pours into step 1), is stirred；
5) thickener, curing agent, environment-friendlyadhesive adhesive that the proportioning is added into step 4) mixture are stirred and are well mixed；
6) mixed liquor pours into step 5) and stirred in step 2)；
7) slurry being stirred is poured into mould, compaction moulding；
8) it is stripped after placing 50-80min, dries, produce.