CN107619240A - A kind of inorganic putty and its production method - Google Patents
A kind of inorganic putty and its production method Download PDFInfo
- Publication number
- CN107619240A CN107619240A CN201710998239.6A CN201710998239A CN107619240A CN 107619240 A CN107619240 A CN 107619240A CN 201710998239 A CN201710998239 A CN 201710998239A CN 107619240 A CN107619240 A CN 107619240A
- Authority
- CN
- China
- Prior art keywords
- parts
- inorganic putty
- inorganic
- putty
- production method
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of inorganic putty, it is made up of following raw material according to parts by weight：Portland cement：100 parts；Interfacial agents：15 25 parts；China clay：38 56 parts；Land plaster：5 10 parts；A kind of production method of inorganic putty, the production method of the inorganic putty comprise the following steps：S1；Stirred under normal pressure；S2：Packaging.Inorganic putty is a kind of grey powder material, the fire resisting wall after it is mixed with water available for the holes blocking of electric wire or as electric wire tunnel.A kind of novel inorganic putty, mixed by high temperature resistant inorganic material and the solid material of speed, inorganic putty can solidify rapidly after being reconciled with a certain proportion of clear water, the inorganic putty has tasteless, nontoxic, fire prevention, oil resistance, suitable for the closure between cable penetration hole, it can also make the box filled plugging material of ships cable.
Description
Technical field
The present invention relates to inorganic putty technical field, specially a kind of inorganic putty and its production method.
Background technology
Inorganic putty is a kind of grey powder material, after it is mixed with water available for electric wire holes blocking or
Fire resisting wall as electric wire tunnel.A kind of novel inorganic putty, mixed by high temperature resistant inorganic material and the solid material of speed, it is inorganic
Putty can solidify rapidly after being reconciled with a certain proportion of clear water, and the inorganic putty has tasteless, nontoxic, fire prevention, oil resistance, is applicable
Closure between cable penetration hole, it can also make the box filled plugging material of ships cable, its oxygen index (OI) is 100, is a kind of noninflammability
Material, fire resistance period can effectively prevent flame from altering and prolong combustion up to more than 3 hours.Inorganic putty is also known as fireproofing inorganic fragment of brick, is
It is made up of non-automatic incombustible material, there is the characteristics of rapid curing, be commonly called as fire proofing tile.Inorganic putty is a kind of the inorganic stifled of non-ignitable waterproof
Material.Their great advantage is easy for construction, and fire protecting performance is good, nontoxic, will not also discharge toxic gas or other at high temperature
Flue gas.Suitable for the cable of the industry indoor and outdoors such as industrial and mining enterprises' electric power, petrochemical industry, metallurgy, chemical industry, telecommunications, main stor(e)y building, shipbuilding
The fireproof blocking of ditch, cable penetration hole, play a part of preventing electrical fire or miscellaneous cause sprawling.
The content of the invention
The invention aims to solve shortcoming present in prior art, and a kind of inorganic putty proposed and its life
Production method.
To achieve the above object, the present invention provides following technical scheme：
A kind of inorganic putty, is made up of following raw material according to parts by weight：
Portland cement：100 parts；
Interfacial agents：15 parts；
China clay：38 parts；
Land plaster：5 parts；
Preferably, the portland cement.
Preferably, the china clay particle diameter is 250 mesh.
A kind of production method of inorganic putty as claimed in claim 1, it is characterised in that：The production method of the inorganic putty
Comprise the following steps：
S1：Stirred under normal pressure：Portland cement：100 parts；Interfacial agents：15 parts；China clay：38 parts；Land plaster：5 parts；Stir
Mix 30 minutes to 50 minutes, that is, can obtain inorganic putty；
S2：Packaging：S1 product is packed according to specification requirement.
A kind of inorganic putty provided by the invention, the inorganic putty not only have preferable antiseptic property, and are a kind of
Cost is cheap, excellent performance, full-featured inorganic putty.
Embodiment
Based on the embodiment in the present invention, those of ordinary skill in the art are obtained under the premise of creative work is not made
The every other embodiment obtained, belongs to the scope of protection of the invention.
Embodiment 1
A kind of inorganic putty, is made up of following raw material according to parts by weight：
Portland cement：100 parts；
Interfacial agents：16 parts；
China clay：40 parts；
Land plaster：6 parts；
Preferably, the portland cement.
Preferably, the china clay particle diameter is 250 mesh.
A kind of production method of inorganic putty, the production method of the inorganic putty comprise the following steps：
S1：Stirred under normal pressure：Portland cement：100 parts；Interfacial agents：16 parts；China clay：40 parts；Land plaster：6 parts；Stir
Mix 40 minutes, that is, can obtain inorganic putty；
S2：Packaging：S1 product is packed according to specification requirement.
Embodiment 2
A kind of inorganic putty, is made up of following raw material according to parts by weight：
Portland cement：100 parts；
Interfacial agents：19 parts；
China clay：43 parts；
Land plaster：7 parts；
Preferably, the portland cement.
Preferably, the china clay particle diameter is 250 mesh.
A kind of production method of inorganic putty, the production method of the inorganic putty comprise the following steps：
S1：Epoxy resin is stirred under normal pressure：Portland cement：100 parts；Interfacial agents：19 parts；China clay：43 parts；Gypsum
Powder：7 parts；Stir 20 minutes to 50 minutes, that is, can obtain inorganic putty；
S2：Packaging：S1 product is packed according to specification requirement.
Embodiment 3
A kind of inorganic putty, the formula of the inorganic putty are made up of the component comprising following parts by weight：
Portland cement：100 parts；
Interfacial agents：25 parts；
China clay；56 parts；
Land plaster：10 parts；
Preferably, the portland cement.
Preferably, the china clay particle diameter is 250 mesh.
A kind of production method of inorganic putty, the production method of the inorganic putty comprise the following steps：
S1：Epoxy resin is stirred under normal pressure：Portland cement：100 parts；Interfacial agents：25 parts；China clay；56 parts；Gypsum
Powder：10 parts；Stir 20 minutes to 50 minutes, that is, can obtain inorganic putty；
S2：Packaging：S1 product is packed according to specification requirement.
Although an embodiment of the present invention has been shown and described, for the ordinary skill in the art, can be with
A variety of changes, modification can be carried out to these embodiments, replace without departing from the principles and spirit of the present invention by understanding
And modification, the scope of the present invention is defined by the appended.
Claims (5)
- A kind of 1. inorganic putty, it is characterised in that：It is made up of following raw material according to parts by weight：Portland cement：100 parts；Interfacial agents：15-25 parts；China clay：38-56 parts；Land plaster：5-10 parts.
- A kind of 2. inorganic putty according to claim 1, it is characterised in that：It is made up of following raw material according to parts by weight：Portland cement：100 parts；Interfacial agents：15 parts；China clay：38 parts；Land plaster：5 parts.
- A kind of 3. inorganic putty according to claim 1, it is characterised in that：The portland cement.
- A kind of 4. inorganic putty according to claim 1, it is characterised in that：The china clay particle diameter is 250 mesh.
- A kind of 5. production method of inorganic putty as claimed in claim 1, it is characterised in that：The production method bag of the inorganic putty Include following steps：S1：Stirred under normal pressure：Portland cement：100 parts；Interfacial agents：15 parts；China clay：38 parts；Land plaster：5 parts；Stirring three Ten minutes to 50 minutes, that is, it can obtain inorganic putty；S2：Packaging：S1 product is packed according to specification requirement.