CN107618192A - A kind of wind power generation unit blade bonding angle and preparation method thereof - Google Patents
A kind of wind power generation unit blade bonding angle and preparation method thereof Download PDFInfo
- Publication number
- CN107618192A CN107618192A CN201710897754.5A CN201710897754A CN107618192A CN 107618192 A CN107618192 A CN 107618192A CN 201710897754 A CN201710897754 A CN 201710897754A CN 107618192 A CN107618192 A CN 107618192A
- Authority
- CN
- China
- Prior art keywords
- bonding angle
- liner plate
- cloth
- bonding
- blade
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a kind of wind power generation unit blade bonding angle, the bonding angle is the bonding angle with liner plate, with U-shape structure, the U-shape structure outer shape matches with corresponding blade bonding region inner shape, and the liner plate is set on the inside of one side or adjacent both sides along U-shape structure.Invention additionally discloses the preparation method of above-mentioned bonding angle, including:(1) liner plate, the liner plate demoulding, trimming are prepared according to inner walls shape within the parting line of the face housing of blade one;(2) bonding angle laying is made by fiber cloth and resin, the parting line side of obtained liner plate is directed at bonding angle laying center line again, together bonding angle laying and liner plate are placed between bonding angle mold and blade shell, liner plate is clamped on bonding angle mold with fixture, bonding angle laying curing and demolding is treated, produces the bonding angle with liner plate.Present invention band liner plate bonding angle is high with type with housing, can overcome existing bonding angle wrinkling deformation, position the defects of bad, improve blade bonding quality.
Description
Technical field
The present invention relates to wind electricity blade preparing technical field, more particularly to a kind of wind power generation unit blade bonding angle and its system
Preparation Method.
Background technology
Wind power generation unit blade is generally divided into pressure face (PS faces) and suction surface (SS faces), and two sides housing passes through shearing resistance at middle part
Web or the connection of box girder construction, it is then by being directly bonded, sandwich of layers bonding, bonding angle bonding and internal mends in front and rear edge
Strong mode connects.
The posterior segment region of trailing edge is connected using direct bonding way more in the prior art, the matched moulds gap in the region
Meet the suitable design thickness of bonding agent;The blade root region of blade is connected by the way of internal reinforcement, the area people side
Just enter, it is easy to operation;Trailing edge leading portion region is bonded using sandwich of layers mode, but sandwich of layers making is present and easily rolled over
The defects of wrinkle, hickie, influence bonding quality;Trailing edge leading portion region and the non-root area of blade inlet edge use bonding angle mode
Bonding, but in thin airfoil region, because operating space limits, bonding angle close to the position of parting line easily occur poor location,
The defects of collapsing, being layered, bonding agent is blocked up, the problems such as cavity occurs so as to causing, and bonding quality hidden danger be present.
The present invention be exactly on above-mentioned prior art basis, found a kind of easy to operate, efficiency high, can overcome bonding angle with
Wind power generation unit blade bonding angle of type difference and preparation method thereof, to improve the quality of bonding angle.
The content of the invention
The technical problem to be solved in the present invention is to provide a kind of wind power generation unit blade bonding angle, can solve bonding angle with
The problem of type difference, so as to overcome the shortcomings of existing bonding angle.
In order to solve the above technical problems, the present invention provides a kind of wind power generation unit blade bonding angle, the bonding angle is belt material
The bonding angle of plate.
As a modification of the present invention, the bonding angle is U-shape structure, the outer shape of the U-shape structure with it is relative
The blade bonding region inner shape answered matches, and the liner plate is set on the inside of one side or adjacent both sides along the U-shape structure
Put.
Further improve, the fiber cloth superposition solidification that the bonding angle and liner plate thereon are impregnated with resin by multilayer is made
Into.
Further improve, the bonding angle includes 4~7 layers of fiber cloth for being impregnated with resin, and the liner plate includes 1~3 layer of leaching
The fiber cloth of saturating resin.
Further improve, the bonding angle includes the SS faces trailing edge bonding angle with PS faces trailing edge liner plate, PS faces trailing edge
The structure of liner plate matches with the structure within the trailing edge housing parting line of blade PS faces;Or
The bonding angle includes the PS faces trailing edge bonding angle with SS faces trailing edge liner plate, the structure of the SS faces trailing edge liner plate with
Structure within the trailing edge housing parting line of blade SS faces matches.
The present invention also technical problems to be solved are to provide a kind of preparation method of wind power generation unit blade bonding angle, make its solution
The problem of certainly bonding angle is with type difference, and this method is easy to operate, efficiency high, so as to overcome existing bonding angle preparation method not
Foot.
In order to solve the above technical problems, the present invention provides a kind of preparation method of wind power generation unit blade bonding angle, including such as
Lower step:
(1) liner plate is made
Mold foundation is shaped as with the inner walls in the face housing parting line of blade one, is made and the face housing of blade one
Inner walls shape identical liner plate;
(2) liner plate is stripped
The liner plate is separated with mould, at least cut corner at the parting line of the liner plate neat;
(3) bonding angle is made
According to bonding angle width requirement, plastic sheeting or the vacuum bag film tiling of corresponding size are taken, in the plastic sheeting
Or 1 layer of three axial cloth or biaxially cloth are laid in vacuum bag film, and in described three axial cloth or biaxially on cloth uniformly on mix
The resin got togather, make three axial cloth described in the resin impregnated or biaxially cloth with roller or brush, drive bubble out of, repeat paving
If 3~6 layers of three axial cloth or biaxially cloth and resin, produce bonding angle laying;
Release cloth is laid in bonding angle die inside, is then connected the bonding angle mold with blade shell flange;
The parting line side of the liner plate is aligned to the center line of the bonding angle laying, will first press close to the bonding angle mold in advance
Laying lift, make to be compacted with type on the outside of itself and the liner plate, then lift it is pre- press close to blade shell side laying, together will described in
Bonding angle laying and liner plate are placed between the bonding angle mold and blade shell, are adjusted the liner plate, are made with the liner plate
Bonding angle laying and Nian Jie angle mold and blade shell it is sturdy, the liner plate is fixed on the bonding angle mold with fixture
On, and drive bubble out of with roller;
(4) the bonding angle solidification demoulding
Treat bonding angle laying solidification, and reach certain degree of hardness, removed after surface is tack-free the bonding angle mold and
Auxiliary material, produce the bonding angle with liner plate.
Further improve, be the step of making liner plate in the step (1):After a face housing precuring of blade, remove
The auxiliary material of bonding region corresponding with offside blade shell is gone, according to the precuring within precuring blade shell parting line
Blade shell inwall is close to lay vacuum bag film and/or release cloth, and 1 slice width is laid in the vacuum bag film and/or release cloth
Degree is more than or equal to the three axial cloth or biaxially cloth, and in described three axial cloth or biaxially uniform on cloth of required bonding angular breadth
The resin mixed on, make three axial cloth or biaxially cloth, and drive bubble out of described in the resin impregnated with roller or brush,
1~3 layer of laying, the three axial cloth or biaxially cloth and resin are repeated, produces the liner plate.
Further improve, be the step of making liner plate in the step (1):In a face housing laying release cloth of blade
Afterwards, it is close to lay 1-3 slice widths degree more than or equal to required bonding angular width according to the inner walls within the housing parting line
Three axial cloth of degree or biaxially cloth, then with blade shell one form, produce the liner plate.
Further improve, be the step of making liner plate in the step (1):The laying demoulding on face is used in bonding angle mold
Cloth, and it is close to lay 1-3 slice widths degree more than or equal to required using face inwall according to the bonding angle mold on the release cloth
Be bonded the three axial cloth or biaxially cloth of angular breadth, and in described three axial cloth or biaxially on cloth uniformly on the tree that mixes
Fat, make three axial cloth or biaxially cloth, and drive bubble out of described in the resin impregnated with roller or brush, repeat laying 1~3
The layer three axial cloth or biaxially cloth and resin, produce the liner plate.
Further improve, every layer of three axial cloth of laying or 5~50mm between cloth biaxially be present in the step (3)
Staggered floor.
After such design, the present invention at least has advantages below:
1. the bonding angle of the invention with liner plate can overcome the existing corrugation of existing bonding angle to become by the supporting role of liner plate
The defects of shape, bad positioning, it is good with type with housing, moreover it is possible to ensures that bonding agent thickness reaches design requirement, improves blade
Bonding quality, avoid the potential problem of cracks of blade adhesive.
2. preparation method of the present invention is first prepared with type liner plate according to blade shell inner side, then makes the bonding angle with liner plate,
The obtained band liner plate bonding angle of this method is high with type with housing, and bonding agent thickness meets design requirement and is evenly distributed, blade
Bonding quality is high, solves the hidden danger of cracks of blade adhesive.
3rd, preparation method of the present invention is easily operated, efficiency high.
Brief description of the drawings
Above-mentioned is only the general introduction of technical solution of the present invention, in order to better understand the technological means of the present invention, below
With reference to accompanying drawing, the present invention is described in further detail with embodiment.
Fig. 1 is the schematic diagram that PS faces trailing edge liner plate step is prepared in preparation method of the present invention.
Fig. 2 is the schematic diagram that the SS faces trailing edge bonding angle step with liner plate is prepared in preparation method of the present invention.
Wherein, 1, PS face-piece bodies, 2, vacuum bag film, 3, PS faces trailing edge liner plate, 4, trailing edge bonding angle mold, 5, SS face-pieces
Body, 6, SS faces trailing edge bonding angle, 7, fixture.
Embodiment
With reference to specific embodiment, technical scheme is expanded on further.This application includes two embodiments,
It should be understood that these embodiments are only used for explaining the present invention rather than limitation the scope of the present invention.Particular content is as follows:
Embodiment one
Referring to the drawings shown in 1 and 2, the present embodiment is used to prepare the SS faces trailing edge bonding angle with PS faces trailing edge liner plate, and it has
Preparation comprises the following steps:
(1) after making the precuring of PS faces trailing edge liner plate blade PS face-pieces body 1, the trailing edge parting of blade PS face-pieces body 1 is removed
Auxiliary material within line L3m~L15m in the range of 200mm, is cleaned out, and is close to lay vacuum bag film 2 according to the inwall of PS face-pieces body 1,
Lay the wide three axial cloth of 1 layer of 150mm within parting line, then three axial cloth uniformly on the resin that mixes, use roller
Resin impregnated fiber cloth is driven out of bubble and the inwall of the fiber cloth and the region housing is repeated above-mentioned action with type by son, then
2 layers of biaxially cloth and resin are laid, PS faces trailing edge liner plate 3 is made.
(2) after liner plate solidification is stripped 2 hours, after resin solidification, tears and drag vacuum bag film 2 by PS faces trailing edge liner plate 3 and PS faces
Housing 1 is separated, and removes the vacuum bag film on liner plate 3, and corner is cut neatly, and the corner cutting especially at liner plate parting line is flat
It is whole.
(3) SS faces trailing edge bonding angle is made
A, the wide vacuum bag films of 1 layer of 400mm are laid, then are laying three wide axial cloth of 1 layer of 240mm thereon, uniformly on
The resin mixed, fiber cloth is impregnated with using roller, drives bubble out of, repeat above-mentioned action, lay altogether 1 layer of three axial cloth and
4 layers of biaxially cloth, and width staggered floor 5mm between layers, length direction staggered floor 50mm, produce bonding angle laying 6;
B, trailing edge is bonded on angle mold 4 and lays release cloth with glue spraying, bonding angle mold 4 is then fixed on SS face-piece bodies
On 5 flanges;
C, the parting line side of PS faces trailing edge liner plate 3 is directed at the center line of bonding angle laying 6, and first will presses close to be bonded angle mold 4 in advance
Laying lift, be compacted with the outside of liner plate 3 with type, then lift housing side laying, be together placed into bonding angle mold 4 and SS face-pieces
Between body 5, liner plate 3 is adjusted, makes the SS faces trailing edge bonding angle laying 6 with liner plate 3 sturdy with Nian Jie angle mold 4 and SS face-pieces body 5,
Liner plate 3 is fixed with fixture 7, then bubble is driven out of with roller.
(4) after solidification is stripped 2 hours, bonding angle laying 6 solidifies, and removes bonding angle mold and release cloth, and band PS faces are made
The SS faces trailing edge bonding angle of trailing edge liner plate.
Embodiment two
The present embodiment is used to prepare the PS faces trailing edge bonding angle with SS faces trailing edge liner plate, and its specific preparation method includes following
Step:
(1) after the completion of making the laying of SS faces trailing edge liner plate blade SS faces shell layer, into auxiliary material arrangement stage, the laying demoulding
After cloth, the wide biaxially cloth of 3 layers of 180mm is laid within blade SS face-piece body trailing edge L8m~L14m parting lines, then with blade
SS face-piece body one forms, produce SS faces trailing edge liner plate.
(2) after resin precuring, vacuum bag film is opened, is drawn SS faces trailing edge liner plate periphery 30mm release cloth with wallpaper knife
Open, and stuck up out from one jiao, tear and drag release cloth and separate SS faces trailing edge liner plate and SS face-piece bodies, remove the release cloth on liner plate, will
Corner cutting is neat, and the corner cutting especially at liner plate parting line is smooth.
(3) PS faces trailing edge bonding angle is made
A, the wide vacuum bag films of 1 layer of 400mm are laid, then are laying the wide biaxially cloth of 1 layer of 300mm thereon, uniformly on
The resin mixed, fiber cloth is impregnated with using roller, drives bubble out of, repeat above-mentioned action, lay 5 layers of biaxially cloth altogether,
And width staggered floor 5mm between layers, length direction staggered floor 50mm, produce bonding angle laying;
B, trailing edge is bonded on angle mold and lays release cloth with glue spraying, bonding angle mold is then fixed on PS face-piece body methods
Lan Shang;
C, SS faces trailing edge liner plate parting line side is directed at bonding angle laying center line, and first will presses close to be bonded the paving of angle mold in advance
Layer lifts, and is compacted with liner plate with type, then lifts housing side laying, is together placed between bonding angle mold and housing, adjustment lining
Plate, the PS faces trailing edge bonding angle laying with liner plate is shown consideration for Nian Jie angle mold and PS face-pieces real, fix liner plate with fixture, use roller
Son drives bubble out of;
(4) after solidification is stripped 2 hours, the solidification of bonding angle laying, bonding angle mold and release cloth is removed, is made with SS faces
The PS faces trailing edge bonding angle of trailing edge liner plate.
The SS faces trailing edge bonding angle of the band PS faces trailing edge liner plate respectively obtained from above-mentioned two embodiment and with SS faces trailing edge
The PS faces trailing edge bonding angle of liner plate can be seen that:The bonding angle with liner plate, is U-shape structure.The outer shape of the U-shape structure with
Corresponding blade bonding region inner shape matches, and the liner plate is set on the inside of one side or adjacent both sides along U-shape structure.
Wherein, bonding angle and liner plate thereon are impregnated with the fiber cloth superposition solidification of resin by multilayer and are made.Specifically, bonding angle includes
4~7 layers of fiber cloth for being impregnated with resin, liner plate include 1~3 layer of fiber cloth for being impregnated with resin.
By the present invention in that making bonding angle with liner plate, existing bonding angle poor location can be overcome, collapse, be layered etc. and be scarce
Fall into, bonding angle quality is substantially increased, especially close to rear side with type, it is ensured that bonding agent thickness reaches design requirement.
The present invention make liner plate technique both can as in embodiment one with the housing hand pasting forming after precuring, also can be such as
Together irrigated with housing in embodiment two it is prefabricated form, liner plate processed can also be turned over by being bonded angle mold and formed, technological design is closed
Reason, workable, production efficiency is high.
Certainly, the bonding angle that prepared by the present invention can also remove liner plate, work according to operating space size after bonding angle solidification
Skill strong operability.
The above described is only a preferred embodiment of the present invention, any formal limitation not is made to the present invention, this
Art personnel make a little simple modification, equivalent variations or modification using the technology contents of the disclosure above, all fall within this hair
In bright protection domain.
Claims (10)
1. a kind of wind power generation unit blade bonding angle, it is characterised in that the bonding angle is the bonding angle with liner plate.
2. wind power generation unit blade bonding angle according to claim 1, it is characterised in that the bonding angle is U-shape structure, institute
The outer shape and corresponding blade bonding region inner shape for stating U-shape structure match, and the liner plate is along the U-shape structure
One side or adjacent both sides on the inside of set.
3. wind power generation unit blade bonding angle according to claim 2, it is characterised in that the bonding angle and liner plate thereon
The fiber cloth superposition solidification that resin is impregnated with by multilayer is made.
4. wind power generation unit blade bonding angle according to claim 3, it is characterised in that the bonding angle includes 4~7 layers of leaching
The fiber cloth of saturating resin, the liner plate include 1~3 layer of fiber cloth for being impregnated with resin.
5. the wind power generation unit blade bonding angle according to any one of Claims 1-4, it is characterised in that the bonding angle bag
Include the SS faces trailing edge bonding angle with PS faces trailing edge liner plate, structure and the blade PS faces trailing edge housing parting of the PS faces trailing edge liner plate
Structure within line matches;Or
The bonding angle includes the PS faces trailing edge bonding angle with SS faces trailing edge liner plate, the structure and blade of the SS faces trailing edge liner plate
Structure within the trailing edge housing parting line of SS faces matches.
6. a kind of preparation method of wind power generation unit blade bonding angle, it is characterised in that comprise the following steps:
(1) liner plate is made
Mold foundation is shaped as with the inner walls in the face housing parting line of blade one, makes the shell with the face housing of blade one
Body inner wall shape identical liner plate;
(2) liner plate is stripped
The liner plate is separated with mould, at least cut corner at the parting line of the liner plate neat;
(3) bonding angle is made
According to bonding angle width requirement, plastic sheeting or the vacuum bag film tiling of corresponding size are taken, in the plastic sheeting or true
Lay 1 layer of three axial cloth or biaxially cloth on empty bag film, and in described three axial cloth or biaxially on cloth uniformly on mix
Resin, make three axial cloth described in the resin impregnated or biaxially cloth with roller or brush, drive bubble out of, repeat laying 3
~6 layers of three axial cloth or biaxially cloth and resin, produce bonding angle laying;
Release cloth is laid in bonding angle die inside, is then connected the bonding angle mold with blade shell flange;
The parting line side of the liner plate is aligned to the center line of the bonding angle laying, will first press close to the paving of the bonding angle mold in advance
Layer lifts, and makes to be compacted with type on the outside of itself and the liner plate, then lift it is pre- press close to blade shell side laying, together by the bonding
Angle laying and liner plate are placed between the bonding angle mold and blade shell, adjust the liner plate, are made viscous with the liner plate
Connect angle laying and Nian Jie angle mold and blade shell are sturdy, the liner plate is fixed on the bonding angle mold with fixture, and
Bubble is driven out of with roller;
(4) the bonding angle solidification demoulding
The bonding angle laying solidification is treated, and reaches certain degree of hardness, the bonding angle mold and auxiliary material are removed after surface is tack-free,
Produce the bonding angle with liner plate.
7. the preparation method of wind power generation unit blade bonding angle according to claim 6, it is characterised in that the step (1)
It is middle making liner plate the step of be:After a face housing precuring of blade, bonding region corresponding with offside blade shell is removed
Auxiliary material, within precuring blade shell parting line according to the precuring blade shell inwall be close to lay vacuum bag film
And/or release cloth, 1 slice width degree is more than or equal to required bonding angular breadth three are laid in the vacuum bag film and/or release cloth
Axial cloth or biaxially cloth, and in described three axial cloth or biaxially on cloth uniformly on the resin that mixes, with roller or brush
Son makes three axial cloth or biaxially cloth, and drive bubble out of described in the resin impregnated, repeats 1~3 layer of laying described three axially
Cloth or biaxially cloth and resin, produce the liner plate.
8. the preparation method of wind power generation unit blade bonding angle according to claim 6, it is characterised in that the step (1)
It is middle making liner plate the step of be:After a face housing laying release cloth of blade, within the housing parting line according to described in
Inner walls are close to laying 1-3 slice widths degree and are more than or equal to the required three axial cloth for being bonded angular breadth or biaxially cloth, then with leaf
Piece housing one form, produces the liner plate.
9. the preparation method of wind power generation unit blade bonding angle according to claim 6, it is characterised in that the step (1)
It is middle making liner plate the step of be:In bonding angle mold using laying release cloth on face, and according to described viscous on the release cloth
Connect angle mold and be close to lay the three axial cloth or biaxially that 1-3 slice widths degree is more than or equal to required bonding angular breadth using face inwall
Cloth, and in described three axial cloth or biaxially on cloth uniformly on the resin that mixes, soak the resin with roller or brush
The saturating three axial cloth or biaxially cloth, and drive bubble out of, repeat 1~3 layer of laying, the three axial cloth or biaxially cloth with
And resin, produce the liner plate.
10. the preparation method of wind power generation unit blade bonding angle according to claim 6, it is characterised in that the step (3)
Every layer of three axial cloth of middle laying or the staggered floor that 5~50mm between cloth biaxially be present.