CN107612233A - The processing method of commutator strengthening ring - Google Patents
The processing method of commutator strengthening ring Download PDFInfo
- Publication number
- CN107612233A CN107612233A CN201710777860.XA CN201710777860A CN107612233A CN 107612233 A CN107612233 A CN 107612233A CN 201710777860 A CN201710777860 A CN 201710777860A CN 107612233 A CN107612233 A CN 107612233A
- Authority
- CN
- China
- Prior art keywords
- resin
- processing method
- glass fiber
- strengthening ring
- supporting layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of motor accessory, more particularly to a kind of processing method of commutator strengthening ring.The invention provides following technical scheme：A kind of processing method of commutator strengthening ring, step are as follows：Step is as follows：A, from the viscous glass fiber provided with resin in outer surface as base material；B, the glass fiber with resin is made into inner layer substrate by the laterally or longitudinally canoe along axle center, and resin is smeared in the outer surface of the inner layer substrate after being completely wound again；C, the supporting layer matrix being made in netted arrangement and the high strength glass fiber bar with resin is arranged in internal layer matrix outer；D, the outer surface of step c supporting layer matrix is covered into carbon fiber top layer；E, glued in step d carbon fiber top layer outer cladding surface and set extexine；F, the semi-finished product of machine-shaping in step e are positioned in baking oven and implement to toast.Using above-mentioned technical proposal, there is provided the processing method of a kind of tensile strength height, the not commutator strengthening ring of cracky.
Description
Technical field
The present invention relates to a kind of motor accessory, more particularly to a kind of processing method of commutator strengthening ring.
Background technology
The commutator strengthening ring of motor is a kind of accessory for being sheathed on and its parts stress intensity being improved on motor.Traditional
Reinforcing ring is that glass fibre processing is annular in shape, then by baking oven baking molding.
In traditional processing mode, glass fibre is perpendicular and the longitudinally staggered preliminary configuration into commutator strengthening ring,
Then the glue that glass fibre is implemented to bonding is coated thereon, finally implements baking.Glass fibre is perpendicular and longitudinally staggered
Afterwards there is larger hollow out in its surface, and the stress intensity of the hollow part is weaker, and during by external impacts, hollow part is easily broken
The situation of damage.
The content of the invention
In view of the deficienciess of the prior art, the invention provides a kind of tensile strength is high, the commutator of cracky does not add
The processing method of strong ring.
To achieve the above object, the invention provides following technical scheme：A kind of processing method of commutator strengthening ring, its
It is characterised by, step is as follows：Step is as follows：A, from the viscous glass fiber provided with resin in outer surface as base material；B, will tool
There is the glass fiber of resin by making inner layer substrate along the laterally or longitudinally canoe in axle center, and be completely wound again
Smear resin in the outer surface of inner layer substrate afterwards；C, it is arranged in internal layer matrix outer in netted arrangement and the high intensity with resin
The supporting layer matrix that glass fibre bar is made, if the high strength glass fiber bar in supporting layer matrix has a dried layer, and with
Diminishing netted arrangement mode implements arrangement, promotes the mesh after netted arrangement to reduce or be blocked completely；D, by step c
Supporting layer matrix outer surface covering carbon fiber top layer；E, glued in step d carbon fiber top layer outer cladding surface and be provided with resin
And extexine that is perpendicular or laterally winding；F, the semi-finished product of machine-shaping in step e are positioned in baking oven and implement to toast；d、
The finished product that baking is completed in step c is cooled down by being taken out in baking oven.
Using above-mentioned technical proposal, it is applied to from resin on rapidoprint, resin not only has preferably viscosity, absolutely
Edge, and environmental protection, the production method of supporting layer matrix is in netted arrangement, and mesh thereon is progressively reduced or covered completely
Lid, when it arrive impulsive force, the impulsive force can will not concentrate on some point impact, so as to preferably in its diffusion into the surface
Protective effect, the tensile strength of the present invention is added, extends service life.The setting on carbon fiber top layer can have the present invention
Anti-flammability, prevent from producing spark in excessive friction, while also further improve the tensile strength of the present invention.
The present invention is further arranged to：Carbon fiber top layer in step d is carbon-fibre strips winding shaping, its winding mode with
The winding mode of supporting layer matrix is identical.
Using above-mentioned technical proposal, the tensile strength that can further improve the present invention is so set.
The present invention is further arranged to：The temperature toasted in step f is 150 DEG C -250 DEG C；Baking time be 8h-
10h。
Using above-mentioned technical proposal, using the specific temperature and time degree of adhesion between each matrix can be made more preferable, no
It is easy to fall off, while the stress intensity of commutator strengthening ring is also further improved, extend its service life.
The invention will be further described below in conjunction with the accompanying drawings.
Brief description of the drawings
Fig. 1 is the structural representation of the embodiment of the present invention.
Embodiment
A kind of processing method of commutator strengthening ring as shown in Figure 1, step are as follows：A, it is provided with resin from outer surface is viscous
Glass fiber as base material；B, the glass fiber with resin is passed through into the laterally or longitudinally canoe system along axle center
Make inner layer substrate 1, and resin is smeared in the outer surface of the inner layer substrate 1 after being completely wound again；C, in the outer cover of inner layer substrate 1
If the supporting layer matrix 2 being made in netted arrangement and the high strength glass fiber bar with resin, in supporting layer matrix 2
If high strength glass fiber bar has dried layer, and implements arrangement with diminishing netted arrangement mode, after promoting netted arrangement
Mesh reduce or be blocked completely；D, the outer surface of step c supporting layer matrix is covered into carbon fiber top layer 3；E, in step d
The outer cladding surface of carbon fiber top layer 3 viscous be provided with resin and extexine 4 that is perpendicular or laterally winding；F, will be processed in step e
The semi-finished product of shaping, which are positioned in baking oven, implements baking；D, the finished product that baking is completed in step c is cooled down by being taken out in baking oven.On
State in scheme, be applied to from resin on rapidoprint, resin not only has preferably viscosity, insulation, and environmental protection, supporting layer
The production method of matrix 2 is in netted arrangement, and mesh thereon is progressively reduced or is completely covered, when it is arrived impulsive force,
The impulsive force can will not concentrate on some point impact, so as to have preferable protective effect, add this hair in its diffusion into the surface
Bright tensile strength, extends service life.The setting on carbon fiber top layer 3 can make the present invention have anti-flammability, prevent excessive
Friction produce spark, while also further improve the present invention tensile strength.
In embodiments of the present invention, in order to further improve the tensile strength of the present invention, the carbon fiber surface in step d
Layer 3 is that carbon-fibre strips winding is molded, and its winding mode is identical with the winding mode of supporting layer matrix.I.e. carbon fiber top layer 3 is also
If for dried layer in netted dislocation arrangement shaping, its surface is also coated with the resin for bonding.The temperature toasted in step f is 150
℃—250℃；Baking time is 8h -10h.
The tensile strength of the commutator strengthening ring of traditional approach processing is used as 1000M；It can only bear 150 DEG C of temperature
Degree.
Use the embodiment of the present invention processing method and parameter implement make motor reinforcing ring tensile strength for
1400M—1600M；It can bear 230 DEG C -280 DEG C of high temperature；Due to netted arrangement, rush makes it have crack resistence
Technique effect.
Claims (3)
1. a kind of processing method of commutator strengthening ring, it is characterised in that step is as follows：Step is as follows：A, glued from outer surface
Glass fiber provided with resin is as base material；B, the glass fiber with resin is passed through into laterally or longitudinally twining along axle center
Inner layer substrate is made around mode, and resin is smeared in the outer surface of the inner layer substrate after being completely wound again；C, in inner layer substrate
Outside is arranged the supporting layer matrix being made in netted arrangement and the high strength glass fiber bar with resin, supporting layer matrix
If high strength glass fiber bar in has dried layer, and implements arrangement with diminishing netted arrangement mode, promotes netted row
Mesh after cloth reduces or is blocked completely；D, the outer surface of step c supporting layer matrix is covered into carbon fiber top layer；E, in step
Rapid d carbon fiber top layer outer cladding surface is viscous to be provided with resin and extexine that is perpendicular or laterally winding；F, will be processed in step e
The semi-finished product of shaping, which are positioned in baking oven, implements baking；D, the finished product that baking is completed in step c is cooled down by being taken out in baking oven.
2. the processing method of commutator strengthening ring according to claim 1, it is characterised in that：Carbon in the step d is fine
Dimension table layer is molded for carbon-fibre strips winding, and its winding mode is identical with the winding mode of supporting layer matrix.
3. the processing method of commutator strengthening ring according to claim 1 or 2, it is characterised in that：Dried in described step f
Roasting temperature is 150 DEG C -250 DEG C；Baking time is 8h -10h.