CN107626864A - 空心锻件的锻造方法 - Google Patents

空心锻件的锻造方法 Download PDF

Info

Publication number
CN107626864A
CN107626864A CN201710720557.6A CN201710720557A CN107626864A CN 107626864 A CN107626864 A CN 107626864A CN 201710720557 A CN201710720557 A CN 201710720557A CN 107626864 A CN107626864 A CN 107626864A
Authority
CN
China
Prior art keywords
forging
frustum
cone
drift
heating
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201710720557.6A
Other languages
English (en)
Inventor
吴海玲
何圣嘉
何拥军
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
LIUZHOU KEERTE FORGING MACHINERY Co Ltd
Original Assignee
LIUZHOU KEERTE FORGING MACHINERY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by LIUZHOU KEERTE FORGING MACHINERY Co Ltd filed Critical LIUZHOU KEERTE FORGING MACHINERY Co Ltd
Priority to CN201710720557.6A priority Critical patent/CN107626864A/zh
Publication of CN107626864A publication Critical patent/CN107626864A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种空心锻件的锻造方法，涉及机械加工技术领域；包括下料、加热、镦粗、成型、再加热、冲上孔、冲下孔、冲芯料等工序。本发明可以解决目前空心锻件采用传统锻造方修正法造成的锻件尺寸难以达到技术要求或材料浪费的问题。

Description

空心锻件的锻造方法
技术领域
本发明涉及机械加工技术领域，尤其是一种空心锻件的锻造方法。
背景技术
空心锻件是常见的锻件，一般采用将棒料镦粗成圆饼坯，再进行加热用冲头进行双面冲孔的方式制得；要制成直径高度比1.5以下或冲通孔直径与饼坯直径比在0.3以上的空心锻件时，如果仍然采用常规的镦粗加双面冲孔的方法，在冲孔位置锻件会产生严重的冲孔拉缩现象，使得到的锻件尺寸达不到技术要求，而产生不合格品；这防止这种拉缩现象，修正的方法一般分成切削法和冲小孔法，切削法就是切削去拉缩部位的高度，保留没有拉缩的部分，这种方法并不能完全消除拉缩带来的缺陷；冲小孔法就是变冲大孔为冲小孔，然后通过机械加工扩孔来达到技术要求，这种方法显而易见是浪费材料，增加加工成本。
发明内容
本发明的目的是提供一种空心锻件的锻造方法，它可以解决目前空心锻件采用传统锻造方修正法造成的锻件尺寸难以达到技术要求或材料浪费的问题。
为了解决上述问题，本发明采用的技术方案是：包括以下步骤：
1）下料：选取适当直径的棒料锯成一定长度的棒料段；
2）加热：将料段在加热炉内加热，加热温度控制在1150℃±50℃并保温1.5小时~2小时，确保料段内外温度均匀；
3）镦粗：将加热好的棒料镦粗至原高度的3/4，形成腰鼓形的料坯；
4）成型：将腰鼓形的料坯在锻锤打击下，慢慢形成圆锥台形状的锻坯，高度保持原高度；
5）再加热：将圆锥台形状的锻坯送入加热炉内加热，加热温度控制在1150℃±50℃并保温2小时，确保圆锥台锻坯的内外温度均匀一致；
6）冲上孔：将圆锥台大端朝上，放置在模具内，用长冲头进行冲孔；
7）冲下孔：将圆锥台翻转，放置在模具内，用短冲头进行冲孔，两孔之间保留一定厚度的芯料；
8）冲芯料：用芯料冲头冲去两孔之间的芯料；即得到空心锻件。
以上技术方案中，更进一步的方案可以是：步骤6）所用冲头的长度等于圆锥台锻坯高度的2/3；步骤7）所用冲头的长度等于圆锥台锻坯高度的1/3。
进一步的：步骤3）和步骤4）采用锻锤。
由于采用了上述技术方案，本发明与现有技术相比具有如下有益效果：
1、本发明通过将棒料预镦成圆锥台形状的料坯，可以克服冲大孔给锻件带来的拉缩现象，完全杜绝了空心锻件冲大孔时需进行修正的方法，节省了原材料和加工时间。
附图说明
图1是本发明预制锻坯的示意图。
图2是本发明空心锻件制作完成的示意图。
具体实施方式
下面结合附图和实施例对本发明做进一步详述：
这种空心锻件的锻造方法，包括以下步骤：
1）下料：选取适当直径的棒料锯成一定长度的棒料段；
2）加热：将料段在加热炉内加热，加热温度控制在1150℃±50℃并保温1.5小时~2小时，确保料段内外温度均匀；
3）镦粗：将加热好的棒料镦粗至原高度的3/4，形成腰鼓形的料坯；
4）成型：将腰鼓形的料坯在锻锤打击下，慢慢形成圆锥台形状的锻坯，高度保持原高度；
5）再加热：将圆锥台形状的锻坯送入加热炉内加热，加热温度控制在1150℃±50℃并保温2小时，确保圆锥台锻坯的内外温度均匀一致；
6）冲上孔：将圆锥台大端朝上，放置在模具3内，用长冲头进行冲孔；如图1所示，图1中，1为坯料；2为冲头；3为模具；
7）冲下孔：将圆锥台翻转，放置在模具3内，用短冲头进行冲孔，两孔之间保留一定厚度的芯料；
8）冲芯料：用芯料冲头冲去两孔之间的芯料；即得到空心锻件，如图2所示。
步骤6）所用冲头的长度等于圆锥台锻坯高度的2/3；步骤7）所用冲头的长度等于圆锥台锻坯高度的1/3。
步骤3）和步骤4）采用锻锤进行。

Claims (3)

1.一种空心锻件的锻造方法，其特征在于：包括以下步骤：
1）下料：选取适当直径的棒料锯成一定长度的棒料段；
2）加热：将料段在加热炉内加热，加热温度控制在1150℃±50℃并保温1.5小时~2小时，确保料段内外温度均匀；
3）镦粗：将加热好的棒料镦粗至原高度的3/4，形成腰鼓形的料坯；
4）成型：将腰鼓形的料坯在锻锤打击下，慢慢形成圆锥台形状的锻坯，高度保持原高度；
5）再加热：将圆锥台形状的锻坯送入加热炉内加热，加热温度控制在1150℃±50℃并保温2小时，确保圆锥台锻坯的内外温度均匀一致；
6）冲上孔：将圆锥台大端朝上，放置在模具内，用长冲头进行冲孔；
7）冲下孔：将圆锥台翻转，放置在模具内，用短冲头进行冲孔，两孔之间保留一定厚度的芯料；
8）冲芯料：用芯料冲头冲去两孔之间的芯料；即得到空心锻件。
2.根据权利要求1所述的空心锻件的锻造方法，其特征在于：步骤6）所用冲头的长度等于圆锥台锻坯高度的2/3；步骤7）所用冲头的长度等于圆锥台锻坯高度的1/3。
3.根据权利要求1或2所述的空心锻件的锻造方法，其特征在于：步骤3）和步骤4）采用锻锤。
CN201710720557.6A 2017-08-21 2017-08-21 空心锻件的锻造方法 Pending CN107626864A (zh)