CN107602061A - A kind of high-quality building template and preparation method thereof - Google Patents
A kind of high-quality building template and preparation method thereof Download PDFInfo
- Publication number
- CN107602061A CN107602061A CN201710945185.7A CN201710945185A CN107602061A CN 107602061 A CN107602061 A CN 107602061A CN 201710945185 A CN201710945185 A CN 201710945185A CN 107602061 A CN107602061 A CN 107602061A
- Authority
- CN
- China
- Prior art keywords
- parts
- building template
- standby
- waterglass
- paraffin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The present invention discloses a kind of high-quality building template and preparation method thereof, is made up of following raw material:Antimony oxide, ceramic wool, sodium metasilicate, hexenoic acid, quartz sand, paraffin, sulfonated-pheno-formoldehyde resin, waterglass, calcium pyrophosphate, magnesium bicarbonate, butyl acrylate, butyl titanate, methyl acetate, titanium oxide and sodium fluoride;The high-quality building template intensity is big, heat resistance is good and sound insulation value is good.
Description
Technical field
The present invention relates to a kind of high-quality building template and preparation method thereof.
Background technology
Building template is a kind of temporary supporting structure, is made by design requirement, makes concrete structure, component by defined
Position, physical dimension shaping, keep its correct position, and bear building template deadweight and act on external loads thereon.Enter
The purpose of row form work engineering, it is to ensure concrete engineering quality and construction safety, accelerating construction progress and reduction engineering cost.It is existing
With the presence of building template insufficient strength it is big, heat-proof quality is not good enough and sound insulation value is not good enough the shortcomings of.
The content of the invention
High-quality build the technical problem to be solved in the present invention is to provide a kind of intensity is big, heat resistance is good and sound insulation value is good
Building mould.
In order to solve the above technical problems, the present invention adopts the following technical scheme that:
A kind of high-quality building template and preparation method thereof, is made up of following raw material:Antimony oxide, ceramic wool, sodium metasilicate,
Hexenoic acid, quartz sand, paraffin, sulfonated-pheno-formoldehyde resin, waterglass, calcium pyrophosphate, magnesium bicarbonate, butyl acrylate, metatitanic acid four
Butyl ester, methyl acetate, titanium oxide and sodium fluoride;The raw material is by following parts by weight proportioning composition:Antimony oxide 12-16
Part, ceramic wool 16-18 parts, sodium metasilicate 18-20 parts, hexenoic acid 10-12 parts, quartz sand 24-28 parts, paraffin 20-22 parts, sulphur methyl
Phenolic resin 10-18 parts, waterglass 12-16 parts, calcium pyrophosphate 20-22 parts, magnesium bicarbonate 12-18 parts, butyl acrylate 16-18
Part, butyl titanate 10-12 parts, methyl acetate 12-14 parts, titanium oxide 10-12 parts and sodium fluoride 12-16 parts.
Further, the raw material is by following parts by weight proportioning composition:12 parts of antimony oxide, 18 parts of ceramic wool, silicon
Sour 20 parts of sodium, 12 parts of hexenoic acid, 28 parts of quartz sand, 22 parts of paraffin, 18 parts of sulfonated-pheno-formoldehyde resin, 16 parts of waterglass, pyrophosphoric acid
22 parts of calcium, 18 parts of magnesium bicarbonate, 18 parts of butyl acrylate, 12 parts of butyl titanate, 14 parts of methyl acetate, 12 parts of titanium oxide and fluorine
Change 16 parts of sodium.
Further, the raw material is by following parts by weight proportioning composition:14 parts of antimony oxide, 17 parts of ceramic wool, silicon
Sour 19 parts of sodium, 11 parts of hexenoic acid, 26 parts of quartz sand, 21 parts of paraffin, 14 parts of sulfonated-pheno-formoldehyde resin, waterglass 12-16 parts, burnt phosphorus
Sour calcium 20-22 parts, magnesium bicarbonate 12-18 parts, butyl acrylate 16-18 parts, butyl titanate 10-12 parts, methyl acetate 12-14
Part, titanium oxide 10-12 parts and sodium fluoride 12-16 parts.
Further, the raw material is by following parts by weight proportioning composition:16 parts of antimony oxide, 16 parts of ceramic wool, silicon
Sour 18 parts of sodium, 10 parts of hexenoic acid, 24 parts of quartz sand, 20 parts of paraffin, 10 parts of sulfonated-pheno-formoldehyde resin, 12 parts of waterglass, pyrophosphoric acid
20 parts of calcium, 12 parts of magnesium bicarbonate, 16 parts of butyl acrylate, 10 parts of butyl titanate, 12 parts of methyl acetate, 10 parts of titanium oxide and fluorine
Change 12 parts of sodium.
Another technical problem to be solved by the present invention is that providing a kind of preparation method of high-quality building template, include following
Step:
1) antimony oxide 12-16 parts, ceramic wool 16-18 parts, sodium metasilicate 18-20 parts and hexenoic acid 10-12 parts are taken, is put into
In mixer, stir;
2) the above-mentioned material to stir is put into heater, temperature rises to 80-100 DEG C, continues 30-50min, standby
With;
3) quartz sand 24-28 parts, paraffin 20-22 parts, sulfonated-pheno-formoldehyde resin 10-18 parts and waterglass 12-16 parts are taken, is put
Enter in reactor, temperature rises to 90-100 DEG C, continues 1-2 hours, standby;
4) calcium pyrophosphate 20-22 parts, magnesium bicarbonate 12-18 parts, butyl acrylate 16-18 parts and butyl titanate 10- are taken
12 parts, it is put into mixer, stirs, it is standby;
5) obtained material in step 2), step 3) and step 4) being put into melting furnace, temperature rises to 200-300 DEG C,
Methyl acetate 12-14 parts, titanium oxide 10-12 parts and sodium fluoride 12-16 parts are added, continues 30-50min, fused mass is made;
6) by obtained fused mass injection building template mould in step 5), conserve 36 hours and be stripped, it is standby;
7) material normal temperature made from step 6) is conserved one week, you can the high-quality building panel of the present invention is made.
Beneficial effects of the present invention are:For the high-quality building template under the mutual cooperation effect of each raw material, it has intensity
Greatly, heat resistance is good and the advantages of sound insulation value is good, has compared with existing building template, in performance significant progressive.
Embodiment
Embodiment 1:
A kind of high-quality building template, the raw material is by following parts by weight proportioning composition:12 parts of antimony oxide, ceramic wool
18 parts, 20 parts of sodium metasilicate, 12 parts of hexenoic acid, 28 parts of quartz sand, 22 parts of paraffin, 18 parts of sulfonated-pheno-formoldehyde resin, 16 parts of waterglass,
22 parts of calcium pyrophosphate, 18 parts of magnesium bicarbonate, 18 parts of butyl acrylate, 12 parts of butyl titanate, 14 parts of methyl acetate, titanium oxide 12
16 parts of part and sodium fluoride.
A kind of preparation method of high-quality building template, includes following steps:
1) 12 parts of 12 parts of antimony oxide, 18 parts of ceramic wool, 20 parts of sodium metasilicate and hexenoic acid are taken, is put into mixer, stirs
Mix uniformly;
2) the above-mentioned material to stir is put into heater, temperature rises to 80-100 DEG C, continues 30-50min, standby
With;
3) 16 parts of 28 parts of quartz sand, 22 parts of paraffin, 18 parts of sulfonated-pheno-formoldehyde resin and waterglass are taken, is put into reactor,
Temperature rises to 90-100 DEG C, continues 1-2 hours, standby;
4) 12 parts of 22 parts of calcium pyrophosphate, 18 parts of magnesium bicarbonate, 18 parts of butyl acrylate and butyl titanate are taken, is put into stirring
In machine, stir, it is standby;
5) obtained material in step 2), step 3) and step 4) being put into melting furnace, temperature rises to 200-300 DEG C,
16 parts of 14 parts of methyl acetate, 12 parts of titanium oxide and sodium fluoride are added, continues 30-50min, fused mass is made;
6) by obtained fused mass injection building template mould in step 5), conserve 36 hours and be stripped, it is standby;
7) material normal temperature made from step 6) is conserved one week, you can the high-quality building panel of the present invention is made.
Embodiment 2:
A kind of high-quality building template, the raw material is by following parts by weight proportioning composition:14 parts of antimony oxide, ceramic wool
17 parts, 19 parts of sodium metasilicate, 11 parts of hexenoic acid, 26 parts of quartz sand, 21 parts of paraffin, 14 parts of sulfonated-pheno-formoldehyde resin, 14 parts of waterglass,
21 parts of calcium pyrophosphate, 15 parts of magnesium bicarbonate, 17 parts of butyl acrylate, 11 parts of butyl titanate, 13 parts of methyl acetate, titanium oxide 11
14 parts of part and sodium fluoride.
A kind of preparation method of high-quality building template, includes following steps:
1) 11 parts of 14 parts of antimony oxide, 17 parts of ceramic wool, 19 parts of sodium metasilicate and hexenoic acid are taken, is put into mixer, stirs
Mix uniformly;
2) the above-mentioned material to stir is put into heater, temperature rises to 80-100 DEG C, continues 30-50min, standby
With;
3) 14 parts of 26 parts of quartz sand, 21 parts of paraffin, 14 parts of sulfonated-pheno-formoldehyde resin and waterglass are taken, is put into reactor,
Temperature rises to 90-100 DEG C, continues 1-2 hours, standby;
4) 11 parts of 21 parts of calcium pyrophosphate, 15 parts of magnesium bicarbonate, 17 parts of butyl acrylate and butyl titanate are taken, is put into stirring
In machine, stir, it is standby;
5) obtained material in step 2), step 3) and step 4) being put into melting furnace, temperature rises to 200-300 DEG C,
14 parts of 13 parts of methyl acetate, 11 parts of titanium oxide and sodium fluoride are added, continues 30-50min, fused mass is made;
6) by obtained fused mass injection building template mould in step 5), conserve 36 hours and be stripped, it is standby;
7) material normal temperature made from step 6) is conserved one week, you can the high-quality building panel of the present invention is made.
Embodiment 3:
A kind of high-quality building template, the raw material is by following parts by weight proportioning composition:16 parts of antimony oxide, ceramic wool
16 parts, 18 parts of sodium metasilicate, 10 parts of hexenoic acid, 24 parts of quartz sand, 20 parts of paraffin, 10 parts of sulfonated-pheno-formoldehyde resin, 12 parts of waterglass,
20 parts of calcium pyrophosphate, 12 parts of magnesium bicarbonate, 16 parts of butyl acrylate, 10 parts of butyl titanate, 12 parts of methyl acetate, titanium oxide 10
12 parts of part and sodium fluoride.
A kind of preparation method of high-quality building template, includes following steps:
1) 10 parts of 16 parts of antimony oxide, 16 parts of ceramic wool, 18 parts of sodium metasilicate and hexenoic acid are taken, is put into mixer, stirs
Mix uniformly;
2) the above-mentioned material to stir is put into heater, temperature rises to 80-100 DEG C, continues 30-50min, standby
With;
3) 12 parts of 24 parts of quartz sand, 20 parts of paraffin, 10 parts of sulfonated-pheno-formoldehyde resin and waterglass are taken, is put into reactor,
Temperature rises to 90-100 DEG C, continues 1-2 hours, standby;
4) 10 parts of 20 parts of calcium pyrophosphate, 12 parts of magnesium bicarbonate, 16 parts of butyl acrylate and butyl titanate are taken, is put into stirring
In machine, stir, it is standby;
5) obtained material in step 2), step 3) and step 4) being put into melting furnace, temperature rises to 200-300 DEG C,
12 parts of methyl acetate 12-14 parts, 10 parts of titanium oxide and sodium fluoride are added, continues 30-50min, fused mass is made;
6) by obtained fused mass injection building template mould in step 5), conserve 36 hours and be stripped, it is standby;
7) material normal temperature made from step 6) is conserved one week, you can the high-quality building panel of the present invention is made.
Experimental example:
Experimental subjects:From the present invention high-quality building template and two pieces of common building templates, be respectively divided into experimental group,
Control group 1 and control group 2.
Experimental method:Test the performance of each group building template.
Experimental result:
As can be seen here, high-quality building template intensity of the invention is big, heat resistance is good and sound insulation value is good, is built with common
Building mould is compared, and has marked improvement in performance.
Beneficial effects of the present invention are:For the high-quality building template under the mutual cooperation effect of each raw material, it has intensity
Greatly, heat resistance is good and the advantages of sound insulation value is good, has compared with existing building template, in performance significant progressive.
Typical case:
Wu, a building engineer, in a construction, Wu, which have purchased a collection of common building template, to be made
With, it is very smooth when just beginning to use, but later building template enters the sun and is exposed to the sun for a long time, and temperature gradually rises, its intensity
Also it is not big enough, the quality of construction is had influence on, later Wu has selected the high-quality building template of the present invention, solved all
Worry, construction carry out very perfect.
The foregoing is only a specific embodiment of the invention, but protection scope of the present invention is not limited thereto, any
The change or replacement expected without creative work, it should all be included within the scope of the present invention.
Claims (1)
- A kind of 1. building template, it is characterised in that:It is made up of following raw material:Antimony oxide, ceramic wool, sodium metasilicate, hexenoic acid, Quartz sand, paraffin, sulfonated-pheno-formoldehyde resin, waterglass, calcium pyrophosphate, magnesium bicarbonate, butyl acrylate, butyl titanate, second Sour methyl esters, titanium oxide and sodium fluoride;The raw material is by following parts by weight proportioning composition:14 parts of antimony oxide, ceramic wool 17 Part, 19 parts of sodium metasilicate, 11 parts of hexenoic acid, 26 parts of quartz sand, 21 parts of paraffin, 14 parts of sulfonated-pheno-formoldehyde resin, 14 parts of waterglass, Jiao 21 parts of calcium phosphate, 15 parts of magnesium bicarbonate, 17 parts of butyl acrylate, 11 parts of butyl titanate, 13 parts of methyl acetate, 11 parts of titanium oxide With 14 parts of sodium fluoride, the preparation method of the building template, comprise the following steps:1) 11 parts of 14 parts of antimony oxide, 17 parts of ceramic wool, 19 parts of sodium metasilicate and hexenoic acid are taken, is put into mixer, stirring is equal It is even;2) the above-mentioned material to stir is put into heater, temperature rises to 80-100 DEG C, continues 30-50min, standby;3) 14 parts of 26 parts of quartz sand, 21 parts of paraffin, 14 parts of sulfonated-pheno-formoldehyde resin and waterglass are taken, is put into reactor, temperature 90-100 DEG C is risen to, continues 1-2 hours, it is standby;4) 11 parts of 21 parts of calcium pyrophosphate, 15 parts of magnesium bicarbonate, 17 parts of butyl acrylate and butyl titanate are taken, is put into mixer In, stir, it is standby;5) obtained material in step 2), step 3) and step 4) is put into melting furnace, temperature rises to 200-300 DEG C, adds 14 parts of 13 parts of methyl acetate, 11 parts of titanium oxide and sodium fluoride, continue 30-50min, fused mass is made;6) by obtained fused mass injection building template mould in step 5), conserve 36 hours and be stripped, it is standby;7) material normal temperature made from step 6) is conserved one week, you can building panel is made.