CN107634209A - A kind of positive electode of lead battery lead plaster - Google Patents
A kind of positive electode of lead battery lead plaster Download PDFInfo
- Publication number
- CN107634209A CN107634209A CN201710869058.3A CN201710869058A CN107634209A CN 107634209 A CN107634209 A CN 107634209A CN 201710869058 A CN201710869058 A CN 201710869058A CN 107634209 A CN107634209 A CN 107634209A
- Authority
- CN
- China
- Prior art keywords
- parts
- lead
- carbon nano
- fiber
- sulfuric acid
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of positive electode of lead battery lead plaster, including following components, each component parts by weight are:75 85 parts of lead powder, 10 20 parts of sulfuric acid, 8 15 parts of deionized water, 0.5 1.5 parts of carbon nano-fiber, 0.1 1.2 parts of polyacrylic acid, 0.05 0.15 parts of polytetrafluoroethylene (PTFE).Polytetrafluoroethylene (PTFE), carbon nano-fiber additive in the present invention, merged with lead plaster active material, the electric conductivity of positive plate can effectively be improved and keep the structure of active material, polyacrylic acid protects liquid stability simultaneously and long-time acid resistance is good, ensure required sulfuric acid during high-rate battery discharge, by the optimum organization of multiple additives, the cold starting performance of lead accumulator is substantially improved.
Description
Technical field
The present invention relates to lead accumulator field, and in particular to a kind of positive electode of lead battery lead plaster.
Background technology
Heavy-current discharge performance is the important parameter of automotive lead-acid battery under low temperature.It is right with the raising of automotive performance
The requirement of lead-acid battery low-temperature high-current discharge performance also more and more higher.
The reason for influenceing automobile using lead battery cold-start performance is mainly internal resistance of cell increase under low temperature, and electrolysis fluid viscosity increases
Greatly, SO4 2-Ion diffusion is difficult, in addition, consuming SO during heavy-current discharge4 2-Speed quickly, SO needed for reaction in pole plate4 2-Amount
It cannot supply in time.Make for the influence calcium alloy of lead additive and electrode plate structure to lead-acid accumulator cold-start performance positive and negative
The maintenance-free battery of grid also exist one between inscribe, i.e., using a period of time after, impedance is increasingly generated between grid and lead plaster
Big barrier layer, the cold-start performance of battery life middle and later periods is set drastically to decline.The major measure for improving cold-start performance is to subtract
Baby battery internal resistance, increase acid content in pole plate lead plaster.
The content of the invention
The present invention is in order to overcome drawbacks described above present in prior art, there is provided one kind can reduce the internal resistance of cell, increase
Add the positive electode of lead battery lead plaster of acid content in pole plate lead plaster.
To solve the above problems, a kind of positive electode of lead battery lead plaster proposed by the present invention, including following components, each component weight
Measuring number is:Lead powder 75-85 parts, sulfuric acid 10-20 parts, deionized water 8-15 parts, carbon nano-fiber 0.5-1.5 parts, polyacrylic acid
0.1-1.2 parts, polytetrafluoroethylene (PTFE) 0.05-0.15 parts.
Preferably, the positive electode of lead battery lead plaster, including following components, each component parts by weight are:Lead powder 80-85
Part, sulfuric acid 10-15 parts, deionized water 8-12 parts, carbon nano-fiber 0.5-1 parts, polyacrylic acid 0.1-0.8 parts, polytetrafluoroethylene (PTFE)
0.05-0.1 parts.
Preferably, the positive electode of lead battery lead plaster, including following components, each component parts by weight are:82 parts of lead powder, sulphur
12 parts of acid, 10 parts of deionized water, 0.8 part of carbon nano-fiber, 0.5 part of polyacrylic acid, 0.08 part of polytetrafluoroethylene (PTFE).
Preferably, the lead powder is Daojin lead powder or Barton oxide, and the sulfuric acid mass percent concentration is 48-80%.
In the present invention, the polyacrylic acid, protects liquid stability and long-time acid resistance is good, is can absorb in lead plaster substantial amounts of
Sulfuric acid, the porosity of lead plaster is improved, the sulfuric acid being badly in need of when providing heavy-current discharge in time, so as to extend high-multiplying power discharge time and electricity
The life-span in pond, and improve battery cold starting performance.
In the present invention, the polytetrafluoroethylene (PTFE) has good cohesive, forms elastic web knot after solidification in lead plaster
Structure, ensure the structure of active material in charge and discharge process, reduce active material softening, come off.
In the present invention, the carbon nano-fiber is a diameter of 50~200nm, and draw ratio is 100~500 new carbon materials
Material.It has filled up conventional carbon fiber (a diameter of 7~10 μm) and single-walled carbon nanotube (SWNTs) (diameter is about 1nm) and more walls
Breach in CNT (MWNTs) (a diameter of 1~50nm) size, there is higher intensity, modulus, draw ratio, thermostabilization
The features such as property, chemism, electric conductivity;In addition, carbon nano-fiber has definitely in cost and yield compared with CNT
Advantage.Carbon nano-fiber shows preferable electric conductivity, mitigates electrode polarization, reduces the internal resistance of cell, improves active material profit
With rate, extend lead accumulator cycle life.Meanwhile hole shape and porosity are kept in charge and discharge process, have positive electrode active material
There are higher a formability and utilization rate of active matter, there is larger capacity, positive active material network structure during high-multiplying power discharge
It is stable.
The present invention is had the advantages that compared with prior art and advantage:
Polytetrafluoroethylene (PTFE), the carbon nano-fiber additive of the present invention, merges with lead plaster active material, can effectively improve
The electric conductivity of positive plate and the structure for keeping active material, while polyacrylic acid protects liquid stability and long-time acid resistance is good, protects
Required sulfuric acid when demonstrate,proving high-rate battery discharge, by the optimum organization of multiple additives, substantially improves the cold of lead accumulator and opens
Dynamic performance and the cycle life for extending battery.
Embodiment
Below in conjunction with specific embodiment, the present invention is described in further detail:
Embodiment 1
A kind of positive electode of lead battery lead plaster, including following components, each component parts by weight are:75 parts of lead powder, 20 parts of sulfuric acid,
12 parts of deionized water, 1.5 parts of carbon nano-fiber, 0.8 part of polyacrylic acid, 0.05 part of polytetrafluoroethylene (PTFE).
Embodiment 2
A kind of positive electode of lead battery lead plaster, including following components, each component parts by weight are:80 parts of lead powder, sulfuric acid part 10,
8 parts of deionized water, 0.5 part of carbon nano-fiber, 1.2 parts of polyacrylic acid, 0.1 part of polytetrafluoroethylene (PTFE).
Embodiment 3
A kind of positive electode of lead battery lead plaster, including following components, each component parts by weight are:82 parts of lead powder, 12 parts of sulfuric acid,
10 parts of deionized water, 0.8 part of carbon nano-fiber, 0.5 part of polyacrylic acid, 0.08 part of polytetrafluoroethylene (PTFE).
Embodiment 4
A kind of positive electode of lead battery lead plaster, including following components, each component parts by weight are:85 parts of lead powder, 15 parts of sulfuric acid,
15 parts of deionized water, 1 part of carbon nano-fiber, 0.1 part of polyacrylic acid, 0.15 part of polytetrafluoroethylene (PTFE).
Pole plate is made according to above example 1 to 4 and cream, is tested after assembled battery, and with existing lead acid storage battery
Pond is contrasted, and battery low-temperature cool starting of the invention improves 35-40%, life 20~30%.
Finally illustrate, the above embodiments are merely illustrative of the technical solutions of the present invention and it is unrestricted, although with reference to compared with
The present invention is described in detail good embodiment, it will be understood by those within the art that, can be to the skill of the present invention
Art scheme is modified or equivalent substitution, and without departing from the objective and scope of technical solution of the present invention, it all should cover at this
In the right of invention.
Claims (4)
1. a kind of positive electode of lead battery lead plaster, it is characterised in that including following components, each component parts by weight are:Lead powder 75-85
Part, sulfuric acid 10-20 parts, deionized water 8-15 parts, carbon nano-fiber 0.5-1.5 parts, polyacrylic acid 0.1-1.2 parts, polytetrafluoroethyl-ne
Alkene 0.05-0.15 parts.
2. positive electode of lead battery lead plaster according to claim 1, it is characterised in that including following components, each component weight
Number is:Lead powder 80-85 parts, sulfuric acid 10-15 parts, deionized water 8-12 parts, carbon nano-fiber 0.5-1 parts, polyacrylic acid 0.1-
0.8 part, polytetrafluoroethylene (PTFE) 0.05-0.1 parts.
3. positive electode of lead battery lead plaster according to claim 1, it is characterised in that including following components, each component weight
Number is:82 parts of lead powder, 12 parts of sulfuric acid, 10 parts of deionized water, 0.8 part of carbon nano-fiber, 0.5 part of polyacrylic acid, polytetrafluoroethyl-ne
0.08 part of alkene.
4. the positive electode of lead battery lead plaster according to any one of claim 1-3, it is characterised in that the lead powder is Shimadzu
Lead powder or Barton oxide, the sulfuric acid mass percent concentration are 48-80%.