CN107606331B - A kind of reinforced concrete sewer pipe - Google Patents
A kind of reinforced concrete sewer pipe Download PDFInfo
- Publication number
- CN107606331B CN107606331B CN201711035696.1A CN201711035696A CN107606331B CN 107606331 B CN107606331 B CN 107606331B CN 201711035696 A CN201711035696 A CN 201711035696A CN 107606331 B CN107606331 B CN 107606331B
- Authority
- CN
- China
- Prior art keywords
- parts
- weight
- emulsion
- reinforced concrete
- fixing layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a kind of reinforced concrete sewer pipes, from outside to inside include: the first fixing layer, pervious bed and the second fixing layer;The thickness ratio of first fixing layer, pervious bed and the second fixing layer is 1-2:1-2:4-6;First fixing layer comprises the following components in parts by weight: the first 90-95 parts of packing material, 3-5 parts of binder and 3-5 parts of preservative;Pervious bed comprises the following components in parts by weight: modified porous cellucotton 94-97 parts, 2-4 parts of binder and 1-2 parts of wetting agent;Second fixing layer comprises the following components in parts by weight: the second 90-95 parts of packing material, 3-5 parts of binder, 3-5 parts of preservative and 20-30 parts of reinforcing material.It is not easy to break in use by the way that the improvement in terms of drain structure and material, which increases, while having stronger corrosion resistance, it is not easy to be influenced by corrosive deposit each in sewage, the service life of drainpipe can be extended.
Description
Technical field
The invention belongs to drainpipe technical fields, and in particular to a kind of reinforced concrete sewer pipe.
Background technique
With the development of urban construction, start to build sewage treatment plant, a large amount of industrial wastewater and sanitary sewage need logical
It crosses drainpipe and enters sewage treatment plant, and often containing acid or other corrosive substances in black water, this requires drainings
Pipe has stronger corrosion resistance, while drainpipe need to carry certain weight, this just need drainpipe mechanical property and
Toughness and intensity are stronger.
But existing drainpipe is generally existing following insufficient: drainpipe intensity is inadequate, and easy fracture, corrosion resistance is poor,
To influence the service life of drainpipe.
Summary of the invention
For above-mentioned deficiency in the prior art, the present invention provides a kind of reinforced concrete sewer pipes, can solve existing
Drainpipe intensity it is inadequate, easy fracture, corrosion resistance is poor, thus the problem of influencing the service life of drainpipe.
To achieve the above object, the technical solution adopted by the present invention to solve the technical problems is:
A kind of reinforced concrete sewer pipe includes: the first fixing layer, pervious bed and the second fixing layer from outside to inside;Wherein,
The thickness ratio of first fixing layer, pervious bed and the second fixing layer is 1-2:1-2:4-6;
First fixing layer comprises the following components in parts by weight: the first 90-95 parts of packing material, 3-5 parts of binder and anti-corrosion
3-5 parts of agent;
Pervious bed comprises the following components in parts by weight: modified porous cellucotton 94-97 parts, 2-4 parts of binder and wetting agent
1-2 parts;Wetting agent is glycerine;
Second fixing layer comprises the following components in parts by weight: the second 90-95 parts of packing material, 3-5 parts of binder, preservative
3-5 parts and reinforcing material 20-30 parts.
The invention has the benefit that the drainpipe includes: that the first fixing layer, pervious bed and second are fixed from outside to inside
Layer.
Second fixing layer mainly plays a part of load capacity, other than it can play the packing material of fixed function, also wraps
Preservative and reinforcing material are included, because of drainpipe mainly transmission city domestic sewage or industrial wastewater, in the water through drainpipe
The antisepsis of drainpipe can be effectively improved containing acid or other corrosive substances, preservative.
Drainpipe can be absorbed when transmitting sewage in material of the portion of water to drainpipe, will affect drainpipe
Service life, we are provided with pervious bed outside the second fixing layer, and it is permeable the moisture in the second fixing layer effectively can be sucked this
Layer, then the effect through this layer discharge moisture, because there is provision of one layer of fixing layer outside the layer, for being held outside load-bearing pervious bed
The weight of load, therefore the first fixing layer is provided with outside pervious bed.
Further, the first packing material comprises the following components in parts by weight: 30-45 parts of cement, hydrotalcite powder 15-25
Part, 15-25 parts of sepiolite, 10-20 parts of haydite, 8-12 parts of sericite and 5-10 parts of apricot spore mushroom waste mushroom.
The invention has the benefit that sepiolite, nontoxic, tasteless, there is extremely strong adsorptivity, decolourising property and thermostabilization
Property, become soft after water suction, and be hardened after drying, large specific surface area has unique cellular structure and caking property, this
Also there is corrosion resistance and radiation resistance outside.
Hydrotalcite powder, good fluidity, ventilative water permeability and intensity are high.
Haydite, density is small, internal porous, and porosity is high, and has some strength and robustness, in addition, there are also corrosion-resistant,
It is freeze proof, the effect of antidetonation.
The water penetrations such as hydrotalcite powder, sepiolite, haydite are strong, under the water penetration effect of these substances, sepiolite and apricot spore
Apricot spore mushroom mycelium in mushroom waste mushroom, which absorbs water, becomes soft, to increase the hole of its concrete, be conducive to it is permeable,
It is hardened after drying, is conducive to the intensity for enhancing concrete, prolongs its service life;Sepiolite, apricot spore mushroom waste mushroom (including are adopted
Remaining compost and mycelium after receipts) adsorptivity, decolourising property are all had, sundries, dye in adsorbable penetrated waste water
Material etc., can to preliminary processing is carried out through sewage.
Furthermore sericite, heat-resisting, acid and alkali-resistance erosion, wear-resistant, anti-aging, uvioresistant, has viscosity.The substance is playing
When fixed function, it can also be cooperateed in conjunction with binder and play the role of gluing, be conducive to for each component being bonded together, enhanced
Its intensity.Sepiolite, sericite can also play synergistic effect in terms of corrosion resistance and radiation resistance, fixed in conjunction with first
The preservative of layer, can enhance the antiseptic property of drainpipe, and then extend its service life.
Further, the first packing material comprises the following components in parts by weight: 40 parts of cement, 18 parts of hydrotalcite powder, Hai Pao
20 parts of stone, 12 parts of haydite, 10 parts of sericite and 8 parts of apricot spore mushroom waste mushroom;
Further, the second packing material comprises the following components in parts by weight: 30-45 parts of cement, hydrotalcite powder 15-25
Part, 15-25 parts of sepiolite, 10-20 parts of haydite, 8-12 parts of sericite, 5-10 parts of apricot spore mushroom waste mushroom, 5-10 parts of metakaolin,
6-12 parts of calcined diatomite, 20-40 parts of the regenerated coarse aggregate and partial size≤0.15mm recycled fine aggregate that partial size is 15-30mm
10-20 parts.
The invention has the benefit that effect of second packing material in drainpipe is very crucial, therefore, filled out first
Fill on the basis of material and increase metakaolin, calcined diatomite, the regenerated coarse aggregate that partial size is 15-30mm and partial size≤
The recycled fine aggregate of 0.15mm.
Metakaolin is a kind of high-activity mineral blending material, has good filing effect in concrete, can be improved mixed
Coagulate microstructure, intensity and the durability of soil.
Calcined diatomite has the characteristics that specific surface area height, finer grain size, is used to inside fill concrete cement matrix
Gap, to improve the compactness of concrete substrate, mechanical property and impervious frost resistance.
Raw coarse aggregate and recycled fine aggregate are prepared by the following method to obtain: being by maximum particle diameter by bulk cement concrete
45mm is crushed, and broken aggregate is sieved, obtain partial size be 15-30mm regenerated coarse aggregate and partial size≤
The recycled fine aggregate of 0.15mm, the present invention are re-used recycled aggregate, reduce its cost.
Further, the second packing material comprises the following components in parts by weight: 40 parts of cement, 18 parts of hydrotalcite powder, Hai Pao
20 parts of stone, 12 parts of haydite, 10 parts of sericite, 8 parts of apricot spore mushroom waste mushroom, 8 parts of metakaolin, 8 parts of calcined diatomite, partial size are
15 parts of 30 parts of the regenerated coarse aggregate of 15-30mm and partial size≤0.15mm recycled fine aggregate.
Further, preservative comprises the following components in parts by weight: 5-10 parts of epoxy resin, 3-8 parts of curing agent, SILICA FUME
4-8 parts, 3-10 parts of iron oxide and 3-8 parts of aluminium powder.
Preservative is prepared by the following method to obtain: with water being by weight that 1:2 is mixed by epoxy resin, is heated to 70-
80 DEG C, 1-2h is kept the temperature, curing agent is then added, mixed, keep the temperature 2-3h, add SILICA FUME, iron oxide and aluminium powder, mixing is equal
Even, cooled to room temperature is made.
The invention has the benefit that the epoxy resin in preservative, strand is long, and molecular weight is bigger, can assign
Give the good flexibility of preservative and caking property, while phenols curing agent and magnesia combine, make epoxy resin formed it is insoluble not
Molten, scleroid tridimensional network can be good at being adhered to rebar surface;SILICA FUME is filler, can improve preservative
Viscosity and compactness;The preservative and reinforcing bar excellent bonding performance, compact structure fast in conjunction with speed can effectively enhance drainpipe
Corrosion resistance, while can also with concrete structure formed stable bond, enhance its intensity;Magnesia is curing agent, can be real
The normal temperature cure of existing preservative.
Further, reinforcing material comprises the following components in parts by weight: 90-100 parts of reinforcing bar, 2-4 parts of castor oil and sponge gourd
5-10 parts of network;
Reinforcing material is prepared by the following method to obtain: after rebar surface is derusted, then smearing one layer of castor oil, then
One layer of luffa is covered again, is made.
The invention has the benefit that rebar surface after derusting, then smears one layer of castor oil, then covers one again
Layer luffa, the luffa can further improve the antiseptic property of reinforcing bar, and material surface is uneven, can also further increase
Frictional force between big reinforcing bar and concrete, and then improve its caking property.
Further, modified porous cellucotton is modified by the way that porous fibre cotton moisture-absorption modifier is added in porous fibre cotton
It obtains;Wherein, porous fibre cotton moisture-absorption modifier additional amount is 1-3wt%, and porous fibre cotton moisture-absorption modifier includes following heavy
Measure the component of percentage:
PVP K30 10-20wt%, polyvinyl acetate emulsion 2-3wt%, acrylic acid 7-9wt%, gather
Ethylene glycol 10-13wt%, aqueous epoxy resin emulsion 1-2wt%, polyaminoester emulsion 2-3wt%, organic silicon emulsion 1-2wt%,
Surplus is water;
Wherein, organic silicon emulsion is simethicone emulsion or the modification simethicone emulsion containing aromatic radical;Polyurethane
Lotion is polyether polyol or polyesterpolyol polyurethane lotion;
Porous fibre cotton moisture-absorption modifier is prepared by following methods:
PVP K30, polyvinyl acetate emulsion, acrylic acid, polyethylene glycol, water are weighed according to formula rate
Property epoxy resin latex, polyaminoester emulsion and organic silicon emulsion, and it is diluted with water or is dissolved respectively, then it is blended in one
It rises, and the water of rated capacity is added, after mixing, obtain.
The invention has the benefit that being modified by the way that cellucotton moisture-absorption modifier is added in porous fibre cotton, make
The wettability power of porous cellucotton is greatly enhanced, effectively solve that existing porous fibre cotton substrate water absorbing capacity is low to ask
Topic;Meanwhile the modified porous cellucotton effectively cooperates with binder and wetting agent, substantially increases the water absorbing capacity of porous fibre cotton
Power;Constitutive material of the invention is nontoxic, harmless, environmentally protective, has huge application potential.
Further, porous fibre cotton moisture-absorption modifier includes following components in percentage by weight:
PVP K30 20wt%, polyvinyl acetate emulsion 3wt%, acrylic acid 9wt%, polyethylene glycol
10wt%, aqueous epoxy resin emulsion 1wt%, polyaminoester emulsion 2wt%, organic silicon emulsion 1wt% and water 54wt%.
Further, binder includes following components in percentage by weight:
Waterglass 60-80wt%, polyvinyl alcohol 10-20wt%, surplus are crosslinking agent ethyl orthosilicate;
The binder is prepared by following methods:
Crosslinking agent ethyl orthosilicate, obtained solution A are added in water glass solution;
Solution A and poly-vinyl alcohol solution are separately heated to 40-50 DEG C, under stirring conditions, solution A is slowly added to
It into poly-vinyl alcohol solution, after mixing, stirs 30min-1 hours, is cooled to room temperature at 50-60 DEG C, be made.
The invention has the benefit that preparing binder by using the substance with special formulation content, greatly increase
The binder is applied in the compositing formula of porous fibre cotton, with modified porous cellucotton by the hydrophilic ability of the binder
It combines, more improves the water absorbing capacity of porous fibre cotton.
Reinforced concrete sewer pipe provided by the invention, has the advantages that
By the specific combination in terms of the structure improvement to drainpipe and material, which increases
Add, it is not easy to break in use, while having stronger corrosion resistance, it is not easy to be influenced by corrosive deposit each in sewage,
The service life of drainpipe can be extended.
Specific embodiment
Embodiment 1
A kind of reinforced concrete sewer pipe, which is characterized in that from outside to inside include: the first fixing layer, pervious bed and second
Fixing layer;Wherein, the thickness ratio of the first fixing layer, pervious bed and the second fixing layer is 1:1:4;
First fixing layer comprises the following components in parts by weight: the first 90 parts of packing material, 3 parts of binder and 3 parts of preservative.
First packing material comprises the following components in parts by weight: 30 parts of cement, 15 parts of hydrotalcite powder, 15 parts of sepiolite, pottery
10 parts of grain, 8 parts of sericite and 5 parts of apricot spore mushroom waste mushroom.
Second fixing layer comprises the following components in parts by weight: the second 90 parts of packing material, 3 parts of binder, 3 parts of preservative and
20 parts of reinforcing material.
Second packing material comprises the following components in parts by weight: 30 parts of cement, 15 parts of hydrotalcite powder, 15 parts of sepiolite, pottery
Grain 10 parts, 8 parts of sericite, 5 parts of apricot spore mushroom waste mushroom, 5 parts of metakaolin, 6 parts of calcined diatomite, partial size be 15-30mm again
10 parts of 20 parts of raw coarse aggregate and partial size≤0.15mm recycled fine aggregate.
Pervious bed comprises the following components in parts by weight: 94 parts of modified porous cellucotton, 2 parts of binder and 1 part of wetting agent;It is wet
Profit agent is glycerine.
Modified porous cellucotton is obtained by the way that the modification of porous fibre cotton moisture-absorption modifier is added in porous fibre cotton;Its
In, porous fibre cotton moisture-absorption modifier additional amount is 1wt%, and porous fibre cotton moisture-absorption modifier includes following weight percent
Component:
PVP K30 10wt%, polyvinyl acetate emulsion 2wt%, acrylic acid 7wt%, polyethylene glycol
10wt%, aqueous epoxy resin emulsion 1wt%, polyaminoester emulsion 2wt%, organic silicon emulsion 1wt%, surplus are water;
Wherein, organic silicon emulsion is simethicone emulsion or the modification simethicone emulsion containing aromatic radical;Polyurethane
Lotion is polyether polyol or polyesterpolyol polyurethane lotion;
Porous fibre cotton moisture-absorption modifier is prepared by following methods:
PVP K30, polyvinyl acetate emulsion, acrylic acid, polyethylene glycol, water are weighed according to formula rate
Property epoxy resin latex, polyaminoester emulsion and organic silicon emulsion, and it is diluted with water or is dissolved respectively, then it is blended in one
It rises, and the water of rated capacity is added, after mixing, obtain.
Binder includes following components in percentage by weight:
Waterglass 60wt%, polyvinyl alcohol 10wt%, surplus are crosslinking agent ethyl orthosilicate;
The binder is prepared by following methods:
Crosslinking agent ethyl orthosilicate, obtained solution A are added in water glass solution;
Solution A and poly-vinyl alcohol solution are separately heated to 40 DEG C, under stirring conditions, solution A is slowly added into
In poly-vinyl alcohol solution, after mixing, 30min is stirred at 50 DEG C, is cooled to room temperature, is made.
Preservative comprises the following components in parts by weight: 5 parts of epoxy resin, 3 parts of curing agent, 4 parts of SILICA FUME, 3 parts of iron oxide
With 3 parts of aluminium powder.
Preservative is prepared by the following method to obtain: with water being by weight that 1:2 is mixed by epoxy resin, is heated to 70
DEG C, 2h is kept the temperature, curing agent is then added, is mixed, 2h is kept the temperature, adds SILICA FUME, iron oxide and aluminium powder, is uniformly mixed, from
It is so cooled to room temperature, is made.
Reinforcing material comprises the following components in parts by weight: 90 parts of reinforcing bar, 2 parts of castor oil and 5 parts of luffa;
Reinforcing material is prepared by the following method to obtain: after rebar surface is derusted, then smearing one layer of castor oil, then
One layer of luffa is covered again, is made.
Above-mentioned material is prepared into reinforced concrete sewer pipe, and detects its each performance, testing result is as follows:
Acidproof and alkali corrosion resistance coefficient >=0.88, drainpipe cracking load >=63kN/m, failing load >=89kN/m reach
I grade of Guan Yaoqiu of Φ 1200mm reinforced concrete sewer pipe.
Embodiment 2
A kind of reinforced concrete sewer pipe, which is characterized in that from outside to inside include: the first fixing layer, pervious bed and second
Fixing layer;Wherein, the thickness ratio of the first fixing layer, pervious bed and the second fixing layer is 2:2:6;
First fixing layer comprises the following components in parts by weight: the first 95 parts of packing material, 5 parts of binder and 5 parts of preservative.
First packing material comprises the following components in parts by weight: 45 parts of cement, 25 parts of hydrotalcite powder, 25 parts of sepiolite, pottery
20 parts of grain, 12 parts of sericite and 10 parts of apricot spore mushroom waste mushroom.
Second fixing layer comprises the following components in parts by weight: the second 95 parts of packing material, 5 parts of binder, 5 parts of preservative and
30 parts of reinforcing material.
Second packing material comprises the following components in parts by weight: 45 parts of cement, 25 parts of hydrotalcite powder, 25 parts of sepiolite, pottery
Grain 20 parts, 12 parts of sericite, 10 parts of apricot spore mushroom waste mushroom, 10 parts of metakaolin, 12 parts of calcined diatomite, partial size 15-30mm
20 parts of 40 parts of regenerated coarse aggregate and partial size≤0.15mm recycled fine aggregate.
Pervious bed comprises the following components in parts by weight: 97 parts of modified porous cellucotton, 4 parts of binder and 2 parts of wetting agent;It is wet
Profit agent is glycerine.
Modified porous cellucotton is obtained by the way that the modification of porous fibre cotton moisture-absorption modifier is added in porous fibre cotton;Its
In, porous fibre cotton moisture-absorption modifier additional amount is 3wt%, and porous fibre cotton moisture-absorption modifier includes following weight percent
Component:
PVP K30 20wt%, polyvinyl acetate emulsion 3wt%, acrylic acid 9wt%, polyethylene glycol
13wt%, aqueous epoxy resin emulsion 2wt%, polyaminoester emulsion 3wt%, organic silicon emulsion 2wt%, surplus are water;
Wherein, organic silicon emulsion is simethicone emulsion or the modification simethicone emulsion containing aromatic radical;Polyurethane
Lotion is polyether polyol or polyesterpolyol polyurethane lotion;
Porous fibre cotton moisture-absorption modifier is prepared by following methods:
PVP K30, polyvinyl acetate emulsion, acrylic acid, polyethylene glycol, water are weighed according to formula rate
Property epoxy resin latex, polyaminoester emulsion and organic silicon emulsion, and it is diluted with water or is dissolved respectively, then it is blended in one
It rises, and the water of rated capacity is added, after mixing, obtain.
Binder includes following components in percentage by weight:
Waterglass 80wt%, polyvinyl alcohol 20wt%, surplus are crosslinking agent ethyl orthosilicate;
The binder is prepared by following methods:
Crosslinking agent ethyl orthosilicate, obtained solution A are added in water glass solution;
Solution A and poly-vinyl alcohol solution are separately heated to 50 DEG C, under stirring conditions, solution A is slowly added into
In poly-vinyl alcohol solution, after mixing, 30min is stirred at 50 DEG C, is cooled to room temperature, is made.
Preservative comprises the following components in parts by weight: 10 parts of epoxy resin, 8 parts of curing agent, 8 parts of SILICA FUME, iron oxide 10
Part and 8 parts of aluminium powder.
Preservative is prepared by the following method to obtain: with water being by weight that 1:2 is mixed by epoxy resin, is heated to 80
DEG C, 1h is kept the temperature, curing agent is then added, is mixed, 2h is kept the temperature, adds SILICA FUME, iron oxide and aluminium powder, is uniformly mixed, from
It is so cooled to room temperature, is made.
Reinforcing material comprises the following components in parts by weight: 100 parts of reinforcing bar, 4 parts of castor oil and 10 parts of luffa;
Reinforcing material is prepared by the following method to obtain: after rebar surface is derusted, then smearing one layer of castor oil, then
One layer of luffa is covered again, is made.
Above-mentioned material is prepared into reinforced concrete sewer pipe, and detects its each performance, testing result is as follows:
Acidproof and alkali corrosion resistance coefficient >=0.85, drainpipe cracking load >=66kN/m, failing load >=92kN/m reach
I grade of Guan Yaoqiu of Φ 1200mm reinforced concrete sewer pipe.
Embodiment 3
A kind of reinforced concrete sewer pipe, which is characterized in that from outside to inside include: the first fixing layer, pervious bed and second
Fixing layer;Wherein, the thickness ratio of the first fixing layer, pervious bed and the second fixing layer is 1:1:5;
First fixing layer comprises the following components in parts by weight: the first 92 parts of packing material, 4 parts of binder and 4 parts of preservative.
First packing material comprises the following components in parts by weight: 40 parts of cement, 18 parts of hydrotalcite powder, 20 parts of sepiolite, pottery
12 parts of grain, 10 parts of sericite and 8 parts of apricot spore mushroom waste mushroom.
Second fixing layer comprises the following components in parts by weight: the second 92 parts of packing material, 5 parts of binder, 4 parts of preservative and
25 parts of reinforcing material.
Second packing material comprises the following components in parts by weight: 40 parts of cement, 18 parts of hydrotalcite powder, 20 parts of sepiolite, pottery
Grain 12 parts, 10 parts of sericite, 8 parts of apricot spore mushroom waste mushroom, 8 parts of metakaolin, 8 parts of calcined diatomite, partial size be 15-30mm again
15 parts of 30 parts of raw coarse aggregate and partial size≤0.15mm recycled fine aggregate.
Pervious bed comprises the following components in parts by weight: 94 parts of modified porous cellucotton, 4 parts of binder and 2 parts of wetting agent;It is wet
Profit agent is glycerine.
Modified porous cellucotton is obtained by the way that the modification of porous fibre cotton moisture-absorption modifier is added in porous fibre cotton;Its
In, porous fibre cotton moisture-absorption modifier additional amount is 2wt%, and porous fibre cotton moisture-absorption modifier includes following weight percent
Component:
PVP K30 20wt%, polyvinyl acetate emulsion 3wt%, acrylic acid 9wt%, polyethylene glycol
10wt%, aqueous epoxy resin emulsion 1wt%, polyaminoester emulsion 2wt%, organic silicon emulsion 1wt% and water 54wt%;
Wherein, organic silicon emulsion is simethicone emulsion or the modification simethicone emulsion containing aromatic radical;Polyurethane
Lotion is polyether polyol or polyesterpolyol polyurethane lotion;
Porous fibre cotton moisture-absorption modifier is prepared by following methods:
PVP K30, polyvinyl acetate emulsion, acrylic acid, polyethylene glycol, water are weighed according to formula rate
Property epoxy resin latex, polyaminoester emulsion and organic silicon emulsion, and it is diluted with water or is dissolved respectively, then it is blended in one
It rises, and the water of rated capacity is added, after mixing, obtain.
Binder includes following components in percentage by weight:
Waterglass 70wt%, polyvinyl alcohol 15wt% and crosslinking agent ethyl orthosilicate 15wt%;
The binder is prepared by following methods:
Crosslinking agent ethyl orthosilicate, obtained solution A are added in water glass solution;
Solution A and poly-vinyl alcohol solution are separately heated to 50 DEG C, under stirring conditions, solution A is slowly added into
In poly-vinyl alcohol solution, after mixing, 40min is stirred at 50 DEG C, is cooled to room temperature, is made.
Preservative comprises the following components in parts by weight: 8 parts of epoxy resin, 6 parts of curing agent, 5 parts of SILICA FUME, 4 parts of iron oxide
With 6 parts of aluminium powder.
Preservative is prepared by the following method to obtain: with water being by weight that 1:2 is mixed by epoxy resin, is heated to 70
DEG C, 2h is kept the temperature, curing agent is then added, is mixed, 2h is kept the temperature, adds SILICA FUME, iron oxide and aluminium powder, is uniformly mixed, from
It is so cooled to room temperature, is made.
Reinforcing material comprises the following components in parts by weight: 100 parts of reinforcing bar, 3 parts of castor oil and 7 parts of luffa;Reinforcing material
It is prepared by the following method to obtain: after rebar surface is derusted, then smearing one layer of castor oil, then cover one layer of sponge gourd again
Network is made.
Above-mentioned material is prepared into reinforced concrete sewer pipe, and detects its each performance, testing result is as follows:
Acidproof and alkali corrosion resistance coefficient >=0.93, drainpipe cracking load >=68kN/m, failing load >=93kN/m reach
I grade of Guan Yaoqiu of Φ 1200mm reinforced concrete sewer pipe.
Claims (9)
1. a kind of reinforced concrete sewer pipe, which is characterized in that from outside to inside include: that the first fixing layer, pervious bed and second are solid
Given layer;Wherein, the thickness ratio of the first fixing layer, pervious bed and the second fixing layer is 1-2:1-2:4-6;
First fixing layer comprises the following components in parts by weight: the first 90-95 parts of packing material, 3-5 parts of binder and preservative 3-5
Part;
Wherein, the first packing material comprises the following components in parts by weight: 30-45 parts of cement, 15-25 parts of hydrotalcite powder, sepiolite
15-25 parts, 10-20 parts of haydite, 8-12 parts of sericite and 5-10 parts of apricot spore mushroom waste mushroom;
Pervious bed comprises the following components in parts by weight: modified porous cellucotton 94-97 parts, 2-4 parts of binder and wetting agent 1-2
Part;Wetting agent is glycerine;
Second fixing layer comprises the following components in parts by weight: the second 90-95 parts of packing material, 3-5 parts of binder, preservative 3-5
Part and reinforcing material 20-30 parts.
2. reinforced concrete sewer pipe according to claim 1, which is characterized in that the first packing material includes following weight
The component of part: 40 parts of cement, 18 parts of hydrotalcite powder, 20 parts of sepiolite, 12 parts of haydite, 10 parts of sericite and apricot spore mushroom waste mushroom 8
Part.
3. reinforced concrete sewer pipe according to claim 1, which is characterized in that the second packing material includes following weight
Part component: 30-45 parts of cement, 15-25 parts of hydrotalcite powder, 15-25 parts of sepiolite, 10-20 parts of haydite, 8-12 parts of sericite,
5-10 parts of apricot spore mushroom waste mushroom, 5-10 parts of metakaolin, 6-12 parts of calcined diatomite, the regenerated coarse aggregate that partial size is 15-30mm
20-40 parts and 10-20 parts of partial size≤0.15mm recycled fine aggregate.
4. reinforced concrete sewer pipe according to claim 1, which is characterized in that the second packing material includes following weight
The component of part: 40 parts of cement, 18 parts of hydrotalcite powder, 20 parts of sepiolite, 12 parts of haydite, 10 parts of sericite, apricot spore mushroom waste mushroom 8
Part, 30 parts of the regenerated coarse aggregate that 8 parts of metakaolin, 8 parts of calcined diatomite, partial size are 15-30mm and partial size≤0.15mm are again
Raw 15 parts of fine aggregate.
5. reinforced concrete sewer pipe according to claim 1, which is characterized in that preservative includes the group of following parts by weight
Point: 5-10 parts of epoxy resin, 3-8 parts of curing agent, 4-8 parts of SILICA FUME, 3-10 parts of iron oxide and 3-8 parts of aluminium powder;
Preservative is prepared by the following method to obtain: with water by weight it is that 1:2 is mixed by epoxy resin, is heated to 70-80 DEG C,
1-2h is kept the temperature, curing agent is then added, is mixed, 2-3h is kept the temperature, adds SILICA FUME, iron oxide and aluminium powder, is uniformly mixed, from
It is so cooled to room temperature, is made.
6. reinforced concrete sewer pipe according to claim 1, which is characterized in that reinforcing material includes following parts by weight
Component: 90-100 parts of reinforcing bar, 2-4 parts of castor oil and 5-10 parts of luffa;
Reinforcing material is prepared by the following method to obtain: after rebar surface is derusted, then smearing one layer of castor oil, then covers again
One layer of luffa of lid is made.
7. reinforced concrete sewer pipe according to claim 1, which is characterized in that modified porous cellucotton passes through porous
The modification of porous fibre cotton moisture-absorption modifier is added in cellucotton to obtain;Wherein, porous fibre cotton moisture-absorption modifier additional amount is 1-
3wt%, porous fibre cotton moisture-absorption modifier includes following components in percentage by weight:
PVP K30 10-20wt%, polyvinyl acetate emulsion 2-3wt%, acrylic acid 7-9wt%, poly- second two
Alcohol 10-13wt%, aqueous epoxy resin emulsion 1-2wt%, polyaminoester emulsion 2-3wt%, organic silicon emulsion 1-2wt%, surplus
For water;
Wherein, organic silicon emulsion is simethicone emulsion or the modification simethicone emulsion containing aromatic radical;Polyaminoester emulsion
It is polyether polyol or polyesterpolyol polyurethane lotion;
Porous fibre cotton moisture-absorption modifier is prepared by following methods:
PVP K30, polyvinyl acetate emulsion, acrylic acid, polyethylene glycol, aqueous ring are weighed according to formula rate
Oxygen resin emulsion, polyaminoester emulsion and organic silicon emulsion, and it is diluted with water or is dissolved respectively, then mix, and
The water that rated capacity is added obtains after mixing.
8. reinforced concrete sewer pipe according to claim 7, which is characterized in that porous fibre cotton moisture-absorption modifier includes
Following components in percentage by weight:
PVP K30 20wt%, polyvinyl acetate emulsion 3wt%, acrylic acid 9wt%, polyethylene glycol
10wt%, aqueous epoxy resin emulsion 1wt%, polyaminoester emulsion 2wt%, organic silicon emulsion 1wt% and water 54wt%.
9. reinforced concrete sewer pipe according to claim 1, which is characterized in that binder includes following weight percent
Component:
Waterglass 60-80wt%, polyvinyl alcohol 10-20wt%, surplus are crosslinking agent ethyl orthosilicate;
The binder is prepared by following methods:
Crosslinking agent ethyl orthosilicate, obtained solution A are added in water glass solution;
Solution A and poly-vinyl alcohol solution are separately heated to 40-50 DEG C, under stirring conditions, solution A is slowly added into poly-
It in glycohol solution, after mixing, stirs 30min-1 hours, is cooled to room temperature at 50-60 DEG C, be made.