CN107603630A - A kind of mercury contaminated soil renovation agent and preparation method thereof - Google Patents
A kind of mercury contaminated soil renovation agent and preparation method thereof Download PDFInfo
- Publication number
- CN107603630A CN107603630A CN201710730422.8A CN201710730422A CN107603630A CN 107603630 A CN107603630 A CN 107603630A CN 201710730422 A CN201710730422 A CN 201710730422A CN 107603630 A CN107603630 A CN 107603630A
- Authority
- CN
- China
- Prior art keywords
- parts
- renovation agent
- mercury
- contaminated soil
- soil
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of mercury contaminated soil renovation agent and preparation method thereof, belong to technical field of soil remediation.It is made up of the raw material of following parts by weight:10 20 parts of 10 20 parts of oyster shell whiting, 10 20 parts of kaolin, 5 15 parts of chitosan, 39 parts of oyster shell whiting, 4 10 parts of thiosulfate, 4 10 parts of Chlorococcum, 5 15 parts of diopside and sepiolite.The renovation agent disposal ability of the present invention is strong, secondary pollution will not be produced, realize and polluted soil is effectively repaired while carrying out by mercury in soils and being effectively passivated and fix, so that the mercury activity in soil significantly reduces, the mercury concentration of soil meets the requirement of national second grade soil quality standard after reparation, has good economic benefit and extensive social benefit.
Description
Technical field
The present invention relates to a kind of mercury contaminated soil renovation agent and preparation method thereof, belong to technical field of soil remediation.
Background technology
Heavy metal pollution of soil refers to that due to mankind's activity content of the minor metallic element in soil in soil exceedes
Background value, too high levels caused by excess deposition, is referred to as heavy metal pollution of soil.And farmland soil heavy metals pollution have it is huge
Big harmfulness, heavy metal in soil pollution can not only cause crop production reduction and quality decline, can also pass through soil-plant
System, enters people's human body through food chain, is detrimental to health and life security.Heavy metal pollution of soil has the hysteresis of disguised harm
Property, chronicity and biological chain heavy metal biological concentration the features such as, heavy metal pollution of soil is recognized if these decide
The serious consequence for being difficult to expect will be brought with hysteresis is administered.
The bio-toxicity of mercury (Hg) is more significant, and its heavy metal ion will produce when mass concentration is 0.01-0.001mg/L
Toxigenicity.Mercury in soil can be divided into mercury metal, inorganic reference state mercury and organically combine state mercury by chemical form.Inorganic mercury enters
Mercuric salt is converted into after human body.Cell eubolism is destroyed, influences function of human body;Organic mercury in soil can not only pass through
Microbial degradation reduces its toxicity, can be converted into the bigger methyl mercury of toxicity by methylation on the contrary, biology is caused
Bigger injury.
In consideration of it, it is necessary to research and develop a kind of mercury contaminated soil renovation agent and preparation method thereof, to solve the above problems.
The content of the invention
An object of the present invention, it is to provide a kind of mercury contaminated soil renovation agent.The renovation agent disposal ability of the present invention is strong,
Secondary pollution will not be produced, realizes and polluted soil is carried out effectively while by mercury in soils be effectively passivated and be fixed
Repair, so that the mercury activity in soil significantly reduces, the mercury concentration of soil meets national second grade soil quality mark after reparation
Accurate requirement, has good economic benefit and extensive social benefit.
The technical scheme that the present invention solves above-mentioned technical problem is as follows:A kind of mercury contaminated soil renovation agent, by following weight
The raw material of number is made:Oyster shell whiting 10-20 parts, kaolin 10-20 parts, chitosan 5-15 parts, oyster shell whiting 3-9 parts, thiosulfuric acid
Salt 4-10 parts, Chlorococcum 4-10 parts, diopside 5-15 parts and sepiolite 10-20 parts.
On the basis of above-mentioned technical proposal, the present invention can also do following improvement.
Further, it is made up of the raw material of following parts by weight:15 parts of oyster shell whiting, 15 parts of kaolin, 10 parts of chitosan, shell
15 parts of 6 parts of powder, 7 parts of thiosulfate, 7 parts of Chlorococcum, 10 parts of diopside and sepiolite.
Further, the thiosulfate is potassium thiosulfate, sodium thiosulfate, magnesium thiosulfate, calcium thiosulfate
With one or more of mixtures in ATS (Ammonium thiosulphate).
Further, the kaolinic particle diameter is 50-100 mesh.
Further, the particle diameter of the oyster shell whiting is 50-100 mesh.
Further, the particle diameter of the zeolite is 50-100 mesh.
Further, the particle diameter of the sepiolite is 50-100 mesh.
The second object of the present invention, it is to put on the preparation method for stating mercury contaminated soil renovation agent.The preparation method of the present invention
Simply, wide market, it is adapted to large-scale production.
The technical scheme that the present invention solves above-mentioned technical problem is as follows:A kind of preparation method of mercury contaminated soil renovation agent,
Comprise the following steps:
Take the raw material of following parts by weight:Oyster shell whiting 10-20 parts, kaolin 10-20 parts, chitosan 5-15 parts, oyster shell whiting
3-9 parts, thiosulfate 4-10 parts, Chlorococcum 4-10 parts, diopside 5-15 parts and sepiolite 10-20 parts, it is well mixed, extruding
It is granulated, that is, obtains the mercury contaminated soil renovation agent.
The beneficial effects of the invention are as follows:
(1) renovation agent disposal ability of the invention is strong, will not produce secondary pollution, realizes and is carried out effectively by mercury in soils
It is passivated and polluted soil is effectively repaired while fixed, so that the mercury activity in soil significantly reduces, repairs
The mercury concentration of soil meets the requirement of national second grade soil quality standard afterwards, and there is good economic benefit and extensive society to imitate
Benefit.
(2) each low raw-material cost of the invention, preparation method is simple, wide market, is adapted to large-scale production.
Embodiment
The principle and feature of the present invention are described below in conjunction with specific embodiment, example is served only for explaining this hair
It is bright, it is not intended to limit the scope of the present invention.
Embodiment 1:
The mercury contaminated soil renovation agent of the present embodiment, is made up of the raw material of following weight:Particle diameter is the oyster shell whiting of 50 mesh
10kg, particle diameter are the kaolin 20kg of 50 mesh, chitosan 5kg, the oyster shell whiting 9kg that particle diameter is 50 mesh, potassium thiosulfate 4kg, green
Ball algae 10kg, diopside 5kg and particle diameter are the sepiolite 20kg of 50 mesh.
The preparation method of above-mentioned mercury contaminated soil renovation agent, comprises the following steps:
Take the raw material of following weight:Particle diameter is that oyster shell whiting 10kg, the particle diameter of 50 mesh are kaolin 20kg, the chitosan of 50 mesh
5kg, particle diameter are the oyster shell whiting 9kg of 50 mesh, potassium thiosulfate 4kg, Chlorococcum 10kg, diopside 5kg and sea that particle diameter is 50 mesh
Afrodite 20kg, it is well mixed, extruder grain, that is, obtains the mercury contaminated soil renovation agent.
Embodiment 2:
The mercury contaminated soil renovation agent of the present embodiment, is made up of the raw material of following weight:Particle diameter is the oyster shell whiting of 75 mesh
15kg, particle diameter are the kaolin 15kg of 75 mesh, chitosan 10kg, the oyster shell whiting 6kg that particle diameter is 75 mesh, potassium thiosulfate 7kg, green
Ball algae 7kg, diopside 10kg and particle diameter are the sepiolite 15kg of 50 mesh.
The preparation method of above-mentioned mercury contaminated soil renovation agent, comprises the following steps:
Take the raw material of following weight:Particle diameter is that oyster shell whiting 15kg, the particle diameter of 75 mesh are kaolin 15kg, the chitosan of 75 mesh
10kg, particle diameter are the oyster shell whiting 6kg of 75 mesh, potassium thiosulfate 7kg, Chlorococcum 7kg, diopside 10kg and sea that particle diameter is 50 mesh
Afrodite 15kg, it is well mixed, extruder grain, that is, obtains the mercury contaminated soil renovation agent.
Embodiment 3:
The mercury contaminated soil renovation agent of the present embodiment, is made up of the raw material of following weight:Particle diameter is the oyster shell whiting of 100 mesh
20kg, particle diameter are kaolin 10kg, chitosan 15kg, the oyster shell whiting 3kg that particle diameter is 100 mesh, the potassium thiosulfate of 100 mesh
10kg, Chlorococcum 4kg, diopside 15kg and particle diameter are the sepiolite 10kg of 100 mesh.
The preparation method of above-mentioned mercury contaminated soil renovation agent, comprises the following steps:
Take the raw material of following weight:Particle diameter is that oyster shell whiting 20kg, the particle diameter of 100 mesh are that kaolin 10kg, the shell of 100 mesh gathers
Sugared 15kg, particle diameter are that oyster shell whiting 3kg, potassium thiosulfate 10kg, Chlorococcum 4kg, diopside 15kg and the particle diameter of 100 mesh are 100
Purpose sepiolite 10kg, it is well mixed, extruder grain, that is, obtains the mercury contaminated soil renovation agent.
Mercury contaminated soil renovation agent obtained by embodiment 1-3 is used for mercury contaminated soil, it is specific as shown in table 1.
Mercury contaminated soil renovation agent is used for the effect of mercury contaminated soil obtained by the embodiment 1-3 of table 1
As can be seen here, renovation agent disposal ability of the invention is strong, will not produce secondary pollution, realize and enter by mercury in soils
Row is effectively passivated and polluted soil is effectively repaired while fixed, so that the mercury activity significantly drop in soil
Low, the mercury concentration of soil meets the requirement of national second grade soil quality standard after reparation, with good economic benefit and extensively
Social benefit.
The foregoing is only presently preferred embodiments of the present invention, be not intended to limit the invention, it is all the present invention spirit and
Within principle, any modification, equivalent substitution and improvements made etc., it should be included in the scope of the protection.
Claims (8)
1. a kind of mercury contaminated soil renovation agent, it is characterised in that be made up of the raw material of following parts by weight:Oyster shell whiting 10-20 parts,
Kaolin 10-20 parts, chitosan 5-15 parts, oyster shell whiting 3-9 parts, thiosulfate 4-10 parts, Chlorococcum 4-10 parts, diopside 5-
15 parts and sepiolite 10-20 parts.
2. a kind of mercury contaminated soil renovation agent according to claim 1, it is characterised in that by the raw material of following parts by weight
It is made:15 parts of oyster shell whiting, 15 parts of kaolin, 10 parts of chitosan, 6 parts of oyster shell whiting, 7 parts of thiosulfate, 7 parts of Chlorococcum, saturating brightness
15 parts of 10 parts of stone and sepiolite.
3. a kind of mercury contaminated soil renovation agent according to claim 1 or 2, it is characterised in that the thiosulfate is
One or more of mixing in potassium thiosulfate, sodium thiosulfate, magnesium thiosulfate, calcium thiosulfate and ATS (Ammonium thiosulphate)
Thing.
A kind of 4. mercury contaminated soil renovation agent according to claim 1 or 2, it is characterised in that the kaolinic particle diameter
For 50-100 mesh.
A kind of 5. mercury contaminated soil renovation agent according to claim 1 or 2, it is characterised in that the particle diameter of the oyster shell whiting
For 50-100 mesh.
6. a kind of mercury contaminated soil renovation agent according to claim 1 or 2, it is characterised in that the particle diameter of the zeolite is
50-100 mesh.
A kind of 7. mercury contaminated soil renovation agent according to claim 1 or 2, it is characterised in that the particle diameter of the sepiolite
For 50-100 mesh.
8. a kind of preparation method of mercury contaminated soil renovation agent, it is characterised in that comprise the following steps:
Take the raw material of following parts by weight:Oyster shell whiting 10-20 parts, kaolin 10-20 parts, chitosan 5-15 parts, oyster shell whiting 3-9
Part, thiosulfate 4-10 parts, Chlorococcum 4-10 parts, diopside 5-15 parts and sepiolite 10-20 parts, it is well mixed, extruding is made
Grain, that is, obtain the mercury contaminated soil renovation agent.