CN103641388B - A kind of glue powder polyphenyl granule external wall thermal insulation powdery material - Google Patents
A kind of glue powder polyphenyl granule external wall thermal insulation powdery material Download PDFInfo
- Publication number
- CN103641388B CN103641388B CN201310554002.0A CN201310554002A CN103641388B CN 103641388 B CN103641388 B CN 103641388B CN 201310554002 A CN201310554002 A CN 201310554002A CN 103641388 B CN103641388 B CN 103641388B
- Authority
- CN
- China
- Prior art keywords
- powder
- thermal insulation
- raw material
- external wall
- weight
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a kind of glue powder polyphenyl granule external wall thermal insulation powdery material, it is obtained by the raw material of following weight parts: cement 50-60,80-120 object sand 10-20, latex powder 7-9, Vltra tears 1-2, starch ethers 1-2, brown sugar 1-2, chromoxide green 1-2, sericite in powder 5-7, MPC filament expansion agent 0.8-1.2, magnesium sulfate 1-2, granular polystyrene 7-9, steel fiber 1-2, coarse whiting 5-7, calcium formiate 0.3-0.6, modified filler 3-5.
Description
Technical field
The present invention relates to thermal insulation mortar field, is exactly a kind of glue powder polyphenyl granule external wall thermal insulation powdery material.
Background technology
Thermal insulation mortar refers to and is mixed by isolation-type lagging material and mortar material, for constructing a kind of material of construction of building surface thermal insulation layer.
The anticracking grout of thermal insulation mortar and corresponding system thereof, be adapted to the Steel Concrete of multilayer structure, gas concrete, lay bricks, the Surgery therapy plastering engineering of the body of wall such as vitrified brick and no-firing brick and inside holding plastering engineering, the insulation improvement project for current all kinds of old building is also very applicable.
Summary of the invention
The object of the present invention is to provide a kind of glue powder polyphenyl granule external wall thermal insulation powdery material.
Above-mentioned purpose is realized by following scheme:
A kind of glue powder polyphenyl granule external wall thermal insulation powdery material, it is characterized in that: it is obtained by the raw material of following weight parts: cement 50-60,80-120 object sand 10-20, latex powder 7-9, Vltra tears 1-2, starch ethers 1-2, brown sugar 1-2, chromoxide green 1-2, sericite in powder 5-7, MPC filament expansion agent 0.8-1.2, magnesium sulfate 1-2, granular polystyrene 7-9, steel fiber 1-2, coarse whiting 5-7, calcium formiate 0.3-0.6, modified filler 3-5;
Described modified filler is made up of the raw material of following weight part:
Modified hydrotalcite powder 13-16, sepiolite 4-5, nano-calcium carbonate 1-2, nanoclay 3-5, dioctyl maleate 2-3, aluminium nitride 1-2;
The preparation method of modified filler is:
(1) hydrotalcite powder being added the concentration being equivalent to its weight 3-4 times is in the hydrogen peroxide of 10-20%, stir after 10-20 minute, deionized water wash, dry, stir with suitable quantity of water afterwards, add the cationic polyacrylamide being equivalent to hydrotalcite powder weight 3-5%, stirring reaction 3-5 hour at 30-50 DEG C, the pH value of regulation system to 8-10, then adds when in the silane coupling agent kh570 of hydrotalcite powder weight 3-5%, stirring reaction 1-2h, by the hydrotalcite powder slurry by filtration of gained, washing, after drying, obtains modified hydrotalcite powder;
(2) by after sepiolite, nano-calcium carbonate fragmentation, 1-2 hour is calcined at 700-800 DEG C, take out, putting into concentration is after the acetic acid solution of 4-6% soaks 8-10 hour, then deionized water wash, dry, put into modified hydrotalcite powder, at 40-50 DEG C, 180-220 rev/min is stirred after 10-20 minute, drying, with after other raw material blending and get final product.
Described a kind of glue powder polyphenyl granule external wall thermal insulation powdery material, is characterized in that:
Preparation method is:
80-120 object sand, sericite in powder, starch ethers are mixed by weight, under 1100-1200 rev/min, stir 5-10 minute, take out, then with the whole raw material blending of residue after, 600-800 rev/min is at the uniform velocity stirred 20-30 minute, after packaging and get final product.
Beneficial effect of the present invention is: the present invention is applicable to heat preservation mortar for outer wall, and after material modification, water proof fire retardant performance is good, safety and environmental protection, constructability, and the life-span is long.
Embodiment
A kind of glue powder polyphenyl granule external wall thermal insulation powdery material, it is obtained by the raw material of following weight kg: cement 50,80-120 object sand 16, latex powder 9, Vltra tears 1, starch ethers 1, brown sugar 1, chromoxide green 2, sericite in powder 5, MPC filament expansion agent 0.8, magnesium sulfate 1, granular polystyrene 7, steel fiber 1, coarse whiting 5, calcium formiate 0.3, modified filler 5;
Described modified filler is made up of the raw material of following weight kg:
Modified hydrotalcite powder 16, sepiolite 5, nano-calcium carbonate 1, nanoclay 5, dioctyl maleate 2, aluminium nitride 1;
The preparation method of modified filler is:
(1) hydrotalcite powder being added the concentration being equivalent to its weight 3 times is in the hydrogen peroxide of 10%, stirs after 20 minutes, deionized water wash, drying, rear and suitable quantity of water stirs, and adds the cationic polyacrylamide being equivalent to hydrotalcite powder weight 5%, stirring reaction 3 hours at 50 DEG C, the pH value to 9 of regulation system, then add when in the silane coupling agent kh570 of hydrotalcite powder weight 3%, stirring reaction 1h, by the hydrotalcite powder slurry by filtration of gained, washing, after drying, obtains modified hydrotalcite powder;
(2) by after sepiolite, nano-calcium carbonate fragmentation, calcine 2 hours at 780 DEG C, take out, put into concentration be 6% acetic acid solution soak after 10 hours, then deionized water wash, dry, put into modified hydrotalcite powder, at 50 DEG C, 220 revs/min are stirred after 20 minutes, drying, with after other raw material blending and get final product.
Described a kind of glue powder polyphenyl granule external wall thermal insulation powdery material, preparation method is:
120 object sand, sericite in powder, starch ethers are mixed by weight, stir 5 minutes under 1100 revs/min, take out, then with the whole raw material blending of residue after, 800 revs/min are at the uniform velocity stirred 20 minutes, after packaging and get final product.
Products obtained therefrom test result is as follows:
Claims (2)
1. a glue powder polyphenyl granule external wall thermal insulation powdery material, it is characterized in that: it is obtained by the raw material of following weight parts: cement 50-60,80-120 object sand 10-20, latex powder 7-9, Vltra tears 1-2, starch ethers 1-2, brown sugar 1-2, chromoxide green 1-2, sericite in powder 5-7, MPC filament expansion agent 0.8-1.2, magnesium sulfate 1-2, granular polystyrene 7-9, steel fiber 1-2, coarse whiting 5-7, calcium formiate 0.3-0.6, modified filler 3-5; Described modified filler is made up of the raw material of following weight part: modified hydrotalcite powder 13-16, sepiolite 4-5, nano-calcium carbonate 1-2, nanoclay 3-5, dioctyl maleate 2-3, aluminium nitride 1-2;
The preparation method of modified filler is:
(1) hydrotalcite powder being added the concentration being equivalent to its weight 3-4 times is in the hydrogen peroxide of 10-20%, stir after 10-20 minute, deionized water wash, dry, stir with suitable quantity of water afterwards, add the cationic polyacrylamide being equivalent to hydrotalcite powder weight 3-5%, stirring reaction 3-5 hour at 30-50 DEG C, the pH value of regulation system to 8-10, then adds the silane coupling agent kh570 being equivalent to hydrotalcite powder weight 3-5%, stirring reaction 1-2h, by the hydrotalcite powder slurry by filtration of gained, washing, after drying, obtains modified hydrotalcite powder;
(2) by after sepiolite, nano-calcium carbonate fragmentation, 1-2 hour is calcined at 700-800 DEG C, take out, putting into concentration is after the acetic acid solution of 4-6% soaks 8-10 hour, then deionized water wash, dry, put into modified hydrotalcite powder, at 40-50 DEG C, 180-220 rev/min is stirred after 10-20 minute, drying, with after other raw material blending and get final product.
2. a kind of glue powder polyphenyl granule external wall thermal insulation powdery material according to claim 1, it is characterized in that: preparation method is: 80-120 object sand, sericite in powder, starch ethers are mixed by weight, 5-10 minute is stirred under 1100-1200 rev/min, take out, again with residue whole raw material blending after, 600-800 rev/min is at the uniform velocity stirred 20-30 minute, after packaging and get final product.