CN107602996A - Eva film - Google Patents
Eva film Download PDFInfo
- Publication number
- CN107602996A CN107602996A CN201710830301.0A CN201710830301A CN107602996A CN 107602996 A CN107602996 A CN 107602996A CN 201710830301 A CN201710830301 A CN 201710830301A CN 107602996 A CN107602996 A CN 107602996A
- Authority
- CN
- China
- Prior art keywords
- parts
- eva film
- density polyethylene
- low density
- film according
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of environment-friendlythin thin film, more particularly to a kind of eva film.The invention provides following technical scheme:A kind of eva film, its processing formula component are configured to by mass fraction:50 parts -70 parts of ethylene vinyl acetate base co-polymer;10 parts -18 parts of antioxidant;20 parts -25 parts of ultraviolet absorber;15 parts -25 parts of degradation agent;5 parts -8 parts of dispersant;Double 3 parts -5 parts of the stearoylketene amine of N, N ethenylidene;2 parts -4 parts of dihydric alcohol.Using above-mentioned technical proposal, there is provided a kind of good hand touch, reduce the eva film that speed is fast, degraded cost is cheap.
Description
Technical field
The present invention relates to a kind of environment-friendlythin thin film, more particularly to a kind of eva film.
Background technology
Eva film is a kind of environment-friendlythin thin film, is to extrude produced film by being cast by EVA raw materials.Its is degradable.Nothing
Poison is tasteless, and is free of heavy metal.High transparency, softness and tough and tensile.With it is superpower low temperature resistant the characteristics of.
However, the degradation time length of traditional eva film, and finished product has toughness, and feel is poor, and inside is deposited
Particulate matter it is more, cause the finish of film poor.
The content of the invention
In view of the deficienciess of the prior art, the invention provides a kind of good hand touch, reduction speed is fast, degraded cost is cheap
Eva film.
To achieve the above object, the invention provides following technical scheme:A kind of eva film, it is characterised in that it is processed
Recipe ingredient is configured to by mass fraction:50 parts -70 parts of ethylene-vinyl acetate base co-polymer;Antioxidant 10 parts -18
Part;20 parts -25 parts of ultraviolet absorber;15 parts -25 parts of degradation agent;5 parts -8 parts of dispersant;The double stearoylketene amine of N, N ethenylidene
3 parts -5 parts;2 parts -4 parts of dihydric alcohol.
Wherein, antioxidant 2,2- methylene-bis-(4- ethyl -6-6 tert-butyl phenols).
Wherein, ultraviolet absorber 3,5- di-tert-butyl-4-hydroxybenzoic acid cetyl esters.
Using above-mentioned technical proposal, N, the addition of the double stearoylketene amine of N ethenylidenes can eliminate film endoparticle, avoid finished product
Jaundice, while feel is without toughness, it is smooth, promote the finish of finished films to be improved, the characteristic with high transparency.Antioxygen
Agent is 2,2- methylene-bis- from antioxidant(4- ethyl -6-6 tert-butyl phenols)On the one hand it is due to that its is cheap,
Good in oxidation resistance simultaneously, further can prevent finished films to turn to be yellow;Ultraviolet absorber has anti-ultraviolet effect, to prevent
Its aging provides guarantee.
It is further arranged to:Degradation agent includes low density polyethylene (LDPE) or ultra-low density polyethylene, Et-MAH-EA ternarys are total to
Polymers and dispersant.
Wherein, dispersant is TAS-2A lubrication dispersing agents.
Using above-mentioned technical proposal, each component has preferable compatibility in depressant, after it is added in film proportioning,
Preferable compatibility is likewise supplied with, and degradation speed is fast, and degradation effect is obvious.
Embodiment
The present invention is a kind of eva film, and its processing formula component is configured to by mass fraction:Ethylene-vinyl acetate base
50 parts -70 parts of copolymer;10 parts -18 parts of antioxidant;20 parts -25 parts of ultraviolet absorber;15 parts -25 parts of degradation agent;Point
5 parts -8 parts of powder;Double 3 parts -5 parts of the stearoylketene amine of N, N ethenylidene;2 parts -4 parts of dihydric alcohol.Wherein, antioxidant 2,2-
Methylene-bis-(4- ethyl -6-6 tert-butyl phenols).Ultraviolet absorber is 3,5- di-tert-butyl-4-hydroxybenzoic acid cetyls
Ester.Degradation agent includes low density polyethylene (LDPE) or ultra-low density polyethylene, Et-MAH-EA terpolymers and dispersant.It is scattered
Agent is TAS-2A lubrication dispersing agents.Degradation agent includes low density polyethylene (LDPE) or ultra-low density polyethylene, Et-MAH-EA ternarys are total to
Polymers and dispersant.In such scheme, N, the addition of the double stearoylketene amine of N ethenylidenes can eliminate film endoparticle, avoid finished product
Jaundice, while feel is without toughness, it is smooth, promote the finish of finished films to be improved, the characteristic with high transparency.Antioxygen
Agent is 2,2- methylene-bis- from antioxidant(4- ethyl -6-6 tert-butyl phenols)On the one hand it is due to that its is cheap,
Good in oxidation resistance simultaneously, further can prevent finished films to turn to be yellow;Ultraviolet absorber has anti-ultraviolet effect, to prevent
Its aging provides guarantee.Each component has preferable compatibility in depressant, after it is added in film proportioning, is likewise supplied with
Preferable compatibility, and degradation speed is fast, and degradation effect is obvious.
In the embodiment of the present invention 1,50 parts of ethylene-vinyl acetate base co-polymer;2,2- methylene-bis-(4- ethyls -6-
6 tert-butyl phenols)10 parts;20 parts of 3,5- di-tert-butyl-4-hydroxybenzoic acids cetyl ester;15 parts of degradation agent;TAS-2A moistens
Sliding 5 parts of dispersant;Double 3 parts of the stearoylketene amine of N, N ethenylidene;2 parts of dihydric alcohol.
Data after it is detected are as follows:
In the embodiment of the present invention 2,60 parts of ethylene-vinyl acetate base co-polymer;2,2- methylene-bis-(4- ethyl -6-6 uncles
Butylphenol)16 parts;23 parts of 3,5- di-tert-butyl-4-hydroxybenzoic acids cetyl ester;20 parts of degradation agent;TAS-2A lubrications point
6 parts of powder;Double 4 parts of the stearoylketene amine of N, N ethenylidene;3 parts of dihydric alcohol.
Data after it is detected are as follows:
In the embodiment of the present invention 3,70 parts of ethylene-vinyl acetate base co-polymer;2,2- methylene-bis-(4- ethyl -6-6 uncles
Butylphenol)18 parts;25 parts of 3,5- di-tert-butyl-4-hydroxybenzoic acids cetyl ester;25 parts of degradation agent;TAS-2A lubrications point
8 parts of powder;Double 5 parts of the stearoylketene amine of N, N ethenylidene;4 parts of dihydric alcohol.
Data after it is detected are as follows:
Claims (6)
1. a kind of eva film, it is characterised in that its processing formula component is configured to by mass fraction:Ethylene-vinyl acetate base
50 parts -70 parts of copolymer;10 parts -18 parts of antioxidant;20 parts -25 parts of ultraviolet absorber;15 parts -25 parts of degradation agent;Point
5 parts -8 parts of powder;Double 3 parts -5 parts of the stearoylketene amine of N, N ethenylidene;2 parts -4 parts of dihydric alcohol.
2. eva film according to claim 1, it is characterised in that:Described antioxidant is 2,2- methylene-bis-(4-
Ethyl -6-6 tert-butyl phenols).
3. eva film according to claim 1 or 2, it is characterised in that:Described ultraviolet absorber is bis- tertiary fourths of 3,5-
Base -4-HBA cetyl ester.
4. eva film according to claim 1 or 2, it is characterised in that:Described degradation agent includes low density polyethylene (LDPE)
Or ultra-low density polyethylene, Et-MAH-EA terpolymers and dispersant.
5. eva film according to claim 4, it is characterised in that:Described dispersant is TAS-2A lubrication dispersing agents.
6. eva film according to claim 3, it is characterised in that:Described degradation agent include low density polyethylene (LDPE) or
Ultra-low density polyethylene, Et-MAH-EA terpolymers and dispersant.