CN107604702A - A kind of One Bath Dyeing Process of acid dyes and blend dye - Google Patents
A kind of One Bath Dyeing Process of acid dyes and blend dye Download PDFInfo
- Publication number
- CN107604702A CN107604702A CN201710850852.3A CN201710850852A CN107604702A CN 107604702 A CN107604702 A CN 107604702A CN 201710850852 A CN201710850852 A CN 201710850852A CN 107604702 A CN107604702 A CN 107604702A
- Authority
- CN
- China
- Prior art keywords
- dye
- dye vat
- steps
- acid dyes
- blend
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of acid dyes and the One Bath Dyeing Process of blend dye, it is characterised in that:Comprise the following steps:At normal temperatures, fabric is imported into dye vat, nylon antitack agent is added in dye vat;Acid dyes is added in dye vat;Blend dye is added in dye vat;Glauber salt is added in dye vat;Dyeing is completed in cooling after the bath temperature of dye vat is completed into heating for the first time from normal temperature and heated up for the second time.The present invention is once cooled by heating up twice, and the technique that traditional handicraft needs the dyeing of two steps to complete disposably is completed in same dye vat, has the characteristics of energy consumption is small, environmentally friendly.
Description
Technical field
The invention belongs to fabric printing field, the one-bath dyeing work of more particularly to a kind of acid dyes and blend dye
Skill.
Background technology
Traditional N/R fabrics need to dye twice, the first step dyeing for acid dyes dyeing, will acid dye vat water temperature by
Normal temperature rises to 98 DEG C and dyed, time 30min;Second step dyeing is blend dyeing, by blending dye vat water temperature by normal temperature liter
Dyed to 95 DEG C, time 20min.Traditional dyeing process needs two dye vats, heats up twice, has what is taken time and effort to lack
Fall into.
The content of the invention
The invention provides a kind of acid dyes and the One Bath Dyeing Process of blend dye, one step solves to dye twice
Technique, it has the characteristics of energy consumption is small, environmentally friendly.
To reach above-mentioned purpose, concrete scheme of the invention is as follows:
A kind of One Bath Dyeing Process of acid dyes and blend dye, comprises the following steps:
The first step, at normal temperatures, fabric is imported into dye vat, nylon antitack agent is added in dye vat;
Second step, after some time, acid dyes is added in dye vat;
3rd step, after some time, blend dye is added in dye vat;
4th step, after some time, glauber salt is added in dye vat;
5th step, acetic acid is added, and the bath temperature of dye vat is heated up and maintained;
6th step, the bath temperature of dye vat is heated up and maintained again;
7th step, the bath temperature of dye vat is cooled, complete dyeing.
Preferably,
The second step concretely comprises the following steps:After 4-6min, acid dyes is added in dye vat.
3rd step concretely comprises the following steps:After 8-12min, blend dye is added in dye vat.
4th step concretely comprises the following steps:After 4-6min, glauber salt is added in dye vat.
5th step concretely comprises the following steps:The bath temperature by dye vat is warming up to 80 ± 5 DEG C from normal temperature, maintains 8-
12min;The programming rate is 1.2 DEG C/min.
6th step concretely comprises the following steps:The bath temperature of dye vat is warming up to 95 ± 5 DEG C from 80 ± 5 DEG C, maintains 24-
36min;The programming rate is 1.2 DEG C/min.
7th step concretely comprises the following steps:, the bath temperature of dye vat is cooled to 70 ± 5 DEG C from 95 ± 5 DEG C;The heating speed
Spend for 2 DEG C/min.
The nylon antitack agent addition is 0.8-1.2g/L.
The addition of the glauber salt is 5-15g/L.
The acetic acid is 100% acetic acid, and the acetic acid addition is 0.2-0.4g/L
The present invention is once cooled by heating up twice, and traditional handicraft is disposably completed in same dye vat needs the dyeing of two steps to complete
Technique, have energy consumption it is small, it is environmentally friendly the characteristics of.
The present invention is further elaborated below by way of brief description of the drawings and embodiment.
Brief description of the drawings
Fig. 1 is the step schematic diagram of the embodiment of the present invention 1.
Embodiment
Purchasing of raw materials side:
Nylon antitack agent RF is purchased from Clariant Corporation;
Glauber salt is purchased from An Xin Chemical Co., Ltd.s of Shaoxin City.
Definition:
Acid dyes is the water-soluble dye that acidic-group is carried on a class formation, is dyed in acid medium.Acidity dye
Material is most of to contain sulfonate sodium, can be dissolved in water, and lovely luster, chromatogram are complete.It is mainly used in the dye such as wool, silk and polyamide fibre
Color, it can also be used to leather, paper, ink etc..To the general non-coloring power of cellulose fibre.
Blend dye is also known as composite dye, is formed by two or more dyestuff blendings of different nature, or can be by one kind simultaneously
The dyestuff of upper two kinds of fibers of dye is formed.The co-bathing dyeing of the fiber mixed fabrics different for two or more dyeabilities.Such as use
In the polyester cotton blend dye of polyester/cotton blended fabric printing and dyeing.
Embodiment 1
A kind of One Bath Dyeing Process of acid dyes and blend dye, as shown in figure 1, comprising the following steps:
The first step, in normal temperature(25℃)Under, fabric is imported into dye vat, nylon antitack agent RF is added in dye vat;The nylon is prevented
Stick RF is 1 g/L(Nylon antitack agent and amount of solution ratio in dye vat);
Second step, after 5min, acid dyes is added in dye vat;
3rd step, after 10min, blend dye is added in dye vat;
4th step, after 5min, glauber salt is added in dye vat;The addition of the glauber salt is 10g/L;
5th step, 100% acetic acid is added, the acetic acid addition is 0.3g/L
80 DEG C are warming up to from normal temperature with 1.2 DEG C/min speed, maintains 10min;
6th step, 90 DEG C are warming up to from 80 DEG C with 1.2 DEG C/min speed, maintains 30min;
7th step, 70 DEG C are cooled to from 90 DEG C with 2 DEG C/min speed, completes dyeing.
Embodiment 2
A kind of One Bath Dyeing Process of acid dyes and blend dye, comprises the following steps:
The first step, in normal temperature(25℃)Under, fabric is imported into dye vat, nylon antitack agent RF is added in dye vat;The nylon is prevented
Stick RF is 0.8 g/L(Nylon antitack agent and amount of solution ratio in dye vat);
Second step, after 4min, acid dyes is added in dye vat;
3rd step, after 8min, blend dye is added in dye vat;
4th step, after 4min, glauber salt is added in dye vat;The addition of the glauber salt is 5g/L;
5th step, 100% acetic acid is added, the acetic acid addition is 0.2g/L, and is heated up with 1.2 DEG C/min speed from normal temperature
To 75 DEG C, 10min is maintained;
6th step, 90 DEG C are warming up to from 75 DEG C with 1.2 DEG C/min speed, maintains 30min;
7th step, 65 DEG C are cooled to from 90 DEG C with 2 DEG C/min speed, completes dyeing.Embodiment 3
A kind of One Bath Dyeing Process of acid dyes and blend dye, comprises the following steps:
The first step, in normal temperature(25℃)Under, fabric is imported into dye vat, nylon antitack agent RF is added in dye vat;The nylon is prevented
Stick RF is 1.2 g/L(Nylon antitack agent and amount of solution ratio in dye vat);
Second step, after 6min, acid dyes is added in dye vat;
3rd step, after 12min, blend dye is added in dye vat;
4th step, after 6min, glauber salt is added in dye vat;The addition of the glauber salt is 15g/L;
5th step, adds 100% acetic acid, and the acetic acid addition is that 0.4g/L is warming up to 1.2 DEG C/min speed from normal temperature
85 DEG C, maintain 10min;
6th step, 100 DEG C are warming up to from 85 DEG C with 1.2 DEG C/min speed, maintains 30min;
7th step, 75 DEG C are cooled to from 100 DEG C with 2 DEG C/min speed, completes dyeing.
Embodiment 4
A kind of One Bath Dyeing Process of acid dyes and blend dye, comprises the following steps:
The first step, in normal temperature(25℃)Under, fabric is imported into dye vat, nylon antitack agent RF is added in dye vat;The nylon is prevented
Stick RF is 1.1 g/L(Nylon antitack agent and amount of solution ratio in dye vat);
Second step, after 5min, acid dyes is added in dye vat;
3rd step, after 11min, blend dye is added in dye vat;
4th step, after 5min, glauber salt is added in dye vat;The addition of the glauber salt is 12g/L;
5th step, 100% acetic acid is added, the acetic acid addition is 0.25g/L, is heated up with 1.2 DEG C/min speed from normal temperature
To 83 DEG C, 10min is maintained;
6th step, 95 DEG C are warming up to from 83 DEG C with 1.2 DEG C/min speed, maintains 30min;
7th step, 72 DEG C are cooled to from 95 DEG C with 2 DEG C/min speed, completes dyeing.
The above embodiments are merely illustrative of the technical solutions of the present invention and it is unrestricted, those of ordinary skill in the art are to this hair
Other modifications or equivalent substitution that bright technical scheme is made, without departing from the spirit and scope of technical solution of the present invention,
It all should cover in scope of the presently claimed invention.
Claims (10)
- A kind of 1. One Bath Dyeing Process of acid dyes and blend dye, it is characterised in that:Comprise the following steps:The first step, fabric is imported into dye vat, nylon antitack agent is added in dye vat;Second step, add acid dyes;3rd step, add blend dye;4th step, add glauber salt;5th step, acetic acid is added, and the bath temperature of dye vat is heated up and maintained;6th step, the bath temperature of dye vat is heated up and maintained again;7th step, the bath temperature of dye vat is cooled.
- 2. the One Bath Dyeing Process of acid dyes according to claim 1 and blend dye, it is characterised in that:Described Two steps concretely comprise the following steps:After 4-6min, acid dyes is added in dye vat.
- 3. the One Bath Dyeing Process of acid dyes according to claim 1 and blend dye, it is characterised in that:Described Three steps concretely comprise the following steps:After 8-12min, blend dye is added in dye vat.
- 4. the One Bath Dyeing Process of acid dyes according to claim 1 and blend dye, it is characterised in that:Described Four steps concretely comprise the following steps:After 4-6min, glauber salt is added in dye vat.
- 5. the One Bath Dyeing Process of acid dyes according to claim 1 and blend dye, it is characterised in that:Described Five steps concretely comprise the following steps:The bath temperature by dye vat is warming up to 80 ± 5 DEG C from normal temperature, maintains 8-12min;The programming rate For 1.2 DEG C/min.
- 6. the One Bath Dyeing Process of acid dyes according to claim 1 and blend dye, it is characterised in that:Described Six steps concretely comprise the following steps:The bath temperature of dye vat is warming up to 95 ± 5 DEG C from 80 ± 5 DEG C, maintains 24-36min;The programming rate For 1.2 DEG C/min.
- 7. the One Bath Dyeing Process of acid dyes according to claim 1 and blend dye, it is characterised in that:Described Seven steps concretely comprise the following steps:, the bath temperature of dye vat is cooled to 70 ± 5 DEG C from 95 ± 5 DEG C;The programming rate is 2 DEG C/min.
- 8. the One Bath Dyeing Process of acid dyes according to claim 1 and blend dye, it is characterised in that:The Buddhist nun Imperial antitack agent addition is 0.8-1.2g/L.
- 9. the One Bath Dyeing Process of acid dyes according to claim 1 and blend dye, it is characterised in that:The member The addition of bright powder is 5-15g/L.
- 10. the One Bath Dyeing Process of acid dyes according to claim 1 and blend dye, it is characterised in that:It is described Acetic acid is 100% acetic acid, and the acetic acid addition is 0.2-0.4g/L.