CN107619225A - A kind of lightweight mixed mortar for being used to make flue - Google Patents
A kind of lightweight mixed mortar for being used to make flue Download PDFInfo
- Publication number
- CN107619225A CN107619225A CN201711019603.6A CN201711019603A CN107619225A CN 107619225 A CN107619225 A CN 107619225A CN 201711019603 A CN201711019603 A CN 201711019603A CN 107619225 A CN107619225 A CN 107619225A
- Authority
- CN
- China
- Prior art keywords
- particle diameter
- flue
- pottery sand
- water
- mixed mortar
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a kind of lightweight mixed mortar for being used to make flue.It is big mainly to solve the flue weight of traditional mortar making, increase building body load is installed and transported the problem of inconvenient simultaneously.To include cement in units of every cubic metre：475kg 512kg, flyash：53 57, particle diameter is no more than 2.5mm pottery sand：395 426, particle diameter 2.5mm 5mm pottery sand：57 263, expanded perlite 0 30, water reducer：1.05 1.14, remaining as water, the mortar with the present invention alleviates flue weight, and ensure that flue prescribed strength simultaneously with flue is made.
Description
Technical field
The present invention relates to a kind of lightweight mixed mortar for being used to make flue.
Background technology
Residence chimney neck is at present more uses cement, and middle sand material texture is into the mortar ratio reclosing nearly 1900kg/m3 is usually used
Flue specification 0.4m*0.5m, three meters long, wall thickness is not less than 1.5cm, and gross weight reaches 160kg, and its weight is excessive, pacifies in construction
Be filled with and transportation in be inconvenient, worker's working strength is larger.
The content of the invention
The invention aims to solve the above-mentioned problems of the prior art, and then provide a kind of for making flue
Lightweight mixed mortar, it significantly alleviates flue weight, convenient construction installation, and has the effect of purifying smoke concurrently.
The purpose of the present invention is achieved through the following technical solutions：
A kind of lightweight mixed mortar for being used to make flue, including cement, strength enhancing agent, light filler, water reducer, water；
Described strength enhancing agent is flyash, and light filler is pottery sand of the particle diameter no more than 2.5mm, particle diameter 2.5mm-5mm
Pottery sand and expanded perlite；
Described strength enhancing agent is volcanic rock, light filler is cinder；
To include cement in units of every cubic metre：475kg-512kg, flyash：53 kg -57 kg, particle diameter are no more than 2.5mm
Pottery sand：395 kg -426 kg, particle diameter 2.5mm-5mm pottery sand：57 kg -263 kg, the kg -30 of expanded perlite 0
Kg, water reducer：1.05 kg -1.14 kg, remaining as water；
To include cement in units of every cubic metre：475kg, flyash：53kg, particle diameter are no more than 2.5mm pottery sand：395kg, grain
Footpath 2.5mm-5mm pottery sand：263kg, water reducer：1.05kg, remaining as water；
To include cement in units of every cubic metre：512kg, flyash：57kg, particle diameter are no more than 2.5mm pottery sand：426kg, grain
Footpath 2.5mm-5mm pottery sand：57kg, expanded perlite：30kg, water reducer：1.14kg, remaining as water.
To include cement in units of every cubic metre：475kg-512kg, volcanic rock：53 kg -57 kg, cinder： 452 kg
- 719 kg, water reducer：1.05 kg -1.14 kg, remaining as water.
The beneficial effects of the invention are as follows：By using technical scheme using flyash, pottery sand, expanded perlite
Or the blended cement such as volcanic rock, cinder forms mortar, relatively conventional mortar Unit Weight is lighter, therefore flue, which is made, to be mitigated significantly
Flue weight, convenient construction and transport, wherein the pottery sand mixed, volcanic rock, cinder etc. also have the effect of purifying smoke concurrently.
Embodiment
The present invention is described in further detail below：The present embodiment is carried out lower premised on technical solution of the present invention
Implement, give detailed embodiment, but protection scope of the present invention is not limited to following embodiments.
It is a kind of to be used to making the lightweight mixed mortar of flue, including cement, strength enhancing agent, light filler, water reducer,
Water.
Described strength enhancing agent is flyash, effectively lifts strength of cement, and light filler is particle diameter no more than 2.5mm's
Pottery sand, particle diameter 2.5mm-5mm pottery sand and expanded perlite, effectively mitigate flue weight, alleviate unit weight.
Described light filler is that volcanic rock or cinder can effectively mitigate flue weight.
Embodiment 1, a kind of lightweight mixed mortar for being used to make flue, to include cement in units of every cubic metre：
475kg-512kg, flyash：53 kg -57 kg, particle diameter are no more than 2.5mm pottery sand：395 kg -426 kg, particle diameter
2.5mm-5mm pottery sand：57 kg -263 kg, kg -30 kg of expanded perlite 0, water reducer：1.05 kg -1.14 kg,
Remaining as water.
Embodiment 2, it is preferred that to include cement in units of every cubic metre：475kg, flyash：53kg, particle diameter are no more than
2.5mm pottery sand：395kg, particle diameter 2.5mm-5mm pottery sand：263kg, water reducer：1.05kg, remaining as water, flue is dried to
After type 28 days, experiment compression strength reaches 30MPa.
Embodiment 3, it is preferred that to include cement in units of every cubic metre：512kg, flyash：57kg, particle diameter are no more than
2.5mm pottery sand：426kg, particle diameter 2.5mm-5mm pottery sand：57kg, expanded perlite：30kg, water reducer：It is 1.14kg remaining
After shredded tobacco for water pipes road drying and moulding 28 days, experiment compression strength reaches 22MPa.
Embodiment 4, to include cement in units of every cubic metre：475kg-512kg, volcanic rock：53 kg -57 kg, coal
Slag：452 kg -719 kg, water reducer：1.05 kg -1.14 kg, remaining as water.
Specifically, concerned countries standard provides, flue compression strength is not less than 20MPa, complete in above example of the present invention
Meet national standard entirely, the lightweight mixed mortar described in above example is wherein mixed with a large amount of particulate materials, is not suitable for
Artificial to smear moulding to flue, the mechanism flue of being suitable as is filled moulding to mould, is vibrated to surface pulp and is defined after moulding.
The foregoing is only a preferred embodiment of the present invention, these embodiments are all based on the present invention
Different implementations under general idea, and protection scope of the present invention is not limited thereto, it is any to be familiar with the art
Technical staff the invention discloses technical scope in, the change or replacement that can readily occur in, should all cover the present invention's
Within protection domain, therefore, protection scope of the present invention should be defined by the protection domain of claims.
Claims (5)
1. a kind of be used to make the lightweight mixed mortar of flue, it is characterised in that including cement, strength enhancing agent, light filler,
Water reducer, water, wherein, described strength enhancing agent includes flyash, light filler include pottery sand of the particle diameter no more than 2.5mm,
Particle diameter 2.5mm-5mm pottery sand, expanded perlite, volcanic rock, cinder.
2. the lightweight mixed mortar according to claim 1 for being used to make flue, to include cement in units of every cubic metre：
475kg-512kg, flyash：53 kg -57 kg, particle diameter are no more than 2.5mm pottery sand：395 kg -426 kg, particle diameter
2.5mm-5mm pottery sand：57 kg -263 kg, kg -30 kg of expanded perlite 0, water reducer：1.05 kg -1.14 kg,
Remaining as water.
3. the lightweight mixed mortar according to claim 2 for being used to make flue, it is characterised in that with every cubic metre for singly
Position includes cement：475kg, flyash：53kg, particle diameter are no more than 2.5mm pottery sand：395kg, particle diameter 2.5mm-5mm pottery sand：
263kg, water reducer：1.05kg, remaining as water consumption.
4. the lightweight mixed mortar according to claim 2 for being used to make flue, it is characterised in that with every cubic metre for singly
Position includes cement：512kg, flyash：57kg, particle diameter are no more than 2.5mm pottery sand：426kg, particle diameter 2.5mm-5mm pottery sand：
57kg, expanded perlite：30kg, water reducer：1.14kg, remaining as water consumption.
5. the lightweight mixed mortar according to claim 1 for being used to make flue, it is characterised in that with every cubic metre for singly
Position includes cement：475kg-512kg, volcanic rock：53 kg -57 kg, cinder：452 kg -719 kg, water reducer：1.05
Kg -1.14 kg, remaining as water.