CN107607427A - Stainless steel band Magnetic sensing methods - Google Patents
Stainless steel band Magnetic sensing methods Download PDFInfo
- Publication number
- CN107607427A CN107607427A CN201710942434.7A CN201710942434A CN107607427A CN 107607427 A CN107607427 A CN 107607427A CN 201710942434 A CN201710942434 A CN 201710942434A CN 107607427 A CN107607427 A CN 107607427A
- Authority
- CN
- China
- Prior art keywords
- balance
- stainless steel
- steel band
- lucite
- semiclosed
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses stainless steel band Magnetic sensing methods, comprise the following steps:Step 1:Prepare stainless steel band test sample;Step 2:Setup test equipment, including balance, semiclosed lucite platform, permanent magnet;Step 3:The stainless steel band test sample of step 1 is placed on the weighing platform of balance, weighed, record weight data m1;Step 4:Semiclosed lucite platform is covered on balance, closing space is formed between balance, keeps semiclosed lucite platform not contacted with the weighing platform of balance;Permanent magnet plane is placed with semiclosed lucite platform table top, record weight data m2;Step 5:Repeat step three and step 4, obtain three groups of m1And m2;According to formula C=(m1‑m2)/m1* 100% calculates heat treatment index C1, C2, C3, take three groups of statistical average CX, CX< 0.2%, then it is determined as that magnetic is qualified.The present invention efficiently and effectively can carry out magnetic detection to stainless steel band, and equipment easily prepares, and method is convenient, as a result accurately.
Description
Technical field
The present invention relates to a kind of stainless steel band Magnetic sensing methods.
Background technology
In cable industry, stainless steel band application is a lot, and many cables are required for using stainless steel band as strengthening core or outer
The armouring in portion.At present, due to lacking the apparatus and method of stainless steel band magnetic detection, acquiescence stainless steel band is non magnetic in industry
, but in fact, stainless steel band carries certain magnetic, in the presence of alternating electric field, eddy-current loss and magnetic hysteresis can be produced
Loss, reduce the current-carrying capacity of cable.
The content of the invention
It is an object of the invention to provide a kind of practicable stainless steel band Magnetic sensing methods.
The technical scheme for realizing the object of the invention is stainless steel band Magnetic sensing methods, is comprised the following steps:
Step 1:Prepare stainless steel band test sample;
Step 2:Setup test equipment, including balance, semiclosed lucite platform, permanent magnet;
Step 3:The stainless steel band test sample of step 1 is placed on the weighing platform of balance, weighed, records weight
Data m1;
Step 4:Semiclosed lucite platform is covered on balance, closing space is formed between balance, is kept semiclosed
Lucite platform does not contact with the weighing platform of balance;Permanent magnet plane is placed with semiclosed lucite platform table top, record
Weight data m2;
Step 5:Repeat step three and step 4, obtain three groups of m1And m2;According to formula C=(m1-m2)/m1* 100% meter
Calculate heat treatment index C1, C2, C3, take three groups of statistical average CX, CX< 0.2%, then it is determined as that magnetic is qualified.
Lucite sealed compartment with door is set on the balance;The lucite sealed compartment bottom centre, which is set, to be lacked
Mouthful, for exposing weighing platform;In the step 4, the semiclosed lucite edge of table is set to cover on lucite sealing
On the gap edge of cabin bottom centre, do not contacted while closing space is formed with the weighing platform of balance.
In the step 4, ensure the weighing platform table top and semiclosed lucite platform table top and permanent magnet plane of balance
It is centrally located on the same straight line with horizontal plane direction.
In the step 4, after having recorded weight data, balance is resetted returned to zero immediately.
In the step 1, stainless steel band to be tested is prepared into 25mm≤length≤100mm, 10mm≤width≤
80mm, deviation ± 1mm regular oblong print.
In the step 2, balance uses minimum range 0.0001g, maximum range 210g AL204- assay balances;Forever
100 ± 1mm of diameter of magnet, thickness 20mm ± 1mm, magnetic induction intensity peak value are more than 1000GS;Semiclosed lucite platform
135 ± 5mm of mesa diameter, height 52 ± 5mm, 4 ± 0.5mm of wall thickness.
In the step 3, balance is returned to zero, reservation is small to count to 0.0001g.
Above-mentioned technical proposal is employed, the present invention efficiently and effectively can carry out magnetic detection, Er Qieshe to stainless steel band
Standby easily to prepare, method is convenient, as a result accurately.
Embodiment
(embodiment 1)
Stainless steel band Magnetic sensing methods, comprise the following steps:
Step 1:Prepare stainless steel band test sample;Stainless steel band to be tested is prepared into 25mm≤length≤100mm,
10mm≤width≤80mm, deviation ± 1mm regular oblong print.
Step 2:Setup test equipment, including balance, semiclosed lucite platform, permanent magnet;Balance uses minimum range
0.0001g, maximum range 210g balance, the lucite sealed compartment with door is set on balance, extraneous magnetic disturbance can be shielded;
Lucite sealed compartment bottom centre sets breach, for exposing weighing platform, can use AL204- assay balances.
100 ± 1mm of diameter of permanent magnet, thickness 20mm ± 1mm, magnetic induction intensity peak value are more than 1000GS.
135 ± 5mm of mesa diameter of semiclosed lucite platform, height 52 ± 5mm, 4 ± 0.5mm of wall thickness.
Step 3:Balance is returned to zero, reservation is small to count to 0.0001g, and the stainless steel band test sample of step 1 is placed on
On the weighing platform of balance, weigh, record weight data m1;
Step 4:The semiclosed lucite edge of table is set to cover on the breach side of lucite sealed compartment bottom centre
On edge, do not contacted while closing space (the outside magnetic disturbance of isolation) is formed with the weighing platform of balance and (avoid influenceing precisely
Degree);Permanent magnet plane is placed with semiclosed lucite platform table top, record weight data m2;After having recorded weight data, stand
Balance is resetted and returned to zero, to eliminate influence of the magnet to balance.In this step in order to ensure data are accurate, balance should ensure that
Weighing platform table top and semiclosed lucite platform table top and permanent magnet plane be centrally located at and horizontal plane direction
On same straight line.
Step 5:Repeat step three and step 4, obtain three groups of m1And m2;According to formula C=(m1-m2)/m1* 100% meter
Calculate heat treatment index C1, C2, C3, take three groups of statistical average CX, CX< 0.2%, then it is determined as that magnetic is qualified.0.2% is Shen
Ask someone by lot of experiments and the referential data being calculated.
Particular embodiments described above, the purpose of the present invention, technical scheme and beneficial effect are carried out further in detail
Describe in detail it is bright, should be understood that the foregoing is only the present invention specific embodiment, be not intended to limit the invention, it is all
Within the spirit and principles in the present invention, any modification, equivalent substitution and improvements done etc., it should be included in the guarantor of the present invention
Within the scope of shield.
Claims (7)
1. stainless steel band Magnetic sensing methods, it is characterised in that comprise the following steps:
Step 1:Prepare stainless steel band test sample;
Step 2:Setup test equipment, including balance, semiclosed lucite platform, permanent magnet;
Step 3:The stainless steel band test sample of step 1 is placed on the weighing platform of balance, weighed, records weight data
m1;
Step 4:Semiclosed lucite platform is covered on balance, closing space is formed between balance, is kept semiclosed organic
Glass platform does not contact with the weighing platform of balance;Permanent magnet plane is placed with semiclosed lucite platform table top, records weight
Data m2;
Step 5:Repeat step three and step 4, obtain three groups of m1And m2;According to formula C=(m1-m2)/m1* 100% calculates magnetic
Property variability index C1, C2, C3, take three groups of statistical average CX, CX< 0.2%, then it is determined as that magnetic is qualified.
2. stainless steel band Magnetic sensing methods according to claim 1, it is characterised in that:Set on the balance with door
Lucite sealed compartment;The lucite sealed compartment bottom centre sets breach, for exposing weighing platform;The step 4
In, the semiclosed lucite edge of table is covered on the gap edge of lucite sealed compartment bottom centre, formed
Weighing platform while closing space not with balance contacts.
3. stainless steel band Magnetic sensing methods according to claim 1, it is characterised in that:In the step 4, ensure day
Flat weighing platform table top is centrally located at and horizontal plane direction with semiclosed lucite platform table top and permanent magnet plane
Same straight line on.
4. stainless steel band Magnetic sensing methods according to claim 2, it is characterised in that:In the step 4, record
After weight data, balance is resetted returned to zero immediately.
5. stainless steel band Magnetic sensing methods according to claim 1, it is characterised in that:, will be to be measured in the step 1
Examination stainless steel band is prepared into 25mm≤length≤100mm, 10mm≤width≤80mm, deviation ± 1mm regular oblong print.
6. stainless steel band Magnetic sensing methods according to claim 1, it is characterised in that:In the step 2, balance is adopted
With minimum range 0.0001g, maximum range 210g AL204- assay balances;100 ± 1mm of diameter of permanent magnet, thickness 20mm
± 1mm, magnetic induction intensity peak value are more than 1000GS;135 ± 5mm of mesa diameter of semiclosed lucite platform, height 52 ±
5mm, 4 ± 0.5mm of wall thickness.
7. stainless steel band Magnetic sensing methods according to claim 1, it is characterised in that:In the step 3, by balance
Zeroing, reservation is small to count to 0.0001g.