CN107633898A - A kind of computer composite cable - Google Patents
A kind of computer composite cable Download PDFInfo
- Publication number
- CN107633898A CN107633898A CN201710787544.0A CN201710787544A CN107633898A CN 107633898 A CN107633898 A CN 107633898A CN 201710787544 A CN201710787544 A CN 201710787544A CN 107633898 A CN107633898 A CN 107633898A
- Authority
- CN
- China
- Prior art keywords
- square
- cable core
- added
- circular arc
- skeleton
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
Claims (4)
- A kind of 1. computer composite cable, it is characterised in that:It is square square rubber skeleton to include cross section, square 1/4 circular arc rubber separator is respectively connected between the middle part of the adjacent interior plate of the inside each two of rubber skeleton, in square rubber The center position of glue skeleton is provided with data cable core, the outer wall of the circular arc rubber separator of wall contacts 1/4 of data cable core, every Individual 1/4 circular arc rubber separator is provided with control cable core with the interior intracavitary that square rubber skeleton interior plate surrounds, in square rubber bone Be coated with successively on the outside of frame porcelain fireproof composite band binding layer, mouse bite preventing wire armor, carbon black paper insulation screen, Nanometer EP rubbers inner restrictive coating and external sheath layer, set between porcelain fireproof composite band binding layer and square rubber skeleton There are multiple open column shape elastic center bodies, power supply core is provided with inside each open column shape elastic center body.
- A kind of 2. computer composite cable according to claim 1, it is characterised in that:Described data cable core includes Data cable core and the cross-linked ethylene TFE copolymer insulating layer of thin-film and Kevlar being coated on successively on the outside of data core Fiber braiding layer.
- A kind of 3. computer composite cable according to claim 1, it is characterised in that:Described control cable core includes Control conductor and the PAEK band lapping layer of the resistance to environmental attack ability of the high temperature resistant being coated on successively on the outside of control conductor, Carbon bellows and nanometer polyimide covercoat.
- A kind of 4. computer composite cable according to claim 2, it is characterised in that:Described cross-linked ethylene tetrafluoro second Alkene copolymer insulating layer of thin-film is made up of the raw material of following weight parts:Talcum powder 6-8, ethylene-tetrafluoroethylene copolymer 150-170, divinylbenzene 3-4, pyromellitic acid anhydride 1-2, N- first Base pyrrolidones 20-30, terpinol 10-14, phosphorus trichloride 6-8, absolute ethyl alcohol 10-13, calcium ricinoleate 0.8-1, acrylamide 10-14, ammonium persulfate 0.6-0.8, precipitated calcium carbonate 3-5, silane coupler kh550 1-3, zinc stearate 2-4;The preparation method of described cross-linked ethylene TFE copolymer insulating layer of thin-film comprises the following steps:(1)Talcum powder, stearic acid mixing are taken, the insulated and stirred 10-20 minutes at 50-60 DEG C, is added to above-mentioned N- methylpyrroles In alkanone, stir to normal temperature, obtain alkanone solution;(2)Precipitated calcium carbonate, calcium ricinoleate mixing are taken, is added in above-mentioned absolute ethyl alcohol, stirs, be sent to reactor In, alkanone solution is added, is stirred, phosphorus trichloride is added dropwise, the insulated and stirred 1-2 hours at 65-70 DEG C, discharging, must be esterified Flame-proof material;(3)Pyromellitic acid anhydride, acrylamide mixing are taken, is added in the deionized water of 20-30 times of compound weight, stirs Uniformly, it is sent in reactor, is passed through nitrogen, regulation temperature of reaction kettle is 60-65 DEG C, adds ammonium persulfate, insulated and stirred 3-4 Hour, discharging, obtain acid doping polymer;(4)Silane coupler kh550 is taken, is added in terpinol, is sent in 150-160 DEG C of oil bath, adds ethene-tetrafluoro Ethylene copolymer, insulated and stirred 20-30 minutes, discharging, obtain ammonification polymer;(5)Divinylbenzene is taken, is added in the isopropanol of 4-6 times of its weight, stirs, obtains crosslinking agent alcohol liquid;(6)Above-mentioned acid doping polymer, ammonification mixed with polymers are taken, rise temperature is 55-60 DEG C, ultrasonic 30-40 minutes, is added Flame-proof material is esterified, rise temperature is 75-80 DEG C, adds above-mentioned crosslinking agent alcohol liquid, insulated and stirred 2-3 hours, with remaining each raw material Mixing, stirs, through film blow molding machine blow molding, produces the cross-linked ethylene TFE copolymer insulating layer of thin-film.